US20060287711A1 - Stent for positioning in a body conduit or method for producing this stent - Google Patents

Abstract

By a contrast means contained in an inventive stent which has a greater permeability for x-radiation features than the body tissue surrounding the stent in a relevant body conduit, this stent can be clearly detected in its position on an x-ray image of the relevant body conduit while at the same time exhibiting good biological compatibility; a gas, especially one contained in cavities of the stent is provided as a contrast means. The inventive production method for this stent with the aid of a catheter embodied specially for the purpose enables the production of the stent from a malleable polymer mass in the relevant body conduit so that the stent is adapted especially precisely to the shape of the relevant body conduit.

Description

CROSS REFERENCE TO RELATED APPLICATIONS
• This application claims priority of German application No. 10 2005 024 625.7 filed May 30, 2005, which is incorporated by reference herein in its entirety.
FIELD OF THE INVENTION
• The invention relates to a stent for positioning in a body conduit or to a method for producing this stent, with the stent containing a contrast means for x-radiation.
BACKGROUND OF THE INVENTION
• A stent is a tubular implant which provides radial outwards support for the wall of a body conduit, e.g. a blood vessel, bile duct, an air conduit or an esophagus. The stent usually consists of the elastic material, e.g. a metal or metal alloy or a polymer, and frequently has a mesh or network or spiral-type structure, with stents in the form of a metal mesh being the most widely used. The stent is introduced into the relevant body conduit with the aid of a catheter and is bought into adhesive contact there with the wall of the body conduit. With blood vessels specifically stents are introduced into the wall of the vessel as endoluminal vessel prostheses for therapy of stenoses caused by arterosclerotic plaque.
• A stent is known from US 2004/0148014 A1 in which markers impermeable to x-rays are distributed, in order to make the position of the stent clearly visible on an x-ray image once it has been used in the relevant body conduit. These markers most contain substances such as heavy metals or iodine compounds which, when used in the body conduit—even with an appropriate encapsulation—present a potential danger to health.
SUMMARY OF THE INVENTION
• The object of the present invention is to specify a stent which is simple to produce, which, despite being easily visible on an x-ray image, still exhibits good biological compatibility without a potential danger to health.
• This object is achieved by a stent or by a method in accordance with the independent claims; advantageous embodiments of the invention are the subject of the assigned subclaims in each case.
• Through the inventive contrast means contained in the stent, which has a greater permeability for x-radiation than body tissue surrounding the stent in the relevant body conduit, the introduction of a potentially hazardous contrast means with a lower permeability for x-radiation in the body conduit is avoided and yet easy identification of the stent introduced into the relevant body conduit on an x-ray image of the body conduit is still guaranteed.
• Contrast means with a higher permeability for x-radiation than the surrounding body tissue in each case are known as negative contrast means; they are shown as dark areas on an x-ray image. On the other hand a contrast means with a lower permeability for x-radiation than the body tissue surrounding it is referred to as a positive contrast means; they are shown as light areas on the x-ray image. Unlike positive contrast means, which as a result of the compounds that they contain, with elements with a high atomic number, are at least potentially damaging to health, negative contrast means mostly have good biological compatibility.
• A negative contrast means in the form of a gas, especially in the form of carbon dioxide, enables an especially high permeability for x-radiation and thus an especially good detectability of the position of the stent in the body conduit on the X-ray image. As a rule gases exhibit a far lower atomic density than a solid or a liquid with the same substance so that gases of the low atomic density are accordingly particularly permeable for x-radiation. In addition gases, especially carbon dioxide, are inexpensive by comparison with the usual positive contrast means.
• By enclosing the gas in cavities of the stent on the one hand the stability of the stent is increased and on the other hand by selecting an appropriate distribution density of the cavities and/or through the form of the hollow cavities the elastic properties of the stent can be adapted to the relevant purpose for which it is used or to the relevant body conduit; tubular cavities extending in the longitudinal direction of the stent for example allow the stent to be bent easily in the longitudinal direction without this process reducing the radial stability of the stent. In addition the stent is then also still able to be detected on the x-ray image if for example a few cavities are not gas-tight and some of the gas escapes when the stent is positioned, during its expansion or during its time in the body conduit. In addition a stent with cavities containing the gas is simple and cheap to produce.
• A stent consisting at least partly of a polymer guarantees especially good biocompatible properties and a low-cost production of the stent; the stent can for example consist entirely of the polymer or be coated with the polymer. A stent made entirely of polymer, such as silicone or rubber for example, where necessary except for the negative contrast means, is in addition especially elastic and can also be easily adapted to a distortion of the body conduit.
