【０００１】[0001]
【産業上の利用分野】本発明は、インクジェット式記録
装置等のプリンタ用流体記録用インクに関するもので、
特に記録紙によらず安定した高品位な印字を得ることが
できる記録インクに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a fluid recording ink for a printer such as an ink jet recording apparatus,
Particularly, the present invention relates to a recording ink capable of obtaining stable high-quality printing regardless of recording paper.
【０００２】[0002]
【従来の技術】インクジェット式記録装置の記録原理
は、直径２０〜１５０μｍの微小インク液滴を発生させ
る手段、液滴を記録紙の所定の位置へ飛行させる手段に
より、所望の記録を可能にするものである。液滴は加圧
されたインクが１５〜１５０μｍ程度の内径をもった微
細なノズルオリフィスから噴出することにより発生し、
液滴に電荷を持たせ、電解操作することにより液滴を記
録紙の所定の位置へ飛行させる静電偏向型インクジェッ
ト方式、液滴を複数のノズルオリフィスより必要な箇所
だけ発生させ、記録紙にダイレクトに飛行させるドロッ
プオンデマンド型インクジェット方式などがある。2. Description of the Related Art The recording principle of an ink jet recording apparatus enables desired recording by means for generating minute ink droplets having a diameter of 20 to 150 .mu.m and means for flying the droplets to a predetermined position on a recording paper. It is a thing. Droplets are generated by ejecting pressurized ink from a fine nozzle orifice having an inner diameter of about 15 to 150 μm,
Electrostatic deflection type ink jet method in which the droplets are charged and then electrolyzed to fly to a predetermined position on the recording paper. There is a drop-on-demand inkjet system that allows direct flight.
【０００３】いずれにおいても、インクジェット記録用
の記録液としては、安全性、記録適性の面から主に水系
のものが使用されており、一方被記録材としてはインク
ジェット用専用紙や一般にはＰＰＣと呼ばれるような普
通紙が使用されている。記録液は、被記録材上で印字濃
度が充分に高く、また、にじまないことが必要であり、
さらに記録液が記録後速やかに乾燥して紙面を汚染しな
いことが望ましい。In any case, as a recording liquid for ink jet recording, an aqueous liquid is mainly used from the viewpoint of safety and recording suitability, and as a recording material, a paper for exclusive use of ink jet or generally PPC is used. The plain paper that is called is used. The recording liquid must have a sufficiently high print density on the recording material and must not bleed.
Further, it is desirable that the recording liquid is dried immediately after recording so as not to contaminate the paper surface.
【０００４】従来、インクジェット用記録液としては、
たとえば特開昭６０−６０１７０号のように多価アルコ
ールや低級アルキルエーテル、含窒素５員環ケト酸の液
媒体からなるものや、特開昭６３−２１３５８１号に示
されるように表面張力を調整したものが知られており、
特に普通紙における高品位な印字を可能としたものでは
特開平１−２１３３７６号のようにインク中に塩基性物
質を含みインクｐＨ値を１２〜１４とし、記録紙を構成
する繊維材料、サイズ剤材料、表面処理剤材料の少なく
とも一つ以上を化学的に溶解させ、インクの普通紙上で
のにじみを少なくしたものが知られている。Conventionally, as an ink jet recording liquid,
For example, as shown in JP-A-60-60170, a liquid medium containing a polyhydric alcohol, a lower alkyl ether, and a nitrogen-containing 5-membered ring keto acid, or the surface tension is adjusted as shown in JP-A-63-213581. Is known,
In particular, in the case of high-quality printing on plain paper, as described in JP-A-1-213376, a basic material is contained in the ink and the pH value of the ink is set to 12 to 14, and a fiber material and a sizing agent constituting the recording paper. It is known that at least one of a material and a surface-treating agent material is chemically dissolved to reduce ink bleeding on plain paper.
【０００５】[0005]
【発明が解決しようとする課題】しかし、特開平１−２
１３３７６号に示されるような普通紙における高品位な
印字を可能とした記録インクは、インク中に塩基性物質
として水酸化ナトリウムあるいは水酸化カリウム等のア
ルカリ金属の水酸化物を含有させた記録インクであり、
しかもｐＨが１２〜１４と強アルカリ性であるため、ユ
ーザーがインクに直接あるいは記録紙表面に記録したイ
ンクを触れるような場合は皮膚等に対して刺激物特有の
炎症を発生するおそれがあり、安全性を確保することは
難しいものであった。However, JP-A 1-2
A recording ink capable of high-quality printing on plain paper as shown in No. 13376 is a recording ink containing an alkali metal hydroxide such as sodium hydroxide or potassium hydroxide as a basic substance in the ink. And
Moreover, since the pH is 12 to 14 and is strongly alkaline, when the user touches the ink directly or with the ink recorded on the surface of the recording paper, irritation peculiar to the irritant may occur on the skin, etc. It was difficult to secure sex.
【０００６】また、上述のような記録インクは普通紙に
おける印字品質は高品位であるが、インクジェット印字
専用に作られた表面にコート層を持ったような特殊紙に
印字する場合、記録インク中のアルカリ性物質がコート
層を溶解してしまい、にじみ等の画像劣化の原因となる
ため、普通紙以外の記録紙では性能が発揮できないとい
う問題点があった。The above-described recording ink has a high print quality on plain paper, but when printing on a special paper having a coat layer on the surface made exclusively for ink jet printing, However, the alkaline substance dissolves in the coating layer and causes image deterioration such as bleeding. Therefore, there is a problem that the performance cannot be exhibited on recording paper other than plain paper.
