【発明の詳細な説明】 〔産業上の利用分野〕 この出願の発明は、油絵や日本画等を描くときに使用
する銅箔を基底材とした絵画用支持体に関する。DETAILED DESCRIPTION OF THE INVENTION [Industrial Application Field] The invention of this application relates to a painting support using copper foil as a base material to be used when drawing oil paintings, Japanese paintings, and the like.
通常油絵を描く場合、木枠に張った麻製のキャンバス
（画布）が使用されている。このキャンバスの材料は木
綿製のものもあるし、また板や石などにも描いてはいけ
ないという制約があるわけでもないので、ベニヤ板に描
き上げて展覧会等に出品する例も多く見かけられる。Usually, when painting oil paintings, hemp canvas (painting cloth) stretched over a wooden frame is used. The canvas material is made of cotton, and there is no restriction that it must not be drawn on boards or stones, so there are many examples of painting on plywood and exhibiting at exhibitions.
しかしながら、多くは布製のキャンバスが用いられて
いる。それは布には生地目があり、絵具ののりが良く、
比較的書いた時の絵具の置き具合が良いという長所があ
るためと考えられる。However, fabric canvases are often used. It has a texture on the cloth, good paint paste,
This is probably due to the fact that the paint is relatively well placed when written.
油絵は明治時代に西洋から導入されたものであるが、
簡単に言えばヤニ分で絵具を固めたものと言える。Oil paintings were introduced from the West in the Meiji era,
In a nutshell, it can be said that the paint is hardened with a tar.
画用液として、水彩画は水で日本画はニカワで溶くよ
うに、油絵（油彩画）は油が非常に大切な役割をもって
いる。Oil is very important in oil painting (oil painting), just as water is used for water and water is used for Japanese painting.
この油は大きく分けると油絵具をそれぞれの技法に合
わせて溶く役目の溶き油と、絵そのものに油絵本来のつ
やを与える役目の油と、また絵を大切に保存するための
油とがある。This oil can be broadly classified into two types: a melting oil that melts oil paints in accordance with each technique, an oil that gives the original luster to the painting itself, and an oil that preserves the painting carefully.
通常、市販されている油絵具自体はすでに使いやすい
ように練り上げられてる。Normally, commercially available oil paints are already kneaded to make them easy to use.
油絵を簡単に紹介すると上記のようなことであるが、
他方日本画の方は従来、麻紙に顔料をしみ込ませ、多く
は巻き物として保存しておくことが多かった。このため
巻回することのできないほど絵具を厚くぬることはでき
なかった。The above is a brief introduction to oil painting.
Japanese paintings, on the other hand, have traditionally been impregnated with hemp paper with pigments and are often stored as scrolls. For this reason, the paint could not be so thick that it could not be wound.
しかしながら、上記の油絵が普及するに従い、日本画
も額に入れるようになり、絵具を厚くする傾向に変って
きている。すなわち、麻紙の上に「どうさ」（ニカワ）
を塗って絵具がしみ込まないようにし、その上に絵具を
厚く盛り上げるように変ってきたのでる。このため日本
画独自の画法と並行して油絵的な日本画も発生した。However, as the above-mentioned oil painting spreads, Japanese paintings are also included in the forehead, and the tendency to thicken the paint is changing. In other words, "how" on linen paper (Nika)
It has been changed to paint so that the paint does not seep into it, and to thicken the paint on it. This led to the development of oil painting-like Japanese paintings in parallel with Japanese paintings.
このように油絵や日本画から出発した種々の技法を発
達せしめ、すぐれた絵画が数多く生れることとなった
が、作成された絵画に非常に大きな問題を有している。As described above, various techniques starting from oil paintings and Japanese paintings have been developed, and many excellent paintings have been produced. However, the created paintings have a very serious problem.
それは、絵画のひび割れ（クラック）であり、場合に
よっては剥落の危険すらある。特に乾湿のはげしい日本
では気候の変動でよりもろくなり、破損し易すい状況に
あると言える。It is a crack in the painting, and in some cases even the risk of spalling. It can be said that especially in Japan where the wet and dry conditions are severe, it becomes brittle due to climate change and is easily damaged.
