Foams are two-phasematerial systems where a gas is dispersed in a second, non-gaseous material, specifically, in whichgas cells are enclosed by a distinctliquid orsolid material.^{[1]: 6 [2]: 4 [3]} The foam "may contain more or less liquid [or solid] according to circumstances",^[1]: 6 although in the case of gas-liquid foams, the gas occupies most of the volume.^[2]: 4 The word derives from themedieval German and otherwise obsoleteveim, in reference to the "frothy head forming in the glass once the beer has been freshly poured" (cf.ausgefeimt).^[1]: 1

Theories regarding foam formation, structure, and properties—inphysics andphysical chemistry—differ somewhat between liquid and solid foams in that the former are dynamic (e.g., in their being "continuously deformed"), as a result of gas diffusing between cells, liquid draining from the foam into a bulk liquid, etc.^[1]: 1–2 Theories regarding liquid foams have as direct analogs theories regardingemulsions,^[1]: 3 two-phasematerial systems in which oneliquid is enclosed by another.^[4]

In most foams, the volume ofgas is large, with thin films of liquid or solid separating the regions of gas.^{[citation needed]} Abath sponge and thehead on a glass of beer are examples of foams; soap foams are also known assuds.^{[not verified in body]}

Solid foams can be closed-cell oropen-cell.^{[citation needed]} In closed-cell foam, the gas forms discrete pockets, each completely surrounded by the solid material. In open-cell foam, gas pockets connect to each other. A bath sponge is an example of an open-cell foam:^{[not verified in body]} water easily flows through the entire structure, displacing the air. Asleeping mat is an example of a product composed of closed-cell foam.^{[not verified in body]}

Foams are examples ofdispersed media.^{[not verified in body]} In general, gas is present, so it divides into gasbubbles of different sizes (i.e., the material ispolydisperse^{[not verified in body]})—separated by liquid regions that may form films, thinner and thinner when the liquid phase drains out of the systemfilms.^{[5][page needed]} When the principal scale is small, i.e., for a very fine foam, this dispersed medium can be considered a type ofcolloid.^{[not verified in body]}

Foam can also refer to something that is analogous to foam, such asquantum foam.^{[not verified in body]}

A foam is, in many cases, a multi-scale system.^{[citation needed]}

One scale is the bubble:material foams are typicallydisordered and have a variety of bubble sizes.^{[citation needed]} At larger sizes, the study of idealized foams is closely linked to the mathematical problems ofminimal surfaces and three-dimensionaltessellations, also calledhoneycombs.^{[citation needed]} TheWeaire–Phelan structure is reported in one primary philosophical source to be the best possible (optimal)unit cell of a perfectly ordered foam,^{[6][better source needed]} whilePlateau's laws describe how soap-films form structures in foams.^{[citation needed]}

At lower scale than the bubble is the thickness of the film formetastable foams, which can be considered a network of interconnected films calledlamellae.^{[citation needed]} Ideally, the lamellae connect in triads and radiate 120° outward from the connection points,^{[according to whom?]} known asPlateau borders.^{[citation needed]}

An even lower scale is the liquid–air interface at the surface of the film.^{[citation needed]} Most of the time this interface is stabilized by a layer ofamphiphilic structure, often made ofsurfactants, particles (Pickering emulsion), or more complex associations.^{[citation needed]}

Several conditions are needed to produce foam: there must be mechanical work,surface active components (surfactants) that reduce thesurface tension, and the formation of foam faster than its breakdown.To create foam,work (W) is needed to increase thesurface area (ΔA):

${\displaystyle W=\gamma \mathrm{\Delta }A}$ 

where γ is the surface tension.

One of the ways foam is created is through dispersion, where a large amount of gas is mixed with a liquid. A more specific method of dispersion involves injecting a gas through a hole in a solid into a liquid. If this process is completed very slowly, then one bubble can be emitted from the orifice at a time as shown in the picture below.

One of the theories for determining the separation time is shown below; however, while this theory produces theoretical data that matches the experimental data, detachment due to capillarity is accepted as a better explanation.