【０００７】さらに、上述のような記録インクを用いカ
ラー印字を行う場合、イエロー色，マゼンタ色，シアン
色等の染料をインク中に含有させる必要があるが、これ
らの染料がｐＨ１２〜１４という強アルカリによって化
学変化をおこしてしまい、染料特有の吸収スペクトルが
変化するため、所望の色が得られないという問題点があ
った。Further, when performing color printing using the above-described recording ink, it is necessary to include a dye of yellow color, magenta color, cyan color or the like in the ink, but these dyes have a strong pH of 12-14. There is a problem in that a desired color cannot be obtained because the alkali causes a chemical change and the absorption spectrum peculiar to the dye changes.
【０００８】そこで、本発明の目的は、従来のこのよう
な課題を解決し、ユーザーに対する安全性を確保し、普
通紙を含めたあらゆる記録紙に対して同様に高品位な印
字が可能であり、またカラー印字も可能であるような記
録用インクを提供するところにある。Therefore, an object of the present invention is to solve the conventional problems as described above, to secure the safety for the user, and to similarly perform high-quality printing on any recording paper including plain paper. Moreover, it is an object to provide a recording ink capable of color printing.
【０００９】[0009]
【課題を解決するための手段】上記課題を解決するため
に、本発明ではノズルより噴射され記録を行うインクジ
ェット記録装置に使用される記録用インクにおいて、
１．５〜８重量％の部分ケン化ポリビニルアルコール
と、５〜２０重量％のエタノールを含有させる。次に部
分ケン化ポリビニルアルコールとしては、重合度が１０
０〜１０００，ケン化率が、５５〜８５％であることを
特徴とする。In order to solve the above problems, according to the present invention, in a recording ink used in an ink jet recording apparatus ejected from a nozzle for recording,
It contains 1.5-8 wt% partially saponified polyvinyl alcohol and 5-20 wt% ethanol. Next, the partially saponified polyvinyl alcohol has a degree of polymerization of 10
It is characterized in that the saponification rate is 0 to 1000 and the saponification rate is 55 to 85%.
【００１０】[0010]
【作用】ポリビニルアルコールの構造式を化１に示す。The structural formula of polyvinyl alcohol is shown in Chemical formula 1.
【００１１】[0011]
【化１】[Chemical 1]
【００１２】[0012]
【化２】[Chemical 2]
【００１３】これは、化２に示すポリ酢酸ビニルをアル
カリ中で加水分解してつくられる。このように、ポリ酢
酸ビニルのＣＯＯＲ基を９０％以上ＯＨ基に置き換えた
ものが一般的なポリビニルアルコールであるが、この置
き換えを９０％以下に調整したものもあり、このような
ものは部分ケン化ポリビニルアルコールと呼ばれてお
り、ケン化率が高くなるほど水に対する溶解性が増大
し、ケン化率が低くなるほど有機溶剤に対する溶解性が
増大する。したがって部分ケン化ポリビニルアルコール
は、水と有機溶剤を特定の比率で混合した溶媒に良好な
溶解性を持たせることが可能な材料である。This is produced by hydrolyzing polyvinyl acetate shown in Chemical formula 2 in an alkali. As described above, it is a general polyvinyl alcohol that the COOR group of polyvinyl acetate is replaced with 90% or more of the OH group. However, there is also one in which this replacement is adjusted to 90% or less. It is called modified polyvinyl alcohol, and the higher the saponification rate, the higher the solubility in water, and the lower the saponification rate, the higher the solubility in organic solvents. Therefore, partially saponified polyvinyl alcohol is a material capable of having good solubility in a solvent obtained by mixing water and an organic solvent in a specific ratio.
【００１４】インクジェット記録装置に使用される記録
用インクにおいて、普通紙ににじみにくく高品位な印字
を可能にするには、特開平１−２１３３７６号に示され
るようにインクのｐＨを１２〜１４にする方法の他に、
記録インクを紙の繊維にしみこみにくくさせるためイン
クの粘度を上げるという方法が考えられる。しかしイン
ク粘度を高くすると、ノズルオリフィス中で記録インク
が目詰まりをおこすといった事故や、記録紙上でのイン
ク乾燥が困難になり、インクが流れたり他の部分に転移
したりして汚染の原因となることがありインクジェット
記録装置用の記録用インクとしては適さなかった。In the recording ink used in the ink jet recording apparatus, in order to prevent bleeding on plain paper and to enable high-quality printing, the pH of the ink is set to 12 to 14 as described in JP-A-1-213376. Besides how to do
A method of increasing the viscosity of the recording ink is considered in order to prevent the recording ink from penetrating into the fibers of the paper. However, increasing the ink viscosity may cause an accident such as clogging of the recording ink in the nozzle orifice, or make it difficult to dry the ink on the recording paper, causing the ink to flow or transfer to other parts and cause contamination. In some cases, it was not suitable as a recording ink for an inkjet recording device.
