CN105331240A - Cloth cart - Google Patents

Abstract

The invention discloses a cloth cart. The cloth cart comprises a metal rotating shaft subjected to surface treatment. The surface treatment process includes the following steps that firstly, by mass, 1-2 parts of mercaptobenzothiazole, 0.9 part of nickel nitrate, 1.4 parts of 1-Hydroxyethylidene-1,1-diphosphonicacid, 2.3 parts of polyvinylpyrrolidone, 1.8 parts of dipyrazolone, 2.3 parts of 2,6-di-t-butyl-alpha-dimethylamino hydroquinone and 1.6 parts of tetramethyl ammonium bromide are added into 12 parts of deionized water and evenly stirred and mixed, and surface treatment working fluid is obtained; secondly, the surface treatment working fluid is heated to 53 DEG C; thirdly, the metal rotating shaft is put into the surface treatment working fluid to be steeped for 32 min, taken out and then dried. Due to the fact that the metal rotating shaft of the cloth cart is subjected to surface treatment, good rub resistance, corrosion resistance, rust resistance, heat resistance, cold resistance and weather resistance are achieved.

Description

Trolley for cloth

Technical field

The present invention relates to Trolley for cloth.

Background technology

Existing Trolley for cloth, the abrasion-resistant of its metal rotating shaft, corrosion-resistant, antirust, heat-resisting, cold-resistant, weather resistance have much room for improvement.

Summary of the invention

The object of the present invention is to provide a kind of Trolley for cloth, its metal rotating shaft, through surface treatment, has excellent abrasion-resistant, corrosion-resistant, antirust, heat-resisting, cold-resistant, weather resistance.

For achieving the above object, technical scheme of the present invention is a kind of Trolley for cloth of design, and it comprises metal rotating shaft, and this metal rotating shaft is through surface treatment, and described surface treatment comprises the steps:

1) in 12 mass parts deionized waters, 1 ~ 2 mass parts coloured glaze base benzothiazole, 0.9 mass parts nickelous nitrate, 1.4 mass parts hydroxy ethylene diphosphonic acids, 2.3 mass parts polyvinylpyrrolidones, 1.8 mass parts diazolones, 2.3 parts of quality 2 are dropped into, 6-di-t-butyl-alpha, alpha-dimethyl amido Pyrogentisinic Acid, 1.6 mass parts 4 bromides, be uniformly mixed, obtained facing operation liquid;

2) facing operation liquid is warming up to 53 DEG C;

3) metal rotating shaft is inserted in facing operation liquid and flood 32 minutes, take out post-drying.

Preferably, Trolley for cloth, it comprises metal rotating shaft, and this metal rotating shaft is through surface treatment, and described surface treatment comprises the steps:

1) in 12 mass parts deionized waters, drop into 1 mass parts coloured glaze base benzothiazole, 0.9 mass parts nickelous nitrate, 1.4 mass parts hydroxy ethylene diphosphonic acids, 2.3 mass parts polyvinylpyrrolidones, 1.8 mass parts diazolones, 2.3 parts of quality 2,6-di-t-butyl-alpha, alpha-dimethyl amido Pyrogentisinic Acid, 1.6 mass parts 4 bromides, be uniformly mixed, obtained facing operation liquid;

2) facing operation liquid is warming up to 53 DEG C;

3) metal rotating shaft is inserted in facing operation liquid and flood 32 minutes, take out post-drying.

Preferably, Trolley for cloth, it comprises metal rotating shaft, and this metal rotating shaft is through surface treatment, and described surface treatment comprises the steps:

1) in 12 mass parts deionized waters, drop into 2 mass parts coloured glaze base benzothiazoles, 0.9 mass parts nickelous nitrate, 1.4 mass parts hydroxy ethylene diphosphonic acids, 2.3 mass parts polyvinylpyrrolidones, 1.8 mass parts diazolones, 2.3 parts of quality 2,6-di-t-butyl-alpha, alpha-dimethyl amido Pyrogentisinic Acid, 1.6 mass parts 4 bromides, be uniformly mixed, obtained facing operation liquid;

2) facing operation liquid is warming up to 53 DEG C;

3) metal rotating shaft is inserted in facing operation liquid and flood 32 minutes, take out post-drying.

Advantage of the present invention and beneficial effect are: provide a kind of Trolley for cloth, and its metal rotating shaft, through surface treatment, has excellent abrasion-resistant, corrosion-resistant, antirust, heat-resisting, cold-resistant, weather resistance.

Embodiment

Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.

