JP2004360087A - Transparent note paper - Google Patents

Abstract

Translated fromJapanese

【課題】タック加工する工程で、断裁カールの発生、糊の付着が少なく接着強度が弱くなるという問題もなく、筆記性、オフセット印刷適性、メモを貼付してコピーしても、メモが透けて下の文字もコピーできる透明性のある透明メモ用紙の提供。
【解決手段】この課題は、木材パルプとしてＮ−ＢＫＰを主体とした坪量８０ｇ／ｍ^２以下の多層抄き原紙に透明化剤、表面サイズ剤が含浸塗布されてあり、その原紙に水４．０μＬを滴下した時の１秒後の接触角を剥離剤加工面は８０度以上、粘着剤加工面は９０度以下とし、ＪＩＳ Ｐ ８１３８による不透明度を６０％以下とすることによって解決される。[PROBLEMS] In a tacking process, there is no problem that cut curl is generated, adhesion of glue is small, and adhesive strength is weakened. Writability, offset printing suitability, memo is transparent even when pasted and copied. Providing transparent memo paper that can copy the characters below.
The object of the present invention is to provide a multi-layered base paper having a basis weight of 80 g / m² or less mainly composed of N-BKP as wood pulp, which is impregnated with a clarifying agent and a surface sizing agent, and the base paper is coated with water. The solution can be solved by setting the contact angle 1 second after dropping 0.0 μL to 80 ° or more for the release agent-processed surface and 90 ° or less for the pressure-sensitive adhesive-processed surface, and setting the opacity according to JIS P 8138 to 60% or less. .

Description

Translated fromJapanese

【０００１】
【発明の属する技術分野】
本発明は、メモ用紙を貼付してコピーしても、メモ用紙が透けて下の文字もコピーできる透明性のある透明メモ用紙に関する。
【０００２】
【従来の技術】
従来、メモ用紙は卓上の片隅や携帯に便利なＢ７、Ａ６が中心サイズで、形態は、はぎとり式・枚葉・ラセンとじなどがあるが、最も一般的なものは、はぎとり式である。また用紙も、融通のきく無地の上質紙が多いが、罫入りや、目的に応じた印刷を施したものがある。最近、粘着・剥離加工を施し、貼着などに便利なタックメモ用紙などがある。タックメモ用紙に求められる品質としては、以下のような特性があげられる。
【０００３】
１．筆記性がある。
２．離型剤及び糊付け加工適性がある。
３．オフセット印刷適性がある。
４．紙グセ、カールがないこと。
５．接着強度が強いこと。
【０００４】
一般にタックメモ用紙の製造過程は、原反の片面に４色のオフセット印刷を行い巻き取られる。その後グラビアコーターなどで片面に離型剤塗布、その反対面に糊塗布を行い、ドライヤーで乾燥後巻き取られる。最後にカッターにて断裁加工が行われて平判化される。
【０００５】
またかゝるタックメモ用紙を透明化剤にて含浸処理して得られる透明紙で造ろうとすると粘着・剥離加工を施しタックメモ用紙として製品化する工程で、断裁カールの発生、糊の付着が少なく接着強度が弱くなるという問題が発生し、商品化が難しかった。
【０００６】
従来、透明紙の製法は種々知られており、代表的な方法として、紙を濃硫酸で処理し透明化する方法、化学パルプを高度に叩解し抄紙する方法、原紙にワックスや合成樹脂等の透明化剤を含浸する方法、合成繊維や合成パルプ混抄紙を加熱加圧処理して透明化する方法等がある。
【０００７】
また透明紙を使用した用途例については下記の特許文献にいろいろと取り上げられている。
【０００８】
特許文献１にはインクジェット記録が可能な透明化剤組成物及び透明紙に関する技術が記載されている。
【０００９】
特許文献２には筆記性、湿度に影響されない寸法安定性、透明性を有し、カール性が良好で、電子写真式複写機にてコピーを行う際のブリスターを防止し、トナー修正性が良好で、細線まで鮮明な高速の青焼き可能な貼り合わせ透明紙に関する技術が記載されている。
【００１０】
特許文献３には透明で筆記性、および繰り返しの筆記／消去性に優れた消去性筆記シートに関する技術が記載されている。
【００１１】
特許文献４には表面の凹凸を感じさせることのないフラットで均質な透明感を持っているにもかかわらず、印刷時のインキの裏移りを防止する効果に優れ、インキのセットや乾燥が早く、また上質紙のような多種類の印刷方式に対応可能な透明紙に関する技術が記載されている。
【００１２】