【００１５】本発明の記録用インクでは、部分ケン化ポ
リビニルアルコールの特性を利用し、エタノールを５〜
２０重量％含有した溶媒によって良好に溶解されること
により、ノズルオリフィス中では充分な溶解性を持つた
め目詰まりをおこすことはなく、ノズルより噴射され記
録紙に付着した状態では急速にエタノールが揮発し部分
ケン化ポリビニルアルコールを含んだ記録用インクの粘
度は急激に上昇しするため、紙繊維にインクがにじむこ
とがなくなり高品位な印字が可能となる。そして、さら
にエタノールが揮発すると、部分ケン化ポリビニルアル
コールの溶解性が低下するため、インクが流れたり他の
部分に転移することはない。ただし、このような特性を
持たせるためには、記録用インク中に含有させる部分ケ
ン化ポリビニルアルコールの重合度は１００〜１０００
程度が望ましく、これより重合度が高くなると粘度が増
大しすぎてしまい、ノズルオリフィスでの目詰まりとい
った事故の原因となってしまう。また、部分ケン化ポリ
ビニルアルコールのケン化率は５５〜８５％が望まし
く、これより低くては水に対する溶解性が低下し記録用
インクとしては適さなくなり、これより高くてはエタノ
ールに対する溶解性が低下し、本発明で必要な挙動を示
さなくなってしまう。In the recording ink of the present invention, the characteristics of partially saponified polyvinyl alcohol are utilized, and ethanol of 5 to 5 is used.
Since it is well dissolved by the solvent containing 20% by weight, it has sufficient solubility in the nozzle orifice and does not cause clogging. Ethanol evaporates rapidly when ejected from the nozzle and attached to the recording paper. Since the viscosity of the recording ink containing the partially saponified polyvinyl alcohol rapidly increases, the ink does not bleed into the paper fiber and high-quality printing becomes possible. When the ethanol is further volatilized, the solubility of the partially saponified polyvinyl alcohol is lowered, so that the ink does not flow or transfer to another portion. However, in order to have such characteristics, the degree of polymerization of the partially saponified polyvinyl alcohol contained in the recording ink is 100 to 1000.
The degree is desirable, and if the degree of polymerization is higher than this, the viscosity increases too much, which causes an accident such as clogging at the nozzle orifice. Further, the saponification ratio of partially saponified polyvinyl alcohol is preferably 55 to 85%, and if it is lower than this, the solubility in water decreases and it becomes unsuitable as a recording ink, and if higher than this, the solubility in ethanol decreases. However, the behavior required by the present invention is not exhibited.
【００１６】尚、本発明の記録用インクでは、インクジ
ェット印字専用に作られた表面にコート層を持ったよう
な特殊紙に印字する場合でも、コート層に影響を及ぼす
ような成分は入っていないため、高品位な印字が可能で
ある。さらに、本発明の記録用インクでは、イエロー
色，マゼンタ色，シアン色等の染料に化学変化をおこさ
せるような成分は入っていないため、カラー印字におい
ても高品位な印字が可能である。The recording ink of the present invention does not contain a component that affects the coat layer even when printing on a special paper having a coat layer on the surface made exclusively for ink jet printing. Therefore, high-quality printing is possible. Further, since the recording ink of the present invention does not contain a component that causes a chemical change in dyes such as yellow, magenta, and cyan, high-quality printing is possible even in color printing.
【００１７】以上説明したような本発明における記録用
インクを調整することで、水酸化ナトリウムあるいは水
酸化カリウム等のような強アルカリ性の塩基性物質を添
加することなく、インクジェット記録専用に作られた特
殊紙にはもちろん、天然パルプからなり親水性や吸水性
の高い普通記録紙に対してもにじみのない高品位な記録
が可能であり、安全性を確保した記録用インクとなる。By adjusting the recording ink according to the present invention as described above, it is made for ink jet recording only without adding a strong alkaline basic substance such as sodium hydroxide or potassium hydroxide. Not only special paper but also ordinary recording paper made of natural pulp and having high hydrophilicity and water absorbency enables high-quality recording without bleeding, and is a recording ink that ensures safety.
【００１８】[0018]
【実施例】以下に、本発明の実施例を説明するが、これ
らの実施例は本発明を更に具体的に説明するものであ
り、実施の態様がこれにより限定されるものではない。 （実施例１）以下に示すように、重合度、ケン化率のそ
れぞれ異なった部分ケン化ポリビニルアルコールを用
い、３種類のインクを調整した。染料としては、黒色の
染料であるＣ．Ｉ．ＤｉｒｅｃｔＢｌａｃｋ１６８を用
いた。比較のために、部分ケン化ポリビニルアルコール
を含まない比較用インクを調整した。EXAMPLES Hereinafter, examples of the present invention will be described, but these examples further specifically describe the present invention, and the embodiments are not limited thereto. (Example 1) As shown below, three types of inks were prepared using partially saponified polyvinyl alcohols having different degrees of polymerization and saponification rates. As the dye, C.I. I. DirectBlack 168 was used. For comparison, a comparative ink containing no partially saponified polyvinyl alcohol was prepared.
