Aplasticizer (UK:plasticiser) is a substance that is added to a material to make it softer and more flexible, to increase itsplasticity, to decrease itsviscosity, and/or to decreasefriction during its handling in manufacture.
Plasticizers are commonly added topolymers andplastics such asPVC, either to facilitate the handling of the raw material during fabrication, or to meet the demands of the end product's application. Plasticizers are especially key to the usability ofpolyvinyl chloride (PVC), the third most widely used plastic. In the absence of plasticizers, PVC is hard and brittle; with plasticizers, it is suitable for products such asvinyl siding,roofing,vinyl flooring,rain gutters,plumbing, and electric wire insulation/coating.[1]
Plasticizers are also often added toconcrete formulations to make them more workable and fluid for pouring, thus allowing the water contents to be reduced. Similarly, they are often added toclays,stucco,solid rocket fuel, and other pastes prior to molding and forming. For these applications, plasticizers largely overlap withdispersants.
Plasticizers for polymers are either liquids with low volatility or solids. According to 2017 data, the total global market for plasticizers was 7.5 million metric tonnes. In North America the 2017 volume was ~1.01 million metric tonnes and in Europe the figure was 1.35 million metric tonnes, split between various end-use applications with a chemical type trend moving to higher molecular weight (HMW) orthophthalates and alternative types following regulatory issues concerning lower molecular weight (LMW) orthophthalates.
Almost 90% of polymer plasticizers, most commonlyphthalateesters, are used inPVC, giving this material improved flexibility and durability.[2] Other polymers which can contain high loadings of plasticizers includeacrylates andcellulose-type plastics, such ascellulose acetate,nitrocellulose andcellulose acetate butyrate.
It was commonly thought that plasticizers work by embedding themselves between the chains ofpolymers, spacing them apart (increasing the "free volume"),[3][4] or swelling them and thus significantly lowering theglass transition temperature for the plastic and making it softer. It was later shown that the free volume explanation could not account for all of the effects of plasticization.[5] The mobility of a polymer chain is more complex in the presence of plasticizer than what theFlory–Fox equation predicts for a simple polymer chain.
The molecules of plasticizer take control over mobility of the chain - a polymer chain does not show an increase of the free volume around polymer ends. If plasticizer/water creates hydrogen bonds with hydrophilic parts of the polymer, the associated free volume can be decreased.[clarification needed][6]
The effect of plasticizers onelastic modulus is dependent on both temperature and plasticizer concentration. Below a certain concentration, referred to as the crossover concentration, a plasticizer can decrease the modulus of a material. The material's glass transition temperature will decrease, however, at all concentrations. In addition to a crossover concentration, a crossover temperature exists. Below the crossover temperature the plasticizer will also increase the modulus.
Over the last 60 years more than 30,000 different substances have been evaluated for their suitability as polymer plasticizers. Of these, only a small number – approximately 50 – are today in commercial use.[7]
Ester plasticizers are selected based upon cost-performance evaluation. The rubber compounder must evaluate ester plasticizers for compatibility, processibility, permanence and other performance properties. The wide variety of ester chemistries that are in production includesebacates,adipates,terephthalates,dibenzoates,glutarates,phthalates,azelates, and other specialty blends. This broad product line provides an array of performance benefits required for the manyelastomer applications such as tubing and hose products, flooring, wall-coverings, seals and gaskets, belts, wire and cable, and print rolls.
Low to high polarity esters provide utility in a wide range of elastomers includingnitrile,polychloroprene,EPDM,chlorinated polyethylene, andepichlorohydrin. Plasticizer-elastomer interaction is governed by many factors such assolubility parameter,molecular weight, and chemical structure. Compatibility and performance attributes are key factors in developing a rubber formulation for a particular application.[8]
Plasticizers used in PVC and other plastics are often based onesters of polycarboxylic acids with linear or branched aliphatic alcohols of moderate chain length. These compounds are selected on the basis of many critieria including low toxicity, compatibility with the host material, nonvolatility, and expense. Phthalate esters of straight-chain and branched-chain alkyl alcohols meet these specifications and are common plasticizers. Ortho-phthalate esters have traditionally been the most dominant plasticizers, but regulatory concerns have led to the move away from classified substances to non-classified which includes high molecular weight ortho-phthalates and other plasticisers, especially in Europe.
Antiplasticizers arepolymer additives that have effect opposite to those of plasticizers. They increase the modulus while decreasing the glass transition temperature.
phthalate.svg)
Substantial concerns have been expressed over the safety of some polymer plasticizers, especially because some low molecular weight ortho-phthalates have been classified as potentialendocrine disruptors with some developmental toxicity reported.[9][10] Plasticizers can escape plastics due to migration and abrasion of the plastic since they are not bound to the polymer matrix. The "new car smell" is often attributed to plasticizers or their degradation products,[11] however, multiple studies on the makeup of the smell do not find phthalates in appreciable amounts, likely due to their extremely low volatility and vapor pressure.[12]
Bio-based plasticizers have been investigated, such asglycerol triacetate (Triacetin) andacetyltributylcitrate. They are used in niche applications.Epoxidized soybean oil is used broadly as a secondary plasticizer in many vinyl applications.
