US20110245831A1 - Reaming device with carbon fiber shaft and molded interface element - Google Patents

Abstract

A reaming device comprising a shaft with a mounting portion, the mounting portion having an outer surface; a carbon fiber layer located on the mounting portion outer surface; an injection molded interface element for mechanical coupling of an external device molded on the carbon fiber layer, the interface element having a mounting portion; wherein the carbon fiber layer extends over the outer surface of the shaft mounting portion and having an outer surface, wherein the carbon fiber layer outer surface has a non-smooth surface structure; wherein the injection molded interface element mounting portion is injection molded over the carbon fiber layer surface structure The method according to claim12, further comprising preparing of shaft mounting portion before wrapping a carbon fiber layer for establishing a reliable connection between the shaft and the carbon fiber layer.

Description

CROSS REFERENCE TO RELATED APPLICATION
• The present application claims priority from European Patent Application No. 10158573.5 filed Mar. 31, 2010, which is incorporated herein by reference
BACKGROUND OF THE INVENTION
• The present invention relates to a reaming device, and in particular to a reaming device providing a reliable connection between a carbon fiber composite shaft and an interface element molded thereon.
• Intramedullary nailing is the method of choice for the fixation of fractures in long bones, in particular bones in long extremities. To have full access to the intramedullary channel, a shaft of a reamer has to be flexible enough in a bending direction to bypass soft tissue and conform to bone curvature. The shaft also has to be rigid enough to convey torsion to the reamer head. Prior art reaming devices have a shaft design consisting of a helix in which residues can be trapped during the reaming procedure, so that the cleaning of the reaming device in hospitals prior to the next usage is complicated, in particular in a sterilization process. The adequate cleaning of the instrument in hospitals demands a great effort and takes a lot of time. Further, some hospitals are not prepared to clean such critical devices because of the great effort involved.
• In some prior art reaming devices, a helix shaft is replaced by a shaft made of so called nitinol, which is a material having a high degree of elasticity (super elasticity) to provide enough flexibility. Nitinol is an acronym for NIckel TItanium Naval Ordnance Laboratory. Nitinol is the inter-metallic phase NiTi having a regular cubic crystal structure being different of the structure of titanium or nickel. Nitinol comprises about 55% nickel and about 45% titanium. Owing to the fact that the nitinol shaft is made of a single tube, the cleaning effort in the hospital is less exhausting. However, recent investigations have shown that the nitinol material has a catastrophic failure mode. In particular, some reports have pointed out that some breakages in multiple fragments of the nitinol shaft occurred during the reaming process during the intervention process in hospitals. Further, the nitinol material is a very expensive material.
• EP 253526 and U.S. Pat. No. 4,751,922 relates to a shaft made of a composite material of filamentous fibers and an appropriate resin.
• From US 2007/0015107, a root canal instrument having an abrasive coating and method for the production thereof is known, wherein the described root canal instrument has a core of a flexible elastic material having a shape memory, wherein the core furthermore has a coating with abrasive particles, wherein the core is made from a nickel-titanium alloy or from a plastic material, e.g. carbon fibre reinforced plastics material.
• CH 668690 relates to a probe electrode cable for medical purposes, e.g. electro cardiogram test, using carbon fibre impregnated plastic insulating coating as a cover with a lead coupled to the test equipment.
• US Patent Publication No. 2010/0239380 relates to a reaming device with a carbon fiber shaft, an interface element and a connecting agent. The disclosure of 2010/0239380 is incorporated herein by reference.
BRIEF SUMMARY OF THE INVENTION
• It is one aspect of the present invention to provide a more reliable reaming device.
• One aspect of the present invention is solved by a reaming device comprising a shaft with a mounting portion, the mounting portion having an outer surface. A carbon fiber layer located on the mounting portion outer surface. An injection molded interface element for mechanical coupling of an external device molded on the carbon fiber layer, the interface element having a mounting portion. The carbon fiber layer extends over the outer surface of the shaft mounting portion and has an outer surface. The carbon fiber layer outer surface has a non-smooth surface structure. The injection molded interface element mounting portion is injection molded over the carbon fiber layer surface structure. The shaft of the reaming device is made of a carbon fiber reinforced material. The carbon fiber layer comprises a wrapped carbon fiber with a resin impregnation. The carbon fiber layer surface structure comprises a pressed tooth structure. The pressed tooth structure comprises an elongated rippled structure. The interface element comprises a coupling portion for coupling a power tool reamer drive as an external device. The coupling portion comprises an end portion being capable of transmitting a torque. The injection molded interface element comprises a rated break section between its mounting portion and its coupling portion. The injection molded interface element comprises a mold material having shape stability at common sterilization temperatures, wherein the injection molded interface element comprises a deformation indicating pattern indicating a pre-breaking deformation. Both, the shaft and the interface element each have an elongated through bore, the both through bores aligning to each other.
