Publication number: US20090074615A1
Application number: US11/856,227
Authority: US
Inventors: Donald R. Moles
Original assignee: YSI Inc
Current assignee: YSI Inc
Priority date: 2007-09-17
Filing date: 2007-09-17
Publication date: 2009-03-19
Also published as: US8137641B2; WO2009038987A1; US20110132870A1

Abstract

A microfluidic module that comprises an adhesiveless self-bonding rebondable polyimide film.

Description

FIELD OF INVENTION

The present application relates to a microfluidic module.

BACKGROUND

Microfluidic modules are useful in various applications. Microfluidic modules can be used to test small amounts of samples in fluid systems for contaminants, chemicals, or other analytes. Microfluidic modules may be used in the body, water systems, industrial fluid systems, or any of a variety of systems having liquid or gaseous components.

Microfluidic modules have been made from a variety of materials. One material is a self-bonding polyimide film that may be etched to form channels. The etched films are then layered and bonded together as described in the commonly assigned U.S. Pat. No. 5,932,799. The self-bonding polyimide film disclosed in the '799 patent contains an organotin compound that is employed in a single bonding operation. The organotin compounds react during bonding, and once bonded are not available for use in a second or subsequent bonding operation.

SUMMARY

One embodiment disclosed is a microfluidic module that comprises a self-bonding rebondable polyimide film. In a particular embodiment, the self-bonding rebondable polyimide film includes at least one fluid flow channel therein. In a still more particular embodiment, a film including a fluid flow channel is bonded to a cover sheet. The cover sheet may be a different plastic or metal but in a particular embodiment it is also a film of a self-bonding rebondable polyimide.

Another embodiment disclosed is a method of making a microfluidic module that comprises providing a sheet of a self-bonding rebondable polyimide, forming a fluid flow channel in the rebondable polyimide to provide a channel sheet, and bonding the channel sheet to a first cover sheet and optionally a second cover sheet.

Another embodiment is a channel sheet useful in a microfluidic module that comprises a sheet of self-bonding rebondable polyimide having a fluid flow channel formed therein.

Another embodiment comprises a channel sheet of self-bonding rebondable polyimide film having a fluid flow channel formed therein, and first or first and second cover sheets of self-bonding rebondable polyimide films directly bonded to the channel sheet and a layer of a metal.

In another embodiment, a microfluidic module comprises a channel sheet of adhesiveless self-bonding rebondable polyimide film having a fluid flow channel formed therein, a first cover sheet of adhesiveless self-bonding rebondable polyimide film directly bonded without adhesive to the channel sheet without adhesive, a second cover sheet of adhesiveless self-bonding rebondable polyimide film directly bonded without adhesive to the channel sheet opposite the first cover sheet, and a metal layer directly bonded to the second cover sheet opposite the channel sheet.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a sectional view of one embodiment of a microfluidic module;

FIG. 2 is a sectional view of one embodiment of a sheet of adhesiveless self-bonding rebondable polyimide film;

FIG. 3 is a sectional view illustrating forming a sheet of masked adhesiveless self-bonding rebondable polyimide;

FIG. 4 is a sectional view of the masked adhesiveless self-bonding rebondable polyimide after bonding of the layers or sheets;

FIGS. 5A and 5B are sectional views of a mask layer(s) having a fluidic pattern therein;

FIGS. 6A and 6B are sectional views of the masked adhesiveless self-bonding rebondable polyimide having channels (FIG. 6A) or partial channels (FIG. 6B) therein;

FIGS. 7A-7C are sectional views of the masked adhesiveless self-bonding rebondable polyimide after removal of the mask layer from the top surface;

FIGS. 8A and 8B illustrate a channel sheet and a cover sheet each including a metal layer prior to bonding;

FIGS. 9A and 9B are sectional views of a cover sheet bonded directly to a channel sheet, the cover sheet and channel sheet include a metal layer;

FIG. 10 is a sectional view of an intermediate useful in forming the microfluidic module in accordance with one embodiment;

FIG. 11 is a sectional view of the second cover sheet and the intermediate ofFIG. 10 before bonding them together;

FIG. 12 is a sectional view of an embodiment of a microfluidic module including a metal reinforcing layer.

DETAILED DESCRIPTION

The following description is intended to be representative only and not limiting. Many variations can be anticipated according to these teachings, which are included within the scope of the present invention. Reference will now be made in detail to the various embodiments of the present invention, examples of which are illustrated in the accompanying drawings.

