Xing ware orXingyao (simplified Chinese:邢窑;traditional Chinese:邢窯;pinyin:Xíngyáo) is a type ofChinese ceramics produced inHebei province in north China, most notably during theTang dynasty. Xing ware typically has a white body covered with a clear glaze. It was named afterXingzhou in southern Hebei where it was made; kilns sites have been identified inNeiqiu County as well as inLincheng although Lincheng was not part of Xingzhou during the Tang dynasty.[1] Some Xing wares were fired at a high enough temperature to be consideredporcelain by Western definition, therefore Xing ware may be considered the world's first true porcelain. Xing ware was produced from theNorthern Qi to theSong dynasty, and its production reached it peak during the Tang dynasty. It was supplanted byDing ware during the Song dynasty
White ceramics began to be made in the Xing kilns of northern China during theNorthern dynasties period. The early wares were coarser but improvements were made and the finest of these wares were made during the Tang dynasty. Xing ware was used at the Tang court; sherds of white ceramics bearing theYing (盈, referring to one of the imperial storehouses) orHanlin (翰林) marks were found at the site ofDaming Palace as well as the kiln sites where they were made. A few in Xingtai have theGuan (官, official) mark. In the Tang dynasty treatise on tea,The Classic of Tea,Lu Yu contrasted the white Xing ware with the greenYue ware of Southern China, and compared the colours of Xing ware to those of snow and silver.[3] The white ware became associated with the north while the green ware was associated with the south.[4] Tang writer Li Zhao (李肇) wrote that the Xing ware of Neiqiu was used by the rich and the poor alike, suggesting that there were both fine and coarse types of Xing ware.[5][6] Xing ware was exported to the outside world during the Tang dynasty. Pieces of Xing ware have been found in theBelitung shipwreck, and examples of Xing ware were found commonly enough inIraq to be referred to as the "Samarra-type".[7]
Ding ware produced in the nearby area ofDingzhou appeared to have started by imitating Xing ware during the Tang dynasty. It may be difficult to distinguish white Ding ware from Xing ware, although Xing ware may have a colder bluer tone through its transparent glaze.[8] Ding ware began to eclipse Xing ware during theFive Dynasties, and by the Song dynasty, Ding kilns had replaced Xing as the renown producers of ceramics of northern China.[1]
The locations that produced Xing ware were not identified until 1980 and 1981 when kiln sites were excavated at Ciqun inLincheng County.[9] Later series of excavations have also identified many kiln sites in Neiqiu andXingtai.[10]
The white body of Xing ware may be thinly potted, and fine enough to not require the application of aslip to hide any imperfection or coarseness. The coarser type of Xing ware, however, may have a layer of white slip. The body is usually covered with a thin colourless glaze, but often the glazes of Xing ware have a bluish tinge. The glaze containedmagnesium oxide andphosphorus pentoxide, which reduce glaze dripping and cracking, and give it a whiter and smoother appearance. Xing ware is primarily white, although some early pieces with green glaze, and other later pieces with yellow or black glazes as well assancai have been found.[10]
The Xing kilns were fired with wood rather than coal.Saggars were used to protect the wares during firing. The pieces were fired at a temperature high enough to approach that required for the production of porcelain, although Xing wares are often not quite vitrified enough to produce the glassy or translucent appearance of true porcelain. Such Xing ware may be consideredstoneware by Western definition, but some pieces are true porcelain. This distinction between stoneware and porcelain, however, is not made in China and it is therefore considered porcelain in Chinese terms.[1][11]
| Ancient pottery |  | |
|---|---|---|
| Earthenwares, stonewares and others | ||
| Porcelain | ||
| Decoration | ||
| Kilns, shapes | ||