【００１９】 （インク１） Ｃ．Ｉ．ＤｉｒｅｃｔＢｌａｃｋ１６８ ３．０重量％ ジエチレングリコール １０．０重量％ エタノール ８．０重量％ 部分ケン化ポリビニルアルコール ４．０重量％ （重合度２２０，ケン化率７８％） イオン交換水 ７５．０重量％ （インク２） Ｃ．Ｉ．ＤｉｒｅｃｔＢｌａｃｋ１６８ ３．０重量％ ジエチレングリコール １０．０重量％ エタノール １２．０重量％ 部分ケン化ポリビニルアルコール ３．０重量％ （重合度４６０，ケン化率７４％） イオン交換水 ７２．０重量％ （インク３） Ｃ．Ｉ．ＤｉｒｅｃｔＢｌａｃｋ１６８ ３．０重量％ ジエチレングリコール １０．０重量％ エタノール １６．０重量％ 部分ケン化ポリビニルアルコール ２．５重量％ （重合度４８０，ケン化率６１％） イオン交換水 ６８．５重量％ （比較用インク） Ｃ．Ｉ．ＤｉｒｅｃｔＢｌａｃｋ１６８ ３．０重量％ ジエチレングリコール １０．０重量％ エタノール １０．０重量％ イオン交換水 ７７．０重量％ 以上のように調整されたそれぞれのインクを、インクジ
ェット記録装置に吸引、充填させ、一般にはＰＰＣと呼
ばれている電子写真用普通記録紙である普通紙ＰＰＣ−
Ｋ（大昭和製紙（株） 商品名）と、インクジェット記
録用特殊紙である三菱ＩＪコート紙（三菱製紙（株）
商品名）に所望するドットを記録した。本実施例に用い
たインクジェット記録装置のノズルオリフィスの開口部
の大きさは縦２５μｍ、横４０μｍの四角形をしてお
り、一回に直径３０〜４０μｍ程度のインク滴を噴射す
ることができる。(Ink 1) C.I. I. DirectBlack 168 3.0 wt% Diethylene glycol 10.0 wt% Ethanol 8.0 wt% Partially saponified polyvinyl alcohol 4.0 wt% (Polymerization degree 220, Saponification rate 78%) Ion-exchanged water 75.0 wt% (Ink 2 ) C. I. DirectBlack 168 3.0 wt% Diethylene glycol 10.0 wt% Ethanol 12.0 wt% Partially saponified polyvinyl alcohol 3.0 wt% (Polymerization degree 460, Saponification rate 74%) Ion-exchanged water 72.0 wt% (Ink 3 ) C. I. DirectBlack 168 3.0 wt% Diethylene glycol 10.0 wt% Ethanol 16.0 wt% Partially saponified polyvinyl alcohol 2.5 wt% (Polymerization degree 480, saponification rate 61%) Ion-exchanged water 68.5 wt% (for comparison) Ink) C.I. I. DirectBlack 168 3.0 wt% Diethylene glycol 10.0 wt% Ethanol 10.0 wt% Ion-exchanged water 77.0 wt% Each ink adjusted as above is sucked and filled into an ink jet recording apparatus, and generally PPC is used. Ordinary paper PPC, which is called electrophotographic ordinary recording paper.
K (trade name of Daishowa Paper Manufacturing Co., Ltd.) and Mitsubishi IJ coated paper (Mitsubishi Paper Manufacturing Co., Ltd.), which is a special paper for inkjet recording.
The desired dot was recorded in the product name). The size of the opening of the nozzle orifice of the ink jet recording apparatus used in this embodiment is a square having a length of 25 μm and a width of 40 μm, and ink droplets having a diameter of about 30 to 40 μm can be ejected at one time.
【００２０】印字されたドットを顕微鏡観察し、直径お
よび真円度を測定した結果を表１に示す。Table 1 shows the results of measuring the diameter and roundness of the printed dots observed under a microscope.
【００２１】[0021]
【表１】[Table 1]
【００２２】三菱ＩＪコート紙に対する印字では、いず
れのドットも８０〜９０μｍの大きさであり真円度も１
に近く高品位な印字が行われていることがわかる。しか
し、普通紙ＰＰＣ−Ｋに対する印字では、部分ケン化ポ
リビニルアルコールを含んだ本発明のインクにおいて
は、インク１では８８μｍ、インク２では８３μｍ、イ
ンク３では８６μｍとインクジェット用の特殊紙に対す
る印字と変わらずに、また真円度も１に近く高品位の印
字が行われているが、従来のインクである比較用インク
においてはインクが記録紙の繊維ににじんでしまいドッ
ト径が１１０μｍ以上と大きくなるばかりでなく、真円
度１．１３と円の形が大きく崩れており高品位な印字は
望めない。In printing on Mitsubishi IJ coated paper, each dot has a size of 80 to 90 μm and a roundness of 1
It can be seen that high-quality printing is carried out close to. However, when printing on plain paper PPC-K, the ink of the present invention containing partially saponified polyvinyl alcohol was 88 μm for ink 1, 83 μm for ink 2, and 86 μm for ink 3, which is different from printing on special paper for inkjet. In addition, the roundness is close to 1 and high-quality printing is performed, but in the comparative ink, which is a conventional ink, the ink bleeds into the fibers of the recording paper, and the dot diameter increases to 110 μm or more. Not only that, the roundness is 1.13 and the shape of the circle is greatly broken, so high-quality printing cannot be expected.
【００２３】以上のように、本発明の記録用インクによ
り、記録紙に影響されず、にじみ等のない高品位な印字
が可能なことを確認した。 （実施例２）以下に示すように、重合度２２０、ケン化
率７８％の部分ケン化ポリビニルアルコールを用い実験
用インクを調整した。染料としては、シアン色の染料で
あるＣ．Ｉ．ＤｉｒｅｃｔＢｌｕｅ１９９を用いた。比
較のために、部分ケン化ポリビニルアルコールを含まな
い比較用インクを調整した。As described above, it was confirmed that the recording ink of the present invention enables high-quality printing without being affected by the recording paper and without bleeding. (Example 2) As shown below, a test ink was prepared using a partially saponified polyvinyl alcohol having a degree of polymerization of 220 and a saponification rate of 78%. As the dye, C.I. which is a cyan dye. I. DirectBlue199 was used. For comparison, a comparative ink containing no partially saponified polyvinyl alcohol was prepared.
