US20210177620A1 - Porous composite biomaterials and related methods - Google Patents

Abstract

A composite material for use, for example, as an orthopedic implant, that includes a porous reinforced composite scaffold that includes a polymer, reinforcement particles distributed throughout the polymer, and a substantially continuously interconnected plurality of pores that are distributed throughout the polymer, each of the pores in the plurality of pores defined by voids interconnected by struts, each pore void having a size within a range from about 10 to 500 μm. The porous reinforced composite scaffold has a scaffold volume that includes a material volume defined by the polymer and the reinforcement particles, and a pore volume defined by the plurality of pores. The reinforcement particles are both embedded within the polymer and exposed on the struts within the pore voids. The polymer may be a polyaryletherketone polymer and the reinforcement particles may be anisometric calcium phosphate particles.

Description

• This application is a continuation of and claims priority to U.S. patent application Ser. No. 14/078,614, filed on Nov. 13, 2013, entitled “Porous Composite Biomaterials and Related Methods,” now patented, which is a continuation of U.S. patent application Ser. No. 12/039,666, filed on Feb. 28, 2008, entitled “Porous Composite Biomaterials and Related Methods,” which claims the benefit of U.S. Provisional Patent Application Ser. No. 60/904,098, filed on Feb. 28, 2007, entitled “Reinforced Porous Polymer Scaffolds,” and U.S. Provisional Patent Application Ser. No. 60/939,256, filed on May 21, 2007, entitled “Interbody Spinal Fusion Cages Containing Anisometric Calcium Phosphate Reinforcements and Related Methods,” each of which is incorporated herein by reference in its entirety.
FIELD OF THE DISCLOSURE
• The present disclosure relates generally to composite biomaterials and more particularly to porous composite biomaterials and related methods.
BACKGROUND
• Natural bone grafts such as autogenous bone grafts (autografts) are commonly used in procedures for repairing or replacing bone defects because they provide good structural support and osteoinductivity. Natural bone grafts involve removing or harvesting tissue from another part of a host's body (e.g., typically from the iliac crest, hip, ribs, etc.) and implanting the harvested tissue in the defect site. Not only do these grafts require an added surgical procedure needed to harvest the bone tissue, these grafts have limitations, including for example, transplant site morbidity. One alternative to autografts is allografts, which involve removing and transplanting tissue from another human (e.g., from bone banks that harvest bone tissue from cadavers) to the defect site. However, allografts are known to induce infection and immunotoxicity, suffer from limited supply and variability, and have a lessened effectiveness because the cells and proteins that promote bone growth are lost during the harvesting process (e.g., during cleansing and disinfecting process). Demineralized bone matrix (DBM) is typically used to induce bone growth at defect sites, but DBM lacks the mechanical properties (e.g., stiffness, strength, toughness, etc.) necessary to be considered a viable option for load-bearing applications.
• Synthetic bone substitute materials have been researched in the treatment of diseased bone (e.g., osteoporosis), injured bone (e.g., fractures), or other bone defects in lieu of natural bone grafts. Synthetic bone substitutes are viable alternatives to the more traditional methods described above. However, synthetic substitute materials used to repair diseased bones and joints should function or perform biologically and mechanically (i.e., as the structural support role of the bone itself) by, for example, mimicking the density and overall physical structure of natural bone to provide a framework for ingrowth of new tissue. One type or application of a synthetic bone substitute is a scaffold, which provides support for bone-producing cells. Scaffolds may be biodegradable, which degrade in vivo, or they may be non-biodegradable to provide permanent implant fixation (e.g., spinal fusion cages). In addition, scaffolds are typically biocompatible, and some may be bioactive, bioresorbable, osteoconductive, and/or osteoinductive. The shapability, deliverability, cost, and ability to match the mechanical properties of the surrounding host tissue are other factors that vary among different types of scaffolds and other bone substitutes.
• Problems may arise when there is a mechanical mismatch between the bone substitute and the surrounding tissue. For example, metallic implants and dense ceramics have mechanical properties that are typically an order of magnitude greater than the bone tissue. As a result, a stiff metal bone substitute implant acts to “shield” the adjacent bone tissue from mechanical stresses, resulting in a weakened bone at the bone-implant interface. Furthermore, efforts to utilize porous ceramics or polymer bone cement in place of stiffer materials have been limited. For example, ceramics possess low fracture toughness, thereby making the orthopedic implant brittle (i.e., susceptible to fracture). Polymers are limited by higher compliance and lower strength, thereby limiting their ability to support physiological load levels. Additionally, conventional orthopedic implant biomaterials are not osteoconductive and bioactive, resulting in a lack of bonding between the implant and the peri-implant tissue.
BRIEF DESCRIPTION OF THE DRAWINGS
• FIG. 1A is a perspective view of an example porous composite material described herein.
• FIG. 1B is a cross-sectional view of a portion of the example porous composite material ofFIG. 1A.
• FIG. 2A-2C are scanning electron micrographs of a portion of the example porous composite material shown in increasing magnification.
• FIGS. 3 is graphical representation of the elastic modulus of example apatite reinforced polymer composites versus the reinforcement volume fraction.
• FIG. 4 shows scanning electron micrograph of a portion of the surface of an example composite material reinforced with calcium phosphate whiskers embedded within and exposed on the surface, and schematically showing the orientation of the whiskers relative to the loading direction of the material or scaffold strut.
• FIG. 5A is a schematic illustration of a known spinal fusion cage inserted between spinal vertebrae.
• FIG. 5B illustrates the example known spinal fusion cage ofFIG. 5A.
• FIG. 6 illustrates another example scaffold described herein.
• FIG. 7 illustrates yet another example scaffold described herein.
• FIG. 8 is a flow diagram illustrating an example process of creating an example composite material apparatus described herein.
DETAILED DESCRIPTION
• In general, the example methods, apparatus, and materials described herein provide a biocompatible, bioactive synthetic porous composite for use as synthetic bone substitute materials. The synthetic composite may provide a synthetic porous scaffold for use an orthopedic implant and/or be injectable via percutaneous or surgical injection to cure in vivo. Because the example composite material is used to form a scaffold or matrix that is used in an implantable device, the descriptions of one or more of these structures may also describe one or more of the other structures. The synthetic porous composites are tailored to mimic biological and mechanical properties of bone tissue for implant fixation, synthetic bone graft substitutes, tissue engineering scaffolds, interbody spinal fusion, or other orthopedic applications. An example porous composite material described herein reduces subsidence and/or bone resorption resulting from mechanical mismatch problems between a synthetic scaffold of an implant device and the peri-implant tissue. Additionally, porosity and/or the pore sizes of the example synthetic composite are tailorable to specific applications to effectively promote the vascularization and growth of bone in the pores and/or void spaces of the example scaffolds, thereby improving bonding between the scaffolds and peri-implant tissue.
• The example composite material or scaffolds are synthesized or made through a process that enables reinforcement particles to be integrally formed with or embedded within polymer matrices. In this manner, the polymer matrices embedded with the reinforcement material provide improved material properties (e.g., stiffness, fatigue strength, and toughness). The reinforcement particles are also exposed on a surface of the matrices, which promotes bioactivity and/or bioresorption. Additionally, the process provides flexibility to tailor the level of reinforcement particles and porosity for a desired application. For example, a porogen material may be used to vary the porosity, while the pore size is tailored by, for example, sieving the porogen to a desired size.
• By varying the volume of the reinforcement particles and the porosity of the example scaffold, the mechanical properties (e.g., stiffness, strength, toughness, etc.) of the example scaffold of the implant device may be tailored to match those of the adjacent peri-implant bone tissue to reduce mechanical mismatch problems. Reducing mechanical mismatch provides a decreased risk of subsidence, stress shielding, bone resorption, and/or subsequent failure of adjacent peri-implant bone tissue. Additionally, the example scaffold of the implant device may include a significantly high porosity to promote bone ingrowth, while exhibiting significantly higher effective mechanical properties such as, for example, the mechanical properties of trabecular bone.
• In particular, the example composite material includes a continuous porous biocompatible matrix having a thermoplastic polymer matrix reinforced with anisometric calcium phosphate particles. More specifically, in one example, a composite material includes a polyetheretherketone (PEEK) or a polyetherketoneketone (PEKK) matrix reinforced with various volume fractions of hydroxyapatite (HA) whiskers (e.g., 20 or 40 volume percent), wherein the matrix is approximately between 70% and 90% porous. In another example, the porous matrix includes a biocompatible, microporous polymer cage reinforced with anisometric calcium phosphate particles and bone morphogenic protein (BMP) such as, for example, rhBMP-2, which can be dispersed or accommodated by the void spaces and/or pores of the example porous scaffold and/or exposed on the surface of the example porous scaffold. Additionally, the BMP binds to the calcium phosphate further localizing the BMP to the surface of the scaffold or matrix.
