(54) DEGASSING AND FILTRATION OF MOLTEN METAL(71) We, SWISS ALUMINIUM LTD., aCompany organised under the laws of Switzerland, of Chippis (Canton of Valais), Switzerland, do hereby declare the invention, for which we pray that a patent may be granted to us and the method by which it is to be per formed, to be particlularly described in and by the following statement:The present invention relates to the degassing and filtration of molten metal, and particularly to the treatment of said metal with a flux inggas.
Molten metal, particularly molten aluminum, in practice generally contains entrained and dissolved impurities, both gaseous and solid, which are deleterious to the final cast product.
The impurities may affect the final cast product after the molten metal is solidified, whereby processing may be hampered or the final product may be less ductile, or have poor finishing and anodizing characteristics. The impurities may originate from several sources. For example, the impurities may include metallic impurities such as alkaline and alkaline earth metals, and occluded hydrogen gas and dissolved surface oxide films which have become broken up and are entrained in the molten metal. In addition, the inclusions may originate as insoluble impurities, such as carbides, borides and others or eroded furnace and trough refractories.
It is naturally highly desirable to improve the degassing and filtration of molten metals in order to remove or minimize such impruities in the final cast product, particularly with respect to molten aluminum and especially, for example, when the resultant metal is to be used in a decorative product, such as decorative trim or sheet, or products bearing critical specifications, such as aircraft forgings and extrusions, and light gauge foil stock. Impurities as aforesaid cause loss of properties such as tensile strength and corrosion resistance in the final solidified alloy and lead to degradation of processing efficiency and loss of properties in the final product. For example, one type of finishing flaw which is particularly significant in decorative trim or sheet is a stringer defect known as a linear defect.
Conventionally conducted gas fluxing processes, such as general hearth fluxing, have involved the introduction of the fluxing gas to a melting or holding furnace containing a quantity of molten metal. This procedure required that the furnace be shut down while the fluxing gas is circulated, so that the metal being treated would remain constant and treatment could take place. This procedure had many drawbacks, among them, the reduced efficiency resulting from the prolonged idleness of the furnace during fluxing, as well as the lack of efficiency due to the low surface area to volume ratio between the gas flux and the molten metal. Further factors comprised the restriction of location to the furnace which permitted the re-entry of impurities to the melt before casting, and the high emissions resulting from both the sheer quantity of flux required and the location of its circulation.
As an alternative to the batch-type fluxing operations employed as set out above, certain fluxing operations were employed in an in-line manner; that is, the operation and associated apparatus were located outside the melting or holding furnace and often between either the melting furnace and the holding furnace or the holding furnace and the casting situation. This helped to alleviate the inefficiency caused by furnace shut-down, but was not as successful in improving the efficiency of the operation itself, in that undesirably large quantities of fluxing gas were often required per unit of molten metal, which was both costly and detrimental to air purity. Some of these processes utilized in conjuction therewith conventional filter media such as open-weave glass cloth screens, and bed filters made up, for example, of tabular alumina, which both exhibit as a primary disadvantage the inability to maintain a uniform pore size.
Porous ceramic foam materials are known in the art, for example, having been described inU.S. Patents 3 090 094 and 3 097 930. These porous ceramic foam materials are known to be particularly useful in filtering molten metal, as described in our U.S. Patent 3 893 917 and also as described in our British Patent ApplicationNo. 12582/76 (1 537 548). The same application No. 12582/76 (1 537 548) also describes an apparatus and method for the filtration of molten metals which employs filter plates prepared from said porous ceramic foam materials.
Porous ceramic foam materials are particularly useful for filtering molten metal for a variety of reasons, included among which are their excellent filtration efficiency, resulting in part from their uniform, controllable pore size, and low cost, as well as ease of use and replaceability. The fact that these ceramic foam filters are convenient and inexpensive to prepare and use has prompted the development of means for easily and conveniently employing these porous, molten metal filters in an in-line degassing and filtration unit which provides a highly efficient assembly.
