| Names | |
|---|---|
| IUPAC name Poly(oxy-1,4-butanediyloxycarbonyl-1,4-phenylenecarbonyl) | |
| Identifiers | |
| ChemSpider |
|
| Properties[1] | |
| (C12H12O4)n | |
| Melting point | 223 °C (433 °F; 496 K) |
Except where otherwise noted, data are given for materials in theirstandard state (at 25 °C [77 °F], 100 kPa). | |
Polybutylene terephthalate (PBT) is athermoplastic engineering polymer that is used as aninsulator in theelectrical andelectronics industries.[2] It is a thermoplastic (semi-)crystallinepolymer, and a type ofpolyester. PBT resists solvents, shrinks very little during forming, is mechanically strong, is heat-resistant up to150 °C (or200 °C withglass-fibre reinforcement), and can be treated withflame retardants to make it noncombustible. It was developed by Britain'sImperial Chemical Industries (ICI).[3]
PBT is closely related to other thermoplastic polyesters.[2] Compared to PET (polyethylene terephthalate), PBT has slightly lower strength and rigidity, slightly better impact resistance, and a slightly lower glass transition temperature. PBT and PET are sensitive to hot water above60 °C (140 °F). PBT and PET needUV protection if used outdoors, and most grades of these polyesters are flammable, although additives can be used to improve both UV and flammability properties.
PBT is produced by the polymerization of1,4-butanediol andterephthalic acid.[4][5]
Polybutylene terephthalate is used for housings in electrical engineering, but also in automotive construction as plug connectors and in households for example in showerheads or irons. It is also found processed into toothbrush fibers and false eyelashes and is used in thekeycaps[6][7] of some high-end computer keyboards because the texture is highly resistant to wear and the plastic is less vulnerable to ultraviolet degradation[8] and discoloration than the conventionalABS alternative.
PBT can also be made into yarn. This has a natural stretch similar toLycra and can be incorporated into sportswear. Due to its chlorine resistance it is commonly found in swimwear. Further, recent studies have shown that PBT has superior UV properties to PET based fabrics such as T400.[9]
PBT, especially glass fibre grades, can be effectively fire-retarded with halogen-free products. Phosphorus-based flame retardant systems are used in thesefire-safe polymers and are based onaluminium diethyl phosphinate and synergists. They are designed to meetUL 94 flammability tests as well as Glow Wire Ignition Tests (GWIT), Glow Wire Flammability Test (GWFI) andComparative Tracking Index (CTI). Main applications are in the electrical and electronics (E&E) industry.