• The example composite materials described herein may be used for applications such as, for example, synthetic bone graft substitutes, bone ingrowth surfaces applied to existing implants, tissue engineering scaffolds, interbody spinal fusion cages, etc. In each of the applications, carrier materials (e.g., collagen, hydrogels, etc.) containing growth factors, such as BMP, may be incorporated into the pore space of the scaffold of the implant device to further enhance osteoinduction and/or osteoconduction to promote osteointegration.
• Human bone tissues exhibit substantial variation in mechanical properties depending on the tissue density and microstructure. The properties are highly dependent on anatomic location and apparent density of the measured specimen. For example, a femur includes a cortical bone that has a relative porosity on the order of about 5-15%, and a trabecular bone that has a porosity on the order of about 75-95%. Due to the highly significant porosity differences, the trabecular bone exhibits significantly lower effective mechanical properties compared to the cortical bone. Therefore, depending on the application, synthetic composite materials for use as scaffolds and/or spinal fusion cages or other implant devices should possess the mechanical properties exhibited by the cortical bone or the trabecular bone, but must also have effective porosity to promote bone growth.
• To avoid the mechanical mismatch problems, such as stress shielding, the example scaffold of the implant device described herein may be tailored to substantially match or mimic the mechanical properties (e.g., stiffness, strength, toughness, etc.) of the adjacent and/or substituted bone tissue. Several factors may be varied during the synthesis of the composite material and scaffold of the implant device to tailor the mechanical properties including the calcium phosphate reinforcement volume fraction, aspect ratio, size and orientation; the polymer; and the size, volume fraction, shape and directionality of the void space and/or porosity. Tailoring the mechanical properties of the scaffold reduces the likelihood of mechanical mismatch leading to a decreased risk of subsidence, stress shielding, bone resorption and/or subsequent failure of adjacent vertebrae.
• FIG. 1A illustrates the example synthetic porouscomposite material100 described herein.FIG. 1B is a cross-sectional view of a portion of the example porouscomposite material100 ofFIG. 1A. The example syntheticcomposite material100 provides a syntheticporous scaffold101 for use or in as an orthopedic implant.
• The example synthetic porouscomposite material100 includes a porous thermoplastic polymer (e.g., a PEEK polymer)matrix102 having anisometric calciumphosphate reinforcement particles104 integrally formed or embedded with thematrix102 and/or exposed on a surface of the matrix. In this manner, thepolymer matrix102 embedded with thereinforcement particles104 provides high material strength, and thereinforcement particles104 exposed on the surface of thematrix102 promote bioactivity and/or bioresorption. Theporous polymer matrix102 includes a substantially continuous porosity and a plurality ofpores106 to enable bone ingrowth into theporous matrix102. In addition, thematrix102 is substantially continuously interconnected via a plurality ofstruts108.
• Furthermore, at least one of the plurality ofstruts108 may be a load-bearing strut.
• FIGS. 2A-2C are scanning electron micrographs showing increasing magnification of a portion of anexample scaffold200 withstruts202. Theexample scaffold200 is a PEEK scaffold reinforced with 40% by volume HA whiskers204.FIG. 2A illustrates the architecture ormatrix206 of thescaffold200 andFIG. 2B illustrates an enlarged portion of thestruts202. In the illustrated example, theHA whiskers204 are integrally formed and/or embedded within thematrix206 of thescaffold200 for reinforcement. The HA whiskers204 are also exposed on asurface208 of the matrix of thescaffold200 for bioactivity and/or bioresorption, as noted above. As shown inFIG. 2C, theHA whiskers204 are aligned in a sheet texture and are exposed on thesurface208 of thestruts202.
• The thermoplastic polymer of the example scaffolds described herein may be a biodegradable polymer for synthetic bone graft substitute applications, or nonbiodegradable for implant fixation applications. The thermoplastic polymer includes a continuous matrix of a composite material and is biocompatible and/or bioresorbable as described above.
• Additionally, or alternatively, the polymer may be a radiolucent polymer, bioresorbable (i.e., a material capable of being resorbed by a patient under normal physiological conditions) and/or non-bioresorbable, as desired. Further, the thermoplastic polymer matrix may include a polymer suitable for injection via percutaneous or surgical injection so that thecomposite material100 cures in vivo.
• Suitable non-resorbable polymers include, without limitation, polyaryletherketone (PAEK), polyetheretherketone (PEEK), polyetherketonekteone (PEKK), polyetherketone (PEK), polyethylene, high density polyethylene (HDPE), ultra-high molecular weight polyethylene (UHMWPE), low density polyethylene (LDPE), polyethylene oxide (PEO), polyurethane, polypropylene, polypropylene oxide (PPO), polysulfone, polypropylene, copolymers thereof, and blends thereof. Suitable bioresorbable polymers include, without limitation, poly(DL-lactide) (PDLA), poly(L-lactide) (PLLA), poly(glycolide) (PGA), poly(□-caprolactone) (PCL), poly(dioxanone) (PDO), poly(glyconate), poly(hydroxybutyrate) (PHB), poly(hydroxyvalerate (PHV), poly(orthoesters), poly(carboxylates), poly(propylene fumarate), poly(phosphates), poly(carbonates), poly(anhydrides), poly(iminocarbonates), poly(phosphazenes), copolymers thereof, and blends thereof. Suitable polymers that are injectable via percutaneous or surgical injection that cure in vivo include, without limitation, polymethylmethacrylate (PMMA), and other polyacrylics from monomers such as bisphenol a hydroxypropylmethacrylate (bis-GMA) and/or tri(ethylene glycol) dimethacrylate (TEG-DMA).
• Although synthetic substitute composite materials made of polymers satisfy the functional criteria of an implantable device because they are, for example, formable and inexpensive, polymers alone lack biological efficacy to promote bone growth and/or may lack requisite mechanical properties to support load levels. To increase the mechanical properties of the polymers, the polymers are reinforced with calcium phosphates. The aspect ratio, size, volume fraction and degree of preferred orientation of the calcium phosphate particles104 (e.g., HA whisker particles) may be tailored for the desired material properties and implant performance. For example, consider the information presented inFIG. 3, which is a graphical illustration of the elastic modulus of HA whisker and powder reinforced polymer composite materials versus the volume fraction percentage of the apatite calcium phosphates that is mixed with the polymer matrix. The shaded areas ofFIG. 3 show approximate regions for the given mechanical property of the human cortical bone tissue. As depicted in the graph, the elastic modulus of the composite materials increases with increasing HA content. In addition, increasing the level of HA reinforcement in polymer composites increases cellular activity during osteointegration.
• The calciumphosphate reinforcement particles104 may be in the form of single crystals or dense polycrystals but are at least in some portion anisometric. “Anisometric” refers to any particle morphology (shape) that is not equiaxed (e.g., spherical), such as whiskers, plates, fibers, etc. Anisometric particles are usually characterized by an aspect ratio. For example, HA single crystals are characterized by the ratio of dimensions in the c- and a-axes of the hexagonal crystal structure. Thus, the anisometric particles in the present disclosure have an aspect ratio greater than 1. In one example, the mean aspect ratio of the reinforcement particles is from about 1 to about 100. By further example, the reinforcement particles can be provided in an amount of from about 1% by volume of the composite biomaterial to about 60% by volume, and for example, from about 20% by volume of the composite to about 50% by volume.
• Due to their morphology, the calciumphosphate reinforcements particles104 may be oriented in bulk or near the surface of thepolymer matrix102 to provide directional properties, if desired. For example, if thereinforcement particles104 are predominately aligned within thematrix102 the morphological alignment of theparticles104 provides anisotropy for theoverall composite100, which can be tailored to be similar to the anisotropic mechanical properties of bone tissues. For example,FIG. 4 shows a micrograph of anisometriccalcium phosphate reinforcement400 on the surface of a densecomposite polymer matrix402. Also shown inFIG. 4 is a schematic illustration of a portion ofmatrix402 and illustratively showing the orientation of thereinforcement particles400 relative to the loading direction of the material and/or a scaffold strut, which is, for example, at an angle θ.
• Furthermore, there are no limits on the size or amount of thecalcium phosphate particles104 inmatrix102, provided that thecalcium phosphate particles104 are dispersed within and/or exposed at the surface of thepolymer matrix102. For example, thereinforcement particles104 may have a maximum dimension from about 20 nm to about 2 mm, and for example, between 20 nm to about 100 μm. While both nano- and micro-scale calcium phosphate particles improve the mechanical properties of the example syntheticcomposite material100 described herein, nano-scale calcium phosphate particles are particularly effective for enhancing bioresorbability and cell attachment, and micro-scale particles are particularly effective for obtaining a uniform dispersion within thematrix102.
