CN103181613A - Preparation method of electric dry distillation type tobacco sheet - Google Patents
Preparation method of electric dry distillation type tobacco sheetDownload PDFInfo
- Publication number
- CN103181613A CN103181613ACN2013101230504ACN201310123050ACN103181613ACN 103181613 ACN103181613 ACN 103181613ACN 2013101230504 ACN2013101230504 ACN 2013101230504ACN 201310123050 ACN201310123050 ACN 201310123050ACN 103181613 ACN103181613 ACN 103181613A
- Authority
- CN
- China
- Prior art keywords
- tobacco
- reconstituted tobacoo
- extract
- sheet base
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Translated fromChineseDescription
Translated fromChinese技术领域technical field
本发明涉及一种烟草薄片的制备方法，具体地说是一种电干馏型烟草薄片的制备方法。The invention relates to a preparation method of tobacco sheet, in particular to a preparation method of electric dry distillation type tobacco sheet.
背景技术Background technique
烟草薄片是指烟厂将包括打叶工序在内的卷烟制造过程中的烟草废弃料如烟末、烟梗、烟叶碎片、低次烟叶等烟草废弃料作为原料，经过重新组合加工而成的再生烟叶。传统再生烟草薄片是将再生烟叶经过加工与烟草掺配加工方式，卷制成卷烟，可以提高烟叶原料的利用率。由于干馏型卷烟所需要的烟草薄片材质要有一定的厚度，能够浸润一定浓度的香精香料和甘油等易挥发性的物质。而一般工艺生产的烟草薄片，再生烟草薄片的片基厚度以及添加的浓缩物都不能够满足电干馏型卷烟的需求，Tobacco sheet refers to the tobacco waste materials such as tobacco dust, tobacco stems, tobacco leaf fragments, low-grade tobacco leaves and other tobacco waste materials in the cigarette manufacturing process including the leaf threshing process as raw materials, which are recombined and processed. tobacco leaf. The traditional reconstituted tobacco sheet is processed by blending reconstituted tobacco leaves with tobacco, and rolled into cigarettes, which can improve the utilization rate of tobacco leaf raw materials. Because the tobacco sheet material required by dry distillation type cigarettes has a certain thickness, it can infiltrate volatile substances such as flavors and fragrances and glycerin of a certain concentration. However, the tobacco sheet produced by the general process, the base thickness of the regenerated tobacco sheet, and the added concentrate cannot meet the needs of electric dry distillation cigarettes.
发明内容Contents of the invention
本发明的目的是根据现有技术的不足提供一种电干馏型烟草薄片的制备方法，用该制备方法的制备得到的电干馏型烟草薄片具有一定的厚度，可以在较低的温度下，通过较低的电干馏的温度干馏出烟草薄片中添加的香精香料和一些易挥发的香味物质，满足电干馏型卷烟的需要。The object of the present invention is to provide a method for preparing electric dry distillation tobacco sheet according to the deficiencies of the prior art. The electric dry distillation tobacco sheet prepared by the preparation method has a certain thickness and can be passed through The lower electric distillation temperature dry-distills the flavors and fragrances and some volatile flavor substances added in the tobacco sheet to meet the needs of electric dry distillation cigarettes.
