USRE46104E1 - Method of making a sandwich-type composite panel having a living hinge and panel obtained by performing the method - Google Patents

Abstract

A method of making a sandwich-type composite panel having a living hinge from a stack of material is provided. The stack includes first and second reinforced thermoplastic skins heated to a softening temperature and a thermoplastic cellular core disposed between the skins. The first skin is stretchable when heated to the softening temperature. A pressure is applied to the stack after the step of heating to form the composite panel. A portion of the composite panel is crushed at a predetermined location simultaneously with the step of applying to locally compact and separate the cellular core at the predetermined location to form two side portions of the panel and a crushed portion of the panel between the two side portions. The first skin stretches during the step of crushing while remaining intact between the two side portions. The skins bond together at the predetermined location to form the living hinge.

Description

TECHNICAL FIELD

This invention relates, in general, to the field of panels having a sandwich-type composite structure with a cellular core and, in particular, to such panels and methods of making such panels so that the panels have a living hinge.

Overview

Sandwich-type panels having cellular cores have very important characteristics because of their light weight and high strength. Conventionally, such panels are constructed by sandwiching a cellular core having low strength characteristics between two skins, each of which is much thinner than the cellular core but has excellent mechanical characteristics.

The prior art discloses a method of making a panel of sandwich-type composite structure having a cellular core in a single processing step. In that method, the panel is made by subjecting a stack of layers of material to cold-pressing in a mold. As shown inFIG. 1, the stack is made up of: at least a first skin made of a stampable reinforced thermoplastics material, a cellular core made of a thermoplastics material, and a second skin also made of a stampable reinforced thermoplastics material. The stack may also include one or more external covering layers made of a woven or non-woven thermoplastic material. The skins are typically pre-heated outside the mold to a softening temperature.

Such a method is particularly advantageous because of the fact that it makes it possible, in a single operation, to generate cohesion and bonding between the various layers of the composite structure as shown inFIG. 2, and to shape the resulting panel while preserving all of the mechanical properties imparted by the cellular-core sandwich structure.

Panels of sandwich-type composition structure having a cellular core have rigidity characteristics sufficient to enable mechanical structures subjected to large stresses to be reinforced structurally without making them too heavy. Such panels are in common use in shipbuilding, aircraft construction, and rail vehicle construction.

To maximize the functionality of such panels, it is known, in particular, that hinges can be added so that the panels can be hinged to other panels. Such hinges are separate parts that are fixed to the panels by gluing, welding, riveting, or some other fastening technique.

Such hinges are fixed to the sandwich-structure composite panels in a separate and subsequent operation, after said panels have been formed. That subsequent operation requires an additional workstation, be it automated or otherwise, which increases, in particular, the manufacturing time and the manufacturing cost of the finished parts.

In addition, the fact that separate external parts are mounted on a composite panel of the sandwich-type is a source of quality defects, and thus adds to the cost of making such panels.

Published U.S. Patent Application 2005/0189674 discloses a method of making a composite panel of sandwich structure provided with a hinge. The panel includes a stack made up of a first skin of a reinforced thermoplastics material, a cellular core made of a thermoplastics material, and a second skin made of a reinforced thermoplastics material. The panel is formed by pressing the stack in a mold. The first and second skins are preheated to a softening temperature. As shown inFIGS. 3 and 4, after the panel has formed, an incision is made at a determined place in the panel so as to cut through one of the first and second skins, and substantially through the entire thickness of the cellular core, while leaving the other skin intact so that it forms a living hinge between two portions of the incised panel.

Other U.S. patent documents related to the present invention include: U.S. Pat. Nos. 5,502,930; 5,915,445; 6,050,630; 6,102,464; 6,435,577; 6,537,413; 6,655,299; 6,682,675; 6,748,876; 6,790,026; 6,682,676; 6,825,803; 6,843,525; 6,890,023; 6,981,863; 7,090,274; 7,909,379; 7,919,031; 8,117,972; 2006/0255611; and 2008/0185866.

One problem associated with living hinges of the prior art panels is that the panels are quite strong but the living hinges may not be strong enough during extended use. Also, the cost of making such living hinges may be significant on a mass production basis as additional process steps may be required to make the living hinges outside of the mold which makes the panels.