• Suitable calcium phosphates may include, without limitation, calcium HA, HA whiskers, HA, carbonated calcium HA, beta-tricalcium phosphate (beta-TCP), alpha-tricalcium phosphate (alpha-TCP), amorphous calcium phosphate (ACP), octacalcium phosphate (OCP), tetracalcium phosphate, biphasic calcium phosphate (BCP), anhydrous dicalcium phosphate (DCPA), dicalcium phosphate dihydrate (DCPD), anhydrous monocalcium phosphate (MCPA), monocalcium phosphate monohydrate (MCPM), and combinations thereof.
• As described above, a syntheticcomposite material100 not only bears physiological levels of load, but also promotes oseteointegration—the direct structural and functional connection between the living bone and the surface of the load-bearing implant. The bioactive calcium phosphate particles104 (e.g., HA whiskers) exposed on the surface of the exampleporous matrix102 promote a stable bone-implant interface. Osteointegration also requires the vascularization and growth of bone into an implant via interconnected and/or continuous porosity.
• Thus, the size, volume fraction, shape, and directionality of the void spaces and/orpores106 may be tailored to optimize osteoconduction and implant mechanical properties. Thepores106 may be any size or shape, while maintaining a continuous network to promote a fusion through the formation of new bone tissue in the void spaces and/or pores106. For example, thepores106 may be present throughout thematrix102 as illustrated inFIG. 1A. Also, thepores106 may be functionally graded in any material or implant direction, for example, radially, as shown inFIGS. 6 and 7, from a highly porous region to a relatively dense region or may include a void space. The change in porosity from one region to another may be very distinct, for example as shown inFIGS. 6 and 7, or gradual. Furthermore, the graded change may be uniform or variant. In addition, instead of a graded change there may be a combination of materials having two or more densities of pores. The central void may be any shape or size, and may receive (e.g., be filled) a material, a structure, or the composite material100 (i.e., the composite material graded from the porous outer surface to a dense center), thereby forming a porous outer perimeter and a dense central region. Examples are further described in connection withFIGS. 6 and 7 below.
• As discussed in greater detail below, the porosity and/or poresizes106 may be selectively formed by the inclusion of, for example, a porogen material during synthesis of thecomposite material100. Pores spaces may range from about 100 μm to about 500 μm, and, for example, from about 250 μm to about 500 μm. The examplecomposite biomaterial100 may additionally contain some fraction of microporosity within scaffold struts that is less than about 10 μm in size. The total amount of porosity within porous regions may range from about 1% to about 90% by volume, and, for example, between about 70% and 90% by volume. However, the porosity may also be tailored via other processes such as, for example, microsphere sintering, fiber weaving, solvent casting, electrospinning, freeze drying (lyophilization), thermally induced phase separation, gas foaming, and rapid prototyping processes such as, for example, solid freeform fabrication, robotic deposition (aka, robocasting), selective laser sintering, fused deposition modeling, three-dimensional printing, laminated object manufacturing, stereolithography, etc., or any other suitable process(es) or combination(s) thereof.
• Additionally, the examplecomposite material100 may optionally include additives, if desired. For example, thecomposite material100 may include one or more surface-active agents to enhance interfacial bonding between thereinforcement particles104 and thepolymer matrix102. The void spaces and/orpores106 may accommodate and deliver one or more growth factors such as, for example, BMP, to enhance osteoinductivity and/or bone regeneration. Furthermore, the void spaces and/orpores106 may also accommodate and deliver one or more transcription factors, matrix metalloproteinases, peptides, proteins, bone cells, progenitor cells, blood plasma, bone marrow aspirate, or combinations thereof, to improve or speed bone regeneration, or resorption and replacement of the biomaterial. In some examples, the void spaces and/orpores106 may further accommodate a carrier material that may be incorporated into the void spaces and/or pores106. The carrier material may include, for example, a collagen sponge, membrane, or a hydrogel material to deliver the growth factor material such as, for example, the BMP. Thecalcium phosphate reinforcements104 exposed on the surface of theporous matrix102, along with the porosity, improves the retention of the BMP within thematrix102 and at the peri-implant interface.
• FIG. 5A is an illustration showing a known interbodyspinal fusion cage500. The examplespinal fusion cage500 is implanted in theinter-vertebral space502 between twoadjacent vertebrae506 and508. Adisc510, due to degeneration, herniation, etc., is typically removed and replaced by thespinal fusion cage500. Thespinal fusion cage500 is used to support or restore vertebral height, and, thus, stabilize or retainadjacent vertebrae506 and508 in a desired position. Additionally, thespinal fusion cage500 is to promote fusion between thevertebrae506 and508.
• FIG. 5B is an enlarged illustration of the knownspinal fusion cage500 ofFIG. 5A. A typicalspinal fusion cage500 includes abody510 having a denseouter region512 and a void514 at its center. The denseouter surface512 may be made of PEEK, titanium, or other material that can be used to support thevertebrae506 and508. However, thespinal fusion cage500 made of a PEEK, titanium, etc., cannot attach to the bone. Thus, to promote bone ingrowth, thecenter void514 is typically provided with a packing material (not shown) such as, a natural bone graft, a collagen sponge that retains bone growth factors, or thespinal fusion cage500 is coated with the bone growth factors or other agents that promote osteoinduction.
• The exampleporous scaffold101 having thecomposite material100 described herein, and with respect toFIG. 1A, can be implemented with thespinal fusion cage500 ofFIGS. 5A and 5B to replace the packing materials, such as natural bone graft. As noted above, theporous scaffold101 promotes bone ingrowth and thepores106 may accommodate or deliver for example, a BMP, to further improve rate of growth (fusion rate). Furthermore, the calcium phosphate (e.g., HA whisker) binds to thebody510 and localizes the BMP within thecentral void514, which further promotes osteointegration.
• FIG. 6 illustrates another example scaffold ormatrix600 implemented with the examplecomposite material100 described herein. Theexample scaffold600 may be implemented as an interbody spinal fusion cage. Thescaffold600 includes abody602 having aporous polymer matrix604 integrally formed or embedded with anisometriccalcium phosphate particles606. Furthermore, thematrix604 of theexample scaffold600 includes a radiolucent polymer (e.g., PEEK) integrally formed or embedded with anisometriccalcium phosphate reinforcements606 such as, for example, HA whiskers. The radiolucent polymer provides improved radiographic analysis of fusion following implantation. Theexample scaffold600 may also include a BMP such as, for example, rhBMP-2. In another example, theexample scaffold600 is a biocompatible, microporous polymer scaffold or matrix supplemented with anisometric calcium phosphate reinforcements and BMP.
• Additionally, theexample scaffold600 may formed so that the pores are functionally graded in any material or implant direction such as, for example, radially, as shown inFIG. 6, from a highly porous center orcentral region608 to relatively dense outer region orsurface610. The change in porosity from one region to another may be distinct or gradual from thecentral region608 to theouter region610. Further, the graded change may be uniform or variant. The denseouter region610 provides structural integrity along with the advantages of thecomposite material100 described herein. In the illustrated example, theporous structure604 has pore sizes that range between about 100 μm and about 500 μm, and preferably, between about 250 μm and about 500 μm, and a porosity that ranges between about 1% to about 90%. Furthermore, the spinalfusion cage material600 may include microporosity having pore sizes less than about 10 μm.FIG. 7 illustrates anotherexample scaffold700. Theporous scaffold700 includes aporous matrix702 having thecomposite material100 described herein. Theporous scaffold700 includes a center orcentral void704 that may be any shape or size. Additionally, or alternatively, thecentral void704 may receive amaterial706, a stem, or any other substance or structure, illustratively depicted by dashed lines. For example, thecentral void704 may receive a stem706 (e.g., an implant) such as, for example, a titanium stem, a dense composite stem (e.g., a PEEK composite stem), or any other suitable material or structure.
• Additionally, in other examples, thescaffold700 is formed so that the pores are functionally graded in any material or implant direction, for example, radially as shown inFIG. 7, from a high porous outer region orsurface702 to a relatively dense center orcentral region708. The change in porosity from one region to another may be distinct or gradual from thecentral region708 to the highly porousouter region702. Further, the graded change may be uniform or variant. In this manner, theexample scaffold700 forms a porous perimeter having a dense core, where the material is continuous from the porous perimeter to the dense core. The densecentral region708 provides structural integrity along with the advantages of thecomposite material100 described herein. In the illustrated example, theporous matrix702 and the densecentral region708 may have pore sizes that range between about 100 μm and about 500 μm, and preferably, between about 250 μm and about 500 μm, and a porosity that ranges between about 1% to about 90%. Furthermore, thespinal fusion cage700 may include a microporosity having pore sizes less than about 10 μm.
• In other examples, thecomposite material100 and/or thescaffolds101,600,700 may also include a roughened surface such as, for example, serrated teeth, that come into direct contact with the adjacent peri-implant tissue to prevent movement relative to the peri-implant tissue after implantation. Additionally, or alternatively, although not shown, thescaffolds101,600,700 may include holes, notches, pins, radiographic markers, or other features that may be gripped or otherwise used for positioning of thescaffolds101,600,700 by minimally invasive surgical tools and procedures.