Apparatus according to the present invention comprises, a chamber having a metal inlet and a metal outlet, at least a first and a second removable filter-type medium supported by wall surfaces in sequential, spaced-apart relationship within the chamber, and at least one conduit providing a fluxing gas inlet port positioned between said first and said second filtertype medium in such relation to said first filtertype medium that fluxing gas issuing from said port is capable of percolation therethrough.
Preferably the filter-type media are each as described in our previsouly-mentioned British patent application No. 12582/76, (1 537 548).
However, other media, especially other known ceramic filters, may be used.
The filter-type media preferably differ in pore size and permeability whereby said first medium possesses a relatively coarser pore structure, higher permeability and larger available flow area than said second medium. In a preferred embodiment, filter-type media are provided which possess an open cell structure characterised by a plurality of interconnected voids, and are preferably prepared from a ceramic foam wherein said voids are surrounded by ceramic material. The filter media may comprise plates having bevelled peripheral surfaces adapted to mate with bevelled wall surfaces on said chamber. A resilient sealing means is provided on each of said bevelled filter plate surfaces which is resistant to said molten metal to sealably engage the bevelled wall surfaces of said chamber upon installation of the filter plates.
In methods according to the present invention, degassing and filtration of molten metal is conducted by passing said molten metal through a chamber wherein said metal travels through at least two sequentially placed, spaced-apart filter-type media and is brought into counter-current contact with a fluxing gas while travelling through the first of said filter-type media, said fluxing gas issuing from at least one inlet provided within said chamber between the first and second of said filter-type media and percolating through the first of said media.
During the operation of the present method, the surface of said first filter-type medium is maintained below the level of the melt. The method employs a fluxing gas such as an inert gas, preferably carrying a small quantity of an active gaseous ingredient such as chlorine or a fully halo genated carbon compound.
Optionally, a supernatant salt cover may be located on the surface of said melt residing above the first of said filter-type media. This cover is a liquid salt mixture comprising halogen - containing compounds, preferably alkali and alkaline earth chlorides and a fluoride.
The present apparatus and method provide a considerable increase in productivity in the degassing of molten metal, as degassing is conducted without interruptions of the melting furnace. Further, the design of the apparatus enables its placement near to the casting station, whereby the possibility of further impurities entering the melt is substantially eliminated.
The employment of the filter-type medium enables the gaseous flux to achieve a greater dispersion throughout the melt whereby greater surface area of flux contact with a unit of melt volume is achieved. Improved kinetics contribute to greater efficiency.
In addition, the efficiency achieved by use of the present invention permits degassing to be conducted with a sufficiently lowered amount of flux material whereby the level of effluents resulting from the fluxing operation is greatly reduced.
By virtue of the employment of conveniently removable filter-type media possessing a carefully controlled gradation of filter properties, the apparatus and method are capable of achieving levels of melt purity heretofore attainable only with the most rigorous of processing. Also, the employment of a relatively coarse first filter-type medium to abstract larger entrained non-metallic particulate before the melt reaches the second fine filter greatly extends the useful life of the latter. In addition, these high levels of purity are attained utilizing inexpensively manufactured filter-type media.
The accompanying drawings show two examples of apparatus embodying the present invention. In these drawings:Figure 1 is a side sectional view of one apparatus, depicting the filter-type plates in place therein substantially horizontally disposed.
Figure 2 is a perspective view, partly broken away, of a filter-type medium for use in the apparatus; andFigure 3 is a side sectional view of a second apparatus, wherein the second filter-type medium is disposed in substantially side-by-side relationship to the first medium.