SUMMARY OF EXAMPLE EMBODIMENTS

An object of at least one embodiment of the present invention is to provide a low-cost, high volume method of making light-weight and strong sandwich-type composite panels having living hinges and panels obtained by performing the method wherein the resulting living hinges are strong enough so they function properly during extended use without the need for additional materials or additional post processing steps.

In carrying out the above object and other objects of at least one method embodiment of the invention, a method of making a sandwich-type composite panel having a living hinge is provided. The method includes providing a stack including first and second reinforced thermoplastic skins and a thermoplastic cellular core disposed between the skins. The method also includes heating the skins to a softening temperature wherein the first skin is stretchable when heated to the softening temperature. The method further includes applying a pressure to the stack after the step of heating to form the composite panel. The method still further includes crushing a portion of the composite panel at a predetermined location simultaneously with the step of applying to locally compact and separate the cellular core at the predetermined location to form two side portions of the panel and a crushed portion of the panel between the two side portions. The first skin stretches during the step of crushing while remaining intact between the two side portions. The first and second skins are bonded together at the predetermined location to form the living hinge between the two side portions.

Further in carrying out the above object and other objects of at least one method embodiment of the present invention, a method of making a carpeted sandwich-type composite panel having a living hinge is provided. The method includes providing a stack including first and second reinforced thermoplastic skins, a thermoplastic cellular core disposed between the skins and a thermoplastic covering layer for covering the second skin. The method also includes heating the skins to a softening temperature wherein the first skin is stretchable when heated to the softening temperature. The method further includes applying a pressure to the stack after the step of heating to form the carpeted composite panel. Finally, the method includes crushing a portion of the composite panel at a predetermined location simultaneously with the step of applying to locally compact and separate the cellular core at the predetermined location to form two side portions of the panel and a crushed portion of the panel between the two side portions. The first skin stretches during the step of crushing while remaining intact between the two side portions, The covering layer and the first and second skins at the predetermined location are bonded together to form the living hinge between the two side portions.

The first and second skins may be chemically bonded to each other at the predetermined location to form the living hinge.

The covering layer may be a resin carpet for covering the second skin. The resin may be polypropylene.

The cellular core may be a honeycomb core.

Each or one of the skins may be fiber reinforced.

The thermoplastic of the skins, the carpet and the core may be polypropylene.

The panel may have a thickness in the range of 5 to 25 mm.

The living hinge may have a thickness less than 3 mm, such as 2 mm or less.

At least one of the skins may be a woven skin such as a woven polypropylene skin.

At least one of the skins may be a woven polypropylene skin.

The pressure may lie in a range including 10×10⁵Pa to 30×10⁵Pa.

Further in carrying out the above object and other objects of at least one carpeted panel embodiment of the present invention, a carpeted panel of a composite-type composite structure is made by performing one of the above-noted methods. The panel includes a stack having a first skin of a reinforced thermoplastic material, a cellular core of a thermoplastic material, a second skin of a reinforced thermoplastic material and a covering layer of a thermoplastics material. The panel also includes a living hinge defined by the crushed portion.

Still further in carrying out the above object and other objects of at least one panel embodiment of the present invention, a panel of sandwich-type composite structure is made by performing another one of the above-noted methods. The panel includes a stack having a first skin of a reinforced thermoplastics material, a cellular core of a thermoplastics material, and a second skin of a reinforced thermoplastics material. The panel also includes a living hinge defined by the crushed portion.

Other technical advantages will be readily apparent to one skilled in the art from the following figures, descriptions and claims. Moreover, while specific advantages have been enumerated, various embodiments may include all, some or none of the enumerated advantages.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a side sectional view showing various separate layers of a prior art stack of thermoplastic-based layers of material;

FIG. 2 is a top perspective sectional view, of the stack ofFIG. 1 after low-pressure, cold compression molding;

FIGS. 3 and 4 are side views, partially broken away and in cross section, of a prior art sandwich-type composite panel having a living hinge and method of making the living hinge;

FIG. 5 is an environmental view, partially broken away, showing a pair of carpeted sandwich-type composite panels having living hinges constructed in accordance with at least one method embodiment of the present invention;

FIG. 6 is a side view, partially broken away and in cross section, of a stack of material positioned between two halves of a mold in its open position wherein one of the mold halves has a protrusion or relief for forming the living hinge of the panel;

FIG. 7 is a view similar to the view ofFIG. 6 but with the mold in its closed position to form the panel and its living hinge in accordance with at least one method embodiment of the invention;

FIG. 8 is an enlarged view of a portion of the view ofFIG. 7 to show the living hinge ofFIG. 7 in detail;

FIG. 9 is an enlarged view, similar to the view ofFIG. 8, but showing a second embodiment of a living hinge wherein one of the skins has been pushed into and merged with the other skin to form a living hinge of reduced thickness as compared to the living hinge ofFIG. 8; and

FIGS. 10a-10f are side views, partially broken away and in cross section, of various alternative sizes and shapes for the crushing protrusion of the mold ofFIGS. 6-9.