• The examplecomposite material100 and/or thescaffolds101,600,700 may be manufactured by methods common to reinforced thermoplastic and thermosetting polymers, including but not limited to injection molding, reaction injection molding, compression molding, transfer molding, extrusion, blow molding, pultrusion, casting/potting, solvent casting, microsphere sintering, fiber weaving, solvent casting, electrospinning, freeze drying (lyophilization), thermally induced phase separation, gas foaming, and rapid prototyping processes such as solid freeform fabrication, robotic deposition (aka, robocasting), selective laser sintering, fused deposition modeling, three-dimensional printing, laminated object manufacturing, stereolithography, etc., or any other suitable process(es) or combination(s) thereof.
• FIG. 8 is a flowchart of anexample method800 that may be used to synthesize the examplecomposite material100 and/orscaffolds101,600,700 described herein. While an example manner of synthesizing the examplecomposite material100 and/orscaffolds101,600,700 has been illustrated inFIG. 8, one or more of the steps and/or processes illustrated inFIG. 8 may be combined, divided, re-arranged, omitted, eliminated and/or implemented in any other way. Further still, the example method ofFIG. 8 may include one or more processes and/or steps in addition to, or instead of, those illustrated inFIG. 8, and/or may include more than one of any or all of the illustrated processes and/or steps. Further, although the example method is described with reference to the flow chart illustrated inFIG. 8, persons of ordinary skill in the art will readily appreciate that many other methods of synthesizing the examplecomposite material100 and/orscaffolds101,600,700 may alternatively be used.
• Thecomposite material100 and/or thescaffolds101,600,700 are processed using a powder processing approach in conjunction with compression molding and particle leaching techniques and is particularly suited for achieving a high concentration (e.g., >40 vol %) of well-dispersed (and aligned, if desired) anisometric calcium phosphate reinforcements (e.g., HA whiskers) in a thermoplastic matrix (e.g., PEEK) with minimal degradation of the calcium phosphate size/shape during processing. In this manner, the calcium phosphate reinforcement volume fraction, aspect ratio, size and orientation; the polymer; and the size, volume fraction, shape and directionality of the void space and/or porosity may be tailored to vary the mechanical properties of thecomposite material100 and/orscaffolds101,600,700.
• A polymer such as, for example, PEEK, and anisometric calcium phosphate particles, such as HA whiskers, are provide in powder form (block802). The PEEK polymer powder may have, for example, a mean particle size of about 26 μm. The HA whiskers may be synthesized (block801) using, for example, the chelate decomposition method.
• The PEEK powder and the synthesized HA whiskers are co-dispersed in a fluid (block804) such as, for example ethanol, and mixed (block804) using, for example, ultrasonication under constant stirring—forming a viscous suspension.
• After the polymer powder and the HA whiskers are mixed, the porosity of the mixture is selectively varied and/or tailored (block806). In one example, the porosity may be formed and tailored by the addition of a suitable porogen material such as, for example, NaCl, wax, polysaccharides (sugars), cellulose, etc. The extent of the porosity can be controlled by varying the amount of porogen used (block805), while the pore size could be tailored by sieving the porogen (block807) to a desired size prior to mixing the porogen with the polymer mixture. In another examples, the porosity and/or the pore size of the polymer matrix may be selectively varied using any other suitable methods and/or process(es) such as, for example, microsphere sintering, fiber weaving, solvent casting, electrospinning, freeze drying (lyophilization), thermally induced phase separation, gas foaming, or rapid prototyping processes such as, for example, solid freeform fabrication, robotic deposition (aka, robocasting), selective laser sintering, fused deposition modeling, three-dimensional printing, laminated object manufacturing, stereolithography, etc., or any other suitable process(es) or combination(s) thereof.
• The viscous suspension is wet-consolidated (block808) by, for example, vacuum filtration and drying to remove any residual fluid (i.e., ethanol). The composite mixture is densified (block810) by, for example, uniaxial compression, to form a composite preform.
• Following the initial densification, the preform is compression molded (block812) and/or sintered at elevated temperatures (e.g., approximately 20° C. to 400° C.) sufficient to fuse the polymer particles with minimal damage to the calcium phosphate reinforcements. The process or composite material may be heated to a desired processing temperature and the implant may be shaped or formed (block814). Densifying and molding the composite material includes aligning the calcium phosphate reinforcement particles (e.g., HA whiskers) morphologically and/or crystallographically within the scaffold struts.
• The scaffold may have any shape and/or size (e.g., any polygonal shape) and can be formed by methods common to reinforced thermoplastic and thermosetting polymers, including but not limited to injection molding, reaction injection molding, compression molding, transfer molding, extrusion, blow molding, pultrusion, casting/potting, solvent casting, and rapid prototyping processes such as, for example, solid freeform fabrication, robotic deposition (aka, robocasting), selective laser sintering, fused deposition modeling, three-dimensional printing, laminated object manufacturing, stereolithography, etc., or any other suitable process(es). Thecomposite material100 and/or thescaffolds101,600,700, are formed by the mold walls and/or machining after molding.
• The composite material undergoes a leaching process (block816) to remove, for example, the porogen used during synthesis of the composite material. The leaching may occur, for example, via a dissolution method, heating method, and/or any other suitable methods and/or process(es). More specifically, dissolution may include immersing the scaffold in a fluid, such as, for example, deionized water.
• Furthermore, viscous flow of the polymer/reinforcement mixture during molding can be designed to tailor the preferred orientation of the anisometric reinforcements in the implant. Additionally, surface-active agents may be added during the mixing process and/or to the surface of the composite material to enhance interfacial bonding between reinforcement particles and the matrix.
• The following example is provided to further illustrate the example apparatus and methods described herein and, of course, should not be construed as in any way limiting in scope. It is to be understood by one of ordinary skill in the art that the following examples are neither comprehensive nor exhaustive of the many types of methods and apparatus which may be prepared in accordance with the present disclosure.
• In the example, commercially available PEKK and sodium chloride (NaCl) powders with mean particle sizes of 70 and 250 μm, respectively, were used as-received. HA whiskers were synthesized using the chelate decomposition method. The as-synthesized HA whiskers were measured by optical microscopy to have a mean length of 21.6 μm, width of μm and aspect ratio of 7.6.
• In the example, composite scaffolds with 75, 82.5 and 90% porosity were processed with 0-40 vol % HA whisker reinforcement. Appropriate amounts of polymer powder and HA whiskers were co-dispersed in ethanol via a sonic dismembrator and mechanical stirring at 1200 rpm. Following dispersion, the appropriate amount of the NaCl (i.e., porogen) was added to the suspension and mixed by hand using a Teflon coated spatula. The total scaffold volume consisted of the material volume plus the pore volume. Thus, the reinforcement level was calculated based the desired material volume, while the porosity level was calculated based on the total scaffold volume. After mixing, the viscous suspension was wet-consolidated using vacuum filtration. The powder mixture was dried overnight in a forced convection oven at 90° C. and densified at 125 MPa in a cylindrical pellet die using a hydraulic platen press. The die and densified powder mixture was heated in a vacuum oven to the desired processing temperature and transferred to a hydraulic platen press for compression molding. Scaffolds with 82.5 and 90% porosity were molded at 350° C., while scaffolds with 75% porosity were molded at 350, 365 and 375° C. A pressure of 250 MPa was applied to the die as the polymer solidified. After cooling to room temperature, the sintered composite pellet was ejected from the die and placed approximately 300 mL deionized water for at least 72 h to dissolve the NaCl crystals. The deionized water was changed daily. The as-molded composite scaffolds had a diameter of 1 cm and were machined to a height of 1 cm.
• In the example, un-confined compression tests were performed to investigate the mechanical properties of the composite scaffolds. Specimens were tested on an electromagnetic test instrument in phosphate buffered saline (PBS) at 37° C. using a crosshead speed of 1 mm/min. Force-displacement data was used to calculate the elastic modulus, compressive yield stress (CYS), and failure strain of the composite scaffolds. One-way analysis of variance (ANOVA) was used to compare mechanical properties between experimental groups. The compressive properties of HA whisker reinforced PEKK scaffolds were tabulated in table 1.
• The table below provides mechanical properties of the example PEKK scaffold reinforced with HA whiskers that was processed using a compression molding/particle leaching method such as, for example, themethod800 ofFIG. 8 as implemented in the description above. The mechanical properties of HA whisker reinforced PEKK were evaluated in uniaxial compression. Tensile properties of the HA whisker reinforced PEKK scaffolds were evaluated prior to scaffold fabrication.