As used herein “rebondable polyimide” refers to a polyimide that can be heat and/or pressure bonded to a material, e.g., a first sheet, in one bonding operation resulting in a composite containing the polyimide. The composite can be re-heat- and/or re-pressure-bonded alone, or in the form of a multilayer structure or module, to a second sheet or module, in a subsequent bonding operation. Thus, the rebondable polyimide is characterized in that it can be used in two or more bonding operations.

One example of a self-bonding rebondable polyimide is UPILEX® VT polyimide film available from UBE Industries, Ltd. The self-bonding rebondable polyimide films used in the modules of the present invention can be distinguished from the self-bonding polyimide films disclosed in U.S. Pat. No. 5,525,405 to Coverdell et al. The Coverdell et al. film is not rebondable. The film contains an organotin compound, the reactivity of which is exhausted after a single bonding operation. Thus, in making microfluidic modules using the Coverdell et al. films, the multiple layers of polyimide films must be stacked and bonded in one operation. Using VT polyimide, for example, the microfluidic module may be made by stacking rebondable polyimide films to form modules or sub-modules in multiple steps with multiple bonding operations and the final product can be built up of multiple modules or sub-modules that are bonded together in a subsequent bonding operation.

Examples of rebondable polyimide films that may be useful in the module are disclosed in U.S. Pat. No. 5,262,227, U.S. Pat. No. 5,741,598, U.S. Pat. No. 6,605,366, and U.S. Pat. No. 6,824,827 all commonly assigned to UBE Industries, Ltd., which are incorporated herein by reference. U.S. Pat. No. 5,262,277 describes an aromatic polyimide film that may have a metal foil directly fixed on the surface (Layer B or B′) of the substrate film with no adhesive. The aromatic polyimide substrate film is described as having a Layer A-Layer B construction or a Layer B-Layer A-Layer B′ construction. Layer A is a biphenyltetracarboxylic acid or its derivative (preferably the acid dianhydride) and a phenylenediamine. Layer B and layer B′ are basically the same and are derived from an aromatic tetracarboxylic acid or its derivatives and an aromatic diamine having two or more benzene rings.

Layer A may be an aromatic polyimide which is derived from a biphenyltetracarboxylic acid or its derivative and a phenylenediamine. Examples of the biphenyltetracarboxylic acid are 3,3′,4,4′-biphenyltetracarboxylic acid and 2,3,3′,4′-biphenyltetracarboxylic acid. Examples of their derivatives are their acid anhydrides and their esters. Their acid dianhydrides are preferred. These biphenyltetracarboxylic acids or their derivatives can be used in combination with other aromatic tetracarboxylic acids (e.g., pyromellitic acid and 3,3′,4,4′-benzophenonetetracarboxylic acid) or their derivatives (e.g., dianhydride), provided that the content of the latter acids or derivatives does not exceed 40 molar % of the total content of tetracarboxylic acids and their derivatives. Examples of the phenylenediamine are o-, m-, and p-phenylenediamine. The phenylenediamine also can be used in combination with other aromatic diamines (e.g., 4,4′-diaminodiphenylether, 3,4′-diaminodiphenylether, 4,4′-diaminodiphenylsulfone, and 3,4′-diaminodiphenylsulfone), provided that the content of the other aromatic diamines does not exceed 50 molar % of the total content of aromatic diamines.

According to the '277 patent, the biphenyltetracarboxylic acid or its derivative (and optionally other aromatic tetracarboxylic acid or its derivative) and the phenylenediamine (and optionally other aromatic diamine) are polymerized together to give a polyamic acid and then imidized to give an aromatic polyimide having a high molecular weight in the known manner. The aromatic polyimide preferably has no secondary transition point, because such polyimide shows high heat-resistance, high mechanical strength, and high dimensional stability.

According to the '277 patent, the aromatic tetracarboxylic acid or its derivative and the aromatic diamine having two or more benzene rings are polymerized together to give a polyamic acid and then imidized to give an aromatic polyimide in the known manner. The resulting aromatic polyimide preferably has a secondary transition point in the range of 250° to 400° C., because such aromatic polyimide shows high heat-resistance as well as high thermal adhesiveness (adhesion using pressure and heat) with a metal foil.