DETAILED DESCRIPTION

As required, detailed embodiments of the present invention are disclosed herein; however, it is to be understood that the disclosed embodiments are merely exemplary of the invention that may be embodied in various and alternative forms. The figures are not necessarily to scale; some features may be exaggerated or minimized to show details of particular components. Therefore, specific structural and functional details disclosed herein are not to be interpreted as limiting, but merely as a representative basis for teaching one skilled in the art to variously employ the present invention.

Referring now to theFIGS. 5-9, in general, one embodiment of a method of making a sandwich-type composite panel, two of which are generally indicated at10 inFIG. 5, having a livinghinge12 is provided. The hingedpanels10 are shown inFIG. 5 as forming separate parts of an automotive vehicle load floor, generally indicated at13. However, it is to be understood that one ormore panels10 constructed in accordance with at least one embodiment of the present invention may be used in a wide variety of environments. Thepanels10 inFIG. 5 are shown carpeted but at least one embodiment of the invention does not require such carpeting.

The method may include providing a stack of material, generally indicated at14 inFIG. 6, located or positioned within a mold, generally indicated at22. Thestack14 includes first and second reinforcedthermoplastic skins16 and18, respectively, a thermoplasticcellular core20 disposed between theskins16 and18 and a covering layer of21 thermoplastics material which covers thesecond skin18. Theskins16 and18 are heated typically outside of themold22 to a softening temperature. Themold22 is preferably a low pressure compression mold which performs a thermo compression process on thestack14. Themold22 has an upper mold half orpart24 and a lower mold half orpart26. Theupper mold part24 has aprotrusion28 extending towards thelower mold half26 for crushing purposes as described in detail below.

Thefirst skin16 is stretchable when heated to the softening temperature and stretches when a pressure is applied to thestack14 by the inner mold surfaces of the mold halves24 and26 including the outer surface of theprotrusion28 within themold22 to form thecomposite panel10 with the livinghinge12. Aportion32 of the composite panel10 (FIG. 6) is crushed at a predetermined location simultaneously with the step of applying the pressure to locally compact and separate thecellular core20 at the predetermined location to form twoside portions34 and36 (FIG. 7) of thepanel10 and the crushedportion32 therebetween. Thefirst skin16 stretches during the step of crushing while remaining intact between the twoside portions34 and36. The first andsecond skins16 and18, respectively, of the crushedportion32 are chemically bonded together to form the livinghinge12 at the predetermined location between the twoside portions34 and36.

As previously mentioned, thestack14 ofFIG. 6 may also preferably include thethermoplastic covering layer21 for covering thesecond skin18 when making a carpeted panel such as thecarpeted panels10 ofFIG. 5. While not shown, thestack14 may also include a second thermoplastic covering layer for at least partially covering thefirst skin16 so that a cover portion of the resultingpanel10 is carpeted on its top and bottom surfaces

Thecovering layer21 may be a resin carpet and the resin may be polypropylene. One side or both sides of the cover portion of thepanel10 may be covered with an outer covering layer made of a woven or non-woven material (typically of the carpet type).

Thecellular core20 may be a honeycomb core. In this example, thecellular core20 is an open-celled structure of the type made up of tubes or of a honeycomb, and it is made mainly of polyolefin and preferably of polypropylene. It is also possible to use a cellular structure having closed cells of the foam type.

Each of theskins16 and18 may be fiber reinforced. The thermoplastic of theskins16 and18, one or more covering layers21 and the core20 may be polypropylene. At least one of theskins16 and18 may be a woven skin, such as polypropylene skin. The first andsecond skins16 and18 may be reinforced with fibers, e.g., glass fibers, carbon fibers or natural fibers. The first andsecond skins16 and18 may advantageously be made up of woven glass fiber fabric and of a thermoplastics material.

The resultingpanel10 may have a thickness in the range of 5 to 25 mm and the crushed portion of thepanel10 may have a thickness less than 3 mm such as 2 mm or less.

