US20010014403A1 - Method and apparatus for making components by direct laser processing - Google Patents

Abstract

The present invention relates to a method an apparatus for fabricating a component by a direct laser process. One form of the present invention contemplates a gas turbine engine blade having an abrasive tip formed directly thereon.

Description

BACKGROUND OF THE INVENTION
• The present invention relates generally to the fabrication of components by the direct laser fusing of the material constituents. More particularly, the present invention has one form wherein the material constituents are directly melted by a laser and solidified to produce a high density part requiring little or no post processing. While, the present invention was developed for fabricating gas turbine engine components, certain applications may be outside of this field.[0001]
• Since its inception in the 1930's, the gas turbine engine has grown to be the workhorse power plant of modern aircraft. Over the years, there has been significant advances in the technology related to aircraft propulsion systems, and the methods of manufacturing these system components. Associated with the technological advances has been a desire to reduce engine life cycle costs by minimizing acquisition, operating, and maintenance costs. While there are many ways to reduce engine life cycle costs, one approach may be through technological developments such as advanced materials, innovative structural designs, improved aerothermodynamics, improved computational methods, and advanced manufacturing techniques.[0002]
• Traditional manufacturing techniques have typically coupled the cost of manufacturing a part with the volume of parts produced. Manufacturing techniques that are designed for large scale production, such as casting and extrusion are often cost effective, but these manufacturing techniques are generally unacceptable for small quantities of parts. Another traditional manufacturing technique for producing parts is powder metallurgy which requires a tool for shaping the powder, therefore often rendering the powder metallurgy process unattractive for producing a limited quantity of parts.[0003]
• Where only a small quantity of parts are desired, conventional subtractive machining method are often employed to produce the part. As is generally known to one familiar with manufacturing and machining processes, a conventional subtractive machining method utilizes the removal of a portion of the material from the initial block of material to produce the desired shape. Examples of conventional subtractive machining methods include: broaching, drilling, electric discharge machining, flame cutting, grinding, turning, etc. While the conventional subtractive machining methods are usually effective in producing the desired component, they have a multitude of limitations.[0004]
• One limitation common to the conventional subtractive machining processes is the waste of a large amount of raw material. The conventional machining process usually involve an extensive setup to properly machine the part, and the setup and operation of the machine often relies a great deal on operator judgment and expertise. Another limitation associated with many conventional subtractive machining methods is the inaccuracies imparted into the manufacturing process due to machine and tooling wear. Further, an additional limitation of many conventional machining techniques relates to the difficulty of making certain part configurations. Therefore, there are certain configurations in which the part must be divided into segments for machining due to the inability of a cutting tool to produce the desired configuration.[0005]
• There are other manufacturing processes which are additive in nature. The type of processes that would be classified as additive in nature include plating, cladding, frame spraying, welding, laminating, etc. However, these processes are generally used in conjunction with the conventional subtractive machining techniques to produce a component that cannot be directly machined.[0006]
• Even with a variety of earlier methods and apparatus for manufacturing components, there remains a need for a method and apparatus for making components by direct laser processing. The present invention satisfies this need in a novel and unobvious way.[0007]
SUMMARY OF THE INVENTION
• One embodiment of the present invention contemplates a an apparatus comprising a free form fabricated gas turbine component having a structure consistent with a metallurgical casting with a refined microstructure.[0008]
• One object of the present invention is to provide a fabricated component for use in a gas turbine engine.[0009]
• Related objects and advantages of the present invention will be apparent from the following description.[0010]
BRIEF DESCRIPTION OF THE DRAWINGS
• FIG. 1 is a perspective view of an aircraft having a gas turbine engine connected thereto.[0011]
• FIG. 2 is an enlarged partially fragmented side elevational view of the gas turbine engine of FIG. 1.[0012]
• FIG. 3 is a partial perspective view of one embodiment of a seal system comprising a portion of the FIG. 2 gas turbine engine.[0013]
• FIG. 4 is a perspective view of one embodiment of the turbine blade with an abrasive cermet tip comprising a portion of the FIG. 3 seal system.[0014]
• FIG. 5 is a partially exploded view of an alternate embodiment of the gas turbine blade with an abrasive cermet tip.[0015]
• FIG. 6 is an illustrative view of one embodiment of the direct laser processing workstation of the present invention.[0016]
• FIG. 7 is a partially fragmented view of the direct laser processing workstation of FIG. 6.[0017]
• FIG. 8 is a schematic view of the portion of the FIG. 6 apparatus which controls the direction of the laser beam within the direct laser processing workstation.[0018]
• FIG. 9 is an illustrative diagram of of the FIG. 5 abrasive cermet blade tip of FIG. 5 formed in the powder parts bed comprising a portion of FIG. 7.[0019]
• FIG. 10 is an illustrative view of a laser scan path for the processing of one embodiment of the abrasive cermet blade tips.[0020]
• FIG. 11[0021]arepresents a portion of the unmelted material constituents that are utilized in the direct laser process.
