This application is a continuation-in-part of new earlier application Ser. No. 441,984 filed Feb. 13, 1974, now abandoned.
BACKGROUND OF THE INVENTIONThis invention concerns improvements in or relating to glass compositions, fiber made therefrom and cementitious materials including such fiber as reinforcement.
Glass compositions, containing beryllia, magnesia, strontium oxide, titania, cadmium oxide or zirconia have been known for many years (see, for example, U.K. Patent Specification Nos. 595,498 and 791,374 and U.S. Pat. No. 2,640,784). From these, refractory glass fiber and other articles may be made.
More recently, U.S. Pat. No. 2,877,124 discloses compositions which are chemically durable, have a low liquidus temperature and slow devitrification and are capable of being formed into fibers by rotary spinning and attenuation of the strands so obtained. These compositions comprise, in weight percent;
______________________________________ SiO.sub.2 50 to 65 Al.sub.2 O.sub.3 0 to 8 CaO 3 to 4 MgO 0 to 10 Na.sub.2 O, K.sub.2 O, L.sub.2 O 10 to 20 B.sub.2 O.sub.3 5 to 15 TiO.sub.2 0 to 8 ZrO.sub.3 0 to 8 BaO 0 to 8 Fe.sub.2 O.sub.3 0 to 12 MnO 0 to 12 ZnO 0 to 2 ______________________________________
And preferably are essentially free from at least a majority of the six last-named components.
U.S. Pat. No. 3,127,277 discloses glasses of high modulus of elasticity, of composition, in weight percent:
______________________________________ SiO.sub.2 45-60 CaO 9-19 MgO 6-10 BeO 7-12 ZrO.sub.2 1-3 Li.sub.2 O up to 4 TiO.sub.2 2-10 CeO.sub.2 up to 4 ______________________________________
Optionally including other ingredients such as Fe2 O3 and Al2 O3.
U.S. Pat. No. 3,817,764 disloses glass compositions, in weight percent:
______________________________________ SiO.sub.2 49-57 Al.sub.2 O.sub.3 3-5 B.sub.2 O.sub.3 6-12 Na.sub.2 O 18-20 CaO 0-2 TiO.sub.2 9-12 ZrO.sub.2 0-7 Fe.sub.2 O.sub.3 0-0.5 LiO.sub.2 0-1 ______________________________________
and states that glass fibers which are especially water durable, and can be made from these compositions by rotary or centrifugal spinning.
Finally, U.S. Pat. No. 3,861,925 discloses alkali resistant fiberizable glass compositions which are zirconia free and consist essentially of, in weight percent.
______________________________________ SiO.sub.2 55-65 TiO.sub.2, La.sub.2 O.sub.2 or CeO.sub.2, 12-25 CaO 4-6 Na.sub.2 O, 12-18 K.sub.2 O 0-3 ______________________________________
Despite such disclosures, however, there is still a need for glasses having improved chemical durability -- in particular improved resistance to alkali attack, for example for use in reinforcing cementitious articles.
DETAILED DESCRIPTION OF THE INVENTIONAccording to the present invention, a glass composition consists essentially, by weight of the composition, of:
from 50 to 75% Silica
from 10 to 25% R2 O
from .[.1.]. .Iadd.7 .Iaddend.to 15% Titania
from 1 to 20% Zirconia
up to 20% Rare Earth Oxide
from 0 to 20% Boric Oxide
from 0 to 10% R1 O
from 0 to 1% Fluorine (as fluoride)
from 0 to 2% Al2 O3
where R2 O is sodium oxide, potassium oxide or a mixture of both, optionally including up to 5% by weight lithium oxide (based on the total composition), and R1 O is MgO, CaO, BaO or SrO, or a mixture of two or more thereof.
A preferred glass composition consists essentially, by weight of the compositions, of:
from 50 - 58% Silica
from 11 - - % R2 O
from 8 - 10% Titania
from 10 - 14% Zirconia
from 0.8 - 15% Rare Earth Oxide
from 0.5 - 4% Boric Oxide
from 0.1 - 6% R1 O
from 0 - 1% Fluorine (as fluoride)
from 0.1 - 0.4% Chlorine (as chloride)
Wherein R2 O is selected from the group consisting of Na2 O, K2 O and mixtures of the two and mixtures thereof additionally containing up to 1% by weight lithium oxide (based on the total weight of the composition) and R1 O is selected from the group consisting of MgO, CaO, BaO, SrO and mixtures of two or more thereof.
The compositions preferably comprise at least 20% by weight of ZrO.sub. 2 and TiO2 together, and at least 23% by weight of ZrO.sub. 2, TiO2 and rare earth oxide together.
The composition preferably contains not more than 30%, and more preferably not more than 25% by weight, of titania and zirconia together, and not more than 7% by weight of R1 O. The R1 O and F may be deliberately added to the composition, within the ranges of content stated above. If Li2 O is used in place of fluorine then comparable amounts of Al2 O3 will be added (necessarily but not desirably) by way of the raw materials commercially available at present. Al2 O3 should not exceed more than 2% by weight of the composition.
The inclusion of a rare earth (metal) oxide imparts to the glass compositions of this invention a degree of alkali resistance not, in general, exhibited by glass compositions of otherwise similar formulation. At least 0.8% rare earth oxide is present in the composition.
The rare earth oxide used may be any of the naturally occurring ones, preferably ceric oxide, or a mixture of naturally occurring rare earth oxides. The term "naturally occurring rare earth oxide mixture" is well recognised in the Art used in the following examples according to its accepted meaning denoting a mixture of rare earth metal compounds (mainly the oxides) in which such metals are present in relative abundancies approximately equivalent to their naturally occurring relative abundancies. Such mixtures are constituted by, for example, a natural rare earth ore such as bastnaesite or monoazite; the term is also used as herein to denote such an ore which has been treated to remove undesirable components such as carbonate, phosphate or fluoride ions. When bastnaesite, for example, is treated to remove such ions, the rare earth metal content remains constant, and remains proportional to the naturally occurring abundance.