U.S. Pat. No. 5,741,598 describes a polyimide/polyimide composite sheet. The sheet has a polyimide substrate film having a polyimide of a specific recurring unit (see formula 1 in the '598 patent) and a polyimide coat having a polyimide of a specific recurring unit (see formula 2 in the '598 patent). The polyimide substrate film is prepared by reaction of 3,4,3′,4′-biphenyltetracarboxylic acid dianhydride (which may be referred to as “s-BPDA”: “s” standing for “symmetric”) and p-phenylenediamine (which may be referred to as “PPD”). According to the '598 patent, the p-phenylenediamine can be employed in combination with 4,4′-diaminodiphenyl ether (which may be referred to as “DADE”) under the condition that the molar ratio of PPD/DADE is in the range of 100/0 to 70/30. The polyamide acid of s-BPDA and PPD/DADE can be prepared from s-BPDA and a mixture of PPD and DADE. Otherwise, a polyamide acid of s-BPDA/PPD and a polyamide acid of s-BPDA/DADE are independently prepared and then both polyamide acids are combined. The polyimide coat is produced from a polyamide acid (or polyamic acid) prepared by reaction of 2,3,3′,4′-biphenyltetracarboxylic acid dianhydride (which may be referred to as “a-BPDA”: “a” standing for “asymmetric”) and 1,3-bis(4-aminophenoxy)benzene (which may be referred to as “TPE-R”). A metal may be fixed onto the polyimide/polyimide composite sheet be a hot melt method. According to the patent, the hot melt can be performed, preferably under the conditions of a temperature of 280° to 330° C., a pressure of 1 to 100 kgf/cm², and a period of 1 sec. to 30 min.

Self-bonding rebondable polyimides as described herein may be used in effectively any known microfluidic module construction. The microfluidic modules of commonly assigned U.S. Pat. No. 5,932,799, U.S. Pat. No. 6,073,482, U.S. Pat. No. 6,293,012, U.S. Pat. No. 6,406,605, and U.S. Pat. No. 6,551,496, all of which are incorporated herein by reference, may be modified and constructed using the adhesiveless self-bonding rebondable polyimide film to produce microfluidic modules.

FIG. 1 is an example of amicrofluidic module10 having afirst cover sheet12, achannel sheet14, and asecond cover sheet16. In one embodiment, these three sheets are self-bonding rebondable polyimide, but in another embodiment any one or more of the sheets can be a self-bonding rebondable polyimide. In particular, in other embodiments, one or both of the cover sheets could be a different plastic, for example a polyimide other than a self-bonding rebondable polyimide, or a metal film that is capable of being bonded to the rebondable polyimide without an adhesive. InFIG. 12, the microfluidic module includes ametal layer62 that, among other advantages, makes the illustrated module easier to handle or adds support to the layers of the microfluidic. In certain embodiments, at least the channel sheet will be a self-bonding rebondable polyimide.

InFIG. 1, thechannel sheet14 is illustrated with twofluid flow channels15 therein. In one embodiment, the microfluidic module may include a plurality of channel sheets. Thechannel sheet14 may have one fluid flow channel or a plurality offluid flow channels15 therein. The term “fluid,” as used herein, includes any material that is capable of flowing through the channels, especially gases, liquids, and solutions, suspensions, or dispersions of materials in gases or liquids. An advantage of using a self-bonding rebondable polyimide film is that it can be bonded to adjacent films without an adhesive. InFIG. 1, thetop surface24 ofchannel sheet14 is shown directly bonded, without adhesive, in a superimposed relation to thebottom surface21 offirst cover sheet12. Likewise, thebottom surface25 ofchannel sheet14 is shown directly bonded without adhesive in a superimposed relation to thetop surface27 ofsecond cover sheet16.FIG. 1 also showstop surface21 offirst cover sheet12 andbottom surface28 ofsecond cover sheet16. Even though this embodiment showsfluid flow channels15 only inchannel layer14, there may be additional fluid flow channels in thefirst cover sheet12 and/or thesecond cover sheet16. In particular, there may bevertical channels13 that link the flow ofchannels15 to other modules or devices. Also, as described below, channels can be partially formed in thechannel sheet14 and the first and/or the second cover sheets (seeFIG. 9B) or another adjacent channel sheet, which are assembled in registration with one another in a manner known in the art.

Thefluid flow channels15 may be of any shape or size sufficient to allow fluids to flow into or through reservoirs or other features within the microfluidic module. Thechannels15 may be networks of channels. The network of channels may be interconnecting. In one embodiment, a microfluidic module may include a feature designed for the mixing of fluids therein. For fluids to flow into and out of thechannels15, there may be openings in the channels. In one embodiment, thechannels15 may be about 1 to about 1000 μm wide and about 0.1 to about 1000 μm deep.

In one embodiment, at least one offirst cover sheet12,channel sheet14, orsecond cover sheet16 is one or a plurality (e.g., a composite) of self-bonded films of the self-bonding rebondable polyimide film. In a more particular embodiment, a plurality (for example, two or more films) of the adhesiveless self-bonding rebondable polyimide films may be heat and/or press laminated to make up thefirst cover sheet12, thechannel sheet14, and/or thesecond cover sheet16. In one embodiment, thechannel sheet14 may be about 25 μm to 1000 μm thick and the cover sheets may be about 25 μm to 1000 μm thick.