乾燥し安定した気候である西欧においてすらも過去の
有名絵画に、近づいて観察すると無数のひび割れが見ら
れる。ひび割れにごみがたまって製作時における鮮烈な
絵画が維持できず長年のうちに絵画が変質してくるのみ
ならず、剥落による絵画の消失になるおそれもあり、無
念の情を禁じ得ない人も多いと思われる。Even in western Europe, where the climate is dry and stable, countless cracks can be seen when approaching famous past paintings. There are many people who can not forgive the relentless feeling that there is a possibility that the painting will be deteriorated over the years and the painting will be lost due to peeling off, and the painting will not be able to be maintained during the production due to the accumulation of garbage due to cracks I think that the.
このような絵画ひび割れは絵具や地塗りにも原因する
ところもあるが、キャンバスなどの基底材の乾湿の変化
や温度変化による伸縮が原因となるところが大きい。Such cracks in painting may be caused by paints and ground paint, but they are largely caused by changes in dryness and moisture of base materials such as canvas and expansion and contraction due to temperature changes.
上記のような絵画におけるひび割れは、厚塗りをする
絵画のみならず、油絵的傾向をもつ日本画などにもみら
れている。The cracks in the above-mentioned paintings have been observed not only in thickly painted paintings but also in Japanese paintings that tend to be oil paintings.
このような問題をかかえながら、高級絵画においては
それを保有するために、修復のための研究すら行われて
いるのが実情である。また、古い絵画においては金属
板、特に腐食に強い銅板が基底材として用いられたこと
がある。Despite these problems, high-quality paintings are even being studied for restoration in order to retain them. In old paintings, a metal plate, particularly a copper plate resistant to corrosion, has been used as a base material.
これは主として宗教改革後、カトリック側が新世界へ
の布教の地を求めて宣教師たちを送り出すと同時に、聖
像を銅板に描いた油彩画を携帯させたものである。This was mainly due to the Catholics sending out missionaries after the Reformation in search of a missionary land for the New World, and carrying oil paintings depicting copper statues on copper plates.
これは板より軽く、かさがなく、布よりもはるかに剥
落やひび割れの心配がなく、また多少の雨や、熱にも強
いという特徴があったためと考えられる。This is probably due to the fact that it is lighter than a board, has no bulk, is much less likely to peel or crack than a cloth, and is resistant to some rain and heat.
しかしながら、銅そのものが高価であり、平面さを得
ることができず、また絵具ののりが悪く、非常に特殊な
技法でのみ製作が可能であったために、18世紀以降殆ど
姿をみせなくなり現在に至っている。However, copper itself was expensive, could not obtain a flat surface, had poor paint adhesion, and could be manufactured only by a very special technique. Has reached.
以上のような絵画用支持体の問題を解決するために開
発された本発明は、電解用陰極ドラムに接する側の平滑
なシャイニング面を非描画面とし、めっき液中に露出す
る該陰極ドラム非接触側の微細凹凸を有するマット面を
描画面として構成された、10μｍ〜0.5mm厚の銅・銅合
金箔を基底材とし、 この基底材のマット面には、銅もしくは銅合金、イン
ジウムもしくはインジウム合金、亜鉛もしくは亜鉛合
金、クロムもしくはクロム合金、ニッケルもしくはニッ
ケル合金、鉄もしくは鉄合金、コバルトもしくはコバル
ト合金、及び上記各金属の酸化物又は上記各金属と前記
酸化物との複合物のうちから選ばれる少なくとも一種以
上のものからなる表面被覆層を有し、 かつ、かかる基底材のシャイニング面には、ポリプロ
ピレン不織布または樹脂の裏材を有することを特徴とす
る絵画用支持体である。The present invention, which has been developed to solve the above-described problem of the support for painting, has a smooth shining surface on the side in contact with the cathode drum for electrolysis as a non-drawing surface, and the cathode drum exposed to the plating solution. The base material is a copper / copper alloy foil of 10 μm to 0.5 mm thick, composed of a mat surface having fine irregularities on the contact side as a drawing surface, and the mat surface of the base material includes copper or a copper alloy, indium or indium. Selected from alloys, zinc or zinc alloys, chromium or chromium alloys, nickel or nickel alloys, iron or iron alloys, cobalt or cobalt alloys, and oxides of the above metals or composites of the above metals and the oxides Having a surface coating layer made of at least one or more materials, and the shining surface of the base material is made of polypropylene non-woven fabric or resin. Is a pictorial for support characterized by having a wood.