【００２４】 （実験用インク） Ｃ．Ｉ．ＤｉｒｅｃｔＢｌｕｅ１９９ ３．０重量％ トリエチレングリコール １５．０重量％ イソプロパノール ５．０重量％ エタノール １０．０重量％ 部分ケン化ポリビニルアルコール ３．０重量％ （重合度２２０，ケン化率７８％） イオン交換水 ６４．０重量％ （比較用インク） Ｃ．Ｉ．ＤｉｒｅｃｔＢｌｕｅ１９９ ３．０重量％ トリエチレングリコール １５．０重量％ イソプロパノール ５．０重量％ エタノール １０．０重量％ イオン交換水 ６７．０重量％ 以上のように調整されたそれぞれのインクの吸収スペク
トルを、自記分光光度計を用いて測定した。図１は実験
用インクの分光吸収特性の測定結果、図２は比較用イン
クの分光吸収特性の測定結果である。測定結果から明か
なように、それぞれのインクの吸収スペクトルは同様な
特性を示しており、本発明の記録用インクに用いる部分
ケン化ポリビニルアルコールのような組成物が、使用す
る染料に対して化学的な悪影響を与えていないことが確
認された。(Experimental Ink) C. I. DirectBlue 199 3.0 wt% Triethylene glycol 15.0 wt% Isopropanol 5.0 wt% Ethanol 10.0 wt% Partially saponified polyvinyl alcohol 3.0 wt% (Polymerization degree 220, Saponification rate 78%) Ion-exchanged water 64.0% by weight (comparative ink) C.I. I. DirectBlue 199 3.0% by weight Triethylene glycol 15.0% by weight Isopropanol 5.0% by weight Ethanol 10.0% by weight Ion-exchanged water 67.0% by weight The absorption spectra of the respective inks adjusted as described above are described by themselves. It measured using the spectrophotometer. FIG. 1 shows the measurement results of the spectral absorption characteristics of the experimental ink, and FIG. 2 shows the measurement results of the spectral absorption characteristics of the comparative ink. As is clear from the measurement results, the absorption spectra of the respective inks show similar characteristics, and the composition such as partially saponified polyvinyl alcohol used in the recording ink of the present invention is chemically different from the dye used. It was confirmed that there was no negative impact on the business.
【００２５】次にそれぞれのインクを、インクジェット
記録装置に吸引、充填させ、一般にはＰＰＣと呼ばれて
いる電子写真用普通記録紙である普通紙ＰＰＣ−Ｋ（大
昭和製紙（株） 商品名）と、インクジェット記録用特
殊紙である三菱ＩＪコート紙（三菱製紙（株） 商品
名）に所望するドットを記録した。本実施例に用いたイ
ンクジェット記録装置のノズルオリフィスの開口部の大
きさは縦２５μｍ、横４０μｍの四角形をしており、一
回に直径３０〜４０μｍ程度のインク滴を噴射すること
ができる。Next, each ink is sucked and filled in an ink jet recording apparatus, and plain paper PPC-K (trade name of Daishowa Paper Manufacturing Co., Ltd.), which is a general recording paper for electrophotography generally called PPC. Then, desired dots were recorded on Mitsubishi IJ coated paper (trade name of Mitsubishi Paper Mills Co., Ltd.) which is a special paper for inkjet recording. The size of the opening of the nozzle orifice of the ink jet recording apparatus used in this embodiment is a square having a length of 25 μm and a width of 40 μm, and ink droplets having a diameter of about 30 to 40 μm can be ejected at one time.
【００２６】[0026]
【表２】[Table 2]
【００２７】印字されたドットを顕微鏡観察し、直径お
よび真円度を測定した結果を表２に示す。三菱ＩＪコー
ト紙に対する印字では、いずれのドットも８０〜９０μ
ｍの大きさであり真円度も１に近く高品位な印字が行わ
れていることがわかる。しかし、普通紙ＰＰＣ−Ｋに対
する印字では、部分ケン化ポリビニルアルコールを含ん
だ本発明のインクにおいては９０μｍであり、真円度も
１に近くインクジェット用の特殊紙に対する印字と変わ
らずに高品位の印字が行われているが、従来のインクで
ある比較用インクにおいてはインクが記録紙の繊維にに
じんでしまい、ドット径が１１０μｍ以上と大きくな
り、真円度も１．１６と円の形が大きく崩れており高品
位な印字は望めない。Table 2 shows the results of measuring the diameter and roundness of the printed dots under a microscope. When printing on Mitsubishi IJ coated paper, every dot is 80-90μ
It can be seen that the size is m and the roundness is close to 1 and high-quality printing is performed. However, in the printing on the plain paper PPC-K, the ink of the present invention containing partially saponified polyvinyl alcohol is 90 μm, and the roundness is close to 1 and is the same as the printing on the special paper for ink jet, and the printing quality is high. Although printing is performed, in the comparative ink, which is a conventional ink, the ink bleeds into the fibers of the recording paper, the dot diameter is increased to 110 μm or more, and the circularity is 1.16. It is greatly broken and high-quality printing cannot be expected.