• In accordance with one embodiment of invention the polymer is embodied in the form of a polymer foam containing the cavities; a stent consisting of this polymer foam is especially simple to produce by foaming up the polymer with the gas. Polyurethane is suitable for example as the polymer and can be foamed up in a manner known per-se with little effort. The still liquid polymer can be foamed up in the production of the stent both by introducing the gas into it and by letting a gas dissolved in the polymer escape.
• In accordance with a further embodiment of the invention the polymer is embodied in the form of small polymer balls containing the cavities; these can be incorporated into the stent particularly easily, e.g. by mixing the polymer balls with a liquid material from which the stent is formed, in which case the liquid material itself can again also be a polymer.
• The inventive method of production for the stent consisting at least partly of the polymer with simultaneous positioning of this stent in the body conduit using a catheter positioned in the body conduit with a filling area at least partly enclosing this catheter which can be filled with a polymer mass to be hardened into a stent provides a simple means of producing the stent which is clearly visible on the x-ray image and yet is still biologically compatible; in addition the stent is precisely adapted to the form of the relevant body conduit by been formed in the body conduit so that the stent is secured against slippage in the body conduit and damage to the body conduit by the stent is avoided.
• In accordance with an embodiment of the invention there is advantageous provision for filling the filling area positioned at the position intended for the stent with a polymer mass temporally accommodated in an inner chamber of the catheter; in this way, especially for simple introduction of the catheter into the body conduit, it is possible to fill the filling area with the plastic mass only once the position intended for the stent is reached.
BRIEF DESCRIPTION OF THE DRAWINGS
• The invention, as well as further advantageous embodiments of the invention in accordance with features of the subclaims, are explained in greater detail below with reference to schematic diagrams of exemplary embodiments in the drawing, without this restricting the invention to this exemplary embodiment in any way; The Figures show:
• FIG. 1 in a perspective view, a stent divided into two parts made of a polymer, with a contrast means in the form of a gas enclosed in cavities;
• FIG. 2 a stent as shown inFIG. 1 made of a polymer foamed up with the gas;
• FIG. 3 a stent as shown inFIG. 1 with the small polymer balls containing the gas;
• FIG. 4 in a longitudinal cross-section, a catheter introduced into the body conduit with a filling area which is enclosed by an envelope and able to be filled with a polymer mass which is held in a capsule arranged in a catheter;
• FIG. 5 the catheter shown inFIG. 4 with the filling area being filled with the polymer mass and thereby expanded towards the wall of the body conduit;
• FIG. 6 the catheter shown inFIG. 4 with the filling openings from the capsule to the filling area closed and the envelope separated from the catheter;
• FIG. 7 the body conduit shown inFIG. 4-6 with the stent produced by the catheter;
DETAILED DESCRIPTION OF THE INVENTION
• FIG. 1 shows in a perspective view, a stent made of a polymer which is shown in a cross section at right angles to the longitudinal direction of the stent, divided into afirst part1 and asecond part2, in order to make thecavities3 surrounded by the polymer and filled with a gas visible in asectional surface4 of thefirst part1.
• There is provision to feed a catheter through anopening5 passing through thestent1,2 and to place thestent1,2 on the catheter in such a way that the stent encloses an expandable balloon section of the catheter in the form of a tube. Subsequently thestent1,2 is introduced with the aid of the catheter into a body conduit and is adapted there to the internal diameter of the body conduit by an expansion of the balloon section. Finally the catheter is removed while thestent1,2 remains in the body conduit and provides radial support for this.
• The gas contained in the cavities, e.g. carbon dioxide, operates as a negative contrast means so that the position of thestent1,2 within the body conduit can be detected on an x-ray image of the body conduit. The more gas is enclosed in the ratio by volume to the remaining stent material in thestent1,2 the more clearly the image of thestent1,2 stands out as a dark area against the image of the body tissue surrounding thestent1,2.
• So that the stent, after its expansion into its expanded form, retains this form even after the catheter has been removed, the stent consists at least partly of a plastic deformable material which permanently assumes its changed shape through a radial expansion. This material can for example be embodied in the form of a number of rings distributed over the length of thestent1,2 and surrounding theopening5 in each case. Alternatively it is also possible to arrange an elastically deformable wire mesh within thestent1,2 which keeps thestent1,2 in the expanded state after its expansion.
• FIG. 2 likeFIG. 1, shows astent1,2 made of polymer, with the polymer being embodied in the form of a polymer foam which can be seen from thecross-sectional surface4. The negative contrast means in the form of a gas is enclosed in thecavities3 of the polymer foam.
• FIG. 3 likeFIGS. 1 and 2, shows astent1,2 made of polymer, with the polymer being embodied in the form ofsmall polymer balls6 which can be seen from thecross-sectional surface4. The negative contrast means is enclosed in gaseous form in the cavities of the polymer foam. The other stent material surrounding the small polymer balls in thestent1,2 can be both the same polymer and also another substance, such as a second polymer for example.
• Instead of a surface enclosed in a radial direction, thestent1,2 can also have a surface in the form of a mesh or in the form of a grid.
• FIGS. 4-7 illustrate typical examples based on an exemplary embodiment for the inventive method for producing astent20 by means of acatheter8 with simultaneous positioning of thestent20 in abody conduit7.