• FIG. 11[0022]brepresents a portion of the material of FIG. 11athat has been melted and allowed to solidify by the direct laser process.
DESCRIPTION OF THE PREFERRED EMBODIMENT
• For the purposes of promoting an understanding of the principles of the invention, reference will now be made to the embodiment illustrated in the drawings and specific language will be used to describe the same. It will nevertheless be understood that no limitation of the scope of the invention is thereby intended, such alterations and further modifications in the illustrated device, and such further applications of the principles of the invention as illustrated therein being contemplated as would normally occur to one skilled in the art to which the invention relates.[0023]
• Referring to FIGS. 1 and 2, there is illustrated an[0024]aircraft10 including an aircraftflight propulsion engine11. It is understood herein that an aircraft is generic and includes helicopters, tactical fighters, trainers, missiles and other related apparatus. In the preferred embodiment, theflight propulsion engine11 includes a compressor12, acombustor13 and a power turbine14. It is important to realize that there are a multitude of ways in which the components can be linked together. Additional compressors and turbines can be added with intercoolers connected between the compressors and reheat combustion chambers could be added between the turbines. Further, the gas turbine engine is equally suited to be used for industrial applications. Historically, there has been the widespread application of industrial gas turbine engines, such as pumping sets for gas and oil transmission lines, electricity generation and naval propulsion.
• With reference to FIG. 2, there is illustrated the enlarged partially fragmented view of the[0025]gas turbine engine11. Thegas turbine engine11 having a rotor disk17, with a plurality ofturbine blades16 mounted thereto, that is coupled to a shaft (not illustrated) within thegas turbine engine11. A plurality of turbine vanes16aform a nozzle within the gas turbine engine for directing the flow of working fluid relative to theblades16. In the preferred form of the present invention the working fluid is air extracted from the compressor12.
• With reference to FIG. 3, there is illustrated a portion of a working[0026]fluid sealing system20. Thesealing system20 is designed to minimize the leakage of working fluid away from and around the working fluid path. The efficiency of the gas turbine engine is dependent upon the ability to control and minimize the leakage of this working fluid. Thus, the clearance between thetip19 of theturbine blade16 and thestatic structure22 of the gas turbine engine assists in controlling the bypassing of the rotor17 andturbine blades16 by the working fluid. Clearance between the rotating and static components (21 and23 respectively) changes with the expansion and contraction of the components due to the thermal cycling occurring in the gas turbine engine.
• In one form of the present invention, the[0027]sealing system20 comprises the two corresponding components that form a virtual seal between the rotating and static components. The two components are anabrasive component21 that is coupled to theturbine blade16, and a stationaryabradable component23 which is coupled to thestationary component22. The stationaryabradable component23 is often referred to as a shroud and is a member that circumscribes the rotor disk17 andblades16 while covering a portion of thestationary component22.
• The[0028]turbine blade16 withabrasive component21 rotates relative to theabradable component23 to wear-form a virtual seal track in theabradable component23. The rotation of the rotor disk17 withturbine blades16 coupled thereto allows theabrasive components21 to abrade theabradable component23 when there is no clearance between the respective components. A particular aspect of theabrasive component21 is the ability to withstand repeated and severe encounters with theabradable component23 with only minimal loss of material from theabrasive component21 and preferential wear of theabradable component23. Thus, instead of a rubbing interface between thecomponents21 and23 when the radial clearance therebetween has disappeared theabrasive component21 cuts theabradable component23 to maintain a minimum clearance therebetween. The abrasion of theabradable component23 by the rotatingabrasive component21 forms a fluid passageway between the rotating components. In one form of the present invention, theabradable component23 is a semi-porous abradable ceramic that is generally known to those of ordinary skill in the art.