【００２８】以上のように、本発明の記録用インクによ
り、記録紙に影響されず、にじみ等のない高品位な印字
が可能で、また染料に悪影響を与えるようなことが無い
ことが確認された。このように、実施例において本発明
の記録用インクを説明したが、記載したインク組成、成
分以外にも請求の範囲において適宜使用可能であること
は言うまでもない。As described above, it was confirmed that the recording ink of the present invention enables high-quality printing without being affected by the recording paper, bleeding, etc. and does not adversely affect the dye. It was As described above, the recording ink of the present invention has been described in the examples, but it goes without saying that other than the described ink composition and components, they can be appropriately used within the scope of the claims.
【００２９】[0029]
【発明の効果】以上説明したように、この発明において
は、ノズルより噴射され記録を行うインクジェット記録
装置に使用される記録用インクにおいて、１．５〜８重
量％の部分ケン化ポリビニルアルコールと、５〜２０重
量％のエタノールを含有させ、その部分ケン化ポリビニ
ルアルコールとしては、重合度が１００〜１０００，ケ
ン化率が、５５〜８５％であることを特徴とすることに
より、ユーザーに対する安全性を確保し、天然パルプか
らなり親水性や吸水性の高い普通紙に対してもインクジ
ェット用専用紙に対する印字と同様に高品位な印字が可
能であるという効果がある。As described above, according to the present invention, the recording ink used in the ink jet recording apparatus which is ejected from the nozzle to perform recording contains 1.5 to 8% by weight of partially saponified polyvinyl alcohol. As a partially saponified polyvinyl alcohol containing 5 to 20% by weight of ethanol, the degree of polymerization is 100 to 1000, and the saponification rate is 55 to 85%. It is possible to obtain high-quality printing even on plain paper that is made of natural pulp and has high hydrophilicity and water absorbency, as well as printing on dedicated paper for inkjet.
【図１】本発明の実施例２に記載した記録用インク及び
比較用インクの分光吸収特性を示す図である。FIG. 1 is a diagram showing spectral absorption characteristics of a recording ink and a comparative ink described in Example 2 of the present invention.
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| JP24785692AJPH06100807A (en) | 1992-09-17 | 1992-09-17 | Recording ink |
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| JP24785692AJPH06100807A (en) | 1992-09-17 | 1992-09-17 | Recording ink |
| Publication Number | Publication Date |
|---|---|
| JPH06100807Atrue JPH06100807A (en) | 1994-04-12 |
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| JP24785692APendingJPH06100807A (en) | 1992-09-17 | 1992-09-17 | Recording ink |
| Country | Link |
|---|---|
| JP (1) | JPH06100807A (en) |
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| JPH0227355A (en)* | 1988-06-03 | 1990-01-30 | Eastman Kodak Co | Photographic stabilzing bath containing hydrolyzing polymaleic dehydride |
| JPH05249638A (en)* | 1986-04-30 | 1993-09-28 | Konica Corp | Method for processing silver halide color photographic sensitive material and color developer composition |
| JP2620581B2 (en)* | 1986-03-26 | 1997-06-18 | コニカ株式会社 | Processing method of silver halide color photographic light-sensitive material enabling rapid development |
| JP2005075849A (en)* | 2003-08-28 | 2005-03-24 | Konica Minolta Holdings Inc | Ink, recording method and inkjet recording method |
| JP2015511984A (en)* | 2012-03-05 | 2015-04-23 | ランダ コーポレイション リミテッド | Ink film construction |
| US10190012B2 (en) | 2012-03-05 | 2019-01-29 | Landa Corporation Ltd. | Treatment of release layer and inkjet ink formulations |
| US10266711B2 (en) | 2012-03-05 | 2019-04-23 | Landa Corporation Ltd. | Ink film constructions |
| US10357963B2 (en) | 2012-03-05 | 2019-07-23 | Landa Corporation Ltd. | Digital printing process |
| US10357985B2 (en) | 2012-03-05 | 2019-07-23 | Landa Corporation Ltd. | Printing system |
| US10427399B2 (en) | 2015-04-14 | 2019-10-01 | Landa Corporation Ltd. | Apparatus for threading an intermediate transfer member of a printing system |
| US10434761B2 (en) | 2012-03-05 | 2019-10-08 | Landa Corporation Ltd. | Digital printing process |
| US10518526B2 (en) | 2012-03-05 | 2019-12-31 | Landa Corporation Ltd. | Apparatus and method for control or monitoring a printing system |
| US10569534B2 (en) | 2012-03-05 | 2020-02-25 | Landa Corporation Ltd. | Digital printing system |
| US10569533B2 (en) | 2012-03-15 | 2020-02-25 | Landa Corporation Ltd. | Endless flexible belt for a printing system |
| US10569532B2 (en) | 2012-03-05 | 2020-02-25 | Landa Corporation Ltd. | Digital printing system |
| US10596804B2 (en) | 2015-03-20 | 2020-03-24 | Landa Corporation Ltd. | Indirect printing system |
| US10632740B2 (en) | 2010-04-23 | 2020-04-28 | Landa Corporation Ltd. | Digital printing process |
| US10642198B2 (en) | 2012-03-05 | 2020-05-05 | Landa Corporation Ltd. | Intermediate transfer members for use with indirect printing systems and protonatable intermediate transfer members for use with indirect printing systems |