上記の絵画用支持体は、それが油彩画用支持体である
こと、日本画用支持体であること、キャンバスであるこ
と、そして壁面用支持体であることを特徴とし、 また、この絵画用支持体は、上記基底材の表面被覆層
がさらに防錆処理をされている他、最外表面には使用の
ときに引剥しが可能な保護樹脂シートを備えていること
を特徴とし、そして該基底材はエンボス加工を施した銅
・銅合金箔であることを特徴とするものである。The above-described painting support is characterized in that it is an oil painting support, a Japanese painting support, a canvas, and a wall support. The support is characterized in that the surface coating layer of the base material is further subjected to a rust-preventive treatment, and the outermost surface is provided with a protective resin sheet that can be peeled off when used, and The base material is an embossed copper / copper alloy foil.
これによって絵画がひび割れや剥離することも抑制
し、絵画製作当時に鮮烈さを維持するとともに、絵具の
のりを良好にし、密着性を高め安定した品質の保持可能
とするものである。This suppresses the cracking and peeling of the painting, maintains the sharpness at the time of painting production, improves the paste of the paint, improves the adhesion, and can maintain stable quality.
銅箔を使用することは、乾湿や温度変化によるひび割
れや剥落を防止する大きな役割をになうのであるが、金
属製の基底材をしようしようとする場合の大きな欠点で
ある絵具の密着性、のりの良さを改善することは極めて
重要なことであり、このような改善は、本発明において
電解銅・銅合金箔のマット面を描画面とすることによっ
て初めて達成されるものである。The use of copper foil plays a major role in preventing cracks and peeling due to dry and wet and temperature changes, but the major drawback when trying to use a metal base material is the adhesion of paint, It is extremely important to improve the quality of the paste, and such an improvement can be achieved only by using the matte surface of the electrolytic copper / copper alloy foil as the drawing surface in the present invention.
なお、この銅箔・銅合金箔の厚さは、10μｍ〜0.5mm
電解銅・銅合金箔を使用する。The thickness of the copper foil / copper alloy foil is 10 μm to 0.5 mm.
Use electrolytic copper / copper alloy foil.
電解銅箔は第１図ａの銅箔製造工程概念図に示すよう
に一般に銅原料１を電解液（硫酸銅水溶液）２とし、回
転する陰極ドラムに銅を析出させ、さらにこれを引剥し
て連続的に銅箔を製造する。このようにして得られた銅
箔は一般に生箔３と称されているが、ドラムに接した面
は平滑でこれをＳ面（シャイニング面）と称し、反対側
の面は第２図に示すように電気的に析出した多数の凹凸
を有する目これをＭ面（マット面）と称している。As shown in the conceptual diagram of the copper foil manufacturing process in FIG. 1a, the copper raw material 1 is generally used as an electrolytic solution (copper sulfate aqueous solution) 2, copper is deposited on a rotating cathode drum, and the electrolytic copper foil is further peeled off. Produce copper foil continuously. The copper foil thus obtained is generally called raw foil 3, but the surface in contact with the drum is smooth and is called the S surface (shining surface), and the opposite surface is shown in FIG. The surface having a large number of irregularities electrically deposited as described above is referred to as an M surface (mat surface).