• A method for manufacturing a reaming device, comprises wrapping a carbon fiber layer over an outer surface of a mounting portion of a shaft. A surface structure is pressed on an outer surface of the carbon fiber layer. An interface element is injection molded over the surface structure. The wrapping comprises impregnating the carbon fiber layer with an impregnation agent being compatible with a material of the shaft. The shaft mounting portion is prepared before wrapping a carbon fiber layer for establishing a reliable connection between the shaft and the carbon fiber layer. The pressing includes heat setting of the carbon fiber layer in a closed mold. According to an exemplary embodiment of the invention, a reaming device has a shaft with a mounting portion. The mounting portion has an outer surface, a carbon fiber layer and an injected-molded interface element for mechanically coupling an external device. The injected-molded interface element has a mounting portion. The carbon fiber layer extends over the outer surface of the shaft mounting portion and has its own surface. The carbon fiber layer outer surface has a surface structure. The injection-molded interface element mounting portion is injection-molded over the carbon fiber layer outer surface structure. Thus, the shaft can be provided with an outer surface structure, so that an injection-molded interface element can be easily integrally formed on the shaft, i.e. the carbon fiber layer extending over the shaft. Thus, the shaft can be designed to fulfill the particular requirements for a shaft, for example flexibility and a particular strength against breakage and wherein the integrally formed injection-molded interface element may be designed to fulfill the particular requirements for coupling an external device. Such requirements may include for example a particular geometry and particular material properties which may be met by the injection-molded interface element.
• According to an exemplary embodiment of the invention, the shaft is made of a carbon fiber reinforced material. Thus, a particular strength for preventing a breakage of a shaft can be provided, in particular as a carbon fiber reinforced material has a particular flexibility and elasticity while maintaining the capability of transmitting torque forces, and at the same time owing to the carbon fiber reinforced structure does not tend to break into multiple fragments.
• According to an exemplary embodiment of the invention, the carbon fiber layer comprises a wrapped carbon fiber with a resin impregnation. Thus, it is possible to bring the carbon fiber layer into a particular shape which is required for molding over the interface element. In particular, the resin impregnation may be a thermosetting resin, so that a particular cast can be heated to set the resin impregnation of the carbon fiber layer.
• According to an exemplary embodiment of the invention, the carbon fiber layer surface structure comprises a pressed tooth structure. Thus, a reliable connection between the shaft and the carbon fiber layer, respectively, on the one hand and the molded interface element on the other hand may be established. In particular, a tooth structure allows for a mechanically reliable force transmission between the shaft and the interface element.
• According to an exemplary embodiment of the invention, the interface element comprises a coupling portion for coupling a power tool reamer drive as an external device. Thus, a drive or any other power tool may be coupled to the coupling portion of the interface element in order to drive the shaft.
• According to an exemplary embodiment of the invention, the coupling portion comprises an end portion being capable of transmitting a torque. Thus, a torque of a power tool can be transmitted to the shaft via the interface element. In particular, the end portion may be designed as a hexagonal cross-section. However, it should be noted that also any other angular geometry may be used. It should be noted that also a free-shape cross-section may be used, e.g. having a waved outer contour. In particular, a unique cross-sectional shape may be used in order to guarantee the correct use of a particular tool together with the corresponding reaming device. In other words, the coupling of an intended combination of a reaming device and a corresponding power tool may be established by a unique corresponding coupling geometry between the power tool and the respective coupling portion or end portion of the interface element.
• According to an exemplary embodiment of the invention, the injection-molded interface element comprises a rated break arrangement or geometry (having a predetermined sheer strength) between its mounting portion and its coupling portion. Thus, a predetermined breaking point or a weak section can be established so that the reaming device will break at this particular section when exceeding a predetermined torque. In particular, this may avoid an unintended break at a location which is not accessible, for example close to the reaming head. In other words, the predetermined breaking point or rated break point will be established in a safe and accessible region of the reaming device so that no broken parts of the reaming device remain in the patient's body.
• According to an exemplary embodiment of the invention, the injection-molded interface element comprises a mold material having shape stability at common sterilization temperatures. Thus, it can be guaranteed that the reaming device cannot be sterilized without losing its particular geometry properties. This is of relevance if providing the reaming device as a single use device. In case, if the surgeon tries to use the reaming device again, he has to sterilize the reaming device, but during this sterilization, the reaming device will be predeterminently destroyed to avoid any reuse of the reaming device. It should be noted that either the entire interface element may be made of the non-heat resistant material, or only particular sections thereof may be made of the non-heat resistant material, if using for example a two stepped molding process using two different molding materials. It should also be noted that a heat resistant portion may be provided to maintain an “emergency” geometry, which however is not comfortable geometry for surgery. In particular one component of a multiple step mold may be heat resistant and the other component of a multiple step mold may be not heat resistant. The lost form stability may also be established by the impact of another parameter of sterilization, e.g. steam or the like. Thus, the interface element may be designed to lose its form stability when being treated by steam.