特許文献５には紙の持つ印刷適性とフィルムの湿度に影響されない寸法安定性により多色印刷時の見当ズレが少なく、装飾的な包装紙、折り加工された封筒やエンボス加工製品に供しても破れることのない強度を有するカラー透明紙に関する技術が記載されている。
【００１３】
特許文献６には紙の持つ筆記性、フィルムの湿度に影響されない寸法安定性と透明性を兼ね備え、電子写真式複写機にてコピーを行う際のトナーの熱定着時にフィルムとペーパーの間で起るブリスターを防止し、コピー後のトナー修正性が良好で、また細線まで鮮明な高速の青焼き可能な貼り合わせ透明紙に関する技術が記載されている。
【００１４】
特許文献７には透明性、寸法安定性、機械的強度および鉛筆筆記性等の第２原図用紙適性を有し、さらにインクにじみが無く、インク乾燥性の速いインクジェット記録用透明紙に関する技術が記載されている。
【００１５】
また透明メモ用紙については下記の特許文献にフィルムタイプのものが取り上げられている。
【００１６】
特許文献８には複写機でコピーする際、複写元を汚さずホワイトボード用マーカーで自由にメモが書き消しできるフィルムタイプのコピー用メモシートに関する技術が記載されている。
【００１７】
特許文献９には薄くて軽い、引張り強度の優れたフィルムタイプの透明メモ用紙に関する技術が記載されている。
【００１８】
しかしながらこれらの特許文献には、タック加工する工程で、断裁カールの発生、糊の付着が少なく接着強度が弱くなるという問題を解決した透明メモ用紙は開示されていない。
【００１９】
特許文献１： 特開２００２−３０９４９８号公報
特許文献２： 特開平８−１９２４９９号公報
特許文献３： 特開平８−１６４７００号公報
特許文献４： 特開平７−３０５２９９号公報
特許文献５： 特開平７−２６６５１０号公報
特許文献６： 特開平７−１６７１号公報
特許文献７： 特開平５−２４６１３０号公報
特許文献８： 特開平７−２４８５４７号公報
特許文献９： 特開２０００−３３５１４０号公報
【００２０】
【発明が解決しようとする課題】
本発明の課題は、タック加工する工程で、断裁カールの発生、糊の付着が少なく接着強度が弱くなるという問題もなく、筆記性、オフセット印刷適性、メモを貼付してコピーしても、メモが透けて下の文字もコピーできる透明性のある透明メモ用紙を提供することにある。
【００２１】
【課題を解決するための手段】
上記の課題は、木材パルプとしてＮ−ＢＫＰ（針葉樹晒クラフトパルプ）を主体とした坪量８０ｇ／ｍ^２以下の多層抄き原紙に透明化剤、表面サイズ剤が含浸塗布されてあり、その原紙に水４．０μＬを滴下した時の１秒後の接触角を剥離剤加工面では８０度以上、粘着剤加工面では９０度以下とし、ＪＩＳ Ｐ ８１３８による不透明度を６０％以下としたことを特徴とする、透明メモ用紙によって解決される。
【００２２】
本発明の透明メモ用紙は、上記の課題を解決した他に、従来技術の上記フィルムタイプと異なり、以下のような長所も有している：
１．離解して再生原料として使用でき省資源の点からも好ましい。
２．水系の接着剤に対する接着性が良く、乾きが速い。
３．ヒートシール適性を有しており、熱接着が可能である。
４．鉛筆に対する筆記性が良い。
【００２３】
【発明の実施の形態】
本発明の有利な一つの実施の態様は、透明化剤としての両性スチレン、ブタジエン、アクリル混合エマルジョンと表面サイズ剤としてのアルキルケテンダイマーを１００：０．１〜１００：１．５の固形分重量比で使用した本発明の透明メモ用紙である。ここで両性スチレンとはアニオン性とカチオン性を同時に付与したスチレンを意味する。
【００２４】
本発明の別の有利な一つの実施の態様は、透明化剤、表面サイズ剤の含浸塗布量の合計が固形分換算で５〜３０ｇ／ｍ^２の範囲で塗布した本発明の透明メモ用紙である。
【００２５】
更に別の本発明の有利な一つの実施態様は、オンマシンサイズプレスにて透明化剤、表面サイズ剤を含浸塗布した本発明の透明メモ用紙である。
【００２６】
また、他の本発明の有利な一つの実施態様は、原紙の片面に剥離剤塗布が、その反対面に粘着剤が塗布された本発明の透明メモ用紙である。
【００２７】
本発明の透明メモ用紙を製造するための使用材料及び製造条件について説明する。本発明に用いられるパルプとしては、通常用いられるパルプが各層に使用されるが、透明紙の片面に４色オフセット印刷するため、原紙強度が必要であることからＢＫＰ（晒クラフトパルプ）を使用する。特に紙の剛度とのバランスを考慮するとＮ−ＢＫＰ（針葉樹晒クラフトパルプ）とＬ−ＢＫＰ（広葉樹晒クラフトパルプ）の使用割合を１０：０〜５：５の重量割合で配合することが好ましい。パルプの叩解度はカナダ標準濾水度（ＣＳＦ）で５００ｍＬ以上が適している。広葉樹晒クラフトパルプ（Ｌ−ＢＫＰ）および針葉樹晒クラフトパルプ（Ｎ−ＢＫＰ）の他に、二次的成分として漂白あるいは未漂白のＮＫＰ（針葉樹クラフトパルプ）やＬＫＰ（広葉樹クラフトパルプ）、高歩留りパルプ、ＧＰ（砕木パルプ）、ＴＭＰ（サーモメカニカルパルプ）等、古紙パルプまたは化学漂白パルプ、例えばＥＣＦまたはＴＣＦ漂白を行ったものも混入することができる。
【００２８】
原紙層には、ポリアクリルアミド樹脂、ポリアミドエピクロロヒドリン樹脂などの紙力増強剤を内添することが必要である。紙力増強剤の添加率は薬品の種類により異なるがパルプに対して固形分重量で１〜１０％の添加が好ましい。また蛍光染料、硫酸バンドなどの各種助剤が適宜添加して用いられる。
【００２９】
本発明の原紙は、乾燥工程の中間に設置されるサイズプレス装置で透明化剤、表面サイズ剤を主体とする含浸処理を行う。通常の２ロールのサイズプレスの他、ゲートロールサイズプレスやメタリングサイズプレスも使用できる。
【００３０】