Referring to Figure 1, an apparatus is illustrated in location within a molten metal transfer system which may include pouring ladles, pouring troughs, tranfer troughs, metal treatment bays or the like. As will be discussed later on, the apparatus and methods embodying the present invention may be employed in a wide variety of locations occurring intermediate the melting and casting stations in a metal processing system. Thus, Figure 1 depicts apparatus 10 in location adjacent the exit port 11 of a holding furnace 12. The rate of flow of metal from holding furnace 12 is controlled by a valve means comprising a check rod 13. Metal flows into apparatus 10 via a short transfer passageway 14 leading to chamber 15 wherein the degassing and filtration operations take place.
By the control of metal flow into transfer passageway 14 by the positioning of check rod 13, melt level 16 is maintained at a point above the first of two filter-type media, at a level depicted in Figure 1 selected for purposes of illustration only.
Chamber 15 is illustrated as roughly bowlshaped and is disposed with its bottom recessed below the level of the transfer passageway 14 so that molten metal travelling thereto will flow downwardly through the filter-type media.
Chamber 15 is characterised by the provision of al least two peripheral rims 17 and 18, comprising, respectively, a first and a second peripheral rim. First peripheral rim 17 is located at the upper portion of chamber 15 and, in Figure 1 is positioned at a level continuous with the bottom of transfer passageway 14. Second peripheral rim 18, as depicted in Figure 1, is disposed within chamber 15 so as to effectively divide it into sub-chambers 19 and 20. As with first peripheral rim 17, second peripheral rim 18 is illustrated in the Figures as defining a downwardly converging bevelled surface which enables the expeditious installation and replacement of appropriately configured filter-type media. Though rims 17 and 18 are illustrated as having bevelled surfaces, the invention is not limited thereto, as rims possessing other means for retaining in place the filter-type media of the present invention may be employed as will be noted later on. Rim 18 is shown to be reduced in size from first rim 17 to enable the unobstructed manipulation of the filter medium located therein.
First sub-chamber 19 comprises the area residing between the first and second filter-type media labelled 21 and 22, respectively. As illustrated herein filter-type media 21 and 22 may likewise possess bevelled peripheral surfaces 23 adapted to mate with correspondingly configured peripheral rims 17 and 18. The bevelled peripheral surfaces 23 when employed are provided with resilient gasket type sealing means 24 thereon, e.g. of ceramic, which are resistant to molten metal, and the respective filter media 21 and 22, including sealing means 24 are sequentially inserted into chamber 15 so that sealing means 24 in each instance engages the respective bevelled surfaces of rims 17 and 18. Preferably as shown, all the mating surfaces are bevelled at substantially the same angle.
As noted earlier, the provision of peripheral rims 17 and 18 supporting respective filter media 21 and 22 effectively divides chamber 15 into sub-chambers 19 and 20. Referring again to Figure 1, sub-chamber 19 is provided with at least one inlet port 25 comprising the opening or openings of a conduit 26 or manifold through which a fluxing gas may be introduced to the melt from an outside source, not shown.
The fluxing gas which may be employed comprises a wide variety of well-known components including chlorine gas and other halogenated gaseous materials, carbon monoxide as well as certain inert gas mixtures derived from and including nitrogen, argon, helium and the like. A preferred gas mixture for use in the present invention comprises a mixture of nitrogen with from about 0.1 to about 5% by volume dicldorodifluoromethane, wherein the inert gas component may further include an inert carrier such as helium, argon and mixtures thereof, and dichlorodifluoromethane may be replaced in whole or in part by chlorine, or fully chlorinated or chlorofluorinated lower hydrocarbon components containing one to six carbon atoms and free of hydrogen.
In conjunction with this gas mixture, a liquid salt mixture may be employed on the surface of the melt residing within transfer passageway 14 which would comprise mixtures of alkali and alkaline earth chlorides and a fluoride. A specific such formulation may, for example include 40-50% Nail, 45-55% KC1 and 5% Na3 AIF6. The foregoing flux materials are fully disclosed in our U.S. Patent No. 3 854 934, the disclosure of which is incorporated herein by reference. As indicated above, the foregoing compositions are presented for purposes of illustration only and do not form a material limitation on the present invention.