• According to an exemplary embodiment of the invention, the injection-molded interface element comprises a deformation indicating pattern indicating a pre-breaking deformation. Thus, the surgeon can directly recognize a critical deformation of the interface element when recognizing the indicating pattern. This indicating pattern may be for example a longitudinal line or a longitudinal groove extending into the longitudinal direction of the interface element. In case the longitudinal groove or line deforms for example like a helix, the surgeon knows that a torque is applied, or that a particular threshold may be extended. It should be noted, that also an interfering grid may be used as a deformation indicating pattern, so that for example a particular Newton pattern may occur at particular stages of deformation, so that a particular Newton pattern may be used as an indicative for the grade of deformation.
• According to an exemplary embodiment of the invention, both, the shaft and the interface element each have an elongated through bore, wherein the both through bores align to each other. Thus, a guide wire or a securing wire can be inserted into the aligning through bores. A guide wire may be used for an improved targeting of the reaming device, wherein a securing wire may be used for a reaming head being provided at the reaming device.
• According to an exemplary embodiment of the invention, a method is provided for manufacturing a reaming device, comprising: wrapping a carbon fiber layer over an outer surface of a mounting portion of a shaft. A surface structure is pressed onto an outer surface of the carbon fiber layer. An interface layer is injection-molded over the surface structure. Thus, in particular when using a shaft made of a carbon fiber reinforced material, a carbon fiber layer may provide a reliable and compatible connection between the carbon fiber layer and the shaft. The outer surface structure of the carbon fiber layer establishes a reliable mechanical connection between the carbon fiber layer and the injection-molded interface element. In particular, such a method allows manufacturing a reaming device without having undue material tensions during a manufacturing process, as an injection-molding more or less provides a material morphology having a low or no material tensions.
• According to an exemplary embodiment of the invention, wrapping comprises impregnating the carbon fiber layer with an impregnation agent being compatible with a material of the shaft. Thus, a reliable connection between the shaft and the carbon fiber layer may be established.
• According to an exemplary embodiment of the invention, the method further comprises preparing a shaft mounting portion before wrapping a carbon fiber layer for establishing a reliable connection between the shaft and the carbon fiber layer. Thus, a kind of priming can be carried out before mounting the wrapped carbon fiber layer onto the shaft in order to establish a reliable connection being capable of transmitting torque.
• According to an exemplary embodiment of the invention, pressing includes heat-setting of the carbon fiber layer in a closed mold. Thus, a fast and reliable manufacturing process can be established. In particular, when using a mold of a thermoplastic material and a thermosetting impregnation for the carbon fiber layer, a defined weak section can be established allowing a reliable transmission of forces and at the same time a predefined weak section as described above.
• It should be noted that the above features may also be combined. The combination of the above features may also lead to a synergetic effect, even if not explicitly described herein in detail.
• These and other aspects of the present invention will become apparent from and elucidated with reference to the embodiments described hereinafter.
BRIEF DESCRIPTION OF THE DRAWINGS
• FIG. 1 illustrates a shaft for a reamer with a carbon fiber layer before wrapping;
• FIG. 2 illustrates a shaft with a wrapped carbon fiber wrapping having a surface structure;
• FIG. 3 illustrates a cross-sectional view of a shaft with an overmolded interface element;
• FIG. 4 illustrates an outer view of a shaft with an overmolded interface element; and
• FIG. 5 illustrates a schematic flow chart of a method for manufacturing a reaming device.
DETAILED DESCRIPTION
• FIG. 1 illustrates ashaft10, in particular a reamer shaft having a mounting portion11. Theshaft10 has an outer surface, onto which acarbon fiber layer30 is wrapped.FIG. 1 illustrates thecarbon fiber layer30 in an unwrapped condition.
• FIG. 2 illustrates the end portion of ashaft10, wherein thecarbon fiber layer30 is wrapped around the outer surface of the mounting portion11. As can be seen fromFIG. 2, the carbon fiber layer comprises asurface structure34 on theouter surface33 of the carbon fiber layer. This outer structure may be formed for example as a tooth structure or a rippled or ripped structure, wherein ripples or rips run along a longitudinal direction of theshaft10. It should be noted that the rips of thesurface structure34 may also run in a helical way in order to carry not only circumferential forces, e.g. torque forces, but also forces in a longitudinal direction of the shaft, like pushing or pulling forces. It should be noted that thesurface structure34 may also have any other structure being capable of transmitting forces from theshaft10 to aninterface element20 or vice versa such as for example splines.
• FIG. 3 illustrates a cross-sectional view of the end section of ashaft10 provided with anovermolded interface element20. Theinterface element20 has a mountingportion21, which engages with the surface structure of the carbon fiber layerouter surface33,34. Thus, forces can be transmitted from theshaft10 to theinterface element20. The interface element and theshaft10 both may comprise a throughbore19,29, respectively, which through bores may align. Thus, a guide wire or a securing wire can be inserted through the aligned throughbores19,29 so as to serve as a guide for the reaming tool and the reaming process, as well as securing for example a reaming head to be mounted on the other end section of the shaft (not shown). The injection-moldedinterface element20 may comprise a ratedbreak section26, which may be for example a groove or a notch. As theinterface element20 also comprises acoupling portion25, the ratedbreak point section26 can be provided between the mountingportion21 on the one hand and thecoupling portion25 on the other hand. Thecoupling portion25 may serve for coupling a power tool