 | This articleusesbare URLs, which are uninformative and vulnerable tolink rot. Please consider converting them tofull citations to ensure the article remainsverifiable and maintains a consistent citation style.Several templates and tools are available to assist in formatting, such asreFill (documentation) andCitation bot (documentation).(August 2022) (Learn how and when to remove this message) |
FLiBe is amolten salt made from a mixture oflithium fluoride (LiF) andberyllium fluoride (BeF2). It is both anuclear reactor coolant and solvent for fertile or fissile material. It served both purposes in theMolten-Salt Reactor Experiment (MSRE) at theOak Ridge National Laboratory.
The 2:1molar mixture forms astoichiometric compound,Li2[BeF4] (lithium tetrafluoroberyllate), which has a melting point of 459 °C (858 °F), a boiling point of 1,430 °C (2,610 °F), and a density of 1.94 g/cm3 (0.070 lb/cu in).
Its volumetricheat capacity, 4540 kJ/(m3·K), is similar to that of water, more than four times that of sodium, and more than 200 times that of helium at typical reactor conditions.[1]Its specificheat capacity is 2414.17 J/(kg·K), or about 60% that of water.[2]Its appearance is white to transparent, with crystalline grains in a solid state, morphing into a completely clear liquid upon melting. However, soluble fluorides such asUF4 andNiF2, can dramatically change the salt's color in both solid and liquid state. This madespectrophotometry a viable analysis tool, and it was employed extensively during the MSRE operations.[3][4][5]
Theeutectic mixture is slightly greater than 50%BeF2 and has a melting point of 360 °C (680 °F).[6] This mixture was never used in practice due to the overwhelming increase in viscosity caused by theBeF2 addition in the eutectic mixture.BeF2, which behaves as a glass, is only fluid in salt mixtures containing enough molar percent ofLewis base. Lewis bases, such as the alkali fluorides, will donate fluoride ions to the beryllium, breaking the glassy bonds which increase viscosity. In FLiBe, beryllium fluoride is able to sequester two fluoride ions from two lithium fluorides in a liquid state, converting it into thetetrafluoroberyllate ion[BeF4]2−.[7]
The chemistry of FLiBe, and otherfluoridesalts, is unique due to the high temperatures at which the reactions occur, the ionic nature of the salt, and the reversibility of many of the reactions. At the most basic level, FLiBe melts and complexes itself through
This reaction occurs upon initial melting. However, if the components are exposed to air they will absorb moisture. This moisture plays a negative role at high temperature by convertingBeF2, and to a lesser extent LiF, into an oxide or hydroxide through the reactions
and
WhileBeF2 is a very stable chemical compound, the formation of oxides, hydroxides, and hydrogen fluoride reduce the stability and inertness of the salt. This leads to corrosion. Its important to understand that all dissolved species in these two reactions cause the corrosion—not just the hydrogen fluoride. This is because all dissolved components alter thereduction potential or redox potential. The redox potential is an innate and measurable voltage in the salt which is the prime indicator of the corrosion potential in salt. Usually, the reaction
is set at zero volts. This reaction proves convenient in a laboratory setting and can be used to set the salt to zero through bubbling a 1:1 mixture of hydrogen fluoride and hydrogen through the salt. Occasionally the reaction:
is used as a reference. Regardless of where the zero is set, all other reactions which occur in the salt will occur at predictable, known voltages relative to the zero. Therefore, if the redox potential of the salt is close to a specific reaction's voltage, that reaction can be expected to be the predominant reaction. Therefore, it is important to keep a salt's redox potential far away from reactions which are undesirable. For example, in a container alloy of nickel, iron, and chromium, the reactions of concern would be the fluorination of container and subsequent dissolution of these metal fluorides. The dissolution of the metal fluorides then alters the redox potential. This process continues until an equilibrium between metals and salt is reached. It is essential that a salt's redox potential be kept as far away from fluorination reactions as possible, and that metals in contact with salt be as far away from the salt's redox potential as possible in order to prevent excessive corrosion.
The easiest method to prevent undesirable reactions is to pick materials whose reaction voltages are far from the redox potential of the salt in the salt's worst case. Some of these materials are tungsten, carbon, molybdenum, platinum, iridium, and nickel. Of all these materials, only two are affordable and weldable: nickel and molybdenum. These two elements were chosen as the main portion ofHastelloy-N, the material of the MSRE.
Altering the redox potential of FLiBe can be done in two ways. First, the salt can be forced by physically applying a voltage to the salt with an inert electrode. The second, more common way, is to perform a chemical reaction in the salt which occurs at the desired voltage. For example, redox potential can be altered bysparging hydrogen and hydrogen fluoride into the salt or by dipping a metal into the salt.
As amolten salt it can serve as acoolant which can be used at high temperatures without reaching a highvapor pressure.Notably, its optical transparency allows easy visual inspection of anything immersed in the coolant as well as any impurities dissolved in it. Unlikesodium orpotassium metals, which can also be used as high-temperature coolants, it does not violently react with air or water. FLiBe salt has lowhygroscopy andsolubility in water.[8]
The lowatomic weight oflithium,beryllium and to a lesser extentfluorine make FLiBe an effectiveneutron moderator. As natural lithium contains ~7.5%lithium-6, which tends toabsorb neutrons producingalpha particles andtritium, nearly purelithium-7 is used to give the FLiBe a smallneutron absorption cross section;[9] e.g. the MSRE secondary coolant was 99.993% lithium-7 FLiBe.[10] When Li-7 does absorb a neutron, it nigh-instantaneously decays via successivebeta- and then alpha decay into a beta particle and two alpha particles.
Beryllium will occasionally disintegrate into two alpha particles and two neutrons when hit by afast neutron. Fluorine has a non-negligible cross section for (α,n) reactions, which needs to be taken into account when calculatingneutronics.[11]
In theliquid fluoride thorium reactor (LFTR) it serves assolvent for thefissile andfertile material fluoride salts, as well as moderator and coolant.
Some other designs (sometimes called molten-salt cooled reactors) use it as coolant, but have conventional solidnuclear fuel instead of dissolving it in the molten salt.
The liquid FLiBe salt was also proposed as a liquid blanket for tritium production and cooling in theARC fusion reactor, a compacttokamak design by MIT.[12]