本发明是通过如下技术方案实现的：一种电干馏型烟草薄片的制备方法，其步骤包括：（1）将烟草提取物和天然植物提取物中的一种或多种混合得到片基喷涂物；（2）再将片基喷涂物均匀涂布在重量为片基喷涂物1-10倍的烟草薄片片基上然后在40-90℃下干燥；（3）然后按照重量百分数为20-75%的丙二醇、10-45%的甘油、1-10%的去离子水、1-10%的酒精、1-10%的烟用香精和1-10%的烟草提取物混合得到雾化剂香料，将烟草薄片片基重量的2-50%的雾化剂香料喷洒在干燥好的烟草薄片片基上；这是由于电干馏卷烟的温度较低，达不到卷烟燃烧的600℃以上，在抽吸的时候，烟草薄片不能燃烧，需要通过加热将烟草制品中的香味物质干馏出来，为了模拟烟草燃烧过程的的烟雾效果，需要辅助的添加一些雾化剂香料，便于产生可见的烟雾；（4）最后将烟草薄片片基干燥后得到所述电干馏型烟草薄片。The present invention is achieved through the following technical scheme: a preparation method of electric dry distillation tobacco sheet, the steps of which include: (1) mixing one or more of tobacco extract and natural plant extract to obtain a base spray (2) Evenly coat the base spray on the tobacco sheet base with a weight of 1-10 times that of the base spray and then dry it at 40-90°C; % propylene glycol, 10-45% glycerin, 1-10% deionized water, 1-10% alcohol, 1-10% tobacco essence and 1-10% tobacco extract are mixed to obtain aerosol flavor , spray 2-50% of the tobacco sheet base weight of the atomizer flavor on the dried tobacco sheet base; When smoking, the tobacco flakes cannot be burned, and the aroma substances in the tobacco products need to be dry-distilled by heating. In order to simulate the smoke effect of the tobacco burning process, it is necessary to add some atomizer spices to facilitate the generation of visible smoke; ( 4) Finally, the tobacco sheet base is dried to obtain the electric dry distillation tobacco sheet.
优选的，所述烟草薄片片基厚度为0.1-0.5mm。Preferably, the base thickness of the tobacco sheet is 0.1-0.5 mm.
更优选的，所述烟草薄片片基厚度为0.2-0.4mm。More preferably, the base thickness of the tobacco sheet is 0.2-0.4mm.
所述烟草提取物为晾晒烟提取物、香料烟提取物、烤烟提取物、白肋烟提取物、雪茄烟提取物以及烟草废弃料提取物中的一种或多种提取物。所述的烟草提取物可以进行单独提取，主要是为了协调加工好的烟草薄片的口味，具体的实际需求根据实际进行调配。The tobacco extract is one or more extracts of air-cured tobacco extract, oriental tobacco extract, flue-cured tobacco extract, Burley tobacco extract, cigar tobacco extract and tobacco waste extract. The tobacco extract can be extracted separately, mainly for the purpose of coordinating the taste of the processed tobacco flakes, and it can be formulated according to the specific actual needs.
所述烟草提取物通过如下方式中的一种提取：（1）将烟草和质量百分数为95%的乙醇按照质量比烟草：乙醇=1:2-5混合，优选为1：3，浸泡在室温干燥处1周，再过滤在50℃以下浓缩得到烟草提取物，该方法该方法浸泡出的成分主要为一些轻组分，保持烟草轻组分的吸味；（2）将烟草和质量百分数为75%的乙醇按照质量比烟草：乙醇=1:2-5混合，优选为1：3，浸泡在室温干燥处1周，再过滤在50℃以下浓缩得到烟草提取物，该方法浸泡出的成分主要为一些轻组分，保持烟草轻组分中较大极性物质的吸味；（3）将烟草和质量百分数为95%的乙醇按照质量比烟草：乙醇=1:1-4混合，优选为1：2，加热回流1-4小时，优选2小时，再过滤在50℃以下浓缩得到烟草提取物，该方法能够较大程度的提取烟草中的醇溶性物质，较高的温度提取对烟草轻组分中易挥发的物质造成损失；（4）将烟草和质量百分数为75%的乙醇按照质量比烟草：乙醇=1:1-4混合，优选为1：2，加热回流1-4小时，优选2小时，再过滤在50℃以下浓缩得到烟草提取物，该方法能够较大程度的提取烟草中的较大极性物质，较高的温度提取对烟草轻组分中易挥发的物质造成损失。The tobacco extract is extracted by one of the following methods: (1) mix tobacco and ethanol with a mass percentage of 95% according to the mass ratio of tobacco: ethanol = 1:2-5, preferably 1:3, soak at room temperature Dry for 1 week, then filter and concentrate below 50°C to obtain tobacco extract. The components soaked by this method are mainly some light components to keep the smoking flavor of tobacco light components; (2) the tobacco and the mass percentage are 75% ethanol is mixed according to the mass ratio of tobacco: ethanol = 1:2-5, preferably 1:3, soaked in a dry place at room temperature for 1 week, then filtered and concentrated below 50°C to obtain tobacco extract, the ingredients soaked by this method Mainly some light components, to keep the taste of relatively large polar substances in the light components of tobacco; (3) Mix tobacco and ethanol with a mass percentage of 95% according to the mass ratio of tobacco: ethanol = 1:1-4, preferably 1:2, heat and reflux for 1-4 hours, preferably 2 hours, then filter and concentrate below 50°C to obtain tobacco extract. The volatile substances in the light component cause loss; (4) Mix tobacco and ethanol with a mass percentage of 75% according to the mass ratio of tobacco: ethanol = 1:1-4, preferably 1:2, and heat and reflux for 1-4 hours , preferably 2 hours, and then filter and concentrate below 50°C to obtain tobacco extract. This method can extract relatively large polar substances in tobacco to a greater extent, and extraction at a higher temperature will cause damage to volatile substances in tobacco light components. loss.
