This is a division of Canadian application serial no. 461,817 filed August 24, 1984.
BACKGROUND AND SUGARY OF THE INVENTION
The present invention relates to a method of texturing a mold surface to provide a desired pattern on a molded article and, more specifically, to a molded article made with a treated mold surface where the molded article is bonded to a masonry unit and the surface of the molded material is patterned to provide a distinctive surface to the masonry unit.
In the past, molded plastic articles have been provided with a variety of surface textures by treating the mold in which the articles are formed. In addition, in the manufacture of molded articles, texturing of the surface of a resulting product has often been accomplished by treating the surface of the article after it has been molded such as by chemical etching, mechanical deformation or the like. While the foregoing procedures have been useful for a number of types of molded articles, where the molded article is employed in a building construction as a wall surface, conventional texturing techniques have been difficult to employ particularly where pigments have been included in the mold composition and where the mold composition includes a substantial quantity of a I
polymerizable resin such as polyester or an epoxy resin. In the mass production of discrete articles wherein each article is provided with a molded surface, it is impractical as a manufacturing expedient to individually treat an article once it has been molded as this appreciably affects the manufacturing cost. In addition, individual handling of articles after they have been molded can all too easily result in non-uniformities in the product as a consequence of the processing steps required subsequent to curing of the article in the mold.
Accordingly, it is an object of the present invention to provide a method of preparing a mold surface so that, in the course of molding an article, the mold will form a pattern on the molded article surface at the same time the article is being formed and cured in the mold.
In summary, the present invention utilizes a mild steel mold element which is first masked to cover a selected surface so that the mold's surface will impress a desired pattern on the molded article. The mold's surface, with the masking material affixed thereto, is then textured as by sandblasting on the uncovered mold surface areas. The mask is then removed and the mold cleaned preparatory to plating the entire mold surface with a metal such as nickel. The plated mold surface is then employed to form a molded article 3~;279~4 with a plastic resin material such as a polyester resin composition or an epoxy resin composition which may, if desired, incorporate a pigment and a filler such as sand. In a preferred embodiment, the plastic material in plowable form is deposited in the mold and a support member such as, for example, a masonry unit, bracket, wire mesh or the like is placed on the plastic composition so that when the plastic composition is cured in an oven, the composition will harden and be bonded to the surface of the support member. The portion of the composition facing the mold surface will then take on the texture as defined by the masking material so that in the finished article, the exterior surface thereof will take on the desired pattern.
With the method of the present invention, it has been found that the resulting product gives a unique appearance to the molded surface. In particular, the pattern has been observed to vary as an observer moves past the surface and as the angle of incidence of lighting to which the surface is exposed is varied.
The foregoing and other advantages will become apparent as consideration is given to the following description taken in conjunction with the accompanying drawings, in which:
BRIEF DESCRIPTION OF THE DRAWINGS
FIGURE 1 is a schematic view of the method of :~Z;~7~
the present invention;
FIGURE 2 is a view in elevation with parts broken away illustrating another step of the present invention;
FIGURE 3 is a sectional view ion elevation of the molding step of the present invention; and FIGURE 4 is a side view in elevation in greatly enlarged detail of the mold surface after plating.
DETAILED DESCRIPTION OF THE INVENTION
The present invention is particularly useful in the field of coating masonry building units with unsaturated polyester resins such as disclosed in United States Patents 2,751,775, 3,328,231, 3,632,725, 4,031,289 and 4,329,822. As described in the first four of the aforementioned United States patents, relatively inexpensive masonry units can be provided with a coating surface to produce a decorative, serviceable surface thereon which does not require any finishing after a wall is erected with the blocks, United States Patent 4,329,822 describes types of support members that may also be provided with finished surfaces.