• With reference to FIG. 4, there is illustrated one embodiment of the[0029]turbine blade16. Theturbine blade16 can be of a wrought or cast structure. In the preferred embodiment, thegas turbine blade16 is a unitary cast alloy structure produced by a precision casting operation utilizing various super alloy compositions. Various types of nickel, titanium, and cobalt super alloy compositions and manufacturers of such compositions are known to those skilled in the art. Most super alloy compositions of interest are complicated mixtures of either titanium, tin, vanadium, aluminum, molybdenum, silicon, neodymium and other select materials; or nickel, cobalt, chromium, aluminum, titanium, iron, tungsten, tantalum, rhenium and other select elements. A preferred group of materials are generally known by the following tradenames CMSX-3, CMSX-4 and MARM-247, and are readily available and known to people of ordinary skill in the art. However, the application of the present invention is not intended herein to be limited to the above materials, and can be utilized with other materials. A technique for producing a castunitary turbine blade16 having equiaxed, directionally solidified or single crystal alloy structures is disclosed in U.S. Pat. No. 5,295,530 to O'Connor which is incorporated by reference herein. A gas turbine blade and a gas turbine vane are often referred to as an airfoil.
• The[0030]abrasive component21 is metallurgically bonded to theblade16 without the presence of a brazing element or other lower melting temperature joining materials. Elimination of the low melting point braze element produces a brazeless cermet having an extended oxidation life and the capability to withstand exposure to higher operating temperatures than components having the braze element. Theabrasive component21 comprising an abrasive cermet composition which includes a metal powder superalloy matrix combined with ceramic abrasive particles. In one form of the present invention the ceramic abrasive particles are coated with a reactive material, and in a second form of the present invention the ceramic abrasive particles are not coated with a reactive material. In one form of the present invention the material composition comprises about 0 wt. % to about 50.0 wt. % ceramic abrasive particles coated with a reactive metal, and about 50.0 wt. % to about 100.0 wt. % superalloy. The ceramic abrasive particles being of a ceramic grit material, and more preferably of at least one of the following: cubic boron nitride; man made diamond; silicon carbide; and aluminum oxide. Further, one embodiment of the present invention contemplates a mixture of at least two of the ceramic grit materials. A more preferred form of the present invention utilizes a mixture of cubic boron nitride and aluminum oxide. In one embodiment the ceramic abrasive particles having a grit size in the range between 80 mesh size and 120 mesh size. It is understood herein that other particle sizes and ceramic grit materials are contemplated herein. The reactive material is preferably titanium which serves to wet the surface of the ceramic abrasive coating to promote a metallurgical bond between the particles and the metal matrix. The titanium coating has preferably been applied using known fluid bed chemical vapor deposition techniques so as to ensure uniformity of the coating on the particles. However, other suitable processes known in the art are acceptable. The ceramic abrasive particles may be homogenous or graded through any portion of the component.
• In one form of the present invention, the bed of material that forms the[0031]abrasive component21 is subjected to a direct through thickness laser processing which causes the metal matrix material to become molten, solidify and bond with theturbine blade16. Direct laser processing is a manufacturing technique for fabricating parts from a powder bed, and details pertaining to the direct laser process utilized to make the abrasive tippedblade16 are provided below. This method is applicable to an entire region of material, a select region of material, and for cutting portions of the component. The direct tipping of the blade with theabrasive component21 through the direct laser process produces a component free of the life degradation that results from many prior art methods that includes the addition of melting point depressants typically present in braze alloys and/or that require exposing the components to a high temperature brazing and/or a diffusion bonding thermal cycle which degrades the morphology of the strengthing phase.
• With reference to FIG. 5, there is illustrated an alternate embodiment of the gas[0032]turbine engine blade160 with anabrasive cermet component210 coupled thereto by a secondary joining operation. The secondary joining operation is generally a brazing operation utilizing abrazing material211 that couples theabrasive component210 to theblade16. In one form of the present invention theabrasive component210 is fabricated by the direct laser process that is used to produce theabrasive component21. Thereafter theabrasive component210 is joined toblade160 with thebrazing material211.
• With reference to FIG. 6, there is illustrated an[0033]apparatus25 for performing the direct laser processing of a powder bed of material (not illustrated) in order to produce a free form fabrication. The term free form fabrication as used herein includes, unless otherwise specified, the capability to make a solid and/or hollow part.Apparatus25 includes achamber26 within which the direct laser process takes place, and alaser28 for performing the melting of the material that is then allowed to solidify.
