US20050084671A1 - Texturized fibrous materials from poly-coated paper and compositions and composites made therefrom - Google Patents

Abstract

Texturized poly-coated paper, and compositions and composites made therefrom, are disclosed.

Description

CROSS REFERENCE TO RELATED APPLICATIONS
• This application is a continuation-in-part of U.S. patent application Ser. No. 08/921,807, filed Sep. 2, 1997.
BACKGROUND OF THE INVENTION
• The invention relates to texturized fibrous materials prepared from poly-coated paper, and compositions and composites made from such materials.
• Paper coated with a polymer (poly-coated paper) is used in a number applications. For example, poly-coated paper is used to make a variety of food containers, including individual-serving size juice cartons and boxes for frozen foods.
SUMMARY OF THE INVENTION
• In general, the invention features texturized poly-coated paper and compositions and composites made therefrom.
• In one embodiment, the invention features a process for preparing a texturized fibrous material. The process includes shearing poly-coated paper having internal fibers, to the extent that the internal fibers are substantially exposed, resulting in a texturized fibrous material. The poly-coated paper can, for example, be made of polyethylene and paper, and, in some cases, one or more layers of aluminum. The exposed fibers of the texturized fibrous material can have a length/diameter (L/D) ratio of at least about 5 (e.g., at least about 5, 10, 25, 50, or more). For example, at least about 50% of the fibers can have L/D ratios of this magnitude.
• In another embodiment, the invention features a texturized fibrous material that includes poly-coated paper having internal fibers, where the poly-coated paper is sheared to the extent that the internal fibers are substantially exposed.
• The texturized fibrous material can, for example, be incorporated into (e.g., associated with, blended with, adjacent to, surrounded by, or within) a structure or carrier (e.g., a netting, a membrane, a flotation device, a bag, a shell, or a biodegradable substance). Optionally, the structure or carrier may itself be made from a texturized fibrous material (e.g., a texturized fibrous material of the invention), or of a composition or composite of a texturized fibrous material.
• The texturized fibrous material can have a bulk density less than about 0.5 grams per cubic centimeter (g/cm³), or even less than about 0.2 g/cm³.
• Compositions that include the texturized fibrous materials described above, together with a chemical or chemical formulation (e.g., a pharmaceutical such as an antibiotic or contraceptive, optionally with an excipient; an agricultural compound such as a fertilizer, herbicide, or pesticide; or a formulation that includes enzymes) are also within the scope of the invention, as are compositions that include the texturized fibrous materials and other liquid or solid ingredients (e.g., particulate, powdered, or granulated solids such as plant seed, foodstuffs, or bacteria).
• Composites that include thermoplastic resin and the texturized fibrous materials are also contemplated. The resin can be, for example, polyethylene, polypropylene, polystyrene, polycarbonate, polybutylene, a thermoplastic polyester, a polyether, a thermoplastic polyurethane, polyvinylchloride, or a polyamide, or a combination of two or more resins.
• In some cases, at least about 5% by weight (e.g., 5%, 10%, 25%, 50%, 75%, 90%, 95%, 99%, or about 100%) of the fibrous material included in the composites is texturized.
• The composite may include, for example, about 30% to about 70% by weight resin and about 30% to about 70% by weight texturized fibrous material, although proportions outside of these ranges may also be used.
• The composites can also, optionally, include lignocellulosic fiber (e.g., wood or derivatives of trees or other plants) or cellulosic fiber (e.g., paper or paper products).
• The composites can be quite strong, in some cases having a flexural strength of at least about 6,000 to 10,000 psi.
• The composites can also include inorganic additives such as calcium carbonate, graphite, asbestos, wollastonite, mica, glass, fiber glass, chalk, talc, silica, ceramic, ground construction waste, tire rubber powder, carbon fibers, or metal fibers (e.g., stainless steel or aluminum). The inorganic additives can represent about 0.5% to about 20% of the total weight of the composite.