In another embodiment, as shown inFIG. 2, therebondable polyimide film30 may be a composite film, e.g., see U.S. Pat. No. 6,605,366, that includes a thermoplastic polyimide, on thetop surface32 and/orbottom surface33. In yet another embodiment, anon-thermoplastic polyimide34 may be sandwiched between thetop surface32 and thebottom surface33 of thermoplastic polyimide.

In another embodiment, as shown inFIG. 3, a sheet of masked adhesiveless self-bonding rebondable polyimide may have afirst mask layer42 and asecond mask layer44 with the adhesiveless self-bondingrebondable polyimide film30 therebetween. Thefirst mask layer42 and thesecond mask layer44 may be metal, plastic, or other films conventionally used as mask layers. In one embodiment, the first and second mask layers42,44 may be copper, stainless steel, aluminum, gold, or any other metal, or silicon, glass, or other material that bonds to the adhesiveless self-bonding rebondable polyimide, and can be etched by a process that will not etch the polyimide. The mask layer(s) stabilize, strengthen, and/or hold the adhesiveless self-bonding rebondable polyimide in place during lamination, bonding, rebonding, and/or etching of the mask layer and/or the polyimide. In one embodiment, for example seeFIG. 12, a metal layer may be used for its structural properties or distinguished from its use as a mask layer. In one embodiment, thefirst mask layer42 may be copper and thesecond mask layer44 may be stainless steel. In one embodiment, the mask layers42,44 may be about 1000 Å to 50 μm thick. The mask layers may be bonded directly to the adhesiveless self-bonding rebondable polyimide30 without adhesive by any of the following methods or other methods known in the art. In another embodiment, metal layers may be applied using sputtering, e-beam, or vapor deposition processes.

An autoclave method utilizes the pressures created by heating a compressed gas, such as nitrogen, in an enclosed space. The materials to be laminated are placed within a bag, which is evacuated and then sealed. The forces of the expanding vapor inside the confines of the autoclave exert pressure upon the bag surface thereby creating the conditions needed for bonding. The pressure may be hydrostatic pressure due to the vapor or the liquid within the autoclave.

A heated press method utilizes a heated platen in combination with a hydraulically, or otherwise mechanically, driven press to create the needed conditions.

Another method uses a high temperature oven in combination with a pressing fixture to accomplish bonding. In this method, the materials to be bonded are stacked in registration between metal platens connected to each other via a plurality of bolts, clamps, or the like, which, after tightening, hold the platens from moving apart from one another. This assembly is placed inside an oven and heated to the required bonding temperature while pressure is exerted upon the lamina inside the metal platens to cause the layers to bond.

In one embodiment, a plurality of adhesiveless self-bonding rebondable polyimide films may be stacked between a copper first mask layer and a stainless steel second mask layer. The bonding operation may be carried out, in the autoclave or other bonding apparatus, at temperatures of about 200° to about 400° C. for adhesiveless self-bonding rebondable polyimide films and at pressures of about 300 to about 400 psi (about 2000 KPa (20 bar) to about 2800 KPa (28 bar)) for a period of about 5 minutes to about 30 minutes. In one embodiment, the bonding may be carried out at about 300° C. with no added pressure. In another embodiment, the bonding operation may be carried out for a period of about 5 minutes to about 3 hours.

FIG. 4 shows a sheet of the masked adhesiveless self-bonding rebondable polyimide40 after bonding. The sheet includes afirst mask layer42 and asecond mask layer44 having the adhesiveless self-bonding rebondable polyimide30 bonded therebetween, such that the mask layers42,44 are on opposite sides of the adhesiveless self-bonding rebondable polyimide30 from one another. The masked adhesiveless self-bonding rebondable polyimide40, as shown inFIG. 4, includes one sheet of the adhesiveless self-bondingrebondable polyimide film30; however, the masked adhesiveless self-bonding rebondable polyimide40 is not limited thereto and may include multiple film layers, e.g., multiple laminates of the composite film shown inFIG. 2.