次にこの銅箔（生箔）は第１図ｂに示すように１段階
又は多段階（図では３段階）で各種の１層又は多層の表
面被覆層を形成する。一例を示すと第１段階４では銅箔
と絵具及び又は裏材との接着強度を増加させるために銅
又は酸化銅の微細粒子を銅箔に付与する。第２段階５で
は長期内の耐食性をもたせるために黄銅又は亜鉛の被覆
層を形成する。第３段階６でさらに銅箔の酸化若しくは
切断時の緑部酸化を防止するための防錆処理を施すこと
ができる。第２図ａは電解銅箔（生箔）マット面の顕微
鏡写真であり、第２図ｂは前記生箔に銅及び又は酸化銅
の微細粒子を電気的に付着（電気めっき）させた後、黄
銅の被覆層（電気めっきにより）を形成した銅箔であ
る。写真に見られるこのような、多数の凹凸により絵具
の密着性は著しく向上している。もちろん電解銅箔のマ
ット面にも同様の被覆層を形成することができる。Next, as shown in FIG. 1b, the copper foil (raw foil) forms various single-layer or multi-layer surface coating layers in one step or in multiple steps (three steps in the figure). For example, in the first step 4, fine particles of copper or copper oxide are applied to the copper foil in order to increase the adhesive strength between the copper foil and the paint and / or the backing. In the second step 5, a coating layer of brass or zinc is formed in order to provide long-term corrosion resistance. In the third step 6, a rust preventive treatment for preventing oxidation of the copper foil or oxidation of the green portion at the time of cutting can be further performed. FIG. 2a is a micrograph of an electrolytic copper foil (raw foil) mat surface, and FIG. 2b is a sheet after fine particles of copper and / or copper oxide are electrically attached (electroplated) to the raw foil. It is a copper foil on which a brass coating layer (by electroplating) is formed. The adhesion of the paint is remarkably improved by such a large number of irregularities seen in the photograph. Of course, a similar coating layer can be formed on the matte surface of the electrolytic copper foil.
さらにこれらの工程の後、キャンバス等の絵画用支持
体の使用時に、手で引剥しできる保護シートを被覆する
ことができる。この保護シートは手の脂等が銅箔につか
ないように汚染防止の役目をもっている。Further, after these steps, a protective sheet that can be peeled off by hand can be coated when using a painting support such as a canvas. This protective sheet has a role of preventing contamination so that grease and the like of hands do not adhere to the copper foil.
以上の表面被覆層を形成することにより絵具の密着性
を著しく高め、かつ耐食性に優れた絵画用基底材とする
ことができる。By forming the above surface coating layer, it is possible to remarkably increase the adhesion of the paint and to obtain a base material for painting excellent in corrosion resistance.
このようにして得られた銅箔基底材は在来の木や布と
比較するとさらにいくつかの長所をもっている。それ
は、絵具の密着性を保有していると同時に平坦性に優
れ、なめらかであり、気孔や表面の起伏を地塗りで充填
する必要もないことである（もちろん地塗りをすること
はさしつかえなく、本願発明はこれを包含してい
る。）。そして主として銅の色調は同時に下塗りとして
使用することもできるからである。赤色など銅色を強く
出そうと思えば銅被覆層（めっき層）を施すことで達成
でき、赤、白、シルバー色、さらに黄銅色から黄金色ま
でも色調をそろえることができる。また、銅−ニッケル
合金層は黒色から茶褐色まで、多種多様に変えることが
できる。The copper foil base material obtained in this way has some further advantages when compared to conventional wood and cloth. It has excellent adhesion and flatness at the same time, it is smooth, and it is not necessary to fill pores and undulations with a ground coat (of course, it is impossible to do a ground coat, The present invention includes this.) And, mainly because the color tone of copper can be used as an undercoat at the same time. If a copper color such as red is strongly desired, it can be achieved by applying a copper coating layer (plating layer), and the color tone can be uniformed from red, white, silver, and even brass to golden. Further, the copper-nickel alloy layer can be varied in various ways from black to brown.
さらにクロム若しくはクロム合金（クロメート、ジン
ククロメート処理を含む）、ニッケル若しくはニッケル
合金、鉄若しくは鉄合金、コバルト若しくはゴバルト合
金、インジウム若しくはインジウム合金、亜鉛若しくは
亜鉛合金又はこれらの酸化物の被覆層を形成することに
より耐食性を高めたり、それぞれの特有の色調をそろえ
ることができる。さらにまた、これらの金属、合金、又
はこれらの酸化物上にさらに貴金属等の他の金属メッキ
を施すことも可能である。Further, a coating layer of chromium or chromium alloy (including chromate or zinc chromate treatment), nickel or nickel alloy, iron or iron alloy, cobalt or gobalt alloy, indium or indium alloy, zinc or zinc alloy, or an oxide thereof is formed. By doing so, it is possible to increase the corrosion resistance and to make the specific color tone uniform. Furthermore, it is also possible to apply another metal plating such as a noble metal on these metals, alloys or oxides thereof.