Referring further to Figure 1, one of the primary features of the present invention comprises the location of the gas inlet comprising port 25 as illustrated herein in relation to the first filter-type medium comprising filter plate 21. Specifically, the placement of port 25 is such that fluxing gas issuing therefrom is cap able of percolating up through the melt residing within sub-chamber 19 to pass through first filter-type medium 21 where it is broken up and dispersed, and is in counter-current contact with molten metal flowing in the opposite direction through said filter-type medium. It is at this point in filter 21 that the unexpectedly efficient impurity removal takes place whereby relatively coarse undesirable particulate inclusions, undesirable gases and certain dissolved metallic elements are separated from the melt and then percolate up to the melt surface by the counter-current action of the fluxing gas, where the particulate material may be subsequently removed if so desired by conventional surface treatment techniques, such as skimming and the like. The action of the fluxing gas is schematically illustrated in Figure 1 wherein the gas is depicted as a plurality of bubbles 27 issuing from inlet port 25 and passing through and above filter medium 21 to the melt surface or level 16. Further, though not illustrated herein, melt surface 16 may optionally possess thereon the liquid salt cover noted earlier in conjunction with a preferred fluxing material useful with the present invention.
After contacting the fluxing gas during passage through filter medium 21, the molten metal flows through sub-chamber 19 and continues through filter medium 22 comprising in the illustration a filter plate possessing a relatively fine pore size. Whereas the primary purpose of first filter-type medium 21 is to break up the fluxing gas into a fine dispersion to assure intimate and extensive contact with the melt, the purpose of second filter-type medium 22 is to remove any remaining non-metallic particulate material from the melt as it passes therethrough. Thus, the molten metal issuing from filter medium 22 into second sub-chamber 20 is purified and is ready for transfer to either a casting station or, if desired, further processing, through exit trough 28.
Preferably the filter-type media each comprise a filter plate such as that illustrated inFigure 2. Filter plate 29 possesses an open cell structure, characterised by a plurality of interconnected voids, such that the molten metal may pass therethrough to remove or minimize entrained solids from the final cast product, or to facilitate the exchange of impurities between the melt and a fluxing gas. Such a filter may comprise, for example, a solid filter plate made from sintered ceramic aggregate, or a porous carbon plate. In the preferred embodiment, a ceramic foam filter is utilized as described in our previously-mentioned British Patent Application No. 12582/76 (1 537 548). In accordance with the teaching of that application, ceramic foam filters may be prepared which have an open cell structure characterised by a plurality of interconnected voids surrounded by a web of said ceramic material. The ceramic filters have an air permeability in the range of from 400 to 8000 x 10~7cm2, preferably from 400 to 2500 x 10-7cm2, a porosity or void fraction of 0.80 to 0.95 and a pore size from 5 to 45 pores per linear inch, preferably from 20 to 45 pores per linear inch and thicknesses of from 1/2 to 4 inches. The molten metal flow rate through the filter may range from 5 to 50 cubic inches per square inch of filter area per minute. The ceramic foam filters described in application No. 12582/76 are particularly suitable in carrying out the present invention since they are of low cost and may be readily employed on a throwaway basis. Futhermore, such filters are surprisingly effective in the filtration of molten metal, especially aluminium, at a low cost, achieving surprising filtration efficiency with considerable flexibility.
Preferably first filter-type medium 21 is of a relatively coarse pore size ranging from 5 to 20 ppi, which possesses an air permeability ranging from 2500 to 8000 x 10-7cm2, while second filter medium 22 is a relatively fine filter possessing a pore size of from 20 to 45 ppi and an air permeability from 400 to 2500 x 10-7cm2. Naturally, as noted earlier, both permeability and pore size of the respective filter-type media may be varied to suit the particular material veing filtered, and the present invention should not be limited to the aforenoted exemplary ranges.