• The composite can be in the form of, for example, a pallet (e.g., an injection molded pallet), pipes, panels, decking materials, boards, housings, sheets, poles, straps, fencing, members, doors, shutters, awnings, shades, signs, frames, window casings, backboards, wallboards, flooring, tiles, railroad ties, forms, trays, tool handles, stalls, bedding, dispensers, staves, films, wraps, totes, barrels, boxes, packing materials, baskets, straps, slips, racks, casings, binders, dividers, walls, indoor and outdoor carpets, rugs, wovens, and mats, frames, bookcases, sculptures, chairs, tables, desks, art, toys, games, wharves, piers, boats, masts, pollution control products, septic tanks, automotive panels, substrates, computer housings, above- and below-ground electrical casings, furniture, picnic tables, tents, playgrounds, benches, shelters, sporting goods, beds, bedpans, thread, filament, cloth, plaques, trays, hangers, servers, pools, insulation, caskets, bookcovers, clothes, canes, crutches, and other construction, agricultural, material handling, transportation, automotive, industrial, environmental, naval, electrical, electronic, recreational, medical, textile, and consumer products. The composites can also be in the form of a fiber, filament, or film.
• The terms “texturized poly-coated paper” and “texturized fibrous material”, as used herein, mean that the poly-coated paper has been sheared to the extent that its internal fibers are substantially exposed. At least about 50%, more preferably at least about 70%, of these fibers, as well as the external polymer fibers, have a length/diameter (L/D) ratio of at least 5, more preferably at least 25, or at least 50. An example of texturized poly-coated paper is shown inFIG. 1.
• The texturized fibrous materials of the invention have properties that render them useful for various applications. For example, the texturized fibrous materials have absorbent properties, which can be exploited, for example, for pollution control. The fibers are generally biodegradable, making them suitable, for example, for drug or chemical delivery (e.g., in the treatment of humans, animals, or in agricultural applications). The texturized fibrous materials can also be used to reinforce polymeric resins.
• Those composites that include texturized fibrous material and resin are strong, light-weight, and inexpensive. The raw materials used to make the composites are available as virgin or recycled materials; for example, they may include discarded containers composed of resins, and discarded containers composed of poly-coated paper.
• Poly-coated paper can be difficult to recycle because the paper and the polymer layers generally cannot be separated. In the present invention, both the paper and the polymer portions are utilized, so there is no need to separate the two. Poly-coated paper including one or more layers of aluminum can similarly be used. The invention thus helps to recycle discarded post-consumer containers, while at the same time producing useful products.
• Other features and advantages of the invention will be apparent from the following detailed description, and from the claims.
BRIEF DESCRIPTION OF THE DRAWING
• FIG. 1 is a photograph of texturized poly-coated paper, magnified 50 times.
• FIG. 2 is a photograph of a half-gallon polyboard juice carton.
• FIG. 3 is a photograph of shredded half-gallon polyboard juice cartons.
• FIG. 4 is a photograph of texturized fibrous material prepared by shearing the shredded half-gallon polyboard juice cartons ofFIG. 3.
DETAILED DESCRIPTION OF THE INVENTION
• Poly-coated paper is available in a variety of forms. For example, whole sheets of virgin poly-coated paper can be purchased from International Paper, New York. Alternatively, virgin waste poly-coated paper (e.g., edge trimmings, surplus, misprinted stock) can be obtained from International Paper or other paper manufacturers. Used poly-coated paper, in the form of discarded food and beverage containers, can be gathered from various sources, including waste and recycling streams. Poly-coated paper that includes one or more layers of aluminum foil as is commonly used for airtight liquid storage, may also be used. Used, waste, or scrap poly-coated paper (e.g., post-consumer waste, industrial offal) can also be purchased from brokers of this material.
• Preparation of the Texturized Fibrous Material
• If scrap poly-coated paper is used, it should be clean and dry. The poly-coated paper can be texturized using any one of a number of mechanical means, or combinations thereof. During the texturizing process, the polymer layers are sheared away from the paper layers, thus exposing the paper fibers. A preferred method of texturizing includes first cutting the poly-coated paper into{fraction (1/4)}- to½-inch pieces, if necessary, using a standard paper-cutting apparatus. Counter-rotating screw shredders and segmented rotating screw shredders such as those manufactured by Munson (Utica, N.Y.) can also be used, as can a standard document shredder as found in many offices.
• The paper is then sheared with a rotary cutter, such as the one manufactured by Sprout, Waldron Companies, as described in Perry's Chem. Eng. Handbook, 6th Ed., at 8-29 (1984). Although other settings can be used, the spacing between the rotating knives and bed knives of the rotary cutter is typically set to 0.020″ or less, and blade rotation is set to 750 rpm or more. The rotary cutter can be cooled to 100° C. or lower during the process, for example, using a water jacket.