本願発明はこれらを包含している。 The present invention includes these.
上記の銅箔基底材は機械的な接着強度を高めるために
エンボス加工を施すこともできる。The above-mentioned copper foil base material may be embossed in order to increase mechanical adhesive strength.
上記の銅箔表面被覆層は、絵具が施されるマット面に
施す。The above-mentioned copper foil surface coating layer is applied to a mat surface on which paint is applied.
このようにして形成された銅箔基底材は切断され所定
の寸法とされる。The copper foil base material thus formed is cut to a predetermined size.
裏材としては、ポリプロピレン不織布または樹脂を使用
する。これらは折り曲げて木枠に固定することでキャン
バスに仕上げるときなどに有利に作用する。As a backing material, a polypropylene nonwoven fabric or a resin is used. These work advantageously when folded and fixed to a wooden frame to finish the canvas.
これは絵画人の好みによって選択できるが、銅箔を用
いた特徴は失われることがない。This can be selected according to the painter's preference, but the features using copper foil are not lost.
また、銅箔基底材はカッター等で簡単に切断できるの
で、キャンバス・ボード、ピンナップ、さらには壁画用
支持体とすることができる。またこれらは、一般建造物
への接着が可能であるから内装、外装品、ドア、棚など
のインテリア品として使用できるとともに、交換や保管
も容易にできるという特徴を有している。In addition, since the copper foil base material can be easily cut with a cutter or the like, it can be used as a canvas board, a pinup, or a mural support. In addition, since they can be bonded to general buildings, they can be used as interior products such as interiors, exterior products, doors, shelves, etc., and can be easily replaced and stored.
キャンバスとする場合には、適度な強度と弾力性を保
有しているので、布などの裏材を張り合わせて木枠に緊
張させ、絵筆をキャンバス地にあてたときに感じられる
心地より弾力を感じとることができる。When used as a canvas, it has moderate strength and elasticity, so you can attach cloth or other backing material and tension it with a wooden frame, and feel elasticity more than you can feel when you put a paintbrush on a canvas. be able to.
また、本願発明の銅箔は純銅のみならずAg,Sn、In、F
e、Ni、Cr、Ｐ、Zn、などの元素を添加して強度、耐食
性等を向上せしめた銅合金箔を対象とするもので、これ
らを全て包含するものである。The copper foil of the present invention is not only pure copper but also Ag, Sn, In, F
It is intended for a copper alloy foil having improved strength, corrosion resistance, etc. by adding elements such as e, Ni, Cr, P, Zn, etc., and includes all of them.
絵としての手法は油彩画（油絵）、アクリルペイント
画、日本画、パステル画、水墨画などに適しているが、
他の画法に適用することはなんらさしつかえない。The method of painting is suitable for oil painting (oil painting), acrylic paint painting, Japanese painting, pastel painting, ink painting, etc.
It can be applied to other styles.
いずれも絵具との密着性に優れており、また、ひび割
れの発生、剥離は大きく改善され、絵画の鮮烈さの維持
と保存性に優れており、さらに絵筆のタッチに快感を強
く与えるものである。All of them have excellent adhesion to paint, and cracking and peeling have been greatly improved, maintaining the sharpness of the painting and preserving it. .
以上で述べたように、本願発明の表面被覆層を形成し
た銅箔を基底材とすることにより、銅箔特有の色感を
得、平坦性に優れ、軽便でしかも得筆のタッチに優れた
快感を得ることができ、さらに銅のもつ大きな欠点であ
った絵具との密着性を著しく改善したものであり、従来
の絵画用支持体として極めて優れたものである。As described above, by using the copper foil on which the surface coating layer of the present invention is formed as the base material, a color feeling unique to the copper foil is obtained, the flatness is excellent, the lightness is excellent, and the touch of the brush is excellent. Pleasant feeling can be obtained, and adhesion to paint, which is a major drawback of copper, has been remarkably improved, and it is extremely excellent as a conventional painting support.
しかも従来の絵画特にキャンバス使用において著しか
ったひび割れの発生を防ぐことができる著しい特性を有
するものである。In addition, it has remarkable characteristics that can prevent the occurrence of cracks, which is remarkable when using a conventional painting, particularly using a canvas.