所述步骤（4）中最后将烟草薄片片基干燥是指在25℃下阴凉干燥处放置2小时。The final drying of the tobacco sheet base in the step (4) refers to placing it in a cool and dry place at 25°C for 2 hours.
所述步骤（1）中干燥好的烟草薄片片基上片基喷涂物含量为150-250g/m2，厚度为0.3-0.4mm，水分的含量为10-12%。In the step (1), the dried tobacco sheet base has a content of 150-250 g/m2 of spray coating on the base, a thickness of 0.3-0.4 mm, and a moisture content of 10-12%.
优选的，所述步骤（1）中将片基喷涂物均匀涂布在重量为片基喷涂物2-8倍的烟草薄片片基上。Preferably, in the step (1), the base spray is evenly coated on the tobacco sheet base whose weight is 2-8 times that of the base spray.
优选的，所述步骤（3）中是将烟草薄片片基重量的5-45%的雾化剂香料喷洒在烟草薄片片基上。Preferably, in the step (3), 5-45% of the weight of the tobacco sheet base is sprayed on the tobacco sheet base with an aerosol spice.
所述步骤（3）中的烟用香精包括天然香料或人工合成香料。如：烃类、醇类、醚类、酚类、含硫化合物、挥发性胺类、醛类、酮类、羧酸类、内酯类或杂环化合物类。The tobacco flavor in the step (3) includes natural flavors or artificial flavors. Such as: hydrocarbons, alcohols, ethers, phenols, sulfur compounds, volatile amines, aldehydes, ketones, carboxylic acids, lactones or heterocyclic compounds.
一种电干馏型烟草薄片的制备方法优选技术方案为：其步骤包括：（1）将烟草提取物和天然植物提取物中的一种或多种混合得到片基喷涂物；（2）再将片基喷涂物均匀涂布在重量为片基喷涂物2-8倍的烟草薄片片基上然后在50-70℃下干燥，得到的烟草薄片片基上片基喷涂物含量为150-250g/m2，厚度为0.3-0.4mm，水分的含量为10-12%；（3）然后按照重量百分数为20-75%的丙二醇、10-45%的甘油、1-10%的去离子水、1-10%的酒精、1-10%的烟用香精和1-10%的烟草提取物混合得到雾化剂香料，将烟草薄片片基重量的5-45%的雾化剂香料喷洒在干燥好的烟草薄片片基上；（4）最后将烟草薄片片基在25℃下阴凉干燥处放置2小时，干燥后得到所述电干馏型烟草薄片。A preferred technical solution for the preparation method of electric dry distillation tobacco sheet is as follows: the steps include: (1) mixing one or more of tobacco extracts and natural plant extracts to obtain a base spray; (2) adding The substrate sprayed material is uniformly coated on the tobacco sheet base whose weight is 2-8 times that of the base sprayed material, and then dried at 50-70°C, and the content of the obtained tobacco sheet base sprayed material is 150-250g/ m2 , the thickness is 0.3-0.4mm, and the water content is 10-12%; (3) Then, according to the weight percentage, it is 20-75% propylene glycol, 10-45% glycerin, 1-10% deionized water, 1-10% alcohol, 1-10% tobacco essence and 1-10% tobacco extract are mixed to obtain an aerosol flavor, and 5-45% of the tobacco sheet basis weight is sprayed on a dry (4) Finally, place the tobacco sheet base in a cool and dry place at 25° C. for 2 hours, and obtain the electric dry distillation tobacco sheet after drying.