• FIG. 4 shows in a longitudinal cross section acatheter8 introduced into abody conduit7 with an essentiallytubular filling area9 surrounding thecatheter8 which is enclosed by anenvelope10 and which is connected via two fillingopenings11 or12 to an inner chamber in the form of acylindrical capsule14 arranged in the catheter, containing a liquefied andhardenable polymer mass13. Theenvelope10 is held onto the catheter at its front and rear end by an extendable andretractable clamping ring15 or16 which encloses the entire circumference of thecatheter8 in each case, so that the fillingarea9 is completely sealed off from thebody conduit7. The two fillingopenings11 and12 each have anopening slider17 or18, with which the fillingopenings11 or12 respectively are closed off. To fill thefilling area9 with thepolymer mass13 from thecapsule14, apiston19 which can be pushed within thecapsule14 is provided. Theclamping rings15 or16, theopening sliders17 or18 and also thepiston19 are remotely operated automatically or at least partly with the involvement of an operator of thecatheter8. Thecatheter8 is already positioned with itsfilling area9 at the position intended for the stent.
• In an especially uncomplicated manner thepolymer mass13 is mixed with the negative contrast means before thefilling area9 is filled with thispolymer mass13; this removes the need for separate filling of thefilling area9 with thepolymer mass13 on the one hand and the negative contrast means6 on the other hand. In this exemplary embodiment the negative contrast means in the form of thesmall polymer balls6 filled with carbon-dioxide is mixed in homogeneously with thepolymer mass13 before thecatheter8 is introduced into thebody conduit7.
• Depending on the contrast means used in each case it is also possible to have the fillingarea9 filled with the negative contrast means before it is filled with thepolymer mass13.
• When a contrast means in the form of a gas, especially in the form of carbon dioxide is used, this is distributed especially easily and cost-effectively by foaming up the polymer mass with the gas in thestent8. The foaming-up of the gas can be undertaken both before and also after the filling of the filling area with thepolymer mass13. In the case of foaming up in the form of letting the gas escape into the polymer, this process is expediently undertaken in the fillingarea9.
• FIG. 5 shows thecatheter8 shown inFIG. 4 with on the one hand the fillingopenings11 and12 opened by moving one of the openingsliders17 or18 and on the other hand thepiston19 pushed into thecapsule14, so that the filling area is filled with thepolymer mass13 from thecapsule14. Filling the filling area with thepolymer mass13 expands the filling area so that this advantageously adapts its form and its size to thebody conduit7. In this case the expansion does not create any undesired expansion forces since the liquefiedpolymer mass13 can distribute itself to match the wall of thebody conduit7.
• After the fillingopenings11 or12 have been closed again thepolymer mass13 is hardened to create thestent20, depending on the polymer for example, simply by a hardening period elapsing.
• FIG. 6 shows thecatheter8 shown inFIG. 5, with the fillingopenings11 or12 being closed again for an especially simple removal of thecatheter8 from thebody conduit7, especially before the hardening of thepolymer mass13. InFIG. 6 thepolymer mass13 is already hardened into thestent20 and in addition theenvelope11 is released from acatheter8 by retraction of the clamping rings15 or16. In this state it is possible to withdraw thecatheter8 from thebody conduit7 with thestent20 simultaneously remaining in thebody conduit7.
• To adapt thestent20 in respect of its internal diameter an inflatable balloon section surrounded by the filling area (9) is additionally provided which is inflated after the positioning of the fillingarea9 at the position intended for thestent20.
• FIG. 7 shows thebody conduit7 shown in theFIGS. 4-6 with thestent20 produced by thecatheter8 after the removal of thecatheter8 from thebody conduit7, with the envelope released from acatheter8 remaining with thestent20 in thebody conduit7 as a component of the latter. By using a material which can be broken down biologically in thebody conduit7 for the envelope, theenvelope10 which is essentially only needed to produce thestent20 and therefore also its possibly undesired ends, is broken down after a period, which depends on the material used in each case.
• By mixing the negative contrast means into thepolymer mass13 thestent20 produced from thispolymer mass13 is easy to detect on an x-ray image of thebody conduit7.
• In an advantageous manner a means for liquefying and/or for hardening of thepolymer mass13 by a change of temperature is provided; this enables thepolymer mass13, because of its good deformability in the liquid state, to be particularly well adapted to the properties of thebody conduit7 and enables the fillingarea9 to be filled especially simply. It is possible for liquefying and/or hardening of thepolymer mass13 by heating it up, to arrange a heating element in thecatheter8.
• To enable stents of different lengths to be produced with the same catheter, further clamping rings can be provided between the clamping rings15 or16. Theenvelope10 is accordingly held by one of its ends with clampingring16 and with its other end by one of the other clamping rings.
• The invention can be summarized as follows: Through a contrast means contained in an inventive stent which exhibits a higher permeability for x-radiation than body tissue surrounding the stent in a relevant body conduit, this stent can be clearly detected in its position on the x-ray image of the relevant body conduit and at the same time has good biological compatibility; A gas contained in a cavities of the stent is in particular provided as the contrast means. The inventive production method for this stent with the aid of a catheter embodied especially for the purpose enables the production of the stent from a malleable polymer mass in the relevant body conduit so that the stent is adapted especially precisely to the shape of the relevant body conduit.