• The texturized material is passed through a discharge screen. Larger screens (e.g., up to 6 mm) can be used in large-scale production. The poly-coated paper feedstock is generally kept in contact with the blades of the rotary cutter until the fibers are pulled apart; smaller screens (e.g., 2 mm mesh) provide longer residence times and more complete texturization, but can result in lower length/diameter (L/D) aspect ratios. A vacuum drawer can be attached to the screen to maximize and maintain fiber length/diameter aspect ratio.
• The texturized fibrous material can be directly stored in sealed bags or may be dried at approximately 105° C. for 4-18 hours (e.g., until the moisture content is less than about 0.5%) immediately before use.FIG. 1 is an SEM photograph of the texturized poly-coated paper.
• Alternative texturizing methods include stone grinding, mechanical ripping or tearing, and other methods whereby the paper's internal fibers can be exposed (e.g., pin grinding, air attrition milling).
• Uses of Texturized Fibrous Material
• Texturized fibrous material and compositions of such materials with other chemicals and chemical formulations can be prepared to take advantage of the material's properties. The materials can be used to absorb chemicals, for example, potentially absorbing many times their own weight. Thus, the material could, for instance, be used to absorb spilled oil, or for clean-up of environmental pollution, for example, in water, in the air, or on land. Similarly, the material's absorbent properties, together with its biodegradability, also make them useful for delivery of chemicals or chemical formulations. For example, the materials can be treated with solutions of enzymes or pharmaceuticals such as antibiotics, nutrients, or contraceptives, and any necessary excipients, for drug delivery (e.g., for treatment of humans or animals, or for use as or in animal feed and/or bedding), as well as with solutions of fertilizers, herbicides, or pesticides. The texturized fibrous materials can optionally be chemically treated to enhance a specific absorption property. For example, the materials can be treated with silanes to render them lipophilic.
• Compositions including texturized materials combined with liquids or particulate, powdered, or granulated solids can also be prepared. For example, the texturized fibrous materials can be blended with seeds (i.e., with or without treatment with a solution of fertilizer, pesticides, etc.), foodstuffs, or bacteria (e.g., bacteria that digest toxins). The ratio of fibrous material to the other components of the compositions will depend on the nature of the components and readily be adjusted for a specific product application.
• In some cases, it may be advantageous to associate the texturized fibrous materials, or compositions or composites of such materials, with a structure or carrier such as a netting, a membrane, a flotation device, a bag, a shell, or a biodegradable substance optionally, the structure or carrier may itself be made of a texturized fibrous material (e.g., a material of the invention), or a composition or composite thereof.
• Composites of Texturized Fibrous Material and Resin
• Texturized fibrous materials can also be combined with resins to form strong, lightweight composites. Materials that have been treated with chemicals or chemical formulations, as described above, can similarly be combined with biodegradable or non-biodegradable resins to form composites, allowing the introduction of, for example, hydrophilic substances into otherwise hydrophobic polymer matrices. Alternatively, the composites including texturized fibrous materials and resin can be treated with chemicals or chemical formulations.
• The texturized poly-coated paper provides the composite with strength. The composite may include from about 10% to about 90%, more preferably from about 30% .to about 70%, of the texturized poly-coated paper by weight. Examples of poly-coated paper include materials having layers of polymer and paper, and materials having layers of polymer, paper, and aluminum.
• The resin encapsulates the texturized poly-coated paper and helps control the shape of the composites. The resin also transfers external loads to the poly-coated paper and protect the poly-coated paper from environmental and structural damage. Composites include, for example, about 10% to about 90%, more preferably about 30% to about 70%, by weight, of the resins.
• Examples of resins include polyethylene (including, e.g., low density polyethylene and high density polyethylene), polypropylene, polystyrene, polycarbonate, polybutylene, thermoplastic polyesters, polyethers, thermoplastic polyurethane, PVC, polyamides (e.g., nylon), and other resins. It is preferred that the resins have a low melt flow index. Preferred resins include polyethylene and polypropylene with melt flow indices of less than 3 g/10 min, and more preferably less than 1 g/10 min.