本发明提供的电干馏型烟草薄片的制备方法制备出的烟草薄片，能够在电干馏装置中燃烧而产生烟雾。电干馏的方式能够干馏出烟草提取物包含的烟草本香。该种薄片制备工艺制备的薄片具有烟草本香与烟用香精香料浑然一体。满足消费的需求，降低卷烟燃烧对消费者的危害，避免二手烟的产生，具有很强的实用性。The tobacco sheet prepared by the method for preparing electric dry distillation tobacco sheet provided by the present invention can be burned in an electric dry distillation device to generate smoke. The method of electric dry distillation can dry distill the tobacco aroma contained in the tobacco extract. The sheet prepared by the thin sheet preparation process has the natural tobacco flavor and tobacco essence and fragrance in one. It is very practical to meet the needs of consumption, reduce the harm of cigarette burning to consumers, and avoid the generation of second-hand smoke.
具体实施方式Detailed ways
以下通过具体实施例来进一步说明本发明：The present invention is further illustrated below by specific examples:
实施例1Example 1
（1）称取烤烟烟叶100g，加入95%乙醇300g，放在室温下浸泡1周。然后过滤掉烟叶，50℃以下浓缩，得到烟草提取物。(1) Weigh 100g of flue-cured tobacco leaves, add 300g of 95% ethanol, and soak at room temperature for 1 week. Then filter out the tobacco leaves and concentrate below 50°C to obtain tobacco extract.
（2）将提取后的烟草提取物涂布在厚度为0.2mm的烟草薄片片基上，每100g烟草提取物涂布烟草薄片片基400g，在40℃下干燥，得到烟草薄片片基喷涂物含量为200g/m2，厚度为0.35mm，水分含量为11%。(2) Coat the extracted tobacco extract on the tobacco sheet base with a thickness of 0.2mm, coat 400g of the tobacco sheet base per 100g of tobacco extract, and dry at 40°C to obtain the tobacco sheet base spray The content is 200g/m2 , the thickness is 0.35mm, and the moisture content is 11%.
（3）按重量百分数为：丙二醇65%，甘油15%，去离子水3%，酒精5%，天然香料6%，烟草提取物6%混合得到雾化剂香料。然后将雾化剂香料喷洒在已经涂布烟草提取物的烟草薄片片基上，涂布量为100g烟草薄片片基喷洒雾化剂香料的量为15g，即15%的雾化剂香料的量。(3) Percentage by weight: 65% propylene glycol, 15% glycerin, 3% deionized water, 5% alcohol, 6% natural flavor, and 6% tobacco extract are mixed to obtain an atomizer flavor. Then the atomizing agent spice is sprayed on the tobacco sheet base that has been coated with tobacco extract, and the coating amount is 100g tobacco sheet base spraying the amount of atomizer spice being 15g, i.e. the amount of 15% atomizer spice .
（4）将喷洒雾化剂的烟草薄片片基在25℃下阴凉干燥处放置2小时，可以保证雾化剂较好的浸润到烟草薄片中，得到电干馏型烟草薄片1。(4) The tobacco sheet base sprayed with the atomizing agent is placed in a cool and dry place at 25°C for 2 hours to ensure that the atomizing agent is well infiltrated into the tobacco sheet, and the electric dry distillation type tobacco sheet 1 is obtained.
实施例2Example 2
（1）称取晾晒烟烟叶100g，加入75%乙醇200g，放在室温下浸泡1周。然后过滤掉烟叶，50℃以下浓缩，得到烟草提取物。(1) Weigh 100g of air-cured tobacco leaves, add 200g of 75% ethanol, and soak at room temperature for 1 week. Then filter out the tobacco leaves and concentrate below 50°C to obtain tobacco extract.