• TABLE 1
  		Molding
  	HA	Temper-	Elastic		Yield
  Porosity	Content	ature	Modulus	CYS	Strain
  (%)	(Vol %)	(° C.)	(MPa)	(MPa)	(%)

  75	0	350	69.5	(12.2)	1.25 (0.16)	5.7	(0.4)
  75	0	365	100.7	(10.7)	2.04 (0.26)	4.4	(1.2)
  75	0	375	95.6	(10.5)	2.55 (0.34)	4.4	(1.1)
  75	20	350	106.3	(15.0)	1.28 (0.13)	3.7	(1.1)
  75	20	365	115.4	(13.4)	1.77 (0.30)	2.9	(0.6)
  75	20	375	141.1	(39.2)	2.28 (0.35)	2.9	(0.7)
  75	40	350	54.0	(18.3)	0.52 (0.17)	2.2	(0.3)
  75	40	365	84.3	(41.5)	1.15 (0.38)	2.7	(0.5)
  75	40	375	120.2	(29.8)	1.65 (0.34)	2.3	(1.9)
  82	40	350	15.7	(6.7)	0.13 (0.03)	2.6	(1.9)
  90	0	350	0.75	(0.18)	0.15 (0.04)	30	(0.0)
  90	40	350	0.23	(0.13)	0.04 (0.01)	30	(0.0)