or a drive tool for driving the reaming device. By providing the ratedweak section26 between thecoupling portion25 and the mountingportion21, an overburden of torque may lead to a predefined breakdown of the ratedbreak section26. As thissection26 may be designed as the weakest section with respect to a torque of the entire reaming device, a predefined breakdown or fracture of the ratedsection26 avoids a breakdown or fracture on a more critical section, like for example close to the reamer head or the shaft being inserted into the patient's body. Thus, in case the reamer breaks, the rated break section provides a break location being outside of the body of the patient. Thecoupling portion25 may further comprise a particular geometry for transmitting torque forces, for example the outer shape of a hexagonal cross-section in order to transmit torque forces. However, also a particular cross-sectional shape can be selected, which may be a unique cross-sectional shape which only fits to the corresponding power tool. Thus, it can be avoided that a not-matching combination of a reaming device and a power tool will be used.
• The material of the injection-molded interface element may be a material which loses its outer shape when being exposed to a common sterilization or autoclave temperature (greater than about 120° C.). This may be of relevance when providing a reaming device for single use only. Thus, if trying to sterilize the reaming device, the outer shape of the interface element loses its predetermined shape, so that a further use of the reaming device is not possible. Thus, a re-use of a reaming device being intended for single use only can be avoided.
• FIG. 4 illustrates the end portion of a reaming device having ashaft10 and an injection-moldedinterface element20. The injection-moldedinterface element20 may be provided with adeformation indicating pattern28. Thisdeformation indicating pattern28 may be for example a line extending into the longitudinal direction of the reaming device. In case, the interface element of the reaming device will deform, also the deformation indicating pattern will significantly deform, so that a surgeon will recognize the deformation. In particular, when stopping to apply a torque on the interface element, the shape of the deformation indicating pattern may be used as an indicative of a deformation of the interface element, even if no torque force is applied. If the interface element is deformed, it may be for example not used any longer. Such a deformation indicating pattern may be for example also an interference mesh or interference grid, so that depending on the deformation, several particular interference patterns may occur, which interference pattern may be used as an indicative for the strength of the deformation. This is illustrated as28aand28b. Thepattern28ais for example slightly inclined with respect to the longitudinal axis of the reaming device or theinterface element20, wherein thesecond pattern28bhas a counter inclination. When, for example, providing these bothpatterns28aand28bwith an intermediate layer, so that the deformation for example will increase the inclination of thefirst pattern28a,and decrease the inclination of thepattern28b,an occurring interference pattern may be used as a unique indication for the extent of the deformation.
• FIG. 5 illustrates a schematic flow of a method for manufacturing a reaming device. In step S10, the surface of the shaft may be prepared to provide an improved adhesion of thecarbon fiber layer30. This process may be considered as a kind of priming process. In step S20, the carbon fiber layer is wrapped over an outer surface of a mounting portion of a shaft. This wrapping optionally may comprise an impregnating process of the carbon fiber layer with an impregnation agent such as for example PEEK so as to increase the adhesion between theshaft10 and the carbon fiber wrapping30. In a subsequent step S30, a surface structure will be pressed on the outer surface of the carbon fiber layer. This can be carried out for example by a heated cast and the use of a thermosetting resin, so that step S30 may optionally include a heat setting process in step S35. Finally, aninterface element20 is injection-molded over the surface structure of the carbon fiber layer.
EXAMPLE
• The process for making a carbon fiber composite (CFC) reamer shaft will now be described:
• A prepreg fabric (Sigratex CE 8011-200-42-SGL Group) is cut into specific pieces for the shaft and the connection area by using a cutter; for example an Aristomat TL 1617. The pieces are then wound on a metal core by using an automatic rolling table. Cellophane tape is then wound over the CFC shaft to fit it and to withstand the expansion during heating. This is done by using a shrink film wrapper. The CFC shaft is then hardened in an oven and the cellophane tape is removed. The CFC shaft is then ground to a tolerance of ±0.05 mm and the core is removed. A small piece of CFC prepreg is wound on the machine connection side to later get a form fit for the injection molding part. A metal dovetail and the drill side of the CFC shaft is threaded over a second core and a CFC prepreg fabric is wound over both ends to fix the dovetail and CFC shaft together. Any cavities present are filled with epoxy. The CFC shaft with dovetail and machine side is then fixed in a mold made of two semicircular parts. By closing the mold the form fit for the later injection moulding of the machine connection and a homogenous smooth transition between dovetail and CFC shaft will be pressed on the shaft. The mold is heated in an oven again to harden the epoxy. Then the machine connection is insert molded with a torque limiter made of SAN on the CFC shaft.
• It should be noted that the term “comprising” does not exclude other elements and that the term “a” or “an” does not exclude a plurality. Also elements described in association with the different embodiments may be combined.
• Although the invention herein has been described with reference to particular embodiments, it is to be understood that these embodiments are merely illustrative of the principles and applications of the present invention. It is therefore to be understood that numerous modifications may be made to the illustrative embodiments and that other arrangements may be devised without departing from the spirit and scope of the present invention as defined by the appended claims.