• The resins can be purchased as virgin material, or obtained as waste materials, and can be purchased in pelletized or granulated form. One source of resin is used polyethylene milk bottles. If surface moisture is present on the pelletized or granulated resin, however, it should be dried before use.
• The composites can also include coupling agents. The coupling agents help to bond the hydrophilic fibers of the poly-coated paper to the hydrophobic resins. Examples of coupling agents include maleic anhydride modified polyethylenes, such those in the FUSABOND® (available from Dupont, Del.) and POLYBOND® (available from Uniroyal Chemical, Conn.) series. One suitable coupling agent is a maleic anhydride modified high density polyethylene such as FUSABOND® MB 100D.
• The composites can also include other cellulosic or lignocellulosic fibers such as paper and paper products, wood, wood fibers, and wood-related materials, as well as materials derived from kenaf, grasses, rice hulls, bagasse, cotton, and jute. These fibers provide extra strength to the composite.
• The quantity of fiber which is incorporated into the composites can vary, depending on the desired physical and mechanical properties of the finished products. Preferred composites contain about 5% to about 50%, more preferably about 10% to about 30%, by weight of the cellulosic or lignocellulosic fiber. The fibers may have, for example, a L/D ratio of at least 5, or at least 25 or 50. If cellulosic or lignocellulosic fibers are used, they can be texturized, using the process described above.
• The composites can also contain additives known to those in the art of compounding, such as plasticizers, lubricants, antioxidants, opacificers, heat stabilizers, colorants, impact modifiers, photostabilizers, flame retardants, biocides, and antistatic agents.
• The composites can also include inorganic additives such as calcium carbonate, graphite, asbestos, wollastonite, mica, glass, fiber glass, chalk, silica, talc, ceramic, ground construction waste, tire rubber powder, carbon fibers, or metal fibers (e.g., aluminum, stainless steel). When such additives are included, they are typically present in quantities of from about 0.5% up to about 20-30% by weight. For example, submicron calcium carbonate can be added to the composites of texturized fibrous material and resin to improve impact modification characteristics or to enhance composite strength.
• Preparation of Compositions
• Compositions containing the texturized cellulosic or lignocellulosic materials and chemicals, chemical formulations, or other solids can be prepared, for example, in various immersion, spraying, or blending apparatuses, including, but not limited to, ribbon blenders, cone blenders, double cone blenders, and Patterson-Kelly “V” blenders.
• For example, a composition containing 90% by weight texturized cellulosic or lignocellulosic material and 10% by weight ammonium phosphate or sodium bicarbonate can be prepared in a cone blender to create a fire-retardant material for absorbing oil.
• Preparation of Composites of Texturized Fibrous Material and Resin
• Composites of texturized poly-coated paper and resin can be prepared as follows. A standard rubber/plastic compounding 2-roll mill is heated to 325-400° F. The resin (usually in the form of pellets or granules) is added to the heated roll mill. After about 5 to 10 minutes, the coupling agent is added to the roll mill. After another five minutes, the texturized poly-coated paper is added to the molten resin/coupling agent mixture. The texturized poly-coated paper is added over a period of about 10 minutes.
• The composite is removed from the roll mill, cut into sheets and allowed to cool to room temperature. It is then compression molded into plaques using standard compression molding techniques.
• Alternatively, a mixer, such as a Banbury internal mixer, is charged with the ingredients. The ingredients are mixed, while the temperature is maintained at less than about 190° C. The mixture can then be compression molded.
• In another embodiment, the ingredients can be mixed in an extruder mixer, such as a twin-screw extruder equipped with co-rotating screws. The resin and the coupling agent are introduced at the extruder feed throat; the texturized poly-coated paper (and cellulosic or lignocellulosic fiber, if used) are introduced about ⅓ of the way down the length of the extruder into the molten resin. The internal temperature of the extruder is maintained at less than about 190° C. At the output, the composite can be, for example, pelletized by cold strand cutting.
• Alternatively, the mixture can first be prepared in a batch mixer, then transferred to an extruder.
• In another embodiment, the composite can be formed into filaments for knitting, warping, weaving, and braiding, and to make non-wovens. In a further embodiment, the composite can be made into film.
• Properties of the Composites of Texturized Fibrous Material and Resin
