Summary of the invention
In order to solve the problems of the prior art, the invention provides a kind of composite fibre wallpaper and manufacture method thereof.
The present invention adopts following technical scheme to realize:
A kind of composite fibre wallpaper, comprises the raw material of following masses part: cotton fiber 20-40, china-hemp fibers 15-30, sodium carboxymethylcellulose 2-5, isobutyl triethoxy silane 4-6, glycerol 10-15.
Manufacture a method for above-mentioned composite fibre wallpaper, manufacturing step is as follows:
1) first glycerol and isobutyl triethoxy silane are added in 10-15 times of 40-45 DEG C of water and mix, then china-hemp fibers is soaked wherein 3-4 hour and be incubated;
2) cotton fiber is added 1) solution in and add cotton quality 25-35 water making beating 0.5-1 hour doubly;
3) by 2) solution warms to 65-70 DEG C, add sodium carboxymethylcellulose wherein, continue making beating 1-1.5 hour, stir to obtain mixing slurry;
4) last, mixing is starched through copy paper, squeezing, dries, batched obtained composite fibre wallpaper.
The silane coupler process china-hemp fibers that composite fibre wallpaper of the present invention adopts, then add sodium carboxymethylcellulose, makes cotton fiber, china-hemp fibers effectively combines, not only have very strong tearing toughness, reach 60mNm2/ more than g, and namely composite fibre wallpaper of the present invention possesses more than 2 grades fungicidal propertiess without the need to other process, also has good moisture resistance and gas permeability.
Detailed description of the invention
The invention will be further described for specific embodiment below.
Embodiment 1
A kind of composite fibre wallpaper, comprises the raw material of following masses part: cotton fiber 20, china-hemp fibers 30, sodium carboxymethylcellulose 4, isobutyl triethoxy silane 4, glycerol 12.
Manufacture the method for above-mentioned composite fibre wallpaper, manufacturing step is as follows:
1) first glycerol and isobutyl triethoxy silane are added in 10 times of 45 DEG C of water and mix, then china-hemp fibers is soaked wherein 3 hours and be incubated;
2) cotton fiber is added 1) solution in and the water adding cotton quality 35 times pull an oar 1 hour;
3) by 2) solution warms to 65 DEG C, add sodium carboxymethylcellulose wherein, continue making beating 1 hour, stir and to obtain mixing slurry;
4) last, mixing is starched through copy paper, squeezing, dries, batched obtained composite fibre wallpaper.
Detect according to GBT 24346-2009, mildew-resistant grade is 1 grade, and tearability is 63mNm2/ g.
Embodiment 2
A kind of composite fibre wallpaper, comprises the raw material of following masses part: cotton fiber 30, china-hemp fibers 15, sodium carboxymethylcellulose 5, isobutyl triethoxy silane 6, glycerol 15.
Manufacture a method for above-mentioned composite fibre wallpaper, manufacturing step is as follows:
1) first glycerol and isobutyl triethoxy silane are added in 10 times of 40 DEG C of water and mix, then china-hemp fibers is soaked wherein 3 hours and be incubated;
2) cotton fiber is added 1) solution in and the water adding cotton quality 25 times pull an oar 1 hour;
3) by 2) solution warms to 70 DEG C, add sodium carboxymethylcellulose wherein, continue making beating 1 hour, stir and to obtain mixing slurry;
4) last, mixing is starched through copy paper, squeezing, dries, batched obtained composite fibre wallpaper.
Detect according to GBT 24346-2009, mildew-resistant grade is 2 grades, and tearability is 60mNm2/ g.
Embodiment 3
A kind of composite fibre wallpaper, comprises the raw material of following masses part: cotton fiber 30, china-hemp fibers 20, sodium carboxymethylcellulose 5, isobutyl triethoxy silane 4, glycerol 15.
Manufacture a method for above-mentioned composite fibre wallpaper, manufacturing step is as follows:
1) first glycerol and isobutyl triethoxy silane are added in 10 times of 45 DEG C of water and mix, then china-hemp fibers is soaked wherein 3 hours and be incubated;
2) cotton fiber is added 1) solution in and the water adding cotton quality 35 times pull an oar 1 hour;
3) by 2) solution warms to 65 DEG C, add sodium carboxymethylcellulose wherein, continue making beating 1 hour, stir and to obtain mixing slurry;
4) last, mixing is starched through copy paper, squeezing, dries, batched obtained composite fibre wallpaper.
Detect according to GBT 24346-2009, mildew-resistant grade is 1 grade, and tearability is 72mNm2/ g.
Above embodiment is just for the object of illustrating and illustrate; instead of the present invention is limited to described embodiment; technical scheme according to the present invention is modified or replaces, and does not depart from the purpose and scope of the invention and is then all encompassed among protection scope of the present invention.