• As shown in the table, for a given reinforcement level, the compressive modulus decreased with increased porosity, and the yield strength decreased with increased porosity. Scaffolds with 0% vol % HA whisker reinforcement and 75% and 90% porosity exhibited moduli of 69.5 and 0.75 MPa, while scaffolds with 40 vol % HA whisker reinforcement and 75%, 82% and 90% porosity exhibited moduli of 54.0, 15.7 and 0.23 MPa, respectively.
• Scaffolds with 0 vol % HA whisker reinforcement and 75% and 90% porosity exhibited yield strengths of 1.25 MPa and 0.15 MPa, respectively. Scaffolds with 40 vol % HA whisker reinforcement and 75%, 82% and 90% porosity exhibited yield strengths of 0.52 MPa, 0.13 MPa and 0.04 MPa, respectively. The HA content also affected the modulus and failure strain of the scaffolds. A scaffold having 75% porosity and 20 vol % reinforcement HA whisker exhibited modulus of 106.3 MPa, compared to a modulus of 69.5 MPa for scaffolds with 0 vol % HA whisker reinforcement.
• The example methods and apparatus described herein offer synthetic porous composite material that may be used for synthetic bone substitutes for implant fixation, fraction fixation, synthetic bone graft substitutes, interbody spinal fusion, tissue engineering scaffolds, or other applications. Many aspects of the of the porous composite material may be tailored to provide specific mechanical, biological, and surgical functions, such as, the polymer composition and molecular orientation, porosity and pore size of the porous matrix, or the HA reinforcement content, morphology, preferred orientation, and size.
• Although the teachings of the present disclosure have been illustrated in connection with certain examples, there is no intent to limit the present disclosure to such examples. On the contrary, the intention of this application is to cover all modifications and examples fairly falling within the scope of the appended claims either literally or under the doctrine of equivalents.

