A kind of production method of Anti-static fabricTechnical field
The invention belongs to textile material technical field, and in particular to a kind of production method of Anti-static fabric.
Background technology
Cotton products fabric and finished product are used and strong acid in high-frequency, textile in the case of highly basic washing, polyester-cotton blend, product meetingOccur decolourizing, shrink, the problems such as service life is short, but again electrostatic occurs during the fiber product use of part.At this stage, it is rightTextile surface is modified, and is the common methods for solving electrostatic phenomenon.Compared to all kinds of antistatic additive, conjugative monomer is in fiberThe polymerization on surface, it is convenient, nontoxic because of it, therefore have evolved into the new methods for preparing antistatic textile.
The content of the invention
The present invention provides a kind of production method of Anti-static fabric, the technical scheme for adopting for：A kind of electrostatic preventive clothThe production method of material, the production method has following steps：
（1）Fiber is being changed in the transition process of solid-state from liquid, adds antistatic auxiliary so as to possess anti-static function；
（2）The fineness of fiber is fine to into 1.0D-1.2D, adopts this anlistatig short fine with the spinning process of Air-Jet Spinning, willShort fine spun yarn respectively；
（3）The technique for taking segmentation sizing warping again, is weaved with satin weave with high speed spray vapour loom；
（4）The cloth that weaving is obtained be impregnated in into 30min in the Na2CO3 solution that mass fraction is 2%, Jing distills in a large number washingAfter washing, dry at 40 DEG C, obtain modified cloth A；
（5）The modified cloth A is placed in into N- (2- the aminoethyls) -3- aminopropyl trimethoxysilanes that mass fraction is 0.5%After immersion 30min in the mixed solution of vinyltrimethoxy silane composition, Jing methyl alcohol, water are washed respectively, are dried at 40 DEG CIt is dry, obtain modified cloth B；
（6）The modified cloth B is placed in the ammonium persulfate aqueous solution that mass fraction is 10%~20% and is soaked after 1h, againJing distills water washing, obtains modified cloth C；
（7）The modified cloth C is placed under 0 DEG C~5 DEG C of ice water bath environment and is standing and soak for after 24h, Jing massive launderings are washed, inDry at 40 DEG C and Antistatic cloth is obtained.
Anti-static fabric antistatic behaviour prepared by the present invention is good.The inventive method, has given full play to aniline and sulfydrylThe concertedness of produced conductive compositions after aniline polymerization, promotes cloth to have higher electrical conductivity, thus antistatic behaviour is good.The preparation process is simple of the present invention, products obtained therefrom antistatic property are excellent, applicability is wide.
Specific embodiment
Embodiment 1, produces according to the following steps：
（1）Fiber is being changed in the transition process of solid-state from liquid, adds antistatic auxiliary so as to possess anti-static function；
（2）The fineness of fiber is fine to into 1.0D, adopts this anlistatig short fine with the spinning process of Air-Jet Spinning, will be short fine pointOther spun yarn；
（3）The technique for taking segmentation sizing warping again, is weaved with satin weave with high speed spray vapour loom；
（4）The cloth that weaving is obtained be impregnated in into 30min in the Na2CO3 solution that mass fraction is 2%, Jing distills in a large number washingAfter washing, dry at 40 DEG C, obtain modified cloth A；
（5）The modified cloth A is placed in into N- (2- the aminoethyls) -3- aminopropyl trimethoxysilanes that mass fraction is 0.5%After immersion 30min in the mixed solution of vinyltrimethoxy silane composition, Jing methyl alcohol, water are washed respectively, are dried at 40 DEG CIt is dry, obtain modified cloth B；
（6）The modified cloth B is placed in the ammonium persulfate aqueous solution that mass fraction is 10% and is soaked after 1h, again Jing distillationsWater washing, obtains modified cloth C；
（7）The modified cloth C is placed under 0 DEG C of ice water bath environment and is standing and soak for after 24h, Jing massive launderings are washed, in 40 DEG CLower drying is obtained Antistatic cloth.
Embodiment 2, produces according to the following steps：
（1）Fiber is being changed in the transition process of solid-state from liquid, adds antistatic auxiliary so as to possess anti-static function；
（2）The fineness of fiber is fine to into 1.1D, adopts this anlistatig short fine with the spinning process of Air-Jet Spinning, will be short fine pointOther spun yarn；
（3）The technique for taking segmentation sizing warping again, is weaved with satin weave with high speed spray vapour loom；
（4）The cloth that weaving is obtained be impregnated in into 30min in the Na2CO3 solution that mass fraction is 2%, Jing distills in a large number washingAfter washing, dry at 40 DEG C, obtain modified cloth A；
（5）The modified cloth A is placed in into N- (2- the aminoethyls) -3- aminopropyl trimethoxysilanes that mass fraction is 0.5%After immersion 30min in the mixed solution of vinyltrimethoxy silane composition, Jing methyl alcohol, water are washed respectively, are dried at 40 DEG CIt is dry, obtain modified cloth B；
（6）The modified cloth B is placed in the ammonium persulfate aqueous solution that mass fraction is 15% and is soaked after 1h, again Jing distillationsWater washing, obtains modified cloth C；
（7）The modified cloth C is placed under 3 DEG C of ice water bath environment and is standing and soak for after 24h, Jing massive launderings are washed, in 40 DEG CLower drying is obtained Antistatic cloth.
Embodiment 3, produces according to the following steps：
（1）Fiber is being changed in the transition process of solid-state from liquid, adds antistatic auxiliary so as to possess anti-static function；
（2）The fineness of fiber is fine to into 1.2D, adopts this anlistatig short fine with the spinning process of Air-Jet Spinning, will be short fine pointOther spun yarn；
（3）The technique for taking segmentation sizing warping again, is weaved with satin weave with high speed spray vapour loom；
（4）The cloth that weaving is obtained be impregnated in into 30min in the Na2CO3 solution that mass fraction is 2%, Jing distills in a large number washingAfter washing, dry at 40 DEG C, obtain modified cloth A；
（5）The modified cloth A is placed in into N- (2- the aminoethyls) -3- aminopropyl trimethoxysilanes that mass fraction is 0.5%After immersion 30min in the mixed solution of vinyltrimethoxy silane composition, Jing methyl alcohol, water are washed respectively, are dried at 40 DEG CIt is dry, obtain modified cloth B；
（6）The modified cloth B is placed in the ammonium persulfate aqueous solution that mass fraction is 20% and is soaked after 1h, again Jing distillationsWater washing, obtains modified cloth C；
（7）The modified cloth C is placed under 5 DEG C of ice water bath environment and is standing and soak for after 24h, Jing massive launderings are washed, in 40 DEG CLower drying is obtained Antistatic cloth.
The preferred embodiments of the present invention are the foregoing is only, the present invention is not limited to, it is general for this areaFor logical technical staff, the present invention can have various modifications and variations；It is all within the spirit and principles in the present invention, made appointWhat modification, equivalent, improvement etc., should be included within the scope of the present invention.