• The resulting composites include a network of fibers, encapsulated within a resin matrix. The fibers form a lattice network, which provides the composite with strength. Since the poly-coated paper is texturized, the amount of surface area available to bond to the resin is increased, in comparison to composites prepared with un-texturized poly-coated paper. The resin binds to the surfaces of the exposed fibers, creating an intimate blend of the fiber network and the resin matrix. The intimate blending of the fibers and the resin matrix further strengthens the composites. Cellulosic or lignocellulosic fibers may also be added to strengthen the composite further.
• Uses of the Composites of Texturized Fibrous Material and Resin
• The poly-coated paper/resin composites can be used in a number of applications. The composites are strong and light weight; they can be used, for example, as wood substitutes. The resin coating renders the composites water-resistant, so they may be used in outdoor applications. For example, the composites may be used to make pallets which are stored outdoors for extended periods of time, wine staves, rowboats, furniture, skis, and oars. Many other uses are contemplated, including pipes, panels, decking materials, boards, housings, sheets, poles, straps, fencing, members, doors, shutters, awnings, shades, signs, frames, window casings, backboards, wallboards, flooring, tiles, railroad ties, forms, trays, tool handles, stalls, bedding, dispensers, staves, films, wraps, totes, barrels, boxes, packing materials, baskets, straps, slips, racks, casings, binders, dividers, walls, indoor and outdoor carpets, rugs, wovens, and mats, frames, bookcases, sculptures, chairs, tables, desks, art, toys, games, wharves, piers, boats, masts, pollution control products, septic tanks, automotive panels, substrates, computer housings, above- and below-ground electrical casings, furniture, picnic tables, tents, playgrounds, benches, shelters, sporting goods, beds, bedpans, thread, filament, cloth, plaques, trays, hangers, servers, pools, insulation, caskets, bookcovers, clothes, canes, crutches, and other construction, agricultural, material handling, transportation, automotive, industrial, environmental, naval, electrical, electronic, recreational, medical, textile, and consumer products. Numerous other applications are also envisioned. The composites may also be used, for example, as the base or carcass for a veneer product.
• Moreover, the composites can be, for example, surface treated, grooved, milled, shaped, imprinted, textured, compressed, punched, or colored. The surface of the composites can be smooth or rough.
• The following examples illustrate certain embodiments and aspects of the present invention and not to be construed as limiting the scope thereof.
EXAMPLESExample 1
• A 1500 pound skid of virgin, half-gallon juice cartons made of poly-coated white kraft board was obtained from International Paper. One such carton is shown inFIG. 2. Each carton was folded flat.
• The cartons were fed into a 3 hp Flinch Baugh shredder at a rate of approximately 15 to 20 pounds per hour. The shredder was equipped with two rotary blades, each 12″ in length, two fixed blades, and a 0.3″ discharge 30 screen. The gap between the rotary and fixed blades was 0.10″.
• A sample of the output from the shredder, consisting primarily of confetti-like pieces, about 0.1″ to 0.5″ in width and about 0.25″ to 1″ in length, is shown inFIG. 3.
• The shredder output was then fed into a Thomas Wiley Mill Model 2D5 rotary cutter. The rotary cutter had four rotary blades, four fixed blades, and a 2 mm discharge screen. Each blade was approximately 2″ long. The blade gap was set at 0.020″.
• The rotary cutter sheared the confetti-like pieces across the knife edges, tearing the pieces apart and releasing a finely texturized fiber at a rate of about one pound per hour. The fiber had an average minimum L/D ratio of between five and 100 or more. The bulk density of the texturized fiber was on the order of 0.1 g/cm₃. A sample of texturized fiber is shown inFIG. 4 at normal magnification, and inFIG. 1 at fifty-fold magnification.
Example 2
• Composites of texturized poly-coated paper and resin were prepared as follows. A standard rubber/plastic compounding 2-roll mill was heated to 325-400° F. The resin (usually in the form of pellets or granules) was added to the heated roll mill. After about 5 to 10 minutes, the resin banded on the rolls (i.e., it melted and fused on the rolls). The coupling agent was then added to the roll mill. After another five minutes, the texturized poly-coated paper was added to the molten resin/coupling agent mixture. The poly-coated paper was added over a period of about 10 minutes.
• The composite was then removed from the roll mill, cut into sheets, and allowed to cool to room temperature. Batches of about 80 g each were compression molded into 6″×6″×⅛″ plaques using standard compression molding techniques.
• One composition contains the following ingredients:

  Composition No. 1

  	Ingredient	Amount (g)

  	High density polyethylene1	160
  	Poly-coated paper2	240
  	Coupling agent3	8
  	1Marlex 6007, melt flow index 0.65 g/10 min, commercially available from Phillips
  	2Texturized using rotary cutter with 2 mm mesh
  	3POLYBOND ® 3009, commercially available from Uniroyal Chemical

• The plaques were machined into appropriate test specimens and tested according to the procedures outlined in the method specified. Three different specimens were tested for each property, and the mean value for each test was calculated.
• The properties of Composition No. 1 are as follows:

  	Tensile modulus (105psi)	8.63	(ASTM D638)
  	Tensile strength at break (psi)	6820	(ASTM D638)
  	Ultimate elongation (%)	<5	(ASTM D638)
  	Flexural Strength (psi)	12,200	(ASTM D790)
  	Flexural modulus (105psi)	6.61	(ASTM D790)

• A second composition contains the following ingredients:

  Composition No. 2

  	Ingredient	Amount (g)

  	High density polyethylene1	160
  	Poly-coated paper2	240
  	Coupling agent3	8
  	1Scrapped milk jugs, melt flow index approximately 0.8 g/10 min
  	2Texturized using rotary cutter with 2 mm mesh
  	3POLYBOND ® 3009

• The properties of Composition No. 2 are as follows:

  	Tensile modulus (105psi)	7.38	(ASTM D638)
  	Tensile strength at break (psi)	6500	(ASTM D638)
  	Ultimate elongation (%)	<5	(ASTM D638)
  	Flexural Strength (psi)	11,900	(ASTM D790)
  	Flexural modulus (105psi)	6.50	(ASTM D790)