Claims (28)

What we claim is:

1. A composite material, comprising:

a porous reinforced composite scaffold, comprising:

a polyaryletherketone polymer and anisometric reinforcement particles distributed throughout the polyaryletherketone polymer, and

a substantially continuously interconnected plurality of pores distributed throughout the polyaryletherketone polymer, each of the pores in the plurality of pores defined by voids interconnected by struts, each pore void having a size within a range from about 10 to 500 μm,

wherein a plurality of the anisometric reinforcement particles are both embedded within the polyaryletherketone polymer and exposed on the struts within the pore voids, and

wherein the porous reinforced composite scaffold has a scaffold volume that includes a material volume defined by the polyaryletherketone polymer and the anisometric reinforcement particles, and a pore volume defined by the plurality of pores.

2. The composite material according toclaim 1, wherein the porous reinforced composite scaffold is formed by mixing polymer, reinforcement, and porogen particles to obtain a substantially uniform particle mixture, compression molding the particle mixture, and removing the porogen particles.

3. The composite material according toclaim 2, wherein the particle mixture is dispersed in a non-solvating fluid, and wherein the non-solvating fluid is removed by one of vacuum, heating or a combination thereof prior to compression molding.

4. The composite material according toclaim 2, wherein each of the pores in the plurality of pores has a pore void size and shape defined by the removed porogen particles, and wherein the porogen particles are either homogenous or heterogeneous in shape and are either homogeneous or heterogeneous in size, the porogen particle size in the range from about 10 to 500 μm.

5. The composite material according toclaim 2, wherein the porogen particles are selected from the group consisting of NaCl, wax, polysaccharides, cellulose, and combinations thereof.

6. The composite material according toclaim 2, wherein the porogen particles have been removed from the porous reinforced composite scaffold material by leaching.

7. The composite material according toclaim 1, wherein the anisometric reinforcement particles are present in the polyaryletherketone polymer from about 1 to about 60% of the material volume.

8. The composite material according toclaim 1, wherein the anisometric reinforcement particles are distributed essentially uniformly throughout the polyaryletherketone polymer.

9. The composite material according toclaim 1, wherein the anisometric reinforcement particles comprise one or more of hydroxyapatite, calcium-deficient hydroxyapatite, carbonated calcium hydroxyapatite, beta-tricalcium phosphate (beta-TCP), alpha-tricalcium phosphate (alpha-TCP), amorphous calcium phosphate (ACP), octacalcium phosphate (OCP), tetracalcium phosphate, biphasic calcium phosphate (BCP), anhydrous dicalcium phosphate (DCPA), dicalcium phosphate dihydrate (DCPD), anhydrous monocalcium phosphate (MCPA), monocalcium phosphate monohydrate (MCPM), and combinations thereof, and, wherein the polyaryletherketone polymer comprises one or more of polyetheretherketone (PEEK), polyetherketonekteone (PEKK), and polyetherketone (PEK).

10. The composite material according toclaim 1, wherein the anisometric reinforcement particles comprise hydroxyapatite whiskers that have a mean aspect ratio (length along c-axis/length along a-axis) of greater than 1 and less than 100, and wherein the size of the anisometric reinforcement particles ranges between 20 nm and 2 mm.

11. The composite material according toclaim 1, wherein the pore volume ranges from about 1 to 95 percent, by volume, based on the scaffold volume.

12. The composite material according toclaim 1, wherein the porosity varies within the porous reinforced composite scaffold either from a highly porous center to a relatively dense exterior surface or from a relatively dense center to a highly porous exterior surface.

13. The composite material according toclaim 1, wherein the porous reinforced composite scaffold has a compressive elastic modulus similar to that of trabecular bone.