The technical scheme that the present invention specifically implements is:

Embodiment 1

A kind of Trolley for cloth, it comprises metal rotating shaft, and this metal rotating shaft is through surface treatment, and described surface treatment comprises the steps:

1) in 12 mass parts deionized waters, 1 ~ 2 mass parts coloured glaze base benzothiazole, 0.9 mass parts nickelous nitrate, 1.4 mass parts hydroxy ethylene diphosphonic acids, 2.3 mass parts polyvinylpyrrolidones, 1.8 mass parts diazolones, 2.3 parts of quality 2 are dropped into, 6-di-t-butyl-alpha, alpha-dimethyl amido Pyrogentisinic Acid, 1.6 mass parts 4 bromides, be uniformly mixed, obtained facing operation liquid;

2) facing operation liquid is warming up to 53 DEG C;

3) metal rotating shaft is inserted in facing operation liquid and flood 32 minutes, take out post-drying.

Embodiment 2

Trolley for cloth, it comprises metal rotating shaft, and this metal rotating shaft is through surface treatment, and described surface treatment comprises the steps:

1) in 12 mass parts deionized waters, drop into 1 mass parts coloured glaze base benzothiazole, 0.9 mass parts nickelous nitrate, 1.4 mass parts hydroxy ethylene diphosphonic acids, 2.3 mass parts polyvinylpyrrolidones, 1.8 mass parts diazolones, 2.3 parts of quality 2,6-di-t-butyl-alpha, alpha-dimethyl amido Pyrogentisinic Acid, 1.6 mass parts 4 bromides, be uniformly mixed, obtained facing operation liquid;

2) facing operation liquid is warming up to 53 DEG C;

3) metal rotating shaft is inserted in facing operation liquid and flood 32 minutes, take out post-drying.

Embodiment 3

Trolley for cloth, it comprises metal rotating shaft, and this metal rotating shaft is through surface treatment, and described surface treatment comprises the steps:

1) in 12 mass parts deionized waters, drop into 2 mass parts coloured glaze base benzothiazoles, 0.9 mass parts nickelous nitrate, 1.4 mass parts hydroxy ethylene diphosphonic acids, 2.3 mass parts polyvinylpyrrolidones, 1.8 mass parts diazolones, 2.3 parts of quality 2,6-di-t-butyl-alpha, alpha-dimethyl amido Pyrogentisinic Acid, 1.6 mass parts 4 bromides, be uniformly mixed, obtained facing operation liquid;

2) facing operation liquid is warming up to 53 DEG C;

3) metal rotating shaft is inserted in facing operation liquid and flood 32 minutes, take out post-drying.

The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.

Claims (3)

1. Trolley for cloth, is characterized in that, it comprises metal rotating shaft, and this metal rotating shaft is through surface treatment, and described surface treatment comprises the steps:

1) in 12 mass parts deionized waters, 1 ~ 2 mass parts coloured glaze base benzothiazole, 0.9 mass parts nickelous nitrate, 1.4 mass parts hydroxy ethylene diphosphonic acids, 2.3 mass parts polyvinylpyrrolidones, 1.8 mass parts diazolones, 2.3 parts of quality 2 are dropped into, 6-di-t-butyl-alpha, alpha-dimethyl amido Pyrogentisinic Acid, 1.6 mass parts 4 bromides, be uniformly mixed, obtained facing operation liquid;

2) facing operation liquid is warming up to 53 DEG C;

3) metal rotating shaft is inserted in facing operation liquid and flood 32 minutes, take out post-drying.

2. Trolley for cloth according to claim 1, is characterized in that, it comprises metal rotating shaft, and this metal rotating shaft is through surface treatment, and described surface treatment comprises the steps:

1) in 12 mass parts deionized waters, drop into 1 mass parts coloured glaze base benzothiazole, 0.9 mass parts nickelous nitrate, 1.4 mass parts hydroxy ethylene diphosphonic acids, 2.3 mass parts polyvinylpyrrolidones, 1.8 mass parts diazolones, 2.3 parts of quality 2,6-di-t-butyl-alpha, alpha-dimethyl amido Pyrogentisinic Acid, 1.6 mass parts 4 bromides, be uniformly mixed, obtained facing operation liquid;

2) facing operation liquid is warming up to 53 DEG C;

3) metal rotating shaft is inserted in facing operation liquid and flood 32 minutes, take out post-drying.

3. Trolley for cloth according to claim 1, is characterized in that, it comprises metal rotating shaft, and this metal rotating shaft is through surface treatment, and described surface treatment comprises the steps:

1) in 12 mass parts deionized waters, drop into 2 mass parts coloured glaze base benzothiazoles, 0.9 mass parts nickelous nitrate, 1.4 mass parts hydroxy ethylene diphosphonic acids, 2.3 mass parts polyvinylpyrrolidones, 1.8 mass parts diazolones, 2.3 parts of quality 2,6-di-t-butyl-alpha, alpha-dimethyl amido Pyrogentisinic Acid, 1.6 mass parts 4 bromides, be uniformly mixed, obtained facing operation liquid;

2) facing operation liquid is warming up to 53 DEG C;

3) metal rotating shaft is inserted in facing operation liquid and flood 32 minutes, take out post-drying.