FIGS. 5A and 5B illustrate that thefirst mask layer42 and/or thesecond mask layer44 of the sheet of masked adhesiveless self-bonding rebondable polyimide40 include afluidic pattern17. Thefluidic pattern17 may be any design that corresponds to the selected placement of channels or other features to be formed in the adhesiveless self-bonding rebondable polyimide30. Thefluidic pattern17 may be etched into the first and/or second mask layers42,44 using etching techniques known in the art. For example, the mask layer may be etched using photolithographic etching techniques. Photolithographic etching may be particularly useful when the mask layer is a metal. The photolithographic etching creates openings in the metal that correspond to the locations where the rebondable polyimide will be subsequently removed. In one embodiment, as shown inFIG. 5A, thefirst mask layer42 is etched with afluidic pattern17, while thesecond mask layer44 is un-etched. In another embodiment, as shown inFIG. 5B, thefirst mask layer42 and thesecond mask layer44 are both etched with afluidic pattern17.

FIGS. 6A and 6B show the masked adhesiveless self-bonding rebondable polyimide40 havingchannels15 formed therein. As shown inFIG. 6A, the masked adhesiveless self-bonding rebondable polyimide40 includes achannel sheet14 having afluid flow channel15, afirst mask layer42 on thetop surface24 of the channel sheet and asecond mask layer44 on thebottom surface25 of the channel sheet. Both thefirst mask layer42 and thesecond mask layer44 include afluidic pattern17. The first or second mask layer also functions to allow the adhesiveless self-bonding rebondable polyimide to be etched completely through while holdingislands19 of the adhesiveless self-bonding rebondable polyimide in place relative to one another. As shown inFIG. 6B, the masked adhesiveless self-bonding rebondable polyimide40 includes achannel sheet14 having a partialfluid flow channel18, afirst mask layer42 on thetop surface24 of the channel sheet and asecond mask layer44 on thebottom surface25 of the channel sheet, where thefirst mask layer42 includes afluidic pattern17.

Channels15 (FIG. 6A) and/or the partial channels18 (FIG. 6B) may be formed in the adhesiveless self-bondingrebondable polyimide film30 to form thechannel sheet14. Thechannels15 orpartial channels18 may be formed through thefluidic pattern17 in the mask layers42 and/or44 into the adhesiveless self-bondingrebondable polyimide film30 by conventional methods such as microlithographic etching techniques, including wet, plasma, laser, ion, e-beam etching, or the like. In other embodiments, the channels may be formed via mechanical methods such as milling, scribing or higher pressure article stream methods, or a combination of any of the above-mentioned methods.

Thefluid flow channels15 and/orpartial channels18 may include, but are not limited to, a feed channel, a sensor channel, an inlet channel, an egress channel, and/or a micro-reactor channel. Any of thesefluid flow channels15 may be branched. A feed channel is a fluid flow channel that provides for feed of calibrant, buffer, analyte, or other solutions into the microfluidic module or for mixing of chemicals or solutions therein. These solutions may be used within the microfluidic module to detect analyte presence and/or concentration. A sensor channel is a fluid flow channel that is adapted so that a sensing element can measure selected data about the fluid within the channel. In one embodiment, the sensing element may be included in the fluid flow channel. In another embodiment, the sensing element may be external to the fluid flow channel; for example, the fluid flow channel may include a window and a sensing element adjacent the window that may measure selected data through the window. The sensing element may be an electrode, working electrode, counter-electrode, an optical sensing element, an electrochemical sensing element, and/or a microporous sensor. The sensing element should be capable of measuring the analyte as it flows past the sensing element. The electrochemical sensing element may include, but is not limited to, an amperometric, potentiometric, or conductimetric element(s). The sensing element may be formed along the sensor channel, as described in the '799 and the '482 patents. In one embodiment, in one fluid flow channel multiple sensing elements may be in an in-line series disposition along the channel to allow multiple analysis to be conducted. An inlet channel is a fluid flow channel that allows fluid to flow into a feature of the microfluidic module. An egress channel is a fluid flow channel that allows fluid to flow from a feature of the microfluidic module. In one embodiment, the inlet and/or egress channels may be disposed within the microfluidic module. In another embodiment, the inlet and/or egress channels may terminate intop surface21 or bottom surface28 (FIG. 1). A micro-reactor may be made by immobilizing biomolecules, such as enzymes, catalytic entities, or the like, within features in the microfluidic module.

FIGS. 7A-7C show the masked adhesiveless self-bonding rebondable polyimide40 in which one of the mask layers is removed. By selecting appropriate materials/metals for the mask layers, as described herein, the mask layers can be selectively and sequentially removed. Thefirst mask layer42 and/or thesecond mask layer44 may be removed.FIG. 7A illustrates achannel sheet14 having amask layer44.FIG. 7B illustrates a first cover sheet having a partialfluid flow channel18 formed therein and amask layer44.FIG. 7C illustrates asecond cover sheet16 including amask layer44. Any of the sheets illustrated inFIGS. 7A-7C may includechannels15,partial channels18, vertical channels13 (show inFIG. 1), or any other feature disclosed herein.