14. A composite material, comprising:

a porous reinforced composite scaffold, comprising:

a polyaryletherketone polymer and anisometric reinforcement particles comprising calcium phosphate crystals distributed essentially uniformly throughout the polyaryletherketone polymer, and

a substantially continuously interconnected plurality of pores that are uniformly distributed throughout the polyaryletherketone polymer, each of the pores in the plurality of pores defined by voids interconnected by struts, each pore void having a size within a range from about 10 to 500 μm, and

wherein the porous reinforced composite scaffold has a scaffold volume that includes a material volume defined by the polyaryletherketone polymer and the anisometric reinforcement particles, and a pore volume defined by the plurality of pores, and

wherein the anisometric reinforcement particles are present in the polyaryletherketone polymer from about 1 to about 60% of the material volume, and

wherein anisometric reinforcement particles are both embedded within the polyaryletherketone polymer and exposed on the struts within the pore voids, and

wherein the porous reinforced composite scaffold is formed by mixing polymer, reinforcement, and porogen particles to obtain a substantially uniform mixture, compression molding the particle mixture at a temperature from between 20 to 400 degrees C., and removing the porogen particles.

15. The composite material according toclaim 14, wherein the particle mixture is dispersed in a non-solvating fluid, and wherein the non-solvating fluid is removed by one of vacuum, heating or a combination thereof prior to compression molding.

16. The composite material according toclaim 14, wherein the compression molding temperature is in a range from about 350 to about 375 degrees C.

17. The composite material according toclaim 14, wherein the compression molding temperature is in a range from about 365 to about 375 degrees C.

18. A method for forming a porous reinforced composite scaffold, comprising:

using a powder processing approach in conjunction with compression molding and particle leaching to prepare the composite scaffold, the process including the steps comprising:

providing a powder mixture densified in a die, the powder mixture comprising a thermoplastic polymer powder, reinforcement particles in powder form, and porogen particles;

compression molding the densified powder mixture at a temperature sufficient to fuse the polymer powder to provide a sintered composite; and

removing the porogen particles a material from the porous reinforced composite scaffold.

19. The method for forming a porous reinforced composite scaffold according toclaim 18, further comprising the steps comprising;

prior to providing the powder mixture densified in a die, first providing each of the thermoplastic polymer powder, the reinforcement particles in powder form, and the porogen particles;

dispersing, in any order, each of the thermoplastic polymer powder, the reinforcement particles in powder form, and the porogen particles in a non-solvating fluid to provide a fluid dispersion of the powder mixture;

wet-consolidating the powder mixture to remove the fluid; and

drying the wet-consolidated powder mixture.

20. The method for forming a porous reinforced composite scaffold according toclaim 18, wherein the compression molding temperature sufficient to fuse the polymer powder is in a range from about 350 to about 375 degrees C.

21. The method for forming a porous reinforced composite scaffold according toclaim 18, wherein the compression molding temperature sufficient to fuse the polymer powder is in a range from about 365 to about 375 degrees C.

22. The method for forming a porous reinforced composite scaffold according toclaim 18, wherein the thermoplastic polymer powder comprises a polyaryletherketone polymer, and wherein the reinforcement particles comprise anisometric calcium phosphate.

23. A composite material, comprising:

a porous reinforced composite scaffold, comprising:

a thermoplastic polymer and reinforcement particles distributed throughout the thermoplastic polymer, and

a substantially continuously interconnected plurality of pores that are distributed throughout the thermoplastic polymer, each of the pores in the plurality of pores defined by voids interconnected by struts, each pore void having a size within a range from about 10 to 500 μm, and

wherein the porous reinforced composite scaffold has a scaffold volume that includes a material volume defined by the thermoplastic polymer and the reinforcement particles, and a pore volume defined by the plurality of pores, and

wherein the reinforcement particles are present in the thermoplastic polymer from about 1 to about 60% of the material volume, and

wherein reinforcement particles are both embedded within the thermoplastic polymer and exposed on the struts within the pore voids.

24. The composite material according toclaim 23, wherein the porous reinforced composite scaffold is formed by mixing thermoplastic polymer, reinforcement, and porogen particles to obtain a substantially uniform mixture, compression molding the particle mixture at a temperature from between 20 to 400 degrees C., and removing the porogen particles.

25. The composite material according toclaim 23, wherein the thermoplastic polymer is selected from the group consisting of a polyaryletherketone polymer, a bioresorbable polymer, and combinations thereof.

26. The composite material according toclaim 23, wherein the thermoplastic polymer is selected from the group consisting of polyaryletherketone (PAEK), polyetheretherketone (PEEK), polyetherketonekteone (PEKK), polyetherketone (PEK), polyethylene, high density polyethylene (HDPE), ultra-high molecular weight polyethylene (UHMWPE), low density polyethylene (LDPE), polyethylene oxide (PEO), polyurethane, polypropylene, polypropylene oxide (PPO), polysulfone, polypropylene, poly(DL-lactide) (PDLA), poly(L-lactide) (PLLA), poly(glycolide) (PGA), poly(c-caprolactone) (PCL), poly(dioxanone) (PDO), poly(glyconate), poly(hydroxybutyrate) (PHB), poly(hydroxyvalerate (PHV), poly(orthoesters), poly(carboxylates), poly(propylene fumarate), poly(phosphates), poly(carbonates), poly(anhydrides), poly(iminocarbonates), poly(phosphazenes), polymethylmethacrylate (PMMA), bisphenol a hydroxypropylmethacrylate (bis-GMA), tri(ethylene glycol) dimethacrylate (TEG-DMA), and combinations thereof.

27. The composite material according toclaim 23, wherein the reinforcement is selected from the group consisting of hydroxyapatite, calcium-deficient hydroxyapatite, carbonated calcium hydroxyapatite, beta-tricalcium phosphate (beta-TCP), alpha-tricalcium phosphate (alpha-TCP), amorphous calcium phosphate (ACP), octacalcium phosphate (OCP), tetracalcium phosphate, biphasic calcium phosphate (BCP), anhydrous dicalcium phosphate (DCPA), dicalcium phosphate dihydrate (DCPD), anhydrous monocalcium phosphate (MCPA), monocalcium phosphate monohydrate (MCPM), and combinations thereof.

28. The composite material according toclaim 23, wherein the thermoplastic polymer comprises a polyaryletherketone polymer, and wherein the reinforcement comprises anisometric calcium phosphate.