Thebuoyancy force acts to raise the bubble, which is

${\displaystyle F_b=Vg({\rho }_2-{\rho }_1)}$ 

where${\displaystyle V}$  is the volume of the bubble,${\displaystyle g}$  is the acceleration due to gravity, and ρ₁ is the density of the gas ρ₂ is the density of the liquid. The force working against the buoyancy force is thesurface tension force, which is

${\displaystyle F_s=2r\pi \gamma }$ ,

where γ is the surface tension, and${\displaystyle r}$  is the radius of the orifice.As more air is pushed into the bubble, the buoyancy force grows quicker than the surface tension force. Thus, detachment occurs when the buoyancy force is large enough to overcome the surface tension force.

${\displaystyle Vg({\rho }_2-{\rho }_1)>2r\pi \gamma }$ 

In addition, if the bubble is treated as a sphere with a radius of${\displaystyle R}$  and the volume${\displaystyle V}$  is substituted in to the equation above, separation occurs at the moment when

${\displaystyle R^3=\frac{3r\gamma }{2g({\rho }_2-{\rho }_1)}}$ 

Examining this phenomenon from a capillarity viewpoint for a bubble that is being formed very slowly, it can be assumed that the pressure${\displaystyle p}$  inside is constant everywhere. The hydrostatic pressure in the liquid is designated by${\displaystyle p_0}$ . The change in pressure across the interface from gas to liquid is equal to the capillary pressure; hence,

${\displaystyle p-p_0=\gamma \left(\frac{1}{R_1}+\frac{1}{R_2}\right)}$ 

where R₁ and R₂ are the radii of curvature and are set as positive. At the stem of the bubble, R₃ and R₄ are the radii of curvature also treated as positive. Here the hydrostatic pressure in the liquid has to take into account z, the distance from the top to the stem of the bubble. The new hydrostatic pressure at the stem of the bubble isp₀(ρ₁ − ρ₂)z. The hydrostatic pressure balances the capillary pressure, which is shown below:

${\displaystyle p-p_0-({\rho }_2-{\rho }_1)gz=\gamma \left(\frac{1}{R_3}+\frac{1}{R_4}\right)}$ 

Finally, the difference in the top and bottom pressure equals the change in hydrostatic pressure:

${\displaystyle ({\rho }_2-{\rho }_1)gz=\gamma \left(\frac{1}{R_1}+\frac{1}{R_2}-\frac{1}{R_3}-\frac{1}{R_4}\right)}$ 

At the stem of the bubble, the shape of the bubble is nearly cylindrical; consequently, either R₃ or R₄ is large while the other radius of curvature is small. As the stem of the bubble grows in length, it becomes more unstable as one of the radius grows and the other shrinks. At a certain point, the vertical length of the stem exceeds the circumference of the stem and due to the buoyancy forces the bubble separates and the process repeats.^[7]

The stabilization of foam is caused byvan der Waals forces between the molecules in the foam,electrical double layers created bydipolar surfactants, and theMarangoni effect, which acts as a restoring force to the lamellae.

The Marangoni effect depends on the liquid that is foaming being impure. Generally, surfactants in the solution decrease the surface tension. The surfactants also clump together on the surface and form a layer as shown below.

For the Marangoni effect to occur, the foam must be indented as shown in the first picture. This indentation increases the local surface area. Surfactants have a larger diffusion time than the bulk of the solution—so the surfactants are less concentrated in the indentation.

Also, surface stretching makes the surface tension of the indented spot greater than the surrounding area. Consequentially—since the diffusion time for the surfactants is large—the Marangoni effect has time to take place. The difference in surface tension creates a gradient, which instigates fluid flow from areas of lower surface tension to areas of higher surface tension. The second picture shows the film at equilibrium after the Marangoni effect has taken place.^[8]

Curing a foam solidifies it, making it indefinitely stable at STP.^[9]

Witold Rybczynski and Jacques Hadamard developed an equation to calculate the velocity of bubbles that rise in foam with the assumption that the bubbles are spherical with a radius${\displaystyle r}$ .

${\displaystyle u=\frac{2g{r}^2}{9{\eta }_2}({\rho }_2-{\rho }_1)\left(\frac{3{\eta }_1+3{\eta }_2}{3{\eta }_1+2{\eta }_2}\right)}$ 

with velocity in units of centimeters per second. ρ₁ and ρ₂ is the density for a gas and liquid respectively in units of g/cm³ and ῃ₁ and ῃ₂ is the dynamic viscosity of the gas and liquid respectively in units of g/cm·s and g is the acceleration of gravity in units of cm/s².