The mask layers may be removed by any suitable method that will not damage the underlying adhesiveless self-bondingrebondable polyimide film30. In one embodiment, a method may be selected to remove thefirst mask layer42 without removing thesecond mask layer44. In one embodiment, the mask layer to be removed may be metal and a chemical solution may be used to remove the metal. In one embodiment, thefirst mask layer42 may be copper. An ammonium persulphate solution may be used to remove the copper. In another embodiment, thesecond mask layer44 may be stainless steel. A ferric chloride solution may be used to remove the stainless steel. The ammonium persulphate solution used to remove thecopper mask layer42 will not remove asecond metal layer44 of stainless steel, such that the metal layers may be removed or retained selectively.

FIGS. 8A and 8B illustrate achannel sheet14 and thecover sheet12 prior to being bonded together by the adhesiveless self-bondingrebondable polyimide films30. The element shown inFIG. 8A is obtained by removing one of the mask layers from the channel sheet. The exposed first surfaces24 of the adhesiveless self-bondingrebondable polyimide film30 face one another such that thechannels15 are appropriately positioned before bonding the

sheets

12,14 together.FIG. 8B shows one embodiment in which achannel sheet14 with a mask layer and afirst cover sheet12 with a metal reinforcing layer that have their exposed first surfaces24 of the adhesiveless self-bondingrebondable polyimide film30 facing one another such that thepartial channels18 are aligned at the interface of the sheets.

It will be apparent that the step of bonding of the adhesiveless self-bondingrebondable polyimide films30 of thefirst cover sheet12 and thechannel sheet14 represents a second bonding (rebonding) of the adhesiveless self-bondingrebondable polyimide film30, since the adhesiveless self-bonding rebondable polyimide film's30

first surface

24 of both thefirst cover sheet12 and thechannel sheet14 are previously bonded to the mask or reinforcing layer. This rebonding step without adhesive is possible due to the rebondable property of the polyimide films used herein. The bonding of thechannel sheet14 to thefirst cover sheet12 may be by any of the methods described above or known methods in the art for the adhesiveless self-bonding rebondable polyimide and the mask layers. In one embodiment, a high temperature autoclave may be used for the step of bonding. These bonding operations may include placing the respective sheets between an upper platen placed on top of the sheets and a lower platen placed on the bottom. In one embodiment, a sheet or film of another material may be between the platen and the adhesiveless self-bonding rebondable polyimide surface nearest the platen to keep the rebondable polyimide from bonding to the platen. The sheet or film may be a metal or an adhesiveless self-bonding polyimide, such as UPILEX®-S by UBE Industries. The platens may include registration pins to keep the fluid flow channels, ports, and other features of the channel sheet, first cover sheet, and second cover sheet in superimposed and/or correct registration. In one method, the sheets between the platens may be heated at about 250° C. to about 350° C. for about 1.5 hours to about 2.5 hours. In another embodiment, the sheets may be heated for about 1 hour to about 3 hours. In one method, the platens may be hydraulically driven together to form a pressure nip on the layers. In another method, heavy cell plates with perimeter bolts may be used to increase the pressure on the sheets.

FIGS. 9A and 9B show the adhesiveless self-bondingrebondable polyimide films30 of thefirst cover sheet12 bonded directly to thechannel sheet14 without adhesive. In one embodiment, as shown inFIG. 9A, the bonded adhesiveless self-bondingrebondable polyimide films30 includeschannels15 that extend through thesheet14. In one embodiment, as shown inFIG. 9B, afluid flow channel18 may be partially formed in the interfacing surface portions of thefirst cover sheet12 and/or inchannel sheet14, or thesecond cover sheet16 and/or inchannel sheet14 such that when directly bonded in registration in a superimposed relation afluid flow channel15 is formed as described in commonly assigned U.S. Pat. No. 5,932,799 (the '799 patent) and U.S. Pat. No. 6,073,482 (the '482 patent). In one embodiment, the second mask layers44 may both be stainless steel. In another embodiment, at least one of the metal layers may be etched with afluidic pattern17.

FIG. 10 shows one embodiment of a two-layer element50 useful in forming microfluidic modules. The two-layer element50 is formed by removing the mask layers from thechannel sheet14 and bonding thecover sheet12 to thechannel sheet14 as described above.