（2）将提取后的烟草提取物涂布在厚度为0.1mm的烟草薄片片基上，每100g烟草提取物涂布烟草薄片片基100g，在50℃下干燥，得到烟草薄片片基喷涂物含量为250g/m2，厚度为0.3mm，水分含量为10%。(2) Coat the extracted tobacco extract on the tobacco sheet base with a thickness of 0.1mm, coat 100g of the tobacco sheet base per 100g of tobacco extract, and dry at 50°C to obtain the tobacco sheet base spray The content is 250g/m2 , the thickness is 0.3mm, and the moisture content is 10%.
（3）按重量百分数为：丙二醇75%，甘油10%，去离子水1%，酒精10%，人工合成香料1%，烟草提取物5%混合得到雾化剂香料。然后将雾化剂香料喷洒在已经涂布烟草提取物的烟草薄片片基上，涂布量为100g烟草薄片片基喷洒雾化剂香料的量为50g，即50%的雾化剂香料的量。(3) Percentage by weight: 75% propylene glycol, 10% glycerin, 1% deionized water, 10% alcohol, 1% artificial flavor, and 5% tobacco extract are mixed to obtain an atomizer flavor. Then the atomizing agent spice is sprayed on the tobacco sheet base that has been coated with tobacco extract, and the coating amount is 100g tobacco sheet base spraying the amount of atomizer spice being 50g, i.e. the amount of 50% atomizer spice .
（4）将喷洒雾化剂的烟草薄片片基在25℃下阴凉干燥处放置2小时，可以保证雾化剂较好的浸润到烟草薄片中，得到电干馏型烟草薄片2。(4) The tobacco sheet base sprayed with the atomizing agent is placed in a cool and dry place at 25°C for 2 hours to ensure that the atomizing agent is well infiltrated into the tobacco sheet, and the electric carbonization type tobacco sheet 2 is obtained.
实施例3Example 3
（1）称取白肋烟烟叶100g，加入95%乙醇200g，加热冷凝回流条件下萃取1-4小时。然后过滤掉烟叶，50℃以下浓缩，得到烟草提取物。(1) Weigh 100g of Burley tobacco leaves, add 200g of 95% ethanol, and extract for 1-4 hours under the condition of heating, condensing and reflux. Then filter out the tobacco leaves and concentrate below 50°C to obtain tobacco extract.
（2）将提取后的烟草提取物涂布在厚度为0.4mm的烟草薄片片基上，每100g烟草提取物涂布烟草薄片片基1000g，在70℃下干燥，得到烟草薄片片基喷涂物含量为150g/m2，厚度为0.4mm，水分含量为12%。(2) Coat the extracted tobacco extract on the tobacco sheet base with a thickness of 0.4mm, coat 1000g of the tobacco sheet base per 100g of tobacco extract, and dry at 70°C to obtain the tobacco sheet base spray The content is 150g/m2 , the thickness is 0.4mm, and the moisture content is 12%.
（3）按重量百分数为：丙二醇20%，甘油45%，去离子水10%，酒精5%，天然香料10%，烟草提取物10%混合得到雾化剂香料。然后将雾化剂香料喷洒在已经涂布烟草提取物的烟草薄片片基上，涂布量为100g烟草薄片片基喷洒雾化剂香料的量为2g，即2%的雾化剂香料的量。(3) Percentage by weight: 20% propylene glycol, 45% glycerin, 10% deionized water, 5% alcohol, 10% natural flavor, and 10% tobacco extract are mixed to obtain an atomizer flavor. Then the atomizing agent flavoring is sprayed on the tobacco sheet base that has been coated with tobacco extract, and the coating amount is that the amount of spraying the atomizing agent flavoring on the 100g tobacco sheet base is 2g, i.e. the amount of 2% atomizing agent flavoring .
（4）将喷洒雾化剂的烟草薄片片基在25℃下阴凉干燥处放置2小时，可以保证雾化剂较好的浸润到烟草薄片中，得到电干馏型烟草薄片3。(4) The tobacco sheet base sprayed with the atomizing agent is placed in a cool and dry place at 25°C for 2 hours to ensure that the atomizing agent is well infiltrated into the tobacco sheet, and the electric dry distillation type tobacco sheet 3 is obtained.
