Shino ware (志野焼,Shino-yaki) isJapanese pottery, usuallystoneware, originally fromMino Province, in present-dayGifu Prefecture,Japan. It emerged in the 16th century, but the use ofshino glaze is now widespread, both in Japan and abroad. It is identified by thick white glazes, red scorch marks, and a texture of small holes. Some experts^[who?] believe it should not be treated as distinct fromOribe ware but described as "white Oribe", with the pottery usually called just Oribe described as "green Oribe" instead.^{[1]: 8, 16}

The origin of the term "Shino" is uncertain. It may be derived from “Shiro”, the Japanese word for “white”. Or it may refer to the tea master Shino Soshin (1444–1523). Kuroda and Murayama^[1] refer to a text by Kanamori Tokusiu (1857) which states;

"Shino Soshin had a favorite white-glazed, 'shoe-shaped bowl, imported from South Asia, which he used as a tea bowl."^[1]

The first Shino ware was developed during theMomoyama period (1568–1600), inkilns in theMino andSeto areas. The glaze, composed primarily of ground localfeldspar and a small amount of local clay, produced a satiny white color. It was the first white glaze used in Japanese ceramics. Wares decorated with Shino were fired in theAnagama kilns used at that time.Anagama kilns were single-chambered kilns made from a trench in a hillside that was covered with an earthen roof. As the anagama kilns were replaced by the multi-chamberednoborigama kilns during the first decade of the 17th century, Shino was supplanted by theOribe ware glazes used in the newer kilns. Shino enjoyed a brief revival in the 19th century, but then faded into obscurity.

In the 1930s and 1940s, two Japanese potters,Toyozo Arakawa andHajime Katō, developed the first modern Shino glaze by studying Momoyama Shino pots. Working independently, in 1974, Virginia Wirt, a student ofWarren MacKenzie at the University of Minnesota, developed a glaze formula that also sought to imitate the historical exemplars. Her glaze, which addedsoda ash andspodumene to the base offeldspar andclays, was the first American Shino.

Shino has since become one of the more popular glazes in American pottery studios. Many variations have spawned from Wirt’s original formula. Although many different colorants and fluxes can be added, creating a wide range of effects, Shino glazes in America are all characterized by the use of soda ash and by a high ratio ofalumina tosilica. Under certain firing conditions, the soda ash causes carbon to be trapped in the glaze, creating the characteristic grey spots or patches on the glaze surface.

Like other Mino wares, the Shino style is based on olderSeto ware with changes to shape, decoration, and finish. Forms are usually squat and cylindrical, thick but lightweight. Dishes, bowls, and tea utensils are most common. Pieces can be grey, red, or white, painted with iron oxide or decorated with glaze.

Shino glaze (志野釉,Shino uwagusuri) is a generic term for a family ofpottery glazes. They tend to range in color from milky white to orange, sometimes with charcoal grey spotting, known as "carbon trap" which is the trapping of carbon in the glaze during the firing process.^[2] The term also refers toJapanese pottery made with the Shino glaze (seeShino-yaki).

Firings of Shino tend to be of lower temperature for a longer period of time, and then a slow cooling process. Due to Shino glazes' low fluxing temperatures, they should be applied before any other glazes. These conditions do not allow the glaze to melt fully, and the result is a thick glaze that often has a crawling pattern. If Shinos are applied on top of most glazes, the off-gassing from the underglaze will bubble through the Shino, resulting in undesirable pitting and other defects.

There is also a class of Shino glazes, called "Crawling" Shino, which are intentionally formulated to exhibit aglaze defect known as crawling. These Shinos form small, regular spots of bare clay all over the surface of the pot, some going so far as to cause the glaze to bead up on the surface of the clay.

• Britt, John. (2004/2007). "The Complete Guide to High Fire Glazes", Lark Books.ISBN 978-1-60059-216-4.
• Herschbach, Heidy. (1973). "Shino Glazes". Master's thesis, University of Puget Sound.
• Jenyns, Soame (1971).Japanese Pottery. London: Faber and Faber Ltd.ISBN 978-0-571-08709-9.LCCN 71594236.OCLC 164404.
• Richer, Lester (ed.). ‘’American Shino: The Glaze of a Thousand Faces’’, Babcock Galleries, 2001.ISBN 0-915829-71-1.
• Wilson, Richard L. (1995).Inside Japanese Ceramics: A Primer Of Materials, Techniques, And Traditions (1st ed.). New York: Weatherhill.ISBN 978-0-834-80346-6.LCCN 95022235.OCLC 32589793.

Media related toShino ware at Wikimedia Commons

• http://shino-oribe.co.jp
• Momoyama, Japanese Art in the Age of Grandeur, an exhibition catalog from The Metropolitan Museum of Art (fully available online as PDF), which contains material on Shino ware

• Japanese pottery
• Prefecture designated intangible cultural property

• Articles with short description
• Short description is different from Wikidata
• Articles containing Japanese-language text
• All articles with specifically marked weasel-worded phrases
• Articles with specifically marked weasel-worded phrases from May 2021
• Commons category link from Wikidata