本発明では公知のあらゆる透明化剤を使用できるが、両性スチレン、ブタジエン、アクリル混合エマルジョンを使用するのが有利であることがわかっている。その他の例を挙げると、パラフィン、高級脂肪酸、脂肪酸アミド、脂肪酸アルコールエステル等のワックス類、フェノール樹脂、尿素樹脂、エポキシ樹脂、メラミン樹脂、アルキッド樹脂等、あるいはこれらを変性した熱硬化性樹脂、ポリアクリル酸エステル、ポリメタクリル酸エステル、ポリ塩化ビニル、ポリ酢酸ビニル、ポリスチレン、ポリブテン、ポリエステル、ポリウレタン、ポリアミドやニトロセルロース、酢酸セルロース、セルロースアセテートブチレート、ヒドロキシエチルセルロース、シュクロースアセテートイソブチレート等のセルロースまたは多糖類の誘導体、ロジン、ロジンエステル、ダンマル樹脂、セラック等、あるいはこれらを変性した樹脂や、分子中にラジカル重合性の不飽和基を有したプレポリマーとスチレン、メチルメタアクリレートのような液状ビニルモノマーと光増感性物質とから成る紫外線硬化樹脂（ＵＶランプ等で硬化）や、分子中にラジカル重合性の不飽和基を有したプレポリマーとスチレン、メチルメタアクリレートのような液状ビニルモノマーと不飽和ポリエステル、ジアクリルフタレート、変性アクリル、変性エポキシ、変性ウレタン、多官能性モノマー等から成る電子線のような放射線で重合可能な樹脂（電子線発生装置等で硬化）等であるが、特にこれらに限定されるものではない。これらの単独または数種類を混合して使用する。
【００３１】
本発明では公知のあらゆる表面サイズ剤を使用できるが、アルキルケテンダイマー系を使用するのが有利であることがわかっている。その他の例を挙げると、スチレン系、アクリル系、スチレン−アクリル系、スチレン−マレイン酸系、スチレン−アクリル酸エステル共重合体等であるが、特にこれらに限定されるものではない。これらを単独でまたは数種類を混合して使用する。
【００３２】
また本発明では透明化剤、表面サイズ剤の他に硬化剤、着色剤、界面活性剤、可塑剤等を適宜混合して使用できる。
【００３３】
含浸処理用の透明化剤と表面サイズ剤は、サイズプレスでドライ付着量が両面で５〜３０ｇ／ｍ^２、好ましくは８〜１０ｇ／ｍ^２の範囲の量で含浸塗布する。５ｇ／ｍ^２以下では目標とする不透明度が得られず、３０ｇ／ｍ^２以上では生産性、コスト面に問題がある。
【００３４】
なお、表面サイズ剤、例えばアルキルケテンダイマーの使用量は透明化剤、例えば両性スチレン、ブタジエン、アクリル混合エマルジョンに対して固形分換算で０．１〜１．５重量％、好ましくは、０．３〜１．０重量％の範囲である。表面サイズ剤が０．１重量％以下では耐水性がなく印刷時の湿し水の影響で断裁カールが発生し、１．５重量％以上では、耐水性がありすぎて糊の付着が少なくなり、接着強度が弱くなる。
【００３５】
従って本発明の原紙は、水４．０μＬを滴下した時の１秒後の動的接触角を剥離剤加工面では８０度以上、粘着剤加工面では９０度以下とすることが重要である。
【００３６】
“接触角”は自動接触角・吸収特性テスターのＦＩＢＲＯ １１００ ＤＡＴＭＫ ＩＩ（ＦＩＢＲＯ社製）を用いて測定される。この装置は、滴下液と試料表面との間の相互作用を詳細に、かつ自動的に分析することを可能とする。時間に依存して濡れ・吸収特性はコーティングやサイジング、又は印刷性や接着性等に相関している。液滴と試料表面が接触した直後の最初の１秒に臨界的な差が見られることがある。この情報は動的なテストでのみ得ることができる。
【００３７】
接触角の測定原理は、予め設定された量（例えば４μＬ）の液滴（例えば水道水）がマイクロピペットを用いて試料表面（例えば原紙）に自動的に滴下される。試料に接触した液滴の画像が設定時間（例えば１秒後）にビデオカメラにより撮られる。液滴と試料間の接触角は撮られた画像を画像分析することにより求められる。接触角が時間の経過と共にどのように変化していくかが示される。
【００３８】
本発明の原紙を、水４．０μＬを滴下した時の１秒後の動的接触角を剥離剤加工面では８０度以上、粘着剤加工面では９０度以下と規定したのは、剥離剤加工面が８０度未満では原紙の耐水性が弱く印刷時の湿し水が染み込み易く、断裁カールが発生すること並びに粘着剤加工面が９０度より多いと耐水性が有り過ぎて糊が原紙へ付着しずらく、その結果、糊の塗布量が少なくなり接着強度が弱くなるためである。
【００３９】
本発明においては含浸塗工方式並びに乾燥方式については特に限定されるものではない。
【００４０】
本発明の原紙抄造は、円網多筒式抄紙機で１層から４層抄き合わせで行われるが、特にこの方式に限定されるものではない。
【００４１】
このようにして得られた原紙は金属ロールと弾性ロールからなるカレンダー装置にて平滑化処理が行われる。
【００４２】
原紙としては、坪量は６０〜７０ｇ／ｍ^２、厚さ０．０７０〜０．０８０ｍｍ、不透明度は６０％以下が適している。不透明度が６０％以上ではメモを貼付してコピーしても、透明性が足りず下の文字がコピーできない。
【００４３】
以下、本発明の透明メモ用紙の具体的な構成を、実施例に基づいて説明する。本発明はこれら実施例によって制限を受けるものではない。なお特に断らない限り例中の配合％および添加％は固形分換算での重量％に関しそして部は重量部に関する。また全ての例についてＪＩＳ Ｐ ８１１１に準じて前処理を行った後、紙質試験を行った。
【００４４】
【実施例】
実施例１：
原紙抄造
原料配合
表層 Ｎ−ＢＫＰ １００％
裏層 Ｎ−ＢＫＰ １００％