• In one form of the present invention the[0034]chamber26 is defined by a fluid tight pressure vessel with avacuum pumping system27 coupled thereto for changing the atmosphere within the chamber, and a heat source capable of heating the powder bed of material30 (FIG. 7) to elevated temperatures. Preheating of thepowder material bed30 prior to the laser beam melting and solidifying aids in the outgassing of the material and improves surface characteristics, wetting and flow.Chamber26 is designed and constructed so as to be capable of maintaining a high purity atmosphere of select gases. The heat source may be located internal or external to thechamber26 and is capable of accurately heating and controlling the powder bed to temperatures within the range from ambient to 2000 degrees centigrade, while the vacuum source is capable of providing a high vacuum. It is preferred that the laser melting and solidifying of the material occur when the material bed is at an elevated temperature thereby improving dimensional stability. In one embodiment temperatures within the range of about 500 degrees centigrade to 750 degrees centigrade are preferred for the material bed during the direct laser processing-melting and solidification stages. In another form of the present invention temperatures greater than 750 degrees centigrade are preferred for the material bed during the laser processing. The vacuum preferably being in the range of about 5×10⁻³Torr to about 1×10⁻⁷Torr, and more preferably is about 5×10⁻⁵. However, other pressures are contemplated herein.
• In a more preferred form of the present invention the[0035]chamber26 could be though of as being analagous to a vacuum furnace that can be adjusted to provide a tightly controlled atmosphere within the chamber. The control of the atmosphere is characterized by the ability to regulate the chemical makeup of the gas within the chamber, degree of vacuum, and temperature. In another form of the present invention an inert atmosphere is utilized to suppress the volatilization of the material constituents within thechamber26.
• The[0036]laser28 provides a beam that selectively melts and allows the resolidification of the material within thechamber26. Other means for melting the material contemplated herein includes but is not limited to ultrasound, x-ray, and microwave. In one form of the present invention thechamber26 has a sealed lasertransparent window29 for allowing the passage of the laser beam therethrough. Laser transparent windows are believed known to persons of ordinary skill in the art. Another form of the present invention includes a disposable or indexable laser transmission window apparatus to compensate for window clouding and deposits. Thereby allowing the ready return to a more completely transparent laser transmission window for facilitating process control and reproducability. The means for melting the material could be confined within thechamber26, the means could be external to the chamber and passable through an opening in the chamber, and/or delivered through a medium coupled to the chamber such as a fiber optic cable.
• With reference to FIG. 7, there is illustrated[0037]chamber26 with a portion removed for purposes of clarity. Positioned within thechamber26 is a powder bed ofmaterial30 for melting with the laser beam. Thematerial holder31 is illustrated as a tray, however other types of material holders are contemplated herein. In one alternate embodiment the material holder fixtures a turbine blade so that the abrasive cermet composite may be directly melted, solidified and bonded on the blade, thereby producing a directly tipped blade. It is understood herein that in one embodiment of the present invention the powder bed ofmaterial30 is not bonded to thematerial holder31. In another form of the present invention a member is positioned on the material holder so that the powder bed of material can be bonded thereto, and another form of the present invention has the powder bed directly bonded to the material holder. Another, form of the present invention allows the holding of a component (such as a tool, blade, etc) at various inclinations so as to orient the component for localized repair within thechamber26. The repair of the component involves the localized heating of the component that is at ambient or near ambient temperatures. The localized heating is done by means such as inductive, electron beam, laser, plasma, focused lamps and/or other suitable means for controlled localized heating. The material holders of the present invention are designed and constructed to withstand the preheat temperatures that thepowder beds30 are subjected to.
• Referring to FIG. 8, there is illustrated[0038]laser28 and an apparatus for it's control. A preferred laser for direct laser processing is a Nd:YAG laser having sufficient power to melt a portion of material bed. Both single pass through thickness melting of the material, and double pass through thickness melting of the material bed are contemplated herein. However, other types of lasers and different power levels are within the contemplation of the present invention. One embodiment of the present invention utilizes a 250 watt laser. The control of a laser is believed within the contemplation of a person of ordinary skill in the art and the particular laser apparatus control scheme disclosed herein is not meant to limit the present methods and apparatus for making components by direct laser processing.
• The components of the laser system as shown in FIG. 8 are integrated within the[0039]laser head28.Laser head28 thus includes such conventional control elements as described in U.S. Pat. Nos. 4,863,538, and No. 5,156,697; for example a safety shutter, a front mirror assembly, and focusing elements such as diverging and converging lenses. Acomputer31 andscanning system32 are also included for controlling the direction of the laser beam as it impinges upon thepowder bed30. In one form of thepresent invention computer31 includes a microprocessor for controllinglaser28, and further includes a CAD/CAM system for generating the data by which the dimensions of the part to be produced is defined. However, other methods to generate the data to define the parts dimensions are contemplated herein. In a preferred form of the present invention the laser scanning position and scan speed are controlled by the computer software.