第１図は、銅箔製造工程を示す概念図であり、第２図
は、電解銅箔とその上に本願発明の被覆層を形成し、密
着性を高めた銅箔表面の粒子構造（表面状態）を示す顕
微鏡写真である。 （a:生箔Ｍ面（×3000）SEM写真 b:被覆箔Ｍ面（×3000）SEM写真）である。 1:銅原料、2:電解液（硫酸銅水溶液） 3:生箔、4:第１段階 5:第２段階、6:第３段階 7:表面被覆層を形成した箔FIG. 1 is a conceptual diagram showing a copper foil manufacturing process, and FIG. 2 is a diagram showing a particle structure (surface) of an electrolytic copper foil and a coating layer of the present invention formed thereon to improve adhesion. 2 is a photomicrograph showing (state). (A: Raw foil M surface (× 3000) SEM photograph b: Covered foil M surface (× 3000) SEM photograph). 1: Copper raw material, 2: Electrolyte solution (copper sulfate aqueous solution) 3: Raw foil, 4: First stage 5: Second stage, 6: Third stage 7: Foil with surface coating layer formed
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| JP63324811AJP2604025B2 (en) | 1988-12-24 | 1988-12-24 | Painting support |
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| JP63324811AJP2604025B2 (en) | 1988-12-24 | 1988-12-24 | Painting support |
| Publication Number | Publication Date |
|---|---|
| JPH02171235A JPH02171235A (en) | 1990-07-02 |
| JP2604025B2true JP2604025B2 (en) | 1997-04-23 |
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| JP63324811AExpired - Fee RelatedJP2604025B2 (en) | 1988-12-24 | 1988-12-24 | Painting support |
| Country | Link |
|---|---|
| JP (1) | JP2604025B2 (en) |
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US8177797B2 (en) | 2003-07-17 | 2012-05-15 | Gunze Limited | Suture reinforement material for automatic suturing device |
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| CN113628982B (en)* | 2021-08-06 | 2024-11-15 | 纳狮新材料有限公司 | Packaging mold and preparation method thereof |
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| JPS63128100U (en)* | 1987-02-16 | 1988-08-22 |
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US8177797B2 (en) | 2003-07-17 | 2012-05-15 | Gunze Limited | Suture reinforement material for automatic suturing device |
| Publication number | Publication date |
|---|---|
| JPH02171235A (en) | 1990-07-02 |
| Publication | Publication Date | Title |
|---|---|---|
| CN101670742B (en) | Sheet material, method for manufacturing same and product shell | |
| JPH0154436B2 (en) | ||
| JP2604025B2 (en) | Painting support | |
| EP0128358B1 (en) | Specular product of bronze-like tone | |
| JP2607286B2 (en) | Painting support | |
| JP2706295B2 (en) | Painting support | |
| JP2706296B2 (en) | Painting support | |
| JPH02185993A (en) | Covering of finishing metal layer on surface of anode-treating metal base | |
| JP2706291B2 (en) | Painting support | |
| JPS6318677B2 (en) | ||
| KR100229208B1 (en) | The print sheet and the same method | |
| JPH02185500A (en) | painting support | |
| JPS602194B2 (en) | decorative board | |
| JPH055005Y2 (en) | ||
| JPWO2009060954A1 (en) | Metal thermoformed body, method for producing the same, and method for producing patterned metal sheet | |
| CN222645528U (en) | Imitation stainless steel composite board | |
| WO2002057515A3 (en) | A continuous electroforming process to form a strip for battery electrodes and a mandrel to be used in said electroforming process | |
| KR100489232B1 (en) | Method for Manufacturing Embossed Steel Sheet | |
| JPS6157073B2 (en) | ||
| JP3057177U (en) | Hinge with fine engraved pattern | |
| JP3602781B2 (en) | Gutter support | |
| JPH04333576A (en) | Production of surface-treated steel sheet having excellent adhesive property | |
| JPH0437900B2 (en) | ||
| JP3540655B2 (en) | Titanium zinc alloy plate | |
| JPH0446918Y2 (en) |
| Date | Code | Title | Description |
|---|---|---|---|
| LAPS | Cancellation because of no payment of annual fees |