上記原料の表層、裏層の叩解度を６００ｃｃとし、紙力増強剤（日本ＰＭＣ社製：商品名ＷＳ−５５２、２５％濃度品）を対パルプ０．８％添加した。また原料には水中に分散させた適量の蛍光染料（日本曹達社製：商品名ケイコールＢＵＬ、４０％濃度品）を、ミキシングタンクに添加し、紙料と十分に混合し、定着剤としては硫酸アルミニウムを添加した２層原紙を抄紙した。またサイズプレスにおいて両性スチレン、ブタジエン、アクリル混合エマルジョン（日新化学研究所社製：商品名リペレットＡ−３、５０％濃度品）２００Ｌ、水２００Ｌ、アルキルケテンダイマー（日本ＰＭＣ社製：商品名ＳＳ３６２、２０％濃度品）１．５Ｌからなるサイズプレス処方液を消費量２００Ｌ／時になるように塗布した。前記原紙はオンマシンキャレンダー装置にて平滑化処理を行い、紙厚０．０７６ｍｍ、坪量６６．１ｇ／ｍ^２、不透明度５７．４％の透明メモ用紙とした。
【００４５】
実施例２：
サイズプレス処方液を両性スチレン、ブタジエン、アクリル混合エマルジョン（日新化学研究所社製：商品名リペレットＡ−３、５０％濃度品）２００Ｌ、水２００Ｌ、アルキルケテンダイマー（日本ＰＭＣ社製：商品名ＳＳ３６２、２０％濃度品）３．０Ｌとした以外は実施例１と同様に行った。
【００４６】
実施例３：
サイズプレス処方液を両性スチレン、ブタジエン、アクリル混合エマルジョン（日新化学研究所社製：商品名リペレットＡ−３、５０％濃度品）２００Ｌ、水２００Ｌ、アルキルケテンダイマー（日本ＰＭＣ社製：商品名ＳＳ３６２、２０％濃度品）４．５Ｌとした以外は実施例１と同様に行った。
【００４７】
比較例１：
サイズプレス処方液を両性スチレン、ブタジエン、アクリル混合エマルジョン（日新化学研究所社製：商品名リペレットＡ−３、５０％濃度品）４００Ｌとした以外は実施例１と同様に行った。
【００４８】
比較例２：
サイズプレス処方液を水４００Ｌとした以外は実施例１と同様に行った。
【００４９】
比較例３：
サイズプレス処方液を両性スチレン、ブタジエン、アクリル混合エマルジョン（日新化学研究所社製：商品名リペレットＡ−３、５０％濃度品）２００Ｌ、水２００Ｌ、アルキルケテンダイマー（日本ＰＭＣ社製：商品名ＳＳ３６２、２０％濃度品）９．０Ｌとした以外は実施例１と同様に行った。
【００５０】
比較例４：
サイズプレス処方液を両性スチレン、ブタジエン、アクリル混合エマルジョン（日新化学研究所社製：商品名リペレットＡ−３、５０％濃度品）２００Ｌ、水２００Ｌ、アルキルケテンダイマー（日本ＰＭＣ社製：商品名ＳＳ３６２、２０％濃度品）１８．０Ｌとした以外は実施例１と同様に行った。
【００５１】
比較例５：
原紙抄造
原料配合
表層 Ｎ−ＢＫＰ １００％
裏層 Ｎ−ＢＫＰ １００％
上記原料の叩解度を５００ｃｃとし、紙力増強剤（日本ＰＭＣ社製：商品名ＷＳ− ５７０、１２．５％濃度品）を対パルプ０．８％添加した。また原料には水中に分散させた適量の蛍光染料（日本曹達社製：商品名ケイコールＢＵＬ、４０％濃度品）を、ミキシングタンクに添加し、紙料と十分に混合し、定着剤としては硫酸アルミニウムを添加した２層原紙を抄紙した。またサイズプレスにおいてＳＢＲラテックス（日本ゼオン社製：商品名ニポールＬＸ−４２６、５０％濃度品）４００Ｌからなるサイズプレス処方液を消費量２００Ｌ／時になるように塗布した。前記原紙はオンマシンキャレンダー装置にて平滑化処理を行い、紙厚０．０８８ｍｍ、坪量７９．５ｇ／ｍ^２、不透明度６７．０％の透明メモ用紙とした。
【００５２】
比較例６：
サイズプレス処方液をパラフィンワックス（互応化学社製：商品名ダイジッドＥＹ、３２％濃度品）４００Ｌとした以外は比較例５と同様に行った。
【００５３】
このようにして得られた透明紙において、白紙物性、筆記適性、印刷適性、断裁カール、接着力、コピー適性、接触角をそれぞれ下記の方法で評価し、表１に示した。
【００５４】
透明紙の評価：
白紙物性は印刷用塗工紙を２３℃、５０％ＲＨで調湿後、ＪＩＳ規格及び以下の方法に準拠して測定した。
坪量：ＪＩＳ Ｐ ８１２４。
厚さ、密度、比容積：ＪＩＳ Ｐ ８１１８。
サイズ度：ＪＩＳ Ｐ ８１２２。
不透明度：ＪＩＳ Ｐ ８１３８。
接触角：ＦＩＢＲＯ １１００ ＤＡＴ ＭＫＩＩ（ＦＩＢＲＯ社製）にて、水道水４．０μＬを滴下した時の１秒後の動的接触角を測定した。
耐刷力：ＲＩ印刷試験機を用い、特殊インキ（ＳＭＸタックグレード１０；東洋インキ社製）を用い塗工面に印刷し、印刷面のピック状態を目視で評価した。○：ピック無し、ピック極めて少ない、△：ピックが散見、×：ピックが非常に多い。
断裁カール：タック加工（離型剤塗布、糊付け）後の製品巻き取り断裁時の両耳の反り上がり具合を目視で評価した。
◎：良好、〇：可、×：不可。
接着力：タック加工（離型剤塗布、糊付け）後のタックメモ用紙の接着強度を評価した。
〇：可、×：不可。
コピー適性：富士ゼロックス社製フルカラー複写機（品番：ドキュセンターカラー５００）を用いてコピーする際に、書籍本文にメモを貼付してコピーしても、メモが透けて下の文字もコピーできるかどうかを目視で評価した。
〇：可、×：不可。
筆記適性：三菱鉛筆社製のＨＢ鉛筆にて筆記した際の書き具合を目視で評価した。
〇：可、×：不可。
【００５５】
【表１】

【００５６】
【発明の効果】
以上のように本発明によって、タック加工する工程で、断裁カールの発生、糊の付着が少なく接着強度が弱くなるという問題もなく、筆記性、オフセット印刷適性があり、メモ用紙を貼付してコピーしても、メモが透けて下の文字もコピーできる透明性のあるメモ用紙を提供することができる。[0001]
TECHNICAL FIELD OF THE INVENTION
TECHNICAL FIELD The present invention relates to a transparent memo paper with transparency that allows the memo paper to be copied and the characters below to be copied even when the memo paper is pasted and copied.