In one example method of making such a panel, thepanel10 is formed by pressing thestack14 in the low-pressure, cold-formingmold22, thestack14 being made up of thefirst skin16, thecellular core20, and thesecond skin18. The stack may be pressed at a pressure lying in therange 10×10⁵Pa. to 30×10⁵Pa. The first andsecond skins16 and18 are preferably pre-heated in the method to make them malleable and stretchable. Advantageously, in order to soften the first and second skins, heat is applied to a pre-assembly constituted by the stack made up of at least thefirst skin16, of thecellular core20, and of thesecond skin18 so that, while thepanel10 is being formed in themold22, the first andsecond skins16 and18 have a forming temperature lying approximately in the range 160° C. to 200° C., and, in this example, about 180° C.

Theprotrusion28 may have other shapes in cross section as shown inFIGS. 10a-10f in order for themold22 to perform the crushing step during the pressure application step.

While exemplary embodiments are described above, it is not intended that these embodiments describe all possible forms of the invention. Rather, the words used in the specification are words of description rather than limitation, and it is understood that various changes may be made without departing from the spirit and scope of the invention. Additionally, the features of various implementing embodiments may be combined to form further embodiments of the invention.

Claims (18)

What is claimed is:

1. A method of making a sandwich-type composite panel having a living hinge, the method comprising:

providing a stack including first and second reinforced thermoplastic skins and a thermoplastic cellular core disposed between the skins;

heating the skins to a softening temperature wherein the first skin is stretchable when heated to the softening temperature;

applying a pressure to the stack after the step of heating to form the composite panel; and

crushing a portion of the composite panel at a predetermined location simultaneously with the step of applying pressure to locally compact and separate the cellular core at the predetermined location to form two side portions of the panel and a crushed portion of the panel between the two side portions, the first skin stretching during the step of crushing while remaining intact between the two side portions, the first and second skins at the predetermined location bonding together to form the living hinge between the two side portions.

2. The method as claimed inclaim 1, wherein the first and second skins are chemically bonded to each other at the predetermined location to form the living hinge.

3. The method as claimed inclaim 1, wherein the stack includes a thermoplastic covering layer for covering the second skin.

4. The method as claimed inclaim 3, wherein the covering layer is a resin carpet.

5. The method as claimed inclaim 4, wherein the resin is polypropylene.

6. The method as claimed inclaim 1, wherein the cellular core is a honeycomb core.

7. The method as claimed inclaim 1, wherein each of the skins is fiber reinforced.

8. The method as claimed inclaim 1, wherein the thermoplastic of the skins and the core is polypropylene.

9. The method as claimed inclaim 1, wherein the panel has a thickness in the range of 5 to 25 mm.

10. The method as claimed inclaim 1, wherein at least one of the skins is a woven skin.

11. The method as claimed inclaim 1, wherein at least one of the skins is a woven polypropylene skin.

12. The method as claimed inclaim 1, wherein the pressure lies in a range including 10×10⁵Pa to 30×10⁵Pa.

13. The method as claimed inclaim 9, wherein the living hinge has a thickness less than 3 mm.

14. The method as claimed inclaim 13, wherein the living hinge has a thickness of 2 mm or less.

15. A method of making a carpeted sandwich-type composite panel having a living hinge, the method comprising:

providing a stack including first and second reinforced thermoplastic skins, a thermoplastic cellular core disposed between the skins and a thermoplastic covering layer for covering the second skin;

heating the skins to a softening temperature wherein the first skin is stretchable when heated to the softening temperature;

applying a pressure to the stack after the step of heating to form the carpeted composite panel; and

crushing a portion of the composite panel at a predetermined location simultaneously with the step of applying pressure to locally compact and separate the cellular core at the predetermined location to form two side portions of the panel and a crushed portion of the panel between the two side portions, the first skin stretching during the step of crushing while remaining intact between the two side portions, the covering layer and first and second skins at the predetermined location bonding together to form the living hinge between the two side portions.

16. The method as claimed inclaim 15, wherein the covering layer and first and second skins are chemically bonded to each other at the predetermined location to form the living hinge.

17. The method as claimed inclaim 15, wherein the thermoplastic of the skins, the covering layer and the core is polypropylene.

18. The method as claimed inclaim 15, wherein the living hinge has a thickness less than 3 mm.