| عمومي خواص |
|---|
| Pronunciation | /ˈsɪəriəm/ |
|---|
| Appearance | silvery white |
|---|
|
| Cerium پهدوراني جدول کې |
|---|
|
| اټومي شمیره(Z) | 58 |
|---|
| گروپ,پیریود | group n/a,period 6 |
|---|
| بلاک | f-block |
|---|
| Element category | lanthanide |
|---|
| معياري اټومي وزن (Ar) | کينډۍ:Val[۱] |
|---|
| Electron configuration | [Xe] 4f1 5d1 6s2[۲] |
|---|
Electrons per shell | 2, 8, 18, 19, 9, 2 |
|---|
| فزیکي خواص |
|---|
| حالت(at STP) | جامد |
|---|
| دويلې کيدو ټکى | 1068 K (795 °C, 1463 °F) |
|---|
| يشنا ټکی | 3716 K (3443 °C, 6229 °F) |
|---|
| Density near r.t. | 6.770 g/cm3 |
|---|
| when liquid, at m.p. | 6.55 g/cm3 |
|---|
| Heat of fusion | 5.46 kJ/mol |
|---|
| Heat of vaporization | 398 kJ/mol |
|---|
| Molar heat capacity | 26.94 J/(mol·K) |
|---|
Vapor pressure| P (Pa) | 1 | 10 | 100 | 1 k | 10 k | 100 k |
|---|
| at T (K) | 1992 | 2194 | 2442 | 2754 | 3159 | 3705 |
|---|
|
| اټومي خواص |
|---|
| Oxidation states | 4,3, 2, 1 (a mildlybasic oxide) |
|---|
| Electronegativity | Pauling scale: 1.12 |
|---|
| Ionization energies | - 1st: 534.4 kJ/mol
- 2nd: 1050 kJ/mol
- 3rd: 1949 kJ/mol
- (more)
|
|---|
| Atomic radius | empirical: 181.8 pm |
|---|
| Covalent radius | 204±9 pm |
|---|
| Miscellanea |
|---|
| Crystal structure | double hexagonal close-packed (dhcp) Double hexagonal close packed crystal structure for cerium
β-Ce |
|---|
| Crystal structure | face-centered cubic (fcc) Face-centered cubic crystal structure for cerium
γ-Ce |
|---|
| Speed of sound thin rod | 2100 m/s (at 20 °C) |
|---|
| Thermal expansion | γ, poly: 6.3 µm/(m·K) (at r.t.) |
|---|
| د تودوخې تېرېدنه | 11.3 W/(m·K) |
|---|
| Electrical resistivity | β, poly: 828 nΩ·m (at r.t.) |
|---|
| Magnetic ordering | paramagnetic[۳] |
|---|
| Magnetic susceptibility(χmol) | (β) +2450.0·10−6 cm3/mol (293 K)[۴] |
|---|
| Young's modulus | γ form: 33.6 GPa |
|---|
| Shear modulus | γ form: 13.5 GPa |
|---|
| Bulk modulus | γ form: 21.5 GPa |
|---|
| Poisson ratio | γ form: 0.24 |
|---|
| Mohs hardness | 2.5 |
|---|
| Vickers hardness | 210–470 MPa |
|---|
| Brinell hardness | 186–412 MPa |
|---|
| CAS Number | 7440-45-1 |
|---|
| History |
|---|
| Naming | after dwarf planetCeres, itself named after Roman deity of agricultureCeres |
|---|
| Discovery | Martin Heinrich Klaproth,Jöns Jakob Berzelius,Wilhelm Hisinger (1803) |
|---|
| First isolation | Carl Gustaf Mosander (1838) |
|---|
| Mainisotopes of cerium |
|---|
|
| | references | in Wikidata |