实施例4Example 4
（1）称取白肋烟烟叶和香料烟烟叶共100g，加入75%乙醇200g，加热冷凝回流条件下萃取1-4小时。然后过滤掉烟叶，50℃以下浓缩，得到烟草提取物。(1) Weigh 100 g of Burley tobacco leaves and oriental tobacco leaves in total, add 200 g of 75% ethanol, and extract under heating, condensing and reflux conditions for 1-4 hours. Then filter out the tobacco leaves and concentrate below 50°C to obtain tobacco extract.
（2）将提取后的烟草提取物涂布在厚度为0.5mm的烟草薄片片基上，每100g烟草提取物涂布烟草薄片片基200g，在90℃下干燥，得到烟草薄片片基喷涂物含量为200g/m2，厚度为0.4mm，水分含量为12%。(2) Coat the extracted tobacco extract on the tobacco sheet base with a thickness of 0.5mm, coat 200g of the tobacco sheet base per 100g of tobacco extract, and dry at 90°C to obtain the sprayed tobacco sheet base The content is 200g/m2 , the thickness is 0.4mm, and the moisture content is 12%.
（3）按重量百分数为：丙二醇58%，甘油30%，去离子水5%，酒精1%，人工合成香料5%，烟草提取物1%混合得到雾化剂香料。然后将雾化剂香料喷洒在已经涂布烟草提取物的烟草薄片片基上，涂布量为100g烟草薄片片基喷洒雾化剂香料的量为45g，即45%的雾化剂香料的量。(3) Percentage by weight: 58% propylene glycol, 30% glycerin, 5% deionized water, 1% alcohol, 5% artificial flavor, and 1% tobacco extract are mixed to obtain an atomizer flavor. Then the atomizing agent spice is sprayed on the tobacco sheet base that has been coated with tobacco extract, and the coating amount is that the amount of spraying atomizer spice on the 100g tobacco sheet base is 45g, i.e. the amount of 45% atomizer spice .
（4）将喷洒雾化剂的烟草薄片片基在25℃下阴凉干燥处放置2小时，可以保证雾化剂较好的浸润到烟草薄片中，得到电干馏型烟草薄片4。(4) The tobacco sheet base sprayed with the atomizing agent is placed in a cool and dry place at 25°C for 2 hours to ensure that the atomizing agent is well infiltrated into the tobacco sheet, and the electric dry distillation type tobacco sheet 4 is obtained.
实施例5Example 5
（1）称取雪茄烟烟叶和烟草废弃料共100g，加入75%乙醇200g，加热冷凝回流条件下萃取1-4小时。然后过滤掉烟叶，50℃以下浓缩，得到烟草提取物。(1) Weigh 100g of cigar tobacco leaves and tobacco waste in total, add 200g of 75% ethanol, and extract under heating, condensing and reflux conditions for 1-4 hours. Then filter out the tobacco leaves and concentrate below 50°C to obtain tobacco extract.
（2）将提取后的烟草提取物涂布在厚度为0.5mm的烟草薄片片基上，每100g烟草提取物涂布烟草薄片片基200g，在90℃下干燥，得到烟草薄片片基喷涂物含量为200g/m2，厚度为0.4mm，水分含量为12%。(2) Coat the extracted tobacco extract on the tobacco sheet base with a thickness of 0.5mm, coat 200g of the tobacco sheet base per 100g of tobacco extract, and dry at 90°C to obtain the sprayed tobacco sheet base The content is 200g/m2 , the thickness is 0.4mm, and the moisture content is 12%.
（3）按重量百分数为：丙二醇58%，甘油30%，去离子水5%，酒精1%，烟用香精5%，烟草提取物1%混合得到雾化剂香料。然后将雾化剂香料喷洒在已经涂布烟草提取物的烟草薄片片基上，涂布量为100g烟草薄片片基喷洒雾化剂香料的量为45g，即45%的雾化剂香料的量。(3) Percentage by weight: 58% propylene glycol, 30% glycerin, 5% deionized water, 1% alcohol, 5% tobacco essence, and 1% tobacco extract are mixed to obtain an atomizer fragrance. Then the atomizing agent spice is sprayed on the tobacco sheet base that has been coated with tobacco extract, and the coating amount is that the amount of spraying atomizer spice on the 100g tobacco sheet base is 45g, i.e. the amount of 45% atomizer spice .