• [0040]Scanning system32 includes prism33 for redirecting the path of travel of the laser beam. The number of prisms necessary for directing the laser beam to the desired location is based on the physical layout of the apparatus. Alternatively, as is well known in the art one or more fixed mirrors can be used in place of prism33 for directing the laser beam from thelaser28 to thescanning system32, depending upon the particular layout of the equipment.Scanning system32 further includes a pair ofmirrors34,35 which are driven byrespective galvanometers36,37.Galvanometers36,37 are coupled to theirrespective mirrors34,35 to selectively orient themirrors34,35 and control the aim of the laser beam.Galvanometers36,37 are mounted perpendicularly to one another so that mirrors34,35 are mounted nominally at a right angle relative to one another. A function generator driver controls the movement ofgalvanometers36,37 to control the aim of the laser beam on thepowder bed30, and in conjunction withcomputer31. The function generator driver is coupled tocomputer31, so that the CAD/CAM data within the computer can be realized in the directional control of the laser beam viamirrors34,35. It is contemplated that alternative scanning systems may be used in place of acousto-optic scanners, rotating polygonal mirrors, and resonant mirror scanners.
• With reference to FIG. 9, there is illustrated a an illustrative plan view of a pair of[0041]abrasive cermet components21 formed in thepowder bed30. Theabrasive cermet components30 formed by the direct laser processing of the material within thepowder bed30 are than coupled to theturbine blade16.
• An enlarged illustrative view of a laser beam scanning sequence is set forth in FIG. 10. Laser scanning sequences are dependent upon the part geometry and the scanning sequence affects the thermal profile of the part. In a preferred form of the present invention it is desired to have a uniform thermal profile. One method of achieving a uniform thermal profile is by the selection of appropriate laser scan speed, scan spacing, and laser beam energy for the individual scan length vector. A scan length vector defines a portion of the component that will be subjected to a particular pass of the laser beam. In one form of the preferred embodiment the scan spacing is preferred less than 0.100 inches, and the scan spacing is more preferred to be in the range of about 0.0001 inches to about 0.0003 inches. With reference to TABLE 1 there are illustrated scan spacings that were utilized to produce abrasive cermet components by direct laser processing. It is understood that the view in FIG. 10 is merely illustrative and is not intended to be limiting in any fashion such as geometry, scan spacing, beam diameter, etc.[0042]Material powder bed30 becomes a target surface for the laser beam during the direct laser processing.
• With the assistance of FIGS.[0043]1-10, there has been provided a description of the method and apparatus to produce a direct laser processed component. More particularly, a description of forming an abrasive cermet component has been set forth, however other components can be fabricated with the present invention. A more detailed description of the process of forming a component by direct laser processing will now be set forth with the aid of FIGS.1-11.
• The direct laser process is a procedure in which the material constituents of the powder bed are directly laser melted and consolidated to produce a solidified part requiring little or no post processing. In the direct laser processing procedure the constituents that were not melted are reusable thereby minimizing the amount of scrap and wasted raw material generated in the process. The components formed are substantially free of voids and cracks and can be fabricated so as to be near net shape. However, in an alternate embodiment the components microstructure is modified by a post process heat treatment. The direct laser process can have parameters adjusted so as produce a highly dense part or a porous part. Further, the process can be used to produce composite components such as cermet abrasive components and/or full density monolithic metallic components.[0044]
• In one form of the present invention a component fabricated of abrasive cermet material has a size less than about four inches in diameter and a thickness less than about 0.100 inches. A component fabricated from abrasive cermet material having a thickness in the range of about 0.035 to about 0.060 is more preferred, and a component fabricated from abrasive cermet material having a thickness of about 0.060 is most preferred. Monolithic metallic components having a size less than four inches in diameter and a thickness of up to four inches are contemplated herein. In one embodiment the monolithic metallic components having a thickness greater than 0.100 inches are fabricated by melting the first powder bed layer and than melting additional layers of powder placed over the first previously melted layer of powder. A more preferred form of the monolithic metallic component has a thickness of about 0.100 inches. In one form of the present invention components formed by the direct laser processing which have a laminar structure are contemplated herein.[0045]
• With reference to FIGS. 11[0046]a&11bthere is illustrated the melting and solidification of the metalmatrix component constituents75 of the abrasive cermet composite material. The laser beam melts the metal matrix composite so as to obtain the appropriate amount of flow from the molten material. The appropriate amount of flow is qualitatively defined as the amount of flow necessary to eliminate porosity, producing a high density part while maintaining high dimensional precision and minimizing tearing. The control of the amount of flow is dependent upon many parameters including the atmosphere in which the melting and solidification occurs, degree of preheat of the material powder bed, and characteristics affecting laser energy density such as laser power, scan spacing and scan speed.
