Solid acid proton conductors: from laboratory curiosities to fuel cell electrolytes
- PMID:17326560
- DOI: 10.1039/b604311a
Solid acid proton conductors: from laboratory curiosities to fuel cell electrolytes
Abstract
The compound CsH2PO4 has emerged as a viable electrolyte for intermediate temperature (200-300 degrees C) fuel cells. In order to settle the question of the high temperature behavior of this material, conductivity measurements were performed by two-point AC impedance spectroscopy under humidified conditions (p[H2O] = 0.4 atm). A transition to a stable, high conductivity phase was observed at 230 degrees C, with the conductivity rising to a value of 2.2 x 10(-2) S cm(-1) at 240 degrees C and the activation energy of proton transport dropping to 0.42 eV. In the absence of active humidification, dehydration of CsH2PO4 does indeed occur, but, in contradiction to some suggestions in the literature, the dehydration process is not responsible for the high conductivity at this temperature. Electrochemical characterization by galvanostatic current interrupt (GCI) methods and three-point AC impedance spectroscopy (under uniform, humidified gases) of CsH2PO4 based fuel cells, in which a composite mixture of the electrolyte, Pt supported on carbon, Pt black and carbon black served as the electrodes, showed that the overpotential for hydrogen electrooxidation was virtually immeasurable. The overpotential for oxygen electroreduction, however, was found to be on the order of 100 mV at 100 mA cm(-2). Thus, for fuel cells in which the supported electrolyte membrane was only 25 microm in thickness and in which a peak power density of 415 mW cm(-2) was achieved, the majority of the overpotential was found to be due to the slow rate of oxygen electrocatalysis. While the much faster kinetics at the anode over those at the cathode are not surprising, the result indicates that enhancing power output beyond the present levels will require improving cathode properties rather than further lowering the electrolyte thickness. In addition to the characterization of the transport and electrochemical properties of CsH2PO4, a discussion of the entropy of the superprotonic transition and the implications for proton transport is presented.
Similar articles
- Platinum-decorated carbon nanotubes for hydrogen oxidation and proton reduction in solid acid electrochemical cells.Thoi VS, Usiskin RE, Haile SM.Thoi VS, et al.Chem Sci. 2015 Feb 1;6(2):1570-1577. doi: 10.1039/c4sc03003f. Epub 2014 Dec 22.Chem Sci. 2015.PMID:29560244Free PMC article.
- Comparative Study of Epoxy-CsH2PO4 Composite Electrolytes and Porous Metal Based Electrocatalysts for Solid Acid Electrochemical Cells.Navarrete L, Yoo CY, Serra JM.Navarrete L, et al.Membranes (Basel). 2021 Mar 11;11(3):196. doi: 10.3390/membranes11030196.Membranes (Basel). 2021.PMID:33799805Free PMC article.
- Structure and Properties of Cs7(H4PO4)(H2PO4)8: A New Superprotonic Solid Acid Featuring the Unusual Polycation (H4PO4).Wang LS, Patel SV, Sanghvi SS, Hu YY, Haile SM.Wang LS, et al.J Am Chem Soc. 2020 Nov 25;142(47):19992-20001. doi: 10.1021/jacs.0c08870. Epub 2020 Nov 12.J Am Chem Soc. 2020.PMID:33180477
- An Overview on the Novel Core-Shell Electrodes for Solid Oxide Fuel Cell (SOFC) Using Polymeric Methodology.Wang RT, Chang HY, Wang JC.Wang RT, et al.Polymers (Basel). 2021 Aug 18;13(16):2774. doi: 10.3390/polym13162774.Polymers (Basel). 2021.PMID:34451313Free PMC article.Review.
- Intermediate temperature proton conductors for PEM fuel cells based on phosphonic acid as protogenic group: a progress report.Steininger H, Schuster M, Kreuer KD, Kaltbeitzel A, Bingöl B, Meyer WH, Schauff S, Brunklaus G, Maier J, Spiess HW.Steininger H, et al.Phys Chem Chem Phys. 2007 Apr 21;9(15):1764-73. doi: 10.1039/b618686f. Epub 2007 Feb 27.Phys Chem Chem Phys. 2007.PMID:17415487Review.
Cited by
- Direct conversion of carbon dioxide and steam into hydrocarbons and oxygenates using solid acid electrolysis cells.Fujiwara N, Tada S, Kikuchi R.Fujiwara N, et al.iScience. 2022 Nov 9;25(11):105381. doi: 10.1016/j.isci.2022.105381. eCollection 2022 Nov 18.iScience. 2022.PMID:36439988Free PMC article.
- A proton conductor electrolyte based on molten CsH5(PO4)2 for intermediate-temperature fuel cells.Chen X, Zhang Y, Ribeiorinha P, Li H, Kong X, Boaventura M.Chen X, et al.RSC Adv. 2018 Jan 30;8(10):5225-5232. doi: 10.1039/c7ra12803g. eCollection 2018 Jan 29.RSC Adv. 2018.PMID:35542448Free PMC article.
- Properties and Applications of Metal Phosphates and Pyrophosphates as Proton Conductors.Colodrero RMP, Olivera-Pastor P, Cabeza A, Bazaga-García M.Colodrero RMP, et al.Materials (Basel). 2022 Feb 9;15(4):1292. doi: 10.3390/ma15041292.Materials (Basel). 2022.PMID:35207833Free PMC article.Review.
- Anhydrous proton conduction at 150 °C in a crystalline metal-organic framework.Hurd JA, Vaidhyanathan R, Thangadurai V, Ratcliffe CI, Moudrakovski IL, Shimizu GK.Hurd JA, et al.Nat Chem. 2009 Dec;1(9):705-10. doi: 10.1038/nchem.402. Epub 2009 Oct 18.Nat Chem. 2009.PMID:21124357
- Stability of Superprotonic CsH2PO4 Hermetically Sealed in Different Environments.Botez CE, Martinez I, Price AD.Botez CE, et al.Materials (Basel). 2022 Jul 17;15(14):4969. doi: 10.3390/ma15144969.Materials (Basel). 2022.PMID:35888435Free PMC article.
LinkOut - more resources
Full Text Sources
Other Literature Sources
Research Materials
Miscellaneous