技术领域technical field
本发明涉及锅类产品生产技术领域，尤其涉及一种内嵌式发热管铝锅及其压铸成型方法。The invention relates to the technical field of production of pot products, in particular to an aluminum pot with a built-in heating tube and a die-casting method thereof.
背景技术Background technique
发热管在压铸过程中和锅一体成型，锅成型后，发热管有可能偏近或偏远于锅的内表面。如偏近于锅的内表面，此次围绕发热管的铝料偏少，使得局部过热，导致铝锅产生裂缝，以致渗漏。如发热管偏近或偏远锅的内表面，使控制锅内温度的恒温器感温有偏差，锅内温度有可能过高，产生危险。The heating pipe is integrally formed with the pot during the die-casting process. After the pot is formed, the heating pipe may be closer to or farther from the inner surface of the pot. If it is closer to the inner surface of the pot, the aluminum material surrounding the heat pipe is too small this time, which makes the local overheating, resulting in cracks in the aluminum pot, resulting in leakage. If the heat pipe is close to or remote from the inner surface of the pot, the temperature of the thermostat that controls the temperature in the pot will be deviated, and the temperature in the pot may be too high, causing danger.
发明内容Contents of the invention
本发明的目的在于针对现有技术的不足而提供一种内嵌式发热管铝锅及其压铸成型方法，使得发热管不会偏近或偏远于锅的内表面，保障了锅的质量和使用安全性能。The purpose of the present invention is to provide a built-in heat pipe aluminum pot and its die-casting molding method in view of the deficiencies in the prior art, so that the heat pipe will not be close to or far from the inner surface of the pot, and the quality and use of the pot will be guaranteed. safety performance.
为实现上述目的，本发明采用如下技术方案。In order to achieve the above object, the present invention adopts the following technical solutions.
一种内嵌式发热管铝锅，其特征在于：它包括铝锅和发热管，所述发热管套设有一个以上起到定位作用的铝环，套设有铝环的发热管与铝锅一起压铸成型为内嵌式发热管铝锅。An aluminum pot with built-in heating tube is characterized in that it includes an aluminum pot and a heating tube, the heating tube is covered with more than one aluminum ring for positioning, and the heating tube with the aluminum ring and the aluminum pot Together, they are die-cast into an aluminum pot with built-in heating tubes.
优选的，所述铝环的外圈成尖形。Preferably, the outer ring of the aluminum ring is pointed.
优选的，所述铝环的外圈比内圈薄。Preferably, the outer ring of the aluminum ring is thinner than the inner ring.
优选的，所述铝环的数量为两个。Preferably, the number of the aluminum rings is two.
一种内嵌式发热管铝锅压铸成型方法，一个以上的铝环在压铸前先套在发热管上起定位作用，再将发热管放置到钢模内进行压铸，成型为内嵌式发热管铝锅；所述铝环的外圈成尖形或铝环的外圈比内圈薄，在压铸过程中铝环的外圈能和压铸进入钢模内的高温铝水更好地融合。该方法可用于锌合金压铸。A die-casting molding method for a built-in heating tube aluminum pot. Before die-casting, more than one aluminum ring is placed on the heating tube for positioning, and then the heating tube is placed in a steel mold for die-casting to form a built-in heating tube. Aluminum pot; the outer ring of the aluminum ring is pointed or the outer ring is thinner than the inner ring, and the outer ring of the aluminum ring can better fuse with the high-temperature aluminum water that die-casts into the steel mold during the die-casting process. This method can be used for zinc alloy die casting.
本发明有益效果为：本发明所述一种内嵌式发热管铝锅及其压铸成型方法，采用定位铝环的结构，使得发热管不会偏近或偏远于锅的内表面，保障了锅的质量和使用安全性能。The beneficial effects of the present invention are as follows: the aluminum pot with built-in heat pipe and its die-casting molding method described in the present invention adopts the structure of positioning the aluminum ring, so that the heat pipe will not be close to or far away from the inner surface of the pot, which ensures that the pot quality and safety performance.
附图说明Description of drawings
图1为本发明的结构示意图。Fig. 1 is a structural schematic diagram of the present invention.
图2为本发明的发热管套设铝环的结构示意图。Fig. 2 is a schematic structural view of the aluminum ring sheathed on the heat pipe of the present invention.
图3为本发明的铝锅去掉一块料后铝环外露的示意图。Fig. 3 is a schematic diagram of the exposed aluminum ring after removing a piece of material from the aluminum pan of the present invention.
具体实施方式Detailed ways
下面结合附图对本发明作进一步的说明。The present invention will be further described below in conjunction with the accompanying drawings.