FIG. 11 illustrates thesecond cover sheet16 and theelement50, which includes thefirst cover sheet12 bonded to thechannel sheet14, prior to being bonded together without adhesive by the adhesiveless self-bondingrebondable polyimide films30. In one embodiment, as shown inFIG. 11, thesecond cover sheet16 and the two-layer intermediate50 are positioned with the exposedfirst surface24 of thesecond cover sheet16 and the exposedsecond surface25 of thechannel sheet14 of the two-layer element50 facing one another prior to bonding. The sheets are appropriately positioned to formchannels15 or other features in the adhesiveless self-bonding rebondable polyimide films. In one embodiment, theelement50 may only have thesecond mask layer44 removed from thesecond surface25 of thechannel sheet14 to expose thesecond surface25 for bonding to thesecond cover sheet16 including amask layer44.

The bonding of theelement50 to thesecond cover sheet16 may be by any of the methods described above for the adhesiveless self-bonding rebondable polyimide and the mask layers. This bonding represents a rebonding of the adhesiveless self-bondingrebondable polyimide films30 because previously the adhesiveless self-bonding rebondable polyimide film's30

first surface

24 and/orsecond surface25 ofelement50 was bonded to a mask layer. In another embodiment, the bonding of thefirst cover sheet12 and thesecond cover sheet16 to thechannel sheet14 may be performed in one step where the sheets are directly bonded to one another without adhesive. Once again, the bonding may be by any of the methods described above for the adhesiveless self-bonding rebondable polyimide and the mask layers.

FIG. 12 shows one embodiment of amicrofluidic module60. Themicrofluidic module60 includes achannel sheet14, afirst cover sheet12, asecond cover sheet16 and amask layer62, which may be metal.Channel sheet14 includes afluid flow channel15 formed therein. Thefluid flow channel15 may be formed by etching as described above. Thefirst cover sheet12 is directly bonded without adhesive to channelsheet14 by the adhesiveless self-bonding rebondable polyimide to coverfluid flow channel15. Thesecond cover sheet16 is also directly bonded without adhesive to channelsheet14 opposite thefirst cover sheet12 by the adhesiveless self-bonding rebondable polyimide of the channel sheet. While all three

sheets

12,14 and16 may be rebondable polyimide films as described above, embodiments are included herein whereonly sheet14 may be rebondable polyimide as well as embodiments in which

sheets

12 and16 are rebondable andsheet14 is a different film.

The cover sheets may include a port (as described below), a vertical channel (seeFIG. 1), or any other feature disclosed herein. Themask layer62 may be directly bonded (preferably without adhesive) to thesecond cover sheet16

opposite channel sheet

14. Themask layer62 may be removed from thesecond cover sheet16 to reveal a microfluidic module similar to that shown inFIG. 1 or the mask layer may be left in place to facilitate handling.

Alternatively, the mask layer may be used to improve the firmness of the polyimide layer to make the module easier to handle or manipulate. Thus, the present invention includes embodiments in which the mask layer is used as a mask and as an intermediate that is useful in forming the microfluidic module. The invention also includes embodiments in which the mask layer forms part of the microfluidic module itself to provide structural support and make the film easier to manipulate. In the latter case, the metal layer is not removed in the fabrication process. The mask layer may function as a shield to protect the microfluidic module from damage from the surroundings. In one embodiment, the mask layer may be copper, which may act as a capacitor, an electrical conductor, or take part in a chemical reaction. In one embodiment, the mask layer may be stainless steel and may have an electrical pathway designed therein, or the stainless steel may be coated with silver to function as an electrode.

In another embodiment, the fluidic design for thefirst cover sheet12 and/or thesecond cover sheet16 may include a port (not shown in the figures). The port may be an opening or channel that allows fluid(s) to move or be transferred between features within the microfluidic module, or between the exterior of the module and the interior of the module. The port may be etched as described above for a sheet having a first metal layer and/or a second metal layer, or a sheet of only rebondable polyimide. The port may be partially positioned over afluid flow channel15 to be in fluid flow communication with thefluid flow channel15. The port may be any size and shape opening as needed to suitably allow fluid communication between the exterior of the microfluidic module andfluid flow channel15, or between various interior features of the microfluidic module, e.g., a reservoir, a valve, a fluid flow channel, a feed channel, a sensor channel. In one embodiment, the port may provide access to the channel layer's14

fluid flow channel

15 from thetop surface21 offirst cover sheet12, from thebottom surface28 ofsecond cover sheet16, or from both. In another embodiment the port may extend partially through thefirst cover sheet12 and/or thesecond cover sheet16 to provide a pathway between interior features of the microfluidic module.