However, since the density and viscosity of a liquid is much greater than the gas, the density and viscosity of the gas can be neglected, which yields the new equation for velocity of bubbles rising as:

${\displaystyle u=\frac{g{r}^2}{3{\eta }_2}({\rho }_2)}$ 

However, through experiments it has been shown that a more accurate model for bubbles rising is:

${\displaystyle u=\frac{2g{r}^2}{9{\eta }_2}({\rho }_2-{\rho }_1)}$ 

Deviations are due to theMarangoni effect and capillary pressure, which affect the assumption that the bubbles are spherical.For laplace pressure of a curved gas liquid interface, the two principal radii of curvature at a point are R₁ and R₂.^[10] With a curved interface, the pressure in one phase is greater than the pressure in another phase. The capillary pressure P_c is given by the equation of:

${\displaystyle P_c=\gamma \left(\frac{1}{R_1}+\frac{1}{R_2}\right)}$ ,

where${\displaystyle \gamma }$  is the surface tension. The bubble shown below is a gas (phase 1) in a liquid (phase 2) and point A designates the top of the bubble while point B designates the bottom of the bubble.

At the top of the bubble at point A, the pressure in the liquid is assumed to be p₀ as well as in the gas. At the bottom of the bubble at point B, the hydrostatic pressure is:

${\displaystyle P_B,1=p_0+g{\rho }_{1}z}$ 

${\displaystyle P_B,2=p_0+g{\rho }_{2}z}$ 

where ρ₁ and ρ₂ is the density for a gas and liquid respectively. The difference in hydrostatic pressure at the top of the bubble is 0, while the difference in hydrostatic pressure at the bottom of the bubble across the interface isgz(ρ₂ − ρ₁). Assuming that the radii of curvature at point A are equal and denoted by R_A and that the radii of curvature at point B are equal and denoted by R_B, then the difference in capillary pressure between point A and point B is:

${\displaystyle P_c=2\gamma \left(\frac{1}{R_A}-\frac{1}{R_B}\right)}$ 

At equilibrium, the difference in capillary pressure must be balanced by the difference in hydrostatic pressure. Hence,

${\displaystyle gz({\rho }_2-{\rho }_1)=2\gamma \left(\frac{1}{R_A}-\frac{1}{R_B}\right)}$ 

Since, the density of the gas is less than the density of the liquid the left hand side of the equation is always positive. Therefore, the inverse of R_A must be larger than the R_B. Meaning that from the top of the bubble to the bottom of the bubble the radius of curvature increases. Therefore, without neglecting gravity the bubbles cannot be spherical. In addition, as z increases, this causes the difference in R_A and R_B too, which means the bubble deviates more from its shape the larger it grows.^[7]

Foam destabilization occurs for several reasons. First,gravitation causes drainage of liquid to the foam base, which Rybczynski and Hadamar include in their theory; however, foam also destabilizes due toosmotic pressure causes drainage from the lamellas to the Plateau borders due to internal concentration differences in the foam, andLaplace pressure causes diffusion of gas from small to large bubbles due to pressure difference. In addition, films can break underdisjoining pressure, These effects can lead to rearrangement of the foam structure at scales larger than the bubbles, which may be individual (T1 process) or collective (even of the "avalanche" type).

Solid foams, both open-cell and closed-cell, are considered as a sub-class of cellular structures. They often have lower nodal connectivity^[jargon] as compared to other cellular structures like honeycombs and truss lattices, and thus, their failure mechanism is dominated by bending of members. Low nodal connectivity and the resulting failure mechanism ultimately lead to their lower mechanical strength and stiffness compared to honeycombs and truss lattices.^[11][12]

The strength of foams can be impacted by the density, the material used, and the arrangement of the cellular structure (open vs closed and pore isotropy).^{[citation needed]} To characterize themechanical properties of foams, compressivestress-strain curves are used to measure their strength and ability to absorb energy since this is an important factor in foam based technologies.^{[citation needed]}

Forelastomeric cellular solids, as the foam is compressed, first it behaves elastically as the cell walls bend, then as the cell walls buckle there is yielding and breakdown of the material until finally the cell walls crush together and the material ruptures.^[13] This is seen in a stress-strain curve as a steep linear elastic regime, a linear regime with a shallow slope after yielding (plateau stress), and an exponentially increasing regime. The stiffness of the material can be calculated from the linear elastic regime^[14] where themodulus for open celled foams can be defined by the equation:

${\displaystyle {\left(\frac{E^{\ast }}{E_s}\right)}_f=C_f{\left(\frac{{\rho }^{\ast }}{{\rho }_s}\right)}^2}$ 

where${\displaystyle E_s}$  is the modulus of the solid component,${\displaystyle E^{\ast }}$  is the modulus of the honeycomb structure,${\displaystyle C_f}$  is a constant having a value close to one,${\displaystyle {\rho }^{\ast }}$  is the density of the honeycomb structure, and${\displaystyle {\rho }_s}$  is the density of the solid. The elastic modulus for closed cell foams can be described similarly by:

${\displaystyle {\left(\frac{E^{\ast }}{E_s}\right)}_f=C_f{\left(\frac{{\rho }^{\ast }}{{\rho }_s}\right)}^3}$ 

where the only difference is the exponent in the density dependence. However, in real materials, a closed-cell foam has more material at the cell edges which makes it more closely follow the equation for open-cell foams.^[15] The ratio of the density of the honeycomb structure compared with the solid structure has a large impact on the modulus of the material. Overall, foam strength increases with density of the cell and stiffness of the matrix material.

Another important property which can be deduced from the stress strain curve is the energy that the foam is able to absorb. The area under the curve (specified to be before rapid densification at the peak stress), represents the energy in the foam in units of energy per unit volume. The maximum energy stored by the foam prior to rupture is described by the equation:^[13]

${\displaystyle \frac{W_{max}}{E_s}=0.05{\left(\frac{{\rho }^{\ast }}{{\rho }_s}\right)}^2\left[0.975-1.4\left(\frac{{\rho }^{\ast }}{{\rho }_s}\right)\right]}$ 

This equation is derived from assuming an idealized foam with engineering approximations from experimental results. Most energy absorption occurs at the plateau stress region after the steep linear elastic regime.^{[citation needed]}

Theisotropy of the cellular structure and the absorption of fluids can also have an impact on the mechanical properties of a foam. If there is anisotropy present, then the materials response to stress will be directionally dependent, and thus the stress-strain curve, modulus, and energy absorption will vary depending on the direction of applied force.^[16] Also, open-cell structures which have connected pores can allow water or other liquids to flow through the structure, which can also affect the rigidity and energy absorption capabilities.^[17]

Liquid foams can be used infire retardant foam, such as those that are used in extinguishing fires, especiallyoil fires.^{[citation needed]}

The dough of leavenedbread has traditionally been understood as a closed-cell foam—yeast causing bread to rise via tiny bubbles of gas that become the breadpores—where the cells do not connect with each other. Cutting the dough releases the gas in the bubbles that are cut, but the gas in the rest of the dough cannot escape.^{[citation needed]} When dough is allowed to rise too far, it becomes an open-cell foam, in which the gas pockets are connected; cutting the dough surface at that point would cause a large volume of gas to escape, and the dough to collapse.^{[citation needed][18]} Recent research has indicated that the pore structure in bread is 99% interconnected into one large vacuole, thus the closed-cell foam of the moist dough is transformed into an open cell solid foam in the bread.^{[19][non-primary source needed]}

The unique property of gas-liquid foams having very high specific surface area is exploited in the chemical processes offroth flotation andfoam fractionation.^{[citation needed]}

Foam depopulation or foaming is a means of mass killing farm animals by spraying foam over a large area to obstruct breathing and ultimately cause suffocation.^[20][21] It is usually used to attempt to stop disease spread.^[22]

Solid foams are a class of lightweight cellular engineering materials. These foams are typically classified into two types based on their pore structure: open-cell-structured foams (also known asreticulated foams) and closed-cell foams. At high enough cell resolutions, any type can be treated as continuous or "continuum" materials and are referred to ascellular solids,^[23] with predictable mechanical properties.

Open-cell foams can be used to filter air. For example, a foam embedded with catalyst has been shown to catalytically convertformaldehyde to benign substances when formaldehyde polluted air passes through the open cell structure.^[24]

Open-cell-structured foams contain pores that are connected to each other and form an interconnected network that is relatively soft. Open-cell foams fill with whatever gas surrounds them. If filled with air, a relatively good insulator results, but, if the open cells fill with water, insulation properties would be reduced. Recent studies have put the focus on studying the properties of open-cell foams as an insulator material. Wheat gluten/TEOSbio-foams have been produced, showing similar insulator properties as for those foams obtained from oil-based resources.^[25] Foam rubber is a type of open-cell foam.