The ceramic foam filters preferably utilized in the present invention are prepared from an open cell, flexible foam material having a plurality of interconnected voids surrounded by a web of said flexible foam material, such as polyurethane foams or cellulosic foams. The ceramic foam filter may be prepared in accordance with the general procedure outlined inPatent 3 893 917, wherein an aqueous ceramic slurry is prepared and the foam material impregnated therewith so that the web thereof is coated therewith and the voids substantially filled therewith. The impregnated material is compressed so that a portion of the slurry is expelled therefrom and the balance uniformly distributed throughout the foam material.
The coated foam material is then dried and heated to first bum out the flexible organic foam and then sinter the ceramic coating, thereby providing a fused ceramic foam having a plurality of interconnected voids surrounded by a web of bonded or fused ceramic in the configuration of the flexible foam. Naturally, a wide variety of ceramic materials may be chosen depending upon the particular metal to be filtered. Preferably, a mixture of alumina and chromia is employed, however, these materials may naturally be utilised separately or in combination with other ceramic materials.
Other typical ceramic materials which may be employed include zirconia, magnesia, titanium dioxide, silica and mixtures thereof. Normally the slurry contains from about 10 to 405'o of water and one or more rheological agents, binders or air setting agents.
As shown in Figure 2, the filter plate 29 may have a bevelled peripheral surface 30 adapted to mate with the similarly bevelled rims of the filter chamber illustrated in Figures 1 and 3.
Preferably all the mating surfaces are bevelled at the same angle. Naturally, variations in design are contemplated within the scope of the present invention and thus a wide variety of geometric configurations may be contemplated within the scope of the apparatus disclosed herein, and the illustration of Figure 2 is not meant to be limiting thereto.
In the instance where the filter plates are designed to be throwaway items it is essential to provide an effective means of sealing the filter plate in place in its holder which is easy to assemble, disassemble and clean up. The holder or filter chamber itself is normally an integral part of a trough, pouring ladle or tundish, etc. and should be constructed of refractory materials resistant to the molten metal similar to those used in standard trough construction. It is greatly preferred to seal the filter plate is place using a resilient gasket type sealing means as illustrated, and as discussed earlier, which peripherally circumscribes the filter plate at the bevelled portion thereof The gaskets ensure a leak-free installation and also provide an effective parting medium which is essential for ease of disassembly. In addition, since the gaskets prevent ingress of metal to the sealing faces of the holder unit, their use considerably eases clean up and effectively prolongs the life of the unit by eliminating problems of metal attack. Furthermore, because of its resiliency, the gasket may provide sufficient frictional force to hold the filter body in place in the holder or filter chamber without resort to other types of hold down devices. The gasket should be non-wetting to the particular molten metal, resist chemical attack therefrom and be refractory enough to withstand the high operating temperatures.
Plate type filter units may be sealed by gaskets around their edges and/or at the periphery of their large faces. The plate type filter units are preferably sealed by an edge type seal along the peripheral surface of the filter plate thus providing a positive seal and, in conjunction with the gasket, a mechanical advantage to hold the filter in place. In the event that a simple press fit is insufficient to hold the filter in place, naturally a variety of mechanical devices such as wedges and hold down weights may be employed. Alternatively, apparatus 10 in Figure 1 can be made to be split at rims 1 7 and 18, in a manner not shown, so that pressure can be applied to the seals by the vise-like action of closing the split unit. The bevelled angle of the filter chamber and corresponding bevelled angle of the filter plate tends to form a positive seal and hold the filter in place against buoyancy forces acting thereupon.
Naturally, as indicated above, the gasket or seal should be resistant to the molten metal utilized. Typical gasket materials utilized in aluminum processing include fibrous refractory type seals of a variety of compositions, as the following illustrative seals: (1) a seal containing about 45% alumina, 52% silica, 1.3% ferric oxide and 1.7% titania; (2) a seal containing about 55% silica, 40.5% alumina, 4% chromia and 0.5% ferric oxide; and (3) a seal containing about 53% silica, 46% alumina and 1% ferric oxide.