The detrimental effect of excessive amounts of certain ions, such as phosphate or fluoride, in glass making is well known to those skilled in the art, so as suitable naturally occurring rare earth oxide mixture can be prepared by taking an ore such as bastnaesite or monazite and pre-treating it in an appropriate manner.
It is already well known that the chemical properties of rare earth metals and their oxides are markedly similar; I would expect that most, if not all, of the rare earth oxides -- and particularly any mixture thereof containing cerium -- give a result closely similar to the results obtained from compositions containing cerium oxide as the sole rare earth oxide.
The glass compositions of this invention consist essentially of the ingredients specified above, but may be found to include also a trace amount, i.e. up to about 1%, of phosphate and/or of chlorine present as the chloride.
Preferred embodiments of the invention, embodying the above principles, are illustrated in the following Examples 1 to 5; comparative results for a modified prior art composition are illustrated in Example A.
EXAMPLE 1A glass of the following composition was prepared and was melt drawn at 1230° C:
______________________________________ Silica 50% weight Sodium Oxide 10% Lithium Oxide 1% Boric Oxide 3% Titania 10% Zirconia 10% Cerium Oxide 15% Sodium Fluoride 1% ______________________________________
The glass fibers obtained exhibited a tensile strength of 1.36 GPa (Giga Pascals - equivalent to GN/m2).
Fibers of this composition were boiled in saturated Ca(OH)2 for 4 hours, washed successively with water, 1% hydrochloric acid (1 minute), water, and acetone, and then dried. The strength of the fiber was increased to 1.55 GPa.
EXAMPLES 2 TO 5Glasses of various compositions as set forth in the following table were melt drawn, and the tensile strength thereof was determined before and after alkali treatment, with the results shown.
______________________________________ Composition Examples % by weight 2 3 4 5 ______________________________________ SiO.sub.2 58 56 58 58 Li.sub.2 O -- -- -- -- Na.sub.2 O 13 12 14 13 TiO.sub.2 9 8 10 7 ZrO.sub.2 12 13 13 14 B.sub.2 O.sub.3 3 3 4 0.5 CaO -- 6 -- 4 BaO -- -- 0.1 0.6 CeO.sub.2 5 2 -- -- Naturally occurring Rare Earth Oxide mixture* -- -- 0.8 2.5 F -- -- -- -- Cl -- -- 0.1 0.4 Tensile Strength (GPa) before alkali treatment 1.22 1.04 1.07 1.25 Tensile Strength (GPa) after alkali treatment 0.87 0.63 0.73 1.19 ______________________________________ *Obtained by treating a bastnaesite ore to remove carbonate and fluoride ions.
The alkali resistance of the above compositions make them eminently suitable for use as fibrous reinforcement in cementitious materials. They may be used in an amount up to 30% by weight of the total dry weight of cementitious materials, preferably in an amount of from 5 to 10% by weight.
COMPARATIVE EXAMPLE AI. A composition was made as disclosed in Example 2 of U.S. Pat. No. 2,877,124 (which Example contains the maximum proportions of TiO2 and ZrO2 exemplified in this patent), and to this composition an addition of 4% by weight of CeO2 was made, 4% CeO2 being the maximum content of rare earth oxide mentioned in U.S. Pat. No. 3,127,277, to provide the following glass composition:
______________________________________ SiO.sub.2 50.98 weight % B.sub.2 O.sub.3 6.04 Al.sub.2 O.sub.3 2.38 Fe.sub.2 O.sub.3 2.97 MgO 3.60 CaO 7.40 BaO 2.80 Na.sub.2 O 12.90 TiO.sub.2 2.97 ZrO.sub.2 3.40 CeO.sub.2 4.00 ______________________________________
At first instance it might appear that this modified composition should provide fibers of an alkali resistance equivalent to that obtained by use of the present invention. I have found, however, that such similar properties are not obtained as demonstrated below.
Fibers were made from this composition, and were tested for alkali resistance, by the methods described in the preceding Examples.
The following results were obtained:
Strength before alkali treatment 0.99 GPa
Strength after alkali treatment 0.64 GPa
II. A composition as in (I) above, but containing no rare earth oxide was formed into fibers, and these were tested, by the same methods, with the following results:
Stength before alkali treatment 1.24 GPa
Strength after alkali treatment 0.48 GPa
The fibers exemplified in Examples 1 to 5 have strengths after alkali treatment of from 1.04 to 1.55 GPa, which clearly shows that fibers produced from these compositions exhibit considerably greater strengths after alkali treatment than can fibers produced by the modification referred to above. That is, fibers made in accordance with this invention have greater alkali resistance.
III. As a further comparison, Example 2 was repeated using 4% ceric oxide; this gave fibers having a strength of 0.94 GPa before treatment with alkali, and 0.90 GPa after alkali treatment. Without any ceric oxide a similar composition gives a strength of 0.66 GPa before treatment and 0.57 after alkali treatment. Thus, the percentage decline in the strength of fibers made from Example 2 composition, with or without ceric oxide, is less than for an Example A (I) composition with ceric oxide.
Obviously, modifications may be made in the compositions of this invention as exemplified above. It should be noted, however, that certain compositions within the composition ranges of this invention may not necessarily exhibit an especially marked increase in alkali resistance over similar compositions not containing rare earth oxide, or may exhibit a tendency to devitrify during fibre drawing; accordingly, the considerations and adjustments already used in glass technology to account for these difficulties should be applied to the invention for such compositions, not exemplified above, as come within the scope of the invention.