[0002]
[Prior art]
Conventionally, memo paper has a center size in one corner of a desk or B7 or A6 which is convenient for carrying, and is in a stripping type, a sheet type, a spiral binding type, etc., but the most common type is a stripping type. In addition, there are many flexible and plain high-quality papers, but some papers are lined or printed according to purpose. Recently, there is a tack memo paper which has been subjected to an adhesive / peeling process and is convenient for sticking. The quality required of the tack memo paper includes the following characteristics.
[0003]
1. Writable.
2. Suitable for release agent and gluing.
3. Suitable for offset printing.
4. There must be no paper curls or curls.
5. Strong bonding strength.
[0004]
Generally, in the manufacturing process of tack memo paper, four colors of offset printing are performed on one side of a raw material and the material is wound. Thereafter, a release agent is applied on one side by a gravure coater or the like, and a glue is applied on the other side, dried by a drier and wound up. Finally, the sheet is trimmed by a cutter and flattened.
[0005]
In addition, when trying to make a tack memo paper with transparent paper obtained by impregnating it with a clarifying agent, the process of applying tackiness and peeling and commercializing it as a tack memo paper produces little cut curl and adhesion of glue with little adhesion The problem that the strength became weak occurred, and commercialization was difficult.
[0006]
Conventionally, various methods for producing transparent paper have been known, and typical methods include a method of treating paper with concentrated sulfuric acid to make it transparent, a method of highly beating chemical pulp to make paper, and a method of making base paper such as wax or synthetic resin. There are a method of impregnating a clarifying agent, and a method of heating and pressurizing synthetic fiber or synthetic pulp mixed paper to make it transparent.
[0007]
Various examples of applications using transparent paper are taken up in the following patent documents.
[0008]
Patent Literature 1 describes a technique relating to a clarifying agent composition capable of inkjet recording and a transparent paper.
[0009]
Patent Literature 2 has a writing property, dimensional stability and transparency that are not affected by humidity, good curling properties, prevents blistering when copying with an electrophotographic copying machine, and has good toner correction properties. A technique relating to a laminated transparent paper capable of high-speed blue printing that is clear even to a fine line is described.
[0010]
Patent Literature 3 describes a technique relating to an erasable writing sheet that is transparent and has excellent writing properties and repetitive writing / erasing properties.
[0011]
Patent Literature 4 has an excellent effect of preventing set-off of ink at the time of printing despite having a flat and uniform transparency without causing surface irregularities, and the ink setting and drying is quick. Also, there is described a technique relating to a transparent paper which can correspond to various types of printing methods such as high quality paper.
[0012]
Patent Literature 5 discloses that the registerability during multicolor printing is small due to the printability of paper and the dimensional stability that is not affected by the humidity of the film, and it can be used for decorative packaging paper, folded envelopes and embossed products. A technique relating to a color transparent paper having strength that does not tear is described.
[0013]
Japanese Patent Application Laid-Open No. H11-163873 discloses a paper which has both writing properties of paper, dimensional stability and transparency which are not affected by the humidity of the film, and occurs between the film and the paper at the time of thermal fixing of toner when performing copying with an electrophotographic copying machine. The technology describes a laminated transparent paper that prevents blisters, improves toner correctability after copying, and is capable of high-speed blue printing even with fine lines.
[0014]
Patent Document 7 describes a technique relating to a transparent paper for ink jet recording which has a second original drawing paper suitability such as transparency, dimensional stability, mechanical strength and pencil writing property, has no ink bleeding, and has a fast ink drying property. Have been.
[0015]
Regarding transparent memo paper, a film type is disclosed in the following patent document.
[0016]
Patent Document 8 describes a technology relating to a film-type copy memo sheet in which a memo can be freely written and erased with a whiteboard marker without soiling a copy source when copying with a copying machine.
[0017]
Patent Document 9 describes a technique relating to a thin, light, film-type transparent note paper having excellent tensile strength.
[0018]
However, these patent documents do not disclose a transparent memo paper that solves the problem of the occurrence of cut curl and adhesion of glue being small and the adhesive strength being weak in the tacking process.
[0019]
Patent Document 1: Japanese Patent Application Laid-Open No. 2002-309498 Patent Document 2: Japanese Patent Application Laid-Open No. 8-192499 Patent Document 3: Japanese Patent Application Laid-Open No. 8-164700 Patent Document 4: Japanese Patent Application Laid-Open No. 7-305299 Patent Document 5: Japanese Patent Application Laid-Open Patent Document 6: Japanese Patent Application Laid-Open No. Hei 7-26701 Patent Document 7: Japanese Patent Application Laid-Open No. Hei 5-246130 Patent Document 8: Japanese Patent Application Laid-Open No. 7-24847 Patent Document 9: Japanese Patent Application Laid-Open No. 2000-335140 [ [0020]
[Problems to be solved by the invention]
The problem of the present invention is that in the step of tacking, there is no problem of occurrence of cutting curl, adhesion of glue is small and adhesive strength is reduced, writability, suitability for offset printing, even if a memo is pasted and copied, It is an object of the present invention to provide a transparent memo paper which can copy the characters below through.
[0021]
[Means for Solving the Problems]
The above problem is that a clarifying agent and a surface sizing agent are impregnated and coated on a multi-layer base paper having a basis weight of 80 g / m² or less mainly composed of N-BKP (softwood bleached kraft pulp) as a wood pulp. The contact angle after 1 second when 4.0 μL of water was dropped on the surface was 80 degrees or more on the release agent-treated surface and 90 degrees or less on the pressure-sensitive adhesive-treated surface, and the opacity according to JIS P 8138 was 60% or less. The feature is solved by transparent note paper.