（4）将喷洒雾化剂的烟草薄片片基在25℃下阴凉干燥处放置2小时，可以保证雾化剂较好的浸润到烟草薄片中，得到电干馏型烟草薄片5。(4) The tobacco sheet base sprayed with the atomizing agent is placed in a cool and dry place at 25°C for 2 hours to ensure that the atomizing agent is well infiltrated into the tobacco sheet, and the electric carbonization type tobacco sheet 5 is obtained.
实施例6Example 6
（1）称取烤烟烟叶100g，加入95%乙醇300g，放在室温下浸泡1周。然后过滤掉烟叶，在50℃以下浓缩，得到烟草提取物(1) Weigh 100g of flue-cured tobacco leaves, add 300g of 95% ethanol, and soak at room temperature for 1 week. The tobacco leaves are then filtered and concentrated below 50°C to obtain tobacco extract
称取雪茄烟烟叶100g，加入95%乙醇200g，加热冷凝回流条件下萃取2小时，冷却、过滤掉烟叶，在50℃以下浓缩，得到一定浓度的浸泡烤烟烟草提取物，备用。Weigh 100g of cigar tobacco leaves, add 200g of 95% ethanol, extract under heating and condensing reflux for 2 hours, cool, filter out the tobacco leaves, concentrate below 50°C to obtain a certain concentration of soaked flue-cured tobacco extract, and set aside.
（2）将两种提取方法的烟草提取物按照1:1的比例调配后，涂布在烟草薄片片基上，每100g烟草提取物涂布烟草薄片400g，在70℃下干燥，得到烟草薄片片基喷涂物含量为200g/m2，厚度为0.4mm，水分含量为11%。(2) After blending the tobacco extracts of the two extraction methods according to the ratio of 1:1, they are coated on the base of the tobacco sheet, and 400g of the tobacco sheet is coated with each 100g of tobacco extract, and dried at 70°C to obtain the tobacco sheet The content of sprayed matter on the film base is 200g/m2 , the thickness is 0.4mm, and the moisture content is 11%.
（3）按重量百分数为：丙二醇58%，甘油30%，去离子水5%，酒精1%，烟用香精5%，烟草提取物1%混合得到雾化剂香料。然后将雾化剂香料喷洒在已经涂布烟草提取物的烟草薄片片基上，涂布量为100g烟草薄片片基喷洒雾化剂香料的量为45g，即45%的雾化剂香料的量。(3) Percentage by weight: 58% propylene glycol, 30% glycerin, 5% deionized water, 1% alcohol, 5% tobacco essence, and 1% tobacco extract are mixed to obtain an atomizer fragrance. Then the atomizing agent spice is sprayed on the tobacco sheet base that has been coated with tobacco extract, and the coating amount is that the amount of spraying atomizer spice on the 100g tobacco sheet base is 45g, i.e. the amount of 45% atomizer spice .
（4）将喷洒雾化剂的烟草薄片片基在25℃下阴凉干燥处放置2小时，可以保证雾化剂较好的浸润到烟草薄片中，得到电干馏型烟草薄片6。(4) The tobacco sheet base sprayed with the atomizing agent is placed in a cool and dry place at 25°C for 2 hours to ensure that the atomizing agent is well infiltrated into the tobacco sheet, and the electric carbonization type tobacco sheet 6 is obtained.
将上述烟草薄片切丝后放置在电干馏装置中进行感官和雾化量评价，得到的结果如表1所示。The above-mentioned tobacco thin slices were shredded and placed in an electric dry distillation device for sensory evaluation and atomization evaluation. The results are shown in Table 1.
表1 烟草薄片在电干馏装置中的感官和雾化量评价Table 1 Sensory and atomization evaluation of tobacco sheet in electric dry distillation device
从上述评价可以看出，本发明方法制备得到的电干馏型烟草薄片感官效果好。It can be seen from the above evaluation that the electric dry distillation tobacco sheet prepared by the method of the present invention has a good sensory effect.
Claims (10)