| US10759953B2 (en) | 2013-09-11 | 2020-09-01 | Landa Corporation Ltd. | Ink formulations and film constructions thereof |
| US10889128B2 (en) | 2016-05-30 | 2021-01-12 | Landa Corporation Ltd. | Intermediate transfer member |
| US10926532B2 (en) | 2017-10-19 | 2021-02-23 | Landa Corporation Ltd. | Endless flexible belt for a printing system |
| US10933661B2 (en) | 2016-05-30 | 2021-03-02 | Landa Corporation Ltd. | Digital printing process |
| US10994528B1 (en) | 2018-08-02 | 2021-05-04 | Landa Corporation Ltd. | Digital printing system with flexible intermediate transfer member |
| US11267239B2 (en) | 2017-11-19 | 2022-03-08 | Landa Corporation Ltd. | Digital printing system |
| US11321028B2 (en) | 2019-12-11 | 2022-05-03 | Landa Corporation Ltd. | Correcting registration errors in digital printing |
| US11318734B2 (en) | 2018-10-08 | 2022-05-03 | Landa Corporation Ltd. | Friction reduction means for printing systems and method |
| US11465426B2 (en) | 2018-06-26 | 2022-10-11 | Landa Corporation Ltd. | Intermediate transfer member for a digital printing system |
| US11511536B2 (en) | 2017-11-27 | 2022-11-29 | Landa Corporation Ltd. | Calibration of runout error in a digital printing system |
| US11679615B2 (en) | 2017-12-07 | 2023-06-20 | Landa Corporation Ltd. | Digital printing process and method |
| US11707943B2 (en) | 2017-12-06 | 2023-07-25 | Landa Corporation Ltd. | Method and apparatus for digital printing |
| US11787170B2 (en) | 2018-12-24 | 2023-10-17 | Landa Corporation Ltd. | Digital printing system |
| US11833813B2 (en) | 2019-11-25 | 2023-12-05 | Landa Corporation Ltd. | Drying ink in digital printing using infrared radiation |
| US12001902B2 (en) | 2018-08-13 | 2024-06-04 | Landa Corporation Ltd. | Correcting distortions in digital printing by implanting dummy pixels in a digital image |
| US12011920B2 (en) | 2019-12-29 | 2024-06-18 | Landa Corporation Ltd. | Printing method and system |
| US12358277B2 (en) | 2019-03-31 | 2025-07-15 | Landa Corporation Ltd. | Systems and methods for preventing or minimizing printing defects in printing processes |
| US12430453B2 (en) | 2021-02-02 | 2025-09-30 | Landa Corporation Ltd. | Mitigating distortions in printed images |
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| JP2620581B2 (en)* | 1986-03-26 | 1997-06-18 | コニカ株式会社 | Processing method of silver halide color photographic light-sensitive material enabling rapid development |
| JPH05249638A (en)* | 1986-04-30 | 1993-09-28 | Konica Corp | Method for processing silver halide color photographic sensitive material and color developer composition |
| JPH05249639A (en)* | 1986-04-30 | 1993-09-28 | Konica Corp | Method for processing silver halide color photographic sensitive material and color developer composition |
| JPH0227355A (en)* | 1988-06-03 | 1990-01-30 | Eastman Kodak Co | Photographic stabilzing bath containing hydrolyzing polymaleic dehydride |
| JP2005075849A (en)* | 2003-08-28 | 2005-03-24 | Konica Minolta Holdings Inc | Ink, recording method and inkjet recording method |
| US10632740B2 (en) | 2010-04-23 | 2020-04-28 | Landa Corporation Ltd. | Digital printing process |
| US10357963B2 (en) | 2012-03-05 | 2019-07-23 | Landa Corporation Ltd. | Digital printing process |
| US10434761B2 (en) | 2012-03-05 | 2019-10-08 | Landa Corporation Ltd. | Digital printing process |
| US10266711B2 (en) | 2012-03-05 | 2019-04-23 | Landa Corporation Ltd. | Ink film constructions |
| US10300690B2 (en) | 2012-03-05 | 2019-05-28 | Landa Corporation Ltd. | Ink film constructions |
| US10642198B2 (en) | 2012-03-05 | 2020-05-05 | Landa Corporation Ltd. | Intermediate transfer members for use with indirect printing systems and protonatable intermediate transfer members for use with indirect printing systems |
| US10357985B2 (en) | 2012-03-05 | 2019-07-23 | Landa Corporation Ltd. | Printing system |
| CN110217010A (en)* | 2012-03-05 | 2019-09-10 | 兰达公司 | Ink film construction |
| JP2019162880A (en)* | 2012-03-05 | 2019-09-26 | ランダ コーポレイション リミテッド | Ink film constructions |
| CN110217010B (en)* | 2012-03-05 | 2021-06-08 | 兰达公司 | Ink film structure |
| US10190012B2 (en) | 2012-03-05 | 2019-01-29 | Landa Corporation Ltd. | Treatment of release layer and inkjet ink formulations |
| US10518526B2 (en) | 2012-03-05 | 2019-12-31 | Landa Corporation Ltd. | Apparatus and method for control or monitoring a printing system |
| US10569534B2 (en) | 2012-03-05 | 2020-02-25 | Landa Corporation Ltd. | Digital printing system |
| JP2015511984A (en)* | 2012-03-05 | 2015-04-23 | ランダ コーポレイション リミテッド | Ink film construction |