In one embodiment, the microfluidic module may include a valve region. The valve region may selectively block or allow communication between the feed and sensor channels. The valve region may be as described in the '799 patent, the '482 patent, or the '605 patent, which are incorporated above. The valve region may include a reservoir, an electroosmotic flow membrane, a diaphragm, a pump, a valve, and channels leading into and/or out of the valve region. Alternatively, a valve construction as described in U.S. Pat. Nos. 4,848,722, 4,858,883, 4,304,257, 4852851 or 5660370 to Webster may be used.

The microfluidic module may include one or more multiple fluid flow channels including a feed channel, a sensor channel, valve region and a sensing element to detect or analyze different analytes.

The preceding description and accompanying drawings are intended to be illustrative of the present invention and not limited. Various other modifications and applications will be apparent to one skilled in the art without departing from the true spirit and scope of the invention as defined by the following claims.

Claims

1. A microfluidic module comprising a self-bonding rebondable polyimide film.

2. The microfluidic module ofclaim 1 wherein the module comprises a plurality of self-bonding rebondable polyimide films.

3. The microfluidic module ofclaim 2 wherein the module includes a channel sheet of a self-bonding rebondable polyimide film.

4. The microfluidic module ofclaim 3 wherein the channel sheet includes a top surface and a bottom surface and the module includes a first cover sheet and/or a second cover sheet respectively bonded to the top surface and/or the bottom surface of the channel sheet.

5. The microfluidic module ofclaim 4 wherein the cover sheet is a plastic film.

6. The microfluidic module ofclaim 4 wherein the plastic film is a self-bonding rebondable polyimide film that is bonded to the channel sheet without an adhesive.

7. The microfluidic module ofclaim 1 wherein the module additionally includes a metal layer.

8. The microfluidic module ofclaim 5 wherein the module additionally includes at least one metal layer bonded to the cover sheet.

9. The microfluidic module ofclaim 1 wherein the self-bonding rebondable polyimide film is a composite film that includes thermoplastic polyimide surface layers on opposite sides of a non-thermoplastic polyimide substrate layer.

10. The microfluidic module ofclaim 1 wherein the module is an analyzer module including a sensor.

11. A method of making a microfluidic module comprising:

(a) forming a fluid flow channel in self-bonding rebondable polyimide film to provide a channel sheet; and

(b) bonding the channel sheet between a first cover sheet and/or a second cover sheet.

12. The method ofclaim 11 wherein the step of forming the fluid flow channel includes etching the rebondable polyimide.

13. The method ofclaim 12 wherein the channel sheet is bonded to a mask layer and the step of forming the fluid flow channels includes etching the mask layer with a fluidic pattern and etching the channel layer through the etched mask layers.

14. The method ofclaim 13 wherein the channel sheet is bonded between first and second mask layers and the step of forming the channels includes etching the mask layers in a fluidic pattern and etching the channel layer through the mask layers.

15. The method ofclaim 14 wherein the first mask layer is copper.

16. The method ofclaim 15 wherein the second mask layer is stainless steel.

17. The method ofclaim 11 wherein the rebondable polyimide film is a composite film that includes a thermoplastic polyimide in at least a top surface and a bottom surface of the film.

18. The method ofclaim 11 wherein the bonding step includes bonding without adhesive the exposed first surface of the channel sheet's rebondable polyimide to the first cover sheet.

19. The method ofclaim 17 wherein the bonding step includes heating at about 275° C. to about 325° C. for about 5 minutes to about 3 hours.

20. In a microfluidic module having a first sheet of an adhesiveless self-bonding polyimide having a top surface and a bottom surface; a second sheet of an adhesiveless self-bonding polyimide having a top surface and a bottom surface, said first and second polyimide sheets being in superposed relation with said bottom surface of said first sheet of polyimide facing said top surface of said second sheet of polyimide, said sheets being directly bonded together at the interface of the sheets without an adhesive; and at least one fluid flow channel at the interface of said first sheet and said second sheet, the improvement comprising:

at least one of the first sheet and the second sheet is an adhesiveless self-bonding rebondable polyimide.

21. The module ofclaim 20 wherein the rebondable polyimide film is a composite film that includes a thermoplastic polyimide in at least a top surface and a bottom surface of the rebondable polyimide film.

22. A microfluidic module comprising:

a channel sheet of adhesiveless self-bonding rebondable polyimide film having a fluid flow channel formed therein; and

a first cover sheet of adhesiveless self-bonding rebondable polyimide film directly bonded to the channel sheet without adhesive.

23. The module ofclaim 22 further comprising a metal layer bonded to the first cover sheet opposite the channel-forming sheet.

24. The module ofclaim 23 further comprising a metal layer bonded to the channel sheet opposite the first cover sheet.