Claims (15)

1. A reaming device comprising

a shaft with a mounting portion, the mounting portion having an outer surface;

a carbon fiber layer located on the mounting portion outer surface;

an injection molded interface element for mechanical coupling of an external device molded on the carbon fiber layer, the interface element having a mounting portion;

wherein the carbon fiber layer extends over the outer surface of the shaft mounting portion and having an outer surface,

wherein the carbon fiber layer outer surface has a non-smooth surface structure;

wherein the injection molded interface element mounting portion is injection molded over the carbon fiber layer surface structure.

2. The reaming device according toclaim 1, wherein the shaft is made of a carbon fiber reinforced material.

3. The reaming device according toclaim 1, wherein the carbon fiber layer comprises a wrapped carbon fiber with a resin impregnation.

4. The reaming device according toclaim 1, wherein the carbon fiber layer surface structure comprises a pressed tooth structure.

5. The reaming device according toclaim 4, wherein the pressed tooth structure comprises an elongated rippled structure.

6. The reaming device according toclaim 1, wherein the interface element comprises a coupling portion for coupling a power tool reamer drive as an external device.

7. The reaming device according toclaim 6, wherein the coupling portion comprises an end portion being capable of transmitting a torque.

8. The reaming device according toclaim 6, wherein the injection molded interface element comprises a rated break section between its mounting portion and its coupling portion.

9. The reaming device according toclaim 1, wherein the injection molded interface element comprises a mold material having shape stability at common sterilization temperatures.

10. The reaming device according toclaim 1, wherein the injection molded interface element comprises a deformation indicating pattern indicating a pre-breaking deformation.

11. The reaming device according toclaim 1, wherein both, the shaft and the interface element each have an elongated through bore, the both through bores aligning to each other.

12. A method for manufacturing a reaming device, comprising:

wrapping a carbon fiber layer over an outer surface of a mounting portion of a shaft; and

pressing a surface structure on an outer surface of the carbon fiber layer;

injection molding an interface element over the surface structure.

13. The method according toclaim 12, wherein wrapping comprises impregnating the carbon fiber layer with an impregnation agent being compatible with a material of the shaft.

14. The method according toclaim 12, further comprising preparing of shaft mounting portion before wrapping a carbon fiber layer for establishing a reliable connection between the shaft and the carbon fiber layer.

15. The method according toclaim 12, wherein pressing includes heat setting of the carbon fiber layer in a closed mold.

Images