| US10569532B2 (en) | 2012-03-05 | 2020-02-25 | Landa Corporation Ltd. | Digital printing system |
| JP2018008520A (en)* | 2012-03-05 | 2018-01-18 | ランダ コーポレイション リミテッド | Ink film construction |
| US10569533B2 (en) | 2012-03-15 | 2020-02-25 | Landa Corporation Ltd. | Endless flexible belt for a printing system |
| US10759953B2 (en) | 2013-09-11 | 2020-09-01 | Landa Corporation Ltd. | Ink formulations and film constructions thereof |
| US10596804B2 (en) | 2015-03-20 | 2020-03-24 | Landa Corporation Ltd. | Indirect printing system |
| US10427399B2 (en) | 2015-04-14 | 2019-10-01 | Landa Corporation Ltd. | Apparatus for threading an intermediate transfer member of a printing system |
| US10889128B2 (en) | 2016-05-30 | 2021-01-12 | Landa Corporation Ltd. | Intermediate transfer member |
| US10933661B2 (en) | 2016-05-30 | 2021-03-02 | Landa Corporation Ltd. | Digital printing process |
| US10926532B2 (en) | 2017-10-19 | 2021-02-23 | Landa Corporation Ltd. | Endless flexible belt for a printing system |
| US11267239B2 (en) | 2017-11-19 | 2022-03-08 | Landa Corporation Ltd. | Digital printing system |
| US11511536B2 (en) | 2017-11-27 | 2022-11-29 | Landa Corporation Ltd. | Calibration of runout error in a digital printing system |
| US11707943B2 (en) | 2017-12-06 | 2023-07-25 | Landa Corporation Ltd. | Method and apparatus for digital printing |
| US11679615B2 (en) | 2017-12-07 | 2023-06-20 | Landa Corporation Ltd. | Digital printing process and method |
| US11465426B2 (en) | 2018-06-26 | 2022-10-11 | Landa Corporation Ltd. | Intermediate transfer member for a digital printing system |
| US10994528B1 (en) | 2018-08-02 | 2021-05-04 | Landa Corporation Ltd. | Digital printing system with flexible intermediate transfer member |
| US12001902B2 (en) | 2018-08-13 | 2024-06-04 | Landa Corporation Ltd. | Correcting distortions in digital printing by implanting dummy pixels in a digital image |
| US11318734B2 (en) | 2018-10-08 | 2022-05-03 | Landa Corporation Ltd. | Friction reduction means for printing systems and method |
| US11787170B2 (en) | 2018-12-24 | 2023-10-17 | Landa Corporation Ltd. | Digital printing system |
| US12358277B2 (en) | 2019-03-31 | 2025-07-15 | Landa Corporation Ltd. | Systems and methods for preventing or minimizing printing defects in printing processes |
| US11833813B2 (en) | 2019-11-25 | 2023-12-05 | Landa Corporation Ltd. | Drying ink in digital printing using infrared radiation |
| US11321028B2 (en) | 2019-12-11 | 2022-05-03 | Landa Corporation Ltd. | Correcting registration errors in digital printing |
| US12011920B2 (en) | 2019-12-29 | 2024-06-18 | Landa Corporation Ltd. | Printing method and system |
| US12430453B2 (en) | 2021-02-02 | 2025-09-30 | Landa Corporation Ltd. | Mitigating distortions in printed images |
| Publication | Publication Date | Title |
|---|---|---|
| JPH06100807A (en) | Recording ink | |
| KR950010165B1 (en) | Recording liquid and ink-jet recording method making use thereof | |
| JP3133428B2 (en) | Ink jet recording liquid, method for producing the same, and ink jet recording method using the same | |
| JP2899088B2 (en) | Ink jet ink, method of manufacturing the same, and ink jet recording method using such ink | |
| JPH07238243A (en) | Recording ink | |
| JP4882201B2 (en) | Inkjet recording method | |
| JP2006249429A (en) | Dye-based ink composition | |
| JPH06192605A (en) | INK, INKJET RECORDING METHOD USING THE SAME, AND DEVICE USING THE INK | |
| JPH04211470A (en) | Ink, inkjet recording method and equipment using the same | |
| JP2011157417A (en) | Inkjet ink | |
| JP4736328B2 (en) | Inkjet recording method | |
| JP2004292817A (en) | Solvent system for ink-jet ink | |
| JP2007145928A (en) | Inkjet ink, method for producing inkjet ink, inkjet printer, and inkjet recording method using the same | |
| JP4158303B2 (en) | Water-based pigment ink for inkjet recording | |
| JPH06116522A (en) | Recording liquid and ink jet recording method using the same | |
| JP2001089686A (en) | Aqueous pigment ink composition | |
| JPS603434B2 (en) | jet printing ink | |
| JP3843535B2 (en) | Water-based ink composition | |
| JP2006232933A (en) | Aqueous ink set for inkjet recording and inkjet recording method | |
| JP4522062B2 (en) | Inkjet ink set and inkjet recording method | |
| JP2007091911A (en) | Ink for inkjet | |
| JP2007153975A (en) | Inkjet image formation method | |
| JP3060320B2 (en) | Ink, inkjet recording method and apparatus using the same | |
| JPH04214781A (en) | Recording liquid | |
| JP2006348272A (en) | Ink-jet ink |