[0022]
In addition to solving the above-mentioned problems, the transparent memo paper of the present invention has the following advantages, unlike the above-mentioned conventional film types:
1. It is disintegrated and can be used as a recycled material, which is preferable from the viewpoint of resource saving.
2. Good adhesion to water-based adhesives and quick drying.
3. It has heat sealing aptitude and can be thermally bonded.
4. Good writing performance on pencil.
[0023]
BEST MODE FOR CARRYING OUT THE INVENTION
One preferred embodiment of the present invention is the use of an amphoteric styrene, butadiene, acrylic mixed emulsion as a clarifying agent and an alkyl ketene dimer as a surface sizing agent in a solids weight of 100: 0.1 to 100: 1.5. It is a transparent note paper of the present invention used in a ratio. Here, amphoteric styrene means styrene to which anionic and cationic properties are simultaneously imparted.
[0024]
Another advantageous embodiment of the present invention is the transparent memo paper of the present invention, wherein the total amount of the clarifying agent and the surface sizing agent impregnated is in the range of 5 to 30 g / m^{2 in} terms of solid content. .
[0025]
Still another advantageous embodiment of the present invention is the transparent memo paper of the present invention which has been applied by impregnation with a clarifying agent and a surface sizing agent by an on-machine size press.
[0026]
Another advantageous embodiment of the present invention is the transparent memo paper of the present invention in which a release agent is applied to one side of a base paper and an adhesive is applied to the opposite side.
[0027]
Materials used for manufacturing the transparent memo paper of the present invention and manufacturing conditions will be described. As the pulp used in the present invention, pulp that is usually used is used for each layer, but BKP (blown kraft pulp) is used because base paper strength is required because four-color offset printing is performed on one side of transparent paper. . In particular, considering the balance with the stiffness of the paper, it is preferable to use N-BKP (softwood bleached kraft pulp) and L-BKP (hardwood bleached kraft pulp) in a weight ratio of 10: 0 to 5: 5. The beating degree of the pulp is suitably at least 500 mL in Canadian Standard Freeness (CSF). In addition to bleached hardwood kraft pulp (L-BKP) and softwood bleached kraft pulp (N-BKP), bleached or unbleached NKP (softwood kraft pulp), LKP (hardwood kraft pulp), and high yield pulp as secondary components , GP (ground wood pulp), TMP (thermomechanical pulp), etc., waste paper pulp or chemically bleached pulp, for example, ECF or TCF bleached can also be mixed.
[0028]
It is necessary to internally add a paper strength enhancer such as a polyacrylamide resin or a polyamide epichlorohydrin resin to the base paper layer. Although the addition ratio of the paper strength enhancer varies depending on the type of chemical, it is preferable to add 1 to 10% by weight of solid content to pulp. Various assistants such as a fluorescent dye and a sulfuric acid band are appropriately added and used.
[0029]
The base paper of the present invention is subjected to an impregnation process mainly using a clarifying agent and a surface sizing agent by a size press device installed in the middle of the drying process. In addition to the usual two-roll size press, a gate roll size press and a metering size press can also be used.
[0030]
Although any known clarifying agent can be used in the present invention, it has been found to be advantageous to use a mixed amphoteric styrene, butadiene, acrylic emulsion. Other examples include waxes such as paraffin, higher fatty acids, fatty acid amides, fatty acid alcohol esters, phenolic resins, urea resins, epoxy resins, melamine resins, alkyd resins, etc. Cellulose such as acrylate, polymethacrylate, polyvinyl chloride, polyvinyl acetate, polystyrene, polybutene, polyester, polyurethane, polyamide, nitrocellulose, cellulose acetate, cellulose acetate butyrate, hydroxyethyl cellulose, sucrose acetate isobutyrate Or polysaccharide derivatives, rosin, rosin ester, dammar resin, shellac, etc., or resins modified from these, or prepolymers having radically polymerizable unsaturated groups in the molecule and polystyrene UV curable resin (cured by a UV lamp or the like) composed of a liquid vinyl monomer such as methyl methacrylate and a photosensitizer, or a prepolymer having a radical polymerizable unsaturated group in the molecule, styrene, methyl methacrylate Radiation-polymerizable resin such as electron beam composed of liquid vinyl monomer such as acrylate and unsaturated polyester, diacryl phthalate, modified acrylic, modified epoxy, modified urethane, polyfunctional monomer, etc. Curing) and the like, but are not particularly limited thereto. These may be used alone or as a mixture of several types.
[0031]
Although any known surface sizing agent can be used in the present invention, it has been found to be advantageous to use an alkyl ketene dimer system. Other examples include styrene, acrylic, styrene-acrylic, styrene-maleic acid, and styrene-acrylate copolymers, but are not particularly limited thereto. These may be used alone or as a mixture of several types.
[0032]
In the present invention, a curing agent, a coloring agent, a surfactant, a plasticizer and the like can be appropriately mixed and used in addition to the clarifying agent and the surface sizing agent.
[0033]
Transparentizing agent and surface sizing agent for impregnation treatment, 5 to 30 g /^{m 2} dry coating weight on both sides in the size press, preferably impregnated applied in an amount ranging from 8~10g /^{m 2.} If it is 5 g / m² or less, the target opacity cannot be obtained, and if it is 30 g / m² or more, there are problems in productivity and cost.
[0034]
The amount of the surface sizing agent, for example, the alkyl ketene dimer used is 0.1 to 1.5% by weight, preferably 0.3 to 0.3% by weight in terms of solid content, based on a transparentizing agent, for example, an amphoteric styrene, butadiene, or acrylic mixed emulsion. １．０1.0% by weight. If the surface sizing agent is less than 0.1% by weight, there is no water resistance and cut curl is generated due to the influence of dampening water during printing. If the surface sizing agent is 1.5% by weight or more, the water resistance is too high and glue adhesion is reduced. And the adhesive strength is weakened.
[0035]
Therefore, in the base paper of the present invention, it is important that the dynamic contact angle after 1 second when 4.0 μL of water is dropped is 80 ° or more on the surface processed with the release agent and 90 ° or less on the surface processed with the adhesive.