如图1至图3所示，本发明所述一种内嵌式发热管铝锅，它包括铝锅1和发热管2，所述发热管2套设有一个以上起到定位作用的铝环3，套设有铝环3的发热管2与铝锅1一起压铸成型为内嵌式发热管铝锅。优选的，所述铝环3的外圈成尖形或铝环3的外圈比内圈薄，该结构使得在压铸过程中铝环3的外圈能和压铸进入钢模内的高温铝水更好地融合。优选的，所述铝环3的数量为两个，或根据需要设定具体个数。优选的，所述铝环3从外表面至内部开设有若干个沉孔，多个沉孔不规则的分散于铝环3的不同位置，压铸过程中高温铝水可渗透入沉孔内，使得铝环3起到更好的定位作用。As shown in Figures 1 to 3, an aluminum pot with built-in heating pipes according to the present invention includes an aluminum pot 1 and a heating pipe 2, and the heating pipe 2 is provided with more than one aluminum ring for positioning. 3. The heat pipe 2 with the aluminum ring 3 and the aluminum pot 1 are die-casted together to form a built-in heat pipe aluminum pot. Preferably, the outer ring of the aluminum ring 3 is pointed or the outer ring of the aluminum ring 3 is thinner than the inner ring. This structure enables the outer ring of the aluminum ring 3 to be closer to the high-temperature aluminum water that is die-cast into the steel mold during the die-casting process. Blends well. Preferably, the number of the aluminum rings 3 is two, or a specific number can be set as required. Preferably, the aluminum ring 3 is provided with several counterbores from the outer surface to the inside, and the plurality of counterbores are irregularly scattered in different positions of the aluminum ring 3, and high-temperature aluminum water can penetrate into the counterbores during the die-casting process, so that The aluminum ring 3 plays a better positioning role.
本发明所述一种内嵌式发热管铝锅压铸成型方法，一个以上的铝环3在压铸前先套在发热管2上起定位作用，再将发热管2放置到钢模内进行压铸，成型为内嵌式发热管铝锅；所述铝环3的外圈成尖形或铝环3的外圈比内圈薄，在压铸过程中铝环3的外圈能和压铸进入钢模内的高温铝水更好地融合。进一步的，铝环3从外表面至内部开设有若干个沉孔，多个沉孔不规则的分散于铝环3的不同位置，压铸过程中高温铝水可渗透入沉孔内，使得铝环3起到更好的定位作用。该方法也可用于锌合金压铸。According to the die-casting molding method of the built-in heat pipe aluminum pot according to the present invention, more than one aluminum ring 3 is set on the heat pipe 2 for positioning before die-casting, and then the heat pipe 2 is placed in the steel mold for die-casting. Formed into an aluminum pot with built-in heat pipe; the outer ring of the aluminum ring 3 is pointed or the outer ring of the aluminum ring 3 is thinner than the inner ring, and the outer ring of the aluminum ring 3 can be compared with the die-casting into the steel mold during the die-casting process. High temperature aluminum water blends better. Further, the aluminum ring 3 is provided with several counterbores from the outer surface to the inside, and the plurality of counterbores are irregularly scattered in different positions of the aluminum ring 3. During the die-casting process, high-temperature aluminum water can penetrate into the counterbores, making the aluminum ring 3 Play a better positioning role. This method can also be used for zinc alloy die casting.
综上所述，本发明所述一种内嵌式发热管铝锅及其压铸成型方法，采用定位铝环的结构，使得发热管2不会偏近或偏远于铝锅1的内表面，保障了锅的质量和使用安全性能。To sum up, the aluminum pot with built-in heating tube and its die-casting molding method described in the present invention adopts the structure of positioning the aluminum ring, so that the heating tube 2 will not be close to or far from the inner surface of the aluminum pot 1, ensuring The quality and safety performance of the pot are guaranteed.
以上所述仅是本发明的较佳实施方式，故凡依本发明专利申请范围所述的构造、特征及原理所做的等效变化或修饰，均包括于本发明专利申请范围内。The above is only a preferred embodiment of the present invention, so all equivalent changes or modifications made according to the structure, features and principles described in the scope of the patent application of the present invention are included in the scope of the patent application of the present invention.