In theconcrete technology, plasticizers andsuperplasticizers are also called high range water reducers. When added to concrete mixtures, they confer a number of properties including improvedworkability and strength. The strength of concrete is inversely proportional to the amount of water added, i.e., the water-cement (w/c) ratio.[17] In order to produce stronger concrete, less water is added (without "starving" the mix), which makes the concrete mixture less workable and difficult to mix, necessitating the use of plasticizers, water reducers, superplasticizers, fluidizer or dispersants.[18]
Plasticizers are also often used whenpozzolanic ash is added to concrete to improve strength. This method of mix proportioning is especially popular when producing high-strength concrete and fiber-reinforced concrete.
Adding 1-2% plasticizer per unit weight of cement is usually sufficient. In some cases, the addition of plasticizer retards curing.
Plasticizers are commonly manufactured fromlignosulfonates, a by-product from thepaper industry. Superplasticizers have generally been manufactured fromsulfonatednaphthalene condensate or sulfonatedmelamineformaldehyde, although newer products based on polycarboxylic ethers are now available. Traditional lignosulfonate-based plasticisers, naphthalene and melamine sulfonate-based superplasticisers disperse the flocculated cement particles through a mechanism of electrostatic repulsion (seecolloid). In normal plasticisers, the active substances areadsorbed on to the cement particles, giving them a negative charge, which leads to repulsion between particles.Lignin, naphthalene, and melamine sulfonate superplasticisers are organic polymers. The long molecules wrap themselves around the cement particles, giving them a highly negative charge so that they repel each other.
Polycarboxylate ethersuperplasticizer (PCE) or justpolycarboxylate (PC), work differently from sulfonate-based superplasticizers, giving cement dispersion by steric stabilisation. This form of dispersion is more powerful in its effect and gives improved workability retention to the cementitious mix.[19]
Plasticizers can be added towallboardstucco mixtures to improve workability. In order to reduce the energy consumed drying wallboard, less water is added, which makes the gypsum mixture very unworkable and difficult to mix, necessitating the use of plasticizers, water reducers, or dispersants. Some studies also show that too much lignosulfonate dispersant could result in a set-retarding effect. Data showed that amorphous crystal formations occurred that detracted from the mechanical needle-like crystal interaction in the core, preventing a stronger core. The sugars, chelating agents in lignosulfonates such asaldonic acids and extractive compounds are mainly responsible for set retardation. These low range water reducing dispersants are commonly manufactured fromlignosulfonates, a by-product from thepaper industry.
High range superplasticizers (dispersants) have generally been manufactured fromsulfonatednaphthalene condensate, although polycarboxylic ethers represent more modern alternatives. Both of these high range water reducers are used at 1/2 to 1/3 of the lignosulfonate types.[20]
Traditional lignosulfonate andnaphthalene sulfonate-based plasticisers disperse the flocculated gypsum particles through a mechanism of electrostatic repulsion (seeColloid). In normal plasticisers, the active substances areadsorbed on to the gypsum particles, giving them a negative charge, which leads to repulsion between particles. Lignin and naphthalene sulfonate plasticizers are organic polymers. The long molecules wrap themselves around the gypsum particles, giving them a highly negative charge so that they repel each other.[21]
Energetic materialpyrotechnic compositions, especially solidrocket propellants andsmokeless powders for guns, often employ plasticizers to improve physical properties of the propellant binder or of the overall propellant, to provide a secondary fuel, and ideally, to improve specific energy yield (e.g.specific impulse, energy yield per gram of propellant, or similar indices) of the propellant. An energetic plasticizer improves the physical properties of an energetic material while also increasing its specific energy yield. Energetic plasticizers are usually preferred to non-energetic plasticizers, especially for solidrocket propellants. Energetic plasticizers reduce the required mass of propellant, enabling a rocket vehicle to carry more payload or reach higher velocities than would otherwise be the case. However, safety or cost considerations may demand that non-energetic plasticizers be used, even in rocket propellants. The solidrocket propellant used to fuel theSpace Shuttlesolid rocket booster employsHTPB, asynthetic rubber, as a non-energetic secondary fuel.
Here are someenergetic plasticizers used inrocket propellants andsmokeless powders:
Due to thesecondary alcohol groups, NG and BTTN have relatively low thermal stability. TMETN, DEGDN, BDNPF, and BDNPA have relatively low energies. NG and DEGDN have relatively highvapor pressure.[22]