عمومي خواص |
---|
Pronunciation | /ˈɪtriəm/ IT-ree-əm |
---|
Appearance | silvery white |
---|
|
Yttrium پهدوراني جدول کې |
---|
|
اټومي شمیره(Z) | 39 |
---|
گروپ,پیریود | group 3,period 5 |
---|
بلاک | d-block |
---|
Element category | transition metal |
---|
معياري اټومي وزن (Ar) | کينډۍ:Val[۱] |
---|
Electron configuration | [Kr] 4d1 5s2 |
---|
Electrons per shell | 2, 8, 18, 9, 2 |
---|
فزیکي خواص |
---|
حالت(at STP) | جامد |
---|
دويلې کيدو ټکى | 1799 K (1526 °C, 2779 °F) |
---|
يشنا ټکی | 3203 K (2930 °C, 5306 °F) |
---|
Density near r.t. | 4.472 g/cm3 |
---|
when liquid, at m.p. | 4.24 g/cm3 |
---|
Heat of fusion | 11.42 kJ/mol |
---|
Heat of vaporization | 363 kJ/mol |
---|
Molar heat capacity | 26.53 J/(mol·K) |
---|
Vapor pressureP (Pa) | 1 | 10 | 100 | 1 k | 10 k | 100 k |
---|
at T (K) | 1883 | 2075 | (2320) | (2627) | (3036) | (3607) |
---|
|
اټومي خواص |
---|
Oxidation states | 3, 2, 1 (a weakly basic oxide) |
---|
Electronegativity | Pauling scale: 1.22 |
---|
Ionization energies | - 1st: 600 kJ/mol
- 2nd: 1180 kJ/mol
- 3rd: 1980 kJ/mol
-
|
---|
Atomic radius | empirical: 180 pm |
---|
Covalent radius | 190±7 pm |
---|
Miscellanea |
---|
Crystal structure | hexagonal close-packed (hcp) Hexagonal close packed crystal structure for yttrium |
---|
Speed of sound thin rod | 3300 m/s (at 20 °C) |
---|
Thermal expansion | α, poly: 10.6 µm/(m·K) (atr.t.) |
---|
د تودوخې تېرېدنه | 17.2 W/(m·K) |
---|
Electrical resistivity | α, poly: 596 nΩ·m (atr.t.) |
---|
Magnetic ordering | paramagnetic[۲] |
---|
Magnetic susceptibility(χmol) | +2.15·10−6 cm3/mol (2928 K)[۳] |
---|
Young's modulus | 63.5 GPa |
---|
Shear modulus | 25.6 GPa |
---|
Bulk modulus | 41.2 GPa |
---|
Poisson ratio | 0.243 |
---|
Brinell hardness | 200–589 MPa |
---|
CAS Number | 7440-65-5 |
---|
History |
---|
Naming | afterYtterby (Sweden) and its mineralytterbite (gadolinite) |
---|
Discovery | Johan Gadolin (1794) |
---|
First isolation | Carl Gustav Mosander (1842) |
---|