• The desire to have a uniform thermal profile implies that a very fine scan spacing with a high scan speed are preferred. The selection of scan speed and scan spacing have a direct affect on the surface roughness of the resulting component. A fine scan spacing will provide a relatively uniform smooth surface, whereas scan speed effects on surface roughness are dependent upon the overall energy density and the associated residence time in the molten material region. For a given material a high scan speed with a high energy density which would produce a long residence molten time will produce a poor surface finish. The same scan speed with a lower energy density will produce a better surface finish. It is preferred to use a fine scan spacing and vary the laser power and scan speed so as to deliver different energy densities, thereby producing a short molten residence time with full through thickness melting and density. TABLE 1 provides test data of various samples that have produced acceptable results.[0047]

  			Scan
  Temperature	Laser Power	Scan Spacing	Speed	Energy Density
  (C)	(Watts)	(in.)	(in./s)	(J/cm2)

  300	115	.000166	33	3202
  300	80	.000166	39	2088
  450	130	.000166	33	3678
  550	145	.000166	33	4102
  615	135	.000166	33	3819
  750	135	.000275	30	2495
  750	200	.000275	30	3696
  860	97.5	.000156	61	1588
  860	150	.000156	61	2443
  860	105	.000156	99	1052
  860	110	.000156	109	1000
  860	97.5	.000156	64	1525
  900	150	.000275	61	1386

• The test data for for the cermet composite indicated that full through thickness melting was achieved with energy densities of approximately 1900 joules/cm[0048]². The sample of cermet composite included 73.5 wt. % metal alloy, and 26.5 wt. % abrasive grit coating. More preferably the metal alloy was a MarM247. In a preferred form the abrasive grit coating comprises an abrasive grit material with about a 2.5 wt. % to 12 wt. % titanium coating forming a uniform coating on all surfaces of the particles. However at these energy levels (1900 Joules/cm²) the samples illustrated porosity entraped around the grit particle76 (FIGS. 11a-b). Energy densities in the range of 2,000 to 4,000 joules/cm²were needed to eliminate porosity retained around thegrit particles76 in the superalloy cermet composite. More specifically in one sample the porosity began to disappear when energy density levels were about 2,500 joules/cm². At the energy level of 2,500 joules/cm²there was a transition in microstructure from very fine equiaxed to dendritic. The very fine grained microstructure,ASTM grain size 10, produced in the samples processed at 1,900 joules/cm²to 2,500 joules/cm²would be very useful in monolithic metallic materials due to the fact that it may behave superplastically at elevated temperatures. This form of microstructure control would enable the production of equiaxed grain parts thus providing more uniform and improved mechanical properties.
• The production of a component by direct laser processing begins by blending the material components together. In one form of the present invention the material is blended for 4-6 hours prior to placing in the[0049]chamber26. The material is then preheated for a period of time to preprocess the material. In a preferred embodiment the preheating occurs within thechamber25. Thereafter the environment within thechamber26 is adjusted and the bed ofmaterial30 is subjected to the direct laser processing. Preferably the direct laser processing occurs while the bed ofmaterial30 is at an elevational temperature so as to enhance dimensional stability. The component formed has a structure consistent with a metallurgical casting with a refined microstructure. Further, the microstructure refinement is dependent upon the energy density, atmosphere, and preheating that thematerial bed30 was subjected to. For example, control of the energy density in this process will enable region specific microstructure control, thereby enabling a part to have multiple microstructures ranging from equiaxed to dendritic. Further, the component may have regions containing equiaxed, dendritic, directionally solidified, and/or single crystal.
• While the invention has been illustrated and described in detail in the drawings and foregoing description, the same is to be considered as illustrative and not restrictive in character, it being understood that only the preferred embodiment has been shown and described and that all changes and modifications that come within the spirit of the invention are desired to be protected.[0050]

Claims (1)

What is claimed is:

1. An apparatus, comprising a free form fabricated gas turbine component having a structure consistent with a metallurgical casting with a refined microstructure.