Claims (20)

1-15. (canceled)

16. A stent arranged in a body conduit of a patient, comprising:

a plastic deformable material that forms the stent; and

a contrast medium that contains in the stent with a higher permeability for an x-radiation than body tissues surrounding the stent and makes the stent to be easily visible in an x-ray image without a potential danger to healthy of the patient.

17. The stent as claimed inclaim 16, wherein the contrast medium is a gas.

18. The stent as claimed inclaim 17, wherein the gas is carbon dioxide.

19. The stent as claimed inclaim 17, wherein the stent has cavities in which the gas is enclosed.

20. The stent as claimed inclaim 16, wherein the stent comprises a polymer material.

21. The stent as claimed inclaim 20, wherein the polymer material is a polymer foam.

22. The stent as claimed inclaim 16, wherein the plastic deformable material permanently maintains a shape change through a radial expansion of the stent when the stent is in the body conduit.

23. A method for forming a stent in a body conduit of a patient, comprising:

positioning a catheter at a position of the body conduit where the stent is intended to be placed;

arranging an tubular filling area surrounding a part of the catheter;

filling the tubular filling area with a hardenable polymer mass;

hardening the polymer mass in the tubular filling area to form the stent; and

removing the catheter from the body conduit with the stent remaining in the body conduit.

24. The method as claimed inclaim 23, wherein a contrast medium is mixed with the polymer mass or brought into the filling area before the filling.

25. The method as claimed inclaim 24, wherein the contrast medium has a higher permeability for an x-radiation than body tissues surrounding the stent which makes the stent to be easily visible in an x-ray image.

26. The method as claimed inclaim 24, wherein the contrast medium is a gas and distributed by foaming up the polymer mass with the gas in the stent.

27. The method as claimed inclaim 26, wherein the gas is a carbon dioxide.

28. The method as claimed inclaim 23, wherein the filling area is expandable by filling with the hardenable polymer mass.

29. The method as claimed inclaim 23, wherein the filling area is accommodated in an inner chamber of the catheter.

30. The method as claimed inclaim 29, wherein the inner chamber is a closable capsule.

31. The method as claimed inclaim 30, wherein an opening from the inner chamber to the filling area is closed off after the filling and before the removal of the catheter from the body conduit.

32. The method as claimed inclaim 31, wherein the opening from the inner chamber to the filling area is closed off after the filling and before the hardening of the polymer mass.

33. The method as claimed inclaim 23, wherein the polymer mass is liquefied or hardened in the filling area by a temperature change.

34. The method as claimed inclaim 23, wherein a balloon section of the catheter surrounded by the filling area is inflated after positioning the catheter in the body conduit.

Images