In order to enhance the decorative appearance of the coatings for such blocks or other materials, the present invention, as illustrated in Figure 1, modifies I
the mold surface of a mold member 10 by providing masking material 12 over selected portions of the surface area of the mold 10. Other portions such as at 14 of the mold surface remain uncovered. The mold 10 has the usual side flanges 16 surrounding the facing surface of the mold. With the masking material 12 in the desired positions on the mold surface of the mold 10, the uncovered area 14 then has its texture altered by directing a media such as sand forcefully there against by means of, for example, a nozzle 18.
While sandblasting is the preferred instrument for altering the texture of the unmasked surface area of the mold 10, it will be apparent to those skilled in this art that other texture altering techniques may be employed.
Turning now to Figure 2, according to the present invention, the masking material 12 is removed from the mold surface and then the mold is then thoroughly cleaned. Thereafter, the mold 10 is subjected to a plating step where a suitable metal is deposited on the surface of the mold including the sandblasting portion 14. While conventional electrolytic deposition plating may be employed, it has been found that the use of electroless plating is preferred so as to minimize the possibility of incorporating any impurities in the metal deposited on the mold which can later affect the resin coating to be I
molded in the mold 10.
A preferred metal for depositing on the mold surface is nickel which can be deposited with a hypo-phosphite solution. A number of commercial baths are available and are described in "Metal Finishing Guidebook and Director", Metals and Plastics Publications, Inc., Hackensack, New Jersey (updated yearly). The process and character of the electroless plating are discussed in Kirk-Othmer Encyclopedia of Chemical Technology, Third Edition, Volume 8, pages 738-750, John Wiley & Sons (1979).
After the mold 10 has been plated with the metal such as nickel, the mold 10 is then ready for forming a molded article.
With reference to Figure 3, a molding composition, which may include a resin, pigment, filler and plasticizer as described in the aforementioned patents, may be milled into plowable form such as a slurry and then deposited in the mold 10 and spread over the appropriate interior surfaces of the mold 10.
In one preferred embodiment, the masonry block 30 is inserted into the mold, and the weight of the block 30 will distribute the composition 28 to a substantially uniform extent over the subjacent surfaces of the mold 10. In many applications, it may be desirable to constitute the molding composition so that it is substantially in liquid form to facilitate even I
distribution over the mold surface. With the face of the block 30 inserted as illustrated in Figure 3 into the mold 10, the mold 10 and block 30 with the coating composition 28 there between are then subjected to heat to cure the molding composition 28. In this regard, the mold 10 is preferably of mild steel, that is, a steel that has a maximum carbon content no greater than 0.25%
as mild steel has superior heat conductivity as compared to stainless steel. Thus, with the mold 10 made of mild steel and plated with nickel as discussed above, a superior finish can be obtained on the cured resin 28 together with a faithful replication of the pattern resulting from the texturing of the bottom surface of the mold 10.
With reference now to Figure 4, there is illustrated in enlarged sectional detail a schematic representation of the effect of texturing with the flow of an abrasive or surface altering media and plating with the solution in the tank 20 to provide the metal coating 24 on the textured surface 26 of the mold 10.
It has been observed in viewing the molded surface of the composition 28 that at different angles of observation, the pattern obtained appears differently to an observer as the observer approaches and passes the molded article. This is believed due to the fact that the texturing of the metal while leaving a roughened surface as schematically illustrated in I
Figure 4, has the texture evened out somewhat by the subsequent metal plating step Thus, it has been observed that when one looked straight on at the pattern on the molded surface, the portion corresponding to the roughened area 14 of the mold 10 tends to blend into the other areas that have not been textured but that as the observer moves past and views the surface of the mold composition 28 at an angle, the pattern becomes strikingly evident. This effect has been noted to vary where the surface is on ground level and an observer moves 360 degrees about the surface creating exciting patterns and unusual color effects.
This novel effect has a very pleasing decorative appearance and the effect is particularly pronounced when the molding composition includes a colored pigment axing described the invention, it will be apparent to those skilled in this art that various modifications may be made thereto whatnot departing from the spirit and scope of this invention as defined in the appended claims.