CN1058946A - A kind of magnesial decorative plate - Google Patents

Abstract

The invention provides a kind of New Building Materials that replace brocatel---magnesial decorative plate.Its technical essential is: it is made up of surface layer and nexine, and surface layer is to be made into by magnesium powder, silica powder and the blending agents ratio in 1: 0.5: 0.9.Nexine is to be made into by magnesium powder, flyash and the blending agents ratio in 1: 2: 1.As the need color, also can in capstock, add an amount of pigment, capstock and nexine material are made in 2: 15 ratio.Decorative sheet after making, light is wear-resisting, lovely luster, with low cost, equipment is simple, and the present invention is fit to use under construction.

Description

A kind of magnesial decorative plate

The invention belongs to a kind of material of construction, particularly have decorative constructional materials.

Colorful terrazzo has attractive in appearance, intensity advantages of higher as decorative constructional materials.But because starting material are more expensive, manufacture craft is complicated, so its cost is higher.Shortcomings such as it also exists heat-insulating property poor simultaneously, and proportion is bigger.

The purpose of this invention is to provide a kind of material of construction-magnesial decorative plate that replaces colorful terrazzo, it can overcome above-mentioned deficiency effectively.

Technical scheme of the present invention is:

(1) it is made up of surface layer and nexine, and its proportioning is:

(1.1) surface layer

Magnesium powder: silica powder (or talcum powder): blending agents=1: 0.5: 0.9-1.1

Wherein:

(1.1.1) concentration of surface layer blending agents is 27 ° of Be-31 ° of Be

Or proportion is 1.23-1.27

(1.2) nexine

Magnesium powder: flyash (or sandstone): blending agents=1: 2-3: 0.7-1.3.

Wherein:

(1.2.1) concentration of nexine blending agents is 18 ° of Be-24 ° of Be

Or proportion is 1.14-1.20

(1.3) surface layer: nexine=2: 15

(2) making method

(2.1) preparation of capstock:

Earlier quantitative magnesium powder is added fully stir in the quantitative blending agents after, add silica powder or talcum powder, continue to stir, shakeout in the mould of packing into.

(2.2) preparation of nexine material:

Earlier quantitative magnesium powder is added fully stir in the quantitative mixture after, add flyash or sandstone.

(2.3) the nexine material is packed in the mould of capstock, treat five, six hours after, the demoulding forms.

The present invention compared with prior art, advantage such as it is simple to have a processing unit, and cost is low, and light is wear-resisting, after adding pigment, lovely luster, attractive in appearance.

Provide an embodiment below

Capstock: magnesium powder: 10Kg

Blending agents: 9Kg, concentration is 29 ° of Be

Silica powder: 5Kg

Pigment: 0.7Kg

Nexine material: magnesium powder: 100Kg

Blending agents: 80Kg, concentration is 18 ° of Be

According to " (2) making method " described step above, promptly can be made into.

Claims (2)

1, a kind of magnesial decorative plate is characterized in that: it is made up of surface layer and nexine, and its proportioning is:

(1) surface layer

Magnesium powder: silica powder (or talcum powder): blending agents=1: 0.5: 0.9-1.1

Wherein:

(1.1) concentration of surface layer blending agents is that 27 ° of Be-31 ° of Be or proportion are 1.23-1.27

(2) nexine

Magnesium powder: flyash (or sandstone): blending agents=1: 2-3: 0.7-1.3.

Wherein:

(2.1) concentration of nexine blending agents is that 18 ° of Be-24 ° of Be or proportion are 1.14-1.20

(3) surface layer: nexine=2: 15.

2, magnesial decorative plate according to claim 1 is characterized in that:

Capstock: magnesium powder: 10Kg

Blending agents: 9Kg, concentration is 29 ° of Be

Silica powder: 5Kg

Pigment: 0.7Kg

Nexine material: magnesium powder: 100Kg

Blending agents: 80Kg, concentration is 18 ° of Be.