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| CN201410611273.XACN104367172A (en) | 2014-11-04 | 2014-11-04 | A kind of built-in heat pipe aluminum pot and its die-casting method |
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| CN201410611273.XACN104367172A (en) | 2014-11-04 | 2014-11-04 | A kind of built-in heat pipe aluminum pot and its die-casting method |
| Publication Number | Publication Date |
|---|---|
| CN104367172Atrue CN104367172A (en) | 2015-02-25 |
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| CN201410611273.XAPendingCN104367172A (en) | 2014-11-04 | 2014-11-04 | A kind of built-in heat pipe aluminum pot and its die-casting method |
| Country | Link |
|---|---|
| CN (1) | CN104367172A (en) |
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| CN108746536A (en)* | 2018-06-07 | 2018-11-06 | 昆山巨石新能源科技有限公司 | The integrated die-casting method of cavity wall water pipe head |
| CN110944772A (en)* | 2017-07-28 | 2020-03-31 | 马瑞利株式会社 | Casting mold and method for manufacturing casting |
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US1778808A (en)* | 1928-05-09 | 1930-10-21 | Griswold Mfg Company | Method of forming electric heater plates |
| GB1095816A (en)* | 1965-01-18 | 1967-12-20 | Hoover Ltd | Improvements relating to the casting of laminated metal articles |
| CN2148921Y (en)* | 1992-09-30 | 1993-12-08 | 佛山市家用电器五厂 | Heating device for automatic electric water heater |
| CN101352753A (en)* | 2007-07-26 | 2009-01-28 | 厉正 | Cast die tool of multi-bottom pan and technique for producing multi-bottom pan using the die |
| US20130175007A1 (en)* | 2012-01-09 | 2013-07-11 | Cooler Master Co., Ltd. | Heat-conducting module and method for manufacturing the same |
| CN203314783U (en)* | 2013-05-08 | 2013-12-04 | 胡岳安 | Multifunctional electric oven |
| CN204292881U (en)* | 2014-11-04 | 2015-04-29 | 东莞清溪华晖电器有限公司 | A kind of embedded heat-generating pipe aluminum pot |
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US1778808A (en)* | 1928-05-09 | 1930-10-21 | Griswold Mfg Company | Method of forming electric heater plates |
| GB1095816A (en)* | 1965-01-18 | 1967-12-20 | Hoover Ltd | Improvements relating to the casting of laminated metal articles |
| CN2148921Y (en)* | 1992-09-30 | 1993-12-08 | 佛山市家用电器五厂 | Heating device for automatic electric water heater |
| CN101352753A (en)* | 2007-07-26 | 2009-01-28 | 厉正 | Cast die tool of multi-bottom pan and technique for producing multi-bottom pan using the die |
| US20130175007A1 (en)* | 2012-01-09 | 2013-07-11 | Cooler Master Co., Ltd. | Heat-conducting module and method for manufacturing the same |
| CN203314783U (en)* | 2013-05-08 | 2013-12-04 | 胡岳安 | Multifunctional electric oven |
| CN204292881U (en)* | 2014-11-04 | 2015-04-29 | 东莞清溪华晖电器有限公司 | A kind of embedded heat-generating pipe aluminum pot |
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| CN110944772A (en)* | 2017-07-28 | 2020-03-31 | 马瑞利株式会社 | Casting mold and method for manufacturing casting |
| CN108746536A (en)* | 2018-06-07 | 2018-11-06 | 昆山巨石新能源科技有限公司 | The integrated die-casting method of cavity wall water pipe head |
| Publication | Publication Date | Title |
|---|---|---|
| CN104367172A (en) | A kind of built-in heat pipe aluminum pot and its die-casting method | |
| MX2018013170A (en) | Ablation casting process. | |
| CN202752591U (en) | Molten steel test sample demolding device | |
| CN104289694A (en) | Pressure casting mold pouring gate bushing | |
| CN204194755U (en) | A kind of pouring bushing for die casting die | |
| CN105499490B (en) | A wax melting pool for lost foam of precision castings | |
| CN205056948U (en) | An electric dewaxing pool | |
| CN204292881U (en) | A kind of embedded heat-generating pipe aluminum pot | |
| CN106270397A (en) | The production technology of copper-casting water jacket is watered, for the core rod of production technology and prepared cast without pipe laying | |
| CN205393483U (en) | Compound crystallizer for titanium -nickel alloy continuous casting | |
| RU2017126680A (en) | METHOD FOR PRODUCING DETAILS PERFORMED FROM LOW SILICON ALUMINUM ALLOY | |
| CN103934438B (en) | Method for casting large and thick steel castings by using internal chill | |
| CN204381340U (en) | Vacuum pressing and casting electronic appliance mold aluminium alloy castings built-in pipe fixing tool | |
| RU2455107C1 (en) | Method of fabricating protectors | |
| CN208483211U (en) | A kind of stalk flange heating device | |
| CN203804055U (en) | Drawing die capable of improving cooling effect | |
| RU2463128C1 (en) | Method of fabricating protectors | |
| CN210160364U (en) | Horizontal continuous casting device of brass brazing filler metal | |
| CN204298443U (en) | Cross strainer | |
| CN104588619B (en) | Vacuum casting electronic appliance mold aluminum alloy casting buries effective frozen iron blocks in advance | |
| CN206326078U (en) | One kind penetrates was moulding device | |
| CN204461812U (en) | A kind of Combinative pattern cup | |
| CN103212686B (en) | A kind of crystallizing wheel thermometer liquid level regulation device | |
| RU2011141762A (en) | CAST CASING WITH INTEGRATED PIPELINES | |
| CN102380606A (en) | Die casting of iron ingot |
| Date | Code | Title | Description |
|---|---|---|---|
| C06 | Publication | ||
| PB01 | Publication | ||
| C10 | Entry into substantive examination | ||
| SE01 | Entry into force of request for substantive examination | ||
| RJ01 | Rejection of invention patent application after publication | ||
| RJ01 | Rejection of invention patent application after publication | Application publication date:20150225 |