In accordance with a further embodiment of the present invention, an apparatus 31 is depicted in Figure 3 which comprises a transfer passageway 32 leading to a continuous filter chamber 33. Chamber 33 differs from chamber 15 of Figure 1 in that it is continuous rather than partitioned into sub-chambers. In this embodiment, coarse filter-type medium 21' is located in essentially side-by-side relationship with fine filter-type medium 22'. The respective filter-type media are separated by partition wall 34 which is integral with and of identical height to transfer passageway 32 and exit trough 35. As in the apparatus of Figure 1, a flux inlet port 25' is located in chamber 33 adjacent and below filter medium 21' and is fed in a similar manner by conduit 26'. Thus, flux material comprising a gaseous fluxing agent may issue from port 25' and will percolate through filter medium 21' to achieve the desired counter-current contact and exchange with the downwardly moving melt. The difference in the configuration of chamber 33 dictates that the melt will flow downward around partition wall 34 and will receive its final filtration as it passes upward through filter medium 22' on its way to exit trough 35. As in the illustration of Figure 1, apparatus 31 is provided with bevelled peripheral rims to accommodate the placement and support of the respective filter media. Likewise, the filter media are provided with resilient sealing means to effect the desired securement of the filters within the rims.
A wide variety of instances exist where the apparatus and methods embodying the present invention may be employed. Specifically in the instance of a continuous casting operation, a pair of flux filtration chambers may be employed in parallel arrangement. In such an operation, the great length and associated total flow of metal involved may require the frequent changing of filter media in mid-run. Such changes may be facilitated by the employment of parallel flow channels each containing a filtration chamber, together with a means for diverting flow from one channel to the other, by valves, dams or the like. Flow would thus be restricted to one filtration chamber at a time and would be diverted to an alternate channel once the head drop across the first filtration chamber became excessive. It can be seen that such a switching procedure could supply an endless stream of filtered metal to a continuous casting station.
In addition to the above, the apparatus and methods illustrated by the drawings are capable of several modifications within the scope of the invention to accommodate variations in operating procedure. For example, in the instance where small, individual lost of molten metal are prepared and cast, it is desirable that the filtertype media remain operable for several such lots. To this end, the filter media may be recessed somewhat from the levels of the transfer passageway and exit trough whereby, after melt flow has ceased, residual melt remains which fills the chamber and covers both filters. In conjunction with this modification, at least one cover unit may be employed which would reside above the remaining melt, and would be provided with heating means such as a plurality of radiant heaters to keep the melt in the liquid state. In the event that such modifications are employed with the apparatus of Figure 1, peripheral rim 1 7 would be recessed and cover member, not illustrated herein, would be placed thereover. Likewise, the bottom of exit trough 28 would be brought into alignment with the bottom of passageway 14 and a similar cover member would be employed at the location where the exit area of sub-chamber 20 abuts with trough 28. In the illustration of Figure 3, filter-type media 21' and 22' could simply be recessed to permit the residence of melt thereover, and appropriately configured cover members could be located thereat.
Other modifications contemplated within the scope of the invention include the provision of a plurality of inlet ports surrounding the respective chambers immediately below the respective first filter-type media. In addition, and likewise not illustrated herein, the inlet ports could be extended to the center of said chambers by the extension of the respective conduits thereinto, whereby fluxing gas may enter the melt from a point centrally located within the chamber.
WHAT WE CLAIM IS:1. An apparatus for the degassing and filtration of molten metal which comprises a chamber having a metal inlet and a metal outlet, at least a first and second removable filter-type medium supported by wall surfaces in sequential, spaced-apart relationship within the chamber, and at least one conduit providing a fluxing gas inlet port positioned between said first and said second filter-type medium in such relation to said first filter-type medium that fluxing gas issuing from said port is capable of percolation therethrough.
2. The apparatus of claim 1, wherein sai