[0036]
The "contact angle" is measured using an automatic contact angle / absorption characteristic tester FIBRO 1100 DATMK II (manufactured by FIBRO). This device makes it possible to analyze the interaction between the dripping liquid and the sample surface in detail and automatically. Depending on the time, the wetting / absorbing properties are correlated with coating, sizing, printability, adhesiveness and the like. A critical difference may be seen in the first second immediately after the contact between the droplet and the sample surface. This information can only be obtained by dynamic testing.
[0037]
The principle of measuring the contact angle is that a predetermined amount (for example, 4 μL) of a droplet (for example, tap water) is automatically dropped on a sample surface (for example, base paper) using a micropipette. An image of the droplet in contact with the sample is taken by a video camera at a set time (for example, after one second). The contact angle between the droplet and the sample can be determined by image analysis of the taken image. It shows how the contact angle changes over time.
[0038]
The dynamic contact angle of the base paper of the present invention after 1 second when 4.0 μL of water was dropped was specified to be 80 ° or more on the release agent-processed surface and 90 ° or less on the pressure-sensitive adhesive-processed surface. If the surface is less than 80 degrees, the water resistance of the base paper is weak, so that the dampening solution easily permeates during printing, cutting curls may occur, and if the adhesive processing surface is more than 90 degrees, the water resistance is too high and the glue adheres to the base paper. This is because the amount of glue applied is reduced and the adhesive strength is reduced.
[0039]
In the present invention, the impregnation coating method and the drying method are not particularly limited.
[0040]
The base paper making of the present invention is performed in a single-layer to four-layer forming by a round-mesh multi-cylinder paper machine, but is not particularly limited to this method.
[0041]
The base paper thus obtained is subjected to a smoothing treatment by a calender device comprising a metal roll and an elastic roll.
[0042]
As the base paper, a basis weight of 60 to 70 g / m² , a thickness of 0.070 to 0.080 mm, and an opacity of 60% or less are suitable. If the opacity is 60% or more, even if the memo is pasted and copied, the transparency is not enough and the characters below cannot be copied.
[0043]
Hereinafter, a specific configuration of the transparent memo paper of the present invention will be described based on examples. The present invention is not limited by these examples. Unless otherwise specified, the blending percentages and addition percentages in the examples relate to% by weight in terms of solid content and parts refer to parts by weight. In addition, all the examples were pre-processed according to JIS P 8111, and then subjected to a paper quality test.
[0044]
【Example】
Example 1
Base papermaking raw material composition surface layer N-BKP 100%
Back layer N-BKP 100%
The beating degree of the surface layer and the back layer of the raw material was set to 600 cc, and a paper strength enhancer (trade name: WS-552, manufactured by Nippon PMC Co., Ltd., 25% concentration product) was added at 0.8% with respect to pulp. As a raw material, an appropriate amount of a fluorescent dye dispersed in water (manufactured by Nippon Soda Co., Ltd., product name: Keicoll BUL, 40% concentration product) is added to a mixing tank, mixed well with the stock, and sulfuric acid is used as a fixing agent. A two-layer base paper to which aluminum was added was made. In a size press, 200 L of an amphoteric styrene, butadiene, and acrylic mixed emulsion (trade name: Repellet A-3, manufactured by Nissin Chemical Laboratory, 50% concentration), 200 L of water, alkyl ketene dimer (trade name: SS362, manufactured by PMC Japan) , 20% concentration product) 1.5 L of a size press formulation was applied so that the consumption was 200 L / hour. The base paper was subjected to a smoothing process using an on-machine calender to obtain a transparent memo paper having a paper thickness of 0.076 mm, a basis weight of 66.1 g / m² , and an opacity of 57.4%.
[0045]
Example 2:
The size press formulation solution was mixed with amphoteric styrene, butadiene, and acrylic mixed emulsion (trade name: Repellet A-3, manufactured by Nissin Chemical Laboratories Co., Ltd., 50% concentration) 200 L, water 200 L, alkyl ketene dimer (trade name, manufactured by PMC Japan, Ltd.) SS362, 20% concentration product) was performed in the same manner as in Example 1 except that 3.0 L was used.
[0046]
Example 3
The size press formulation solution was mixed with amphoteric styrene, butadiene, and acrylic mixed emulsion (trade name: Repellet A-3, manufactured by Nissin Chemical Laboratories Co., Ltd., 50% concentration) 200 L, water 200 L, alkyl ketene dimer (trade name, manufactured by PMC Japan, Ltd.) (SS362, 20% concentration product) The same procedure as in Example 1 was carried out except that 4.5 L was used.
[0047]
Comparative Example 1:
The procedure was performed in the same manner as in Example 1 except that the size press formulation liquid was 400 L of an amphoteric styrene, butadiene, acrylic mixed emulsion (trade name: Repellet A-3, manufactured by Nissin Chemical Laboratory Co., Ltd., 50% concentration).
[0048]
Comparative Example 2:
The procedure was performed in the same manner as in Example 1 except that the size press formulation liquid was changed to 400 L of water.
[0049]
Comparative Example 3:
The size press formulation solution was mixed with amphoteric styrene, butadiene, and acrylic mixed emulsion (trade name: Repellet A-3, manufactured by Nissin Chemical Laboratories Co., Ltd., 50% concentration) 200 L, water 200 L, alkyl ketene dimer (trade name, manufactured by PMC Japan, Ltd.) SS362, 20% concentration product) was performed in the same manner as in Example 1 except that 9.0 L was used.
[0050]
Comparative Example 4:
The size press formulation solution was mixed with amphoteric styrene, butadiene, and acrylic mixed emulsion (trade name: Repellet A-3, manufactured by Nissin Chemical Laboratories Co., Ltd., 50% concentration) 200 L, water 200 L, alkyl ketene dimer (trade name, manufactured by PMC Japan, Ltd.) (SS362, 20% concentration product) The same procedure as in Example 1 was performed except that the amount was 18.0 L.
