Chipseal (alsochip seal orchip and seal orspray seal) is apavement surface treatment that combines one or more layers ofasphalt with one or more layers of fineaggregate. In the United States, chipseals are typically used on rural roads carrying lower traffic volumes, and the process is often referred to asasphaltic surface treatment. This type of surface has a variety of other names includingtar-seal[1] ortarseal,[2]tar and chip,sprayed seal[3]surface dressing,[4] or simplyseal.[5]
In Australia as well as New Zealand, chipseal roads are common, including usage on major highways.
Chipsealing is cheaper than resurfacing anasphalt concrete or aPortland cement concrete pavement, but not as long-lasting.
Chipseals are constructed by evenly distributing a thin base of hot tar,bitumen or asphalt onto an existing pavement and then embedding finely graded aggregate into it. The aggregate is evenly distributed over the hot seal spray, then rolled into the bitumen using heavy rubber tired rollers creating a paved surface. A chip-seal-surfaced pavement can optionally be sealed with a top layer, which is referred to as a fog seal or enrichment.
The introduction of polymer-modified bitumen and emulsion binder has increased chipseal's ability to preventcrack reflection and improve stone retention by improving the properties of the bitumen binder. Newer techniques use asphaltemulsion (a mixture of liquid asphalt,surfactant, and water) instead of asphalt. This has been shown to help reduce aggregate loss and reduce cost of installation, but can increase stripping (separation of the binder from the aggregate). It reduces emissions ofvolatile organic compounds (VOCs) due to the lower solvent content. New methods also utilize cross linking styrene acrylic polymers which also provide quality water resistance. Chips precoated with about one percent bitumen have been used successfully to minimize aggregate loss and to give the surface a black look.
It can keep good pavement in good condition by sealing out water, but provides no structural strength and will repair only minor cracks. While the small stones used as surface yield a relatively even surface without the edges of patches, it also results in a very rough surface that leads to louderrolling noise from automobile wheels.
Although chipseal is an effective low-cost way to repair roads, it has some drawbacks. Loosecrushed stone is often left on the surface, owing to underapplication of bitumen or overapplication of stone. If not removed, this can cause safety and environmental problems such as cracked windshields, chipped paint, loss-of-control crashes (especially for motorcyclists, bicyclists and small trucks), and deposition of foreign material into drainage courses. Therefore, it is very important to sweep the road after the emulsion sets. As mentioned earlier, this problem can be minimized by using chips precoated with bitumen. Overapplication of emulsion can lead tobleeding, a condition where the excess asphalt rises to the surface, creating a very smooth surface that is veryslippery when wet and bubbling in the hotter summer months. As cars drive over it the tires kick up this tarry substance on to the side of the car. It can only be cleaned off with a solvent remover or diesel fuel.
Chip seal products can be installed over gravel roads to eliminate the cost of grading, road roughness, dust, mud, and the cost of adding gravel lost from grading. Adding chip seal over gravel is about 25% of the price of resurfacing withasphalt, $170,000 for a 4-mile project done in Minnesota[6] compared to $760,000 had it been redone with asphalt. The surface lasts for 5–7 years. Patch work can be done with a bucket of tar sealer and more chip seal over the top. The chip seal matt surface handles thermal variation well and doesn't crack like asphalt roads. A thin penetrating emulsion primer (PEP) coat is usually applied over the gravel before the chip seal matt is applied.
The rough wearing surface of the chipseal generates moreroadway noise at any operating speed than do typical asphalt or concrete surfaces. These sound intensities increase with higher vehicle speeds.[7] There is a considerable range in acoustical intensities produced depending upon the specific tire tread design and its interaction with the roadway surface type.
The rough surface causes noticeable increases in vibration and rolling resistance for bicyclists, and increased tire wear in all types of tires.
Vehicle speed can affect the set up time with chipseal. Shortly after construction (depending on weather conditions) the set speed for chipseal is 10–15 miles per hour (16–24 km/h) for the first 24–48 hours after construction.[citation needed]