Closed-cell foams do not have interconnected pores. The closed-cell foams normally have higher compressive strength due to their structures. However, closed-cell foams are also, in general more dense, require more material, and as a consequence are more expensive to produce. The closed cells can be filled with a specialized gas to provide improved insulation. The closed-cell structure foams have higher dimensional stability, low moisture absorption coefficients, and higher strength compared to open-cell-structured foams. All types of foam are widely used as core material insandwich-structured composite materials.

The earliest known engineering use of cellular solids is with wood, which in its dry form is a closed-cell foam composed of lignin, cellulose, and air. From the early 20th century, various types of specially manufactured solid foams came into use. The lowdensity of these foams makes them excellent as thermalinsulators and flotation devices and their lightness and compressibility make them ideal as packing materials and stuffings.

An example of the use of azodicarbonamide^[26] as ablowing agent is found in the manufacture ofvinyl (PVC) andEVA-PE foams, where it plays a role in the formation of air bubbles by breaking down into gas at high temperature.^[27][28][29]

The random or "stochastic" geometry of these foams makes them good for energy absorption, as well. In the late 20th century to early 21st century, new manufacturing techniques have allowed for geometry that results in excellent strength and stiffness per weight. These new materials are typically referred to as engineered cellular solids.^[23]

Integral skin foam, also known asself-skin foam, is a type of foam with a high-density skin and a low-density core. It can be formed in anopen-mold process or aclosed-mold process. In the open-mold process, two reactive components are mixed and poured into an open mold. The mold is then closed and the mixture is allowed to expand and cure. Examples of items produced using this process includearm rests,baby seats,shoe soles, andmattresses. The closed-mold process, more commonly known asreaction injection molding (RIM), injects the mixed components into a closed mold under high pressures.^[30]

•  
  Micrograph oftemper (memory) foam
•  
  Silicone foampenetration seal^{[clarification needed]}
•  
  Industrial CT scanning of a foam ball^{[clarification needed]}
•  
  Polystyrene foamcushioning
•  
  Foamedaluminum^{[clarification needed]}

• Aluminium foam sandwich
• Ballistic foam
• Chaotic bubble
• Defoamer
• Foam glass
• Metal foam
• Nanofoam
• Sea foam
• Reversibly assembled cellular composite materials
• Foam party
• Soft matter

• Weaire, D.L.; Hutzler, Stefan (1999).The Physics of Foams. Oxford, England: Oxford University Press.ISBN 0198510977. RetrievedAugust 30, 2024. A modern treatise almost exclusively focused on liquid foams.
• Gibson, Lorna J.; Ashby, Michael F. (1997).Cellular Solids: Structure and Properties. Cambridge Solid State Science. Cambridge, England: Cambridge University Press.ISBN 0521499119. RetrievedAugust 30, 2024. A treatise termed a classic by Weaire & Hutzler (1999), on solid foams, and the reason they limit their focus to liquid foams.
• Cantat, I; Cohen-Addad, S; Elias, F; Graner, F; Höhler, R; Pitois, O; Rouyer, F; Saint-Jalmes, A (2013).Foams: Structure and Dynamics. Oxford, England: Oxford University Press.ISBN 978-0199662890. RetrievedAugust 30, 2024. Note, this source also focuses on liquid foams.
• Thomas Hipke, Günther Lange, René Poss: Taschenbuch für Aluminiumschäume. Aluminium-Verlag, Düsseldorf 2007,ISBN 978-3-87017-285-5.
• Hannelore Dittmar-Ilgen: Metalle lernen schwimmen. In: Dies.: Wie der Kork-Krümel ans Weinglas kommt. Hirzel, Stuttgart 2006,ISBN 978-3-7776-1440-3, S. 74.

• Andrew M. Kraynik, Douglas A. Reinelt, Frank van SwolStructure of random monodisperse foam
• Moriarty, Philip (2010)."Foam Physics".Sixty Symbols.Brady Haran for theUniversity of Nottingham.