• A third composition contains the following ingredients:

  Composition No. 3

  	Ingredient	Amount (g)

  	High density polyethylene1	160
  	Poly-coated paper2	240
  	Coupling agent3	8
  	1Scrap milk jugs, melt flow index approximately 0.8 g/10 min
  	2Texturized using rotary cutter with 2 mm mesh
  	3FUSABOND ® MB 100D, commercially available from DuPont

• The properties of Composition No. 3 are as follows:

  Tensile modulus (105psi)	7.08	(ASTM D638)
  Tensile strength at break (psi)	6480	(ASTM D638)
  Ultimate elongation (%)	<5	(ASTM D638)
  Flexural Strength (psi)	10,200	(ASTM D790)
  Flexural modulus (105psi)	5.73	(ASTM D790)

• A fourth composition contains the following ingredients:

  Composition No. 4

  	Ingredient	Amount (g)

  	High density polyethylene1	160
  	Poly-coated paper2	240
  	Coupling agent3	8
  	1Marlex 6007, melt flow index 0.65 g/10 min
  	2texturized using rotary cutter with 2 mm mesh
  	3FUSABOND ® MB 100D

• The properties of Composition No. 4 are as follows:

  Tensile modulus (105psi)	7.17	(ASTM D638)
  Tensile strength at break (psi)	6860	(ASTM D638)
  Ultimate elongation (%)	<5	(ASTM D638)
  Flexural Strength (psi)	12,200	(ASTM D790)
  Flexural modulus (105psi)	7.50	(ASTM D790)

• A fifth composition contains the following ingredients:

  Composition No. 5

  	Ingredient	Amount (g)

  	SUPERFLEX ™ CaCO3	33
  	Fiber2,4	67
  	HDPE (w/3% compatibilizer)1,3	100
  	4virgin poly-coated milk cartons

• The properties of Composition No. 5 are as follows:

  	Flexural strength (105psi)	8.29	(ASTM D790)
  	Ultimate elongation (%)	<5	(ASTM D638)
  	Flexural modulus (105psi)	10.1	(ASTM D790)
  	Notch Izod (ft-lb/in)	1.39	(ASTM D256-97)

• A sixth composition contains the following ingredients:

  Composition No. 6

  	Ingredient	Amount (parts)

  	SUPERFLEX ™ CaCO3	22
  	Fiber2,4	67
  	HDPE (w/3% compatibilizer)1,3	100

• The properties of Composition No. 6 are as follows:

  	Flexural strength (105psi)	8.38	(ASTM D790)
  	Ultimate elongation (%)	<5	(ASTM D638)
  	Flexural modulus (105psi)	9.86	(ASTM D790)
  	Notch Izod (ft-lb/in)	1.37	(ASTM D256-97)

• A seventh composition contains the following ingredients:

  Composition No. 7

  	Ingredient	Amount (parts)

  	ULTRAFLEX ™ CaCO3	33
  	Fiber2,4	67
  	HDPE/compatibilizer1,3	100

• The properties of Composition No. 7 are as follows:

  	Flexural strength (105psi)	7.43	(ASTM D790)
  	Ultimate elongation (%)	<5	(ASTM D638)
  	Flexural modulus (105psi)	11.6	(ASTM D790)
  	Notch Izod (ft-lb/in)	1.27	(ASTM D256-97)

  
  other embodiments are with the claims.

Claims (6)

1-6. (canceled)

7. A texturized fibrous material comprising poly-coated paper having internal fibers, wherein said poly-coated paper is sheared to the extent that the internal fibers are substantially exposed.

8-9. (canceled)

10. The texturized fibrous material ofclaim 7, wherein said texturized fibrous material has a bulk density less than about 0.5 grams per cubic centimeter.

11. The texturized fibrous material ofclaim 7, wherein said texturized fibrous material has a bulk density less than about 0.2 grams per cubic centimeter.

12-36. (canceled)