[0051]
Comparative Example 5:
Base papermaking raw material composition surface layer N-BKP 100%
Back layer N-BKP 100%
The beating degree of the raw material was set to 500 cc, and a paper strength enhancer (trade name: WS-570, manufactured by Nippon PMC Co., Ltd., 12.5% concentration product) was added at 0.8% with respect to pulp. As a raw material, an appropriate amount of a fluorescent dye dispersed in water (manufactured by Nippon Soda Co., Ltd., product name: Keicoll BUL, 40% concentration product) is added to a mixing tank, mixed well with the stock, and sulfuric acid is used as a fixing agent. A two-layer base paper to which aluminum was added was made. Further, in a size press, a size press formulation liquid consisting of 400 L of SBR latex (trade name: Nipol LX-426, manufactured by Zeon Corporation, 50% concentration) was applied at a consumption of 200 L / hour. The base paper was subjected to a smoothing treatment using an on-machine calender to obtain a transparent memo paper having a paper thickness of 0.088 mm, a basis weight of 79.5 g / m² , and an opacity of 67.0%.
[0052]
Comparative Example 6:
The procedure was performed in the same manner as in Comparative Example 5 except that the size press formulation liquid was changed to 400 L of paraffin wax (trade name: DIGID EY, product of 32% concentration, manufactured by Yoyo Kagaku Co., Ltd.).
[0053]
The transparent paper thus obtained was evaluated for blank paper properties, writing suitability, printability, cut curl, adhesive strength, copy suitability, and contact angle, respectively, by the following methods.
[0054]
Transparency evaluation:
The physical properties of the blank paper were measured according to JIS standards and the following method after adjusting the humidity of the coated paper for printing at 23 ° C. and 50% RH.
Basis weight: JIS P 8124.
Thickness, density, specific volume: JIS P 8118.
Size degree: JIS P8122.
Opacity: JIS P 8138.
Contact angle: Using FIBRO 1100 DAT MKII (manufactured by FIBRO), the dynamic contact angle one second after dropping 4.0 μL of tap water was measured.
Printing durability: Using a RI printing tester, printing was performed on the coated surface using a special ink (SMX tack grade 10; manufactured by Toyo Ink Co., Ltd.), and the picking state of the printed surface was visually evaluated. ：: no pick, very few picks, △: scattered picks, ×: very many picks.
Cutting curl: The degree of warpage of both ears at the time of winding and cutting the product after tack processing (application of a release agent, gluing) was visually evaluated.
◎: good, △: acceptable, ×: not acceptable.
Adhesive strength: The adhesive strength of tack memo paper after tack processing (application of a release agent, gluing) was evaluated.
〇: Possible, ×: Not possible.
Copy aptitude: When using a Fuji Xerox full-color copier (product number: DocuCenter Color 500) to copy and attach the memo to the body of the book, can the memo be transparent and copy the characters below? It was visually evaluated.
〇: Possible, ×: Not possible.
Writing aptitude: The writing condition when writing with an HB pencil manufactured by Mitsubishi Pencil Co., Ltd. was visually evaluated.
〇: Possible, ×: Not possible.
[0055]
[Table 1]

[0056]
【The invention's effect】
As described above, according to the present invention, in the step of tacking, the occurrence of cutting curl, there is no problem that adhesive strength is weakened with less adhesion of glue, writability, offset printing suitability, pasting memo paper and copying. However, it is possible to provide a transparent memo sheet through which the memo can be transparently copied.

Claims (5)

Translated fromJapanese

木材パルプとしてＮ−ＢＫＰ（針葉樹晒クラフトパルプ）を主体とした坪量８０ｇ／ｍ^２以下の多層抄き原紙に透明化剤、表面サイズ剤が含浸塗布されてあり、その原紙に水４．０μＬを滴下した時の１秒後の接触角を剥離剤加工面では８０度以上、粘着剤加工面では９０度以下とし、ＪＩＳ Ｐ ８１３８による不透明度を６０％以下としたことを特徴とする、透明メモ用紙。As a wood pulp, a clarifying agent and a surface sizing agent are impregnated and coated on a multi-layer base paper having a basis weight of 80 g / m² or less, mainly composed of N-BKP (softwood bleached kraft pulp), and 4.0 μL of water is applied to the base paper. The contact angle at 1 second after dropping is 80 ° or more on the release agent-processed surface, 90 ° or less on the pressure-sensitive adhesive-processed surface, and the opacity according to JIS P 8138 is 60% or less. Note paper.透明化剤としての両性スチレン、ブタジエン、アクリル混合エマルジョンと表面サイズ剤としてのアルキルケテンダイマーを１００：０．１〜１００：１．５の固形分重量比で使用したことを特徴とする、請求項１記載の透明メモ用紙。An amphoteric styrene, butadiene, acrylic mixed emulsion as a clarifying agent and an alkyl ketene dimer as a surface sizing agent are used in a solid content weight ratio of 100: 0.1 to 100: 1.5. 1. The transparent memo paper according to 1.透明化剤、表面サイズ剤の含浸塗布量の合計が固形分換算で５〜３０ｇ／ｍ^２の範囲で塗布されていることを特徴とする、請求項１または２に記載の透明メモ用紙。The transparent memo paper according to claim 1, wherein the total amount of the clarifying agent and the surface sizing agent is in the range of 5 to 30 g / m^{2 in} terms of solid content.オンマシンサイズプレスにて透明化剤、表面サイズ剤を含浸塗布したことを特徴とする、請求項１〜３のいずれか一つに記載の透明メモ用紙。The transparent memo paper according to any one of claims 1 to 3, wherein a transparentizing agent and a surface sizing agent are impregnated and applied by an on-machine size press.原紙の片面に剥離剤が塗布され、その反対面に粘着剤が塗布されていることを特徴とする、請求項１〜４のいずれか一つに記載の透明メモ用紙。The transparent memo paper according to any one of claims 1 to 4, wherein a release agent is applied to one side of the base paper and an adhesive is applied to the opposite side.