From Wikipedia, the free encyclopedia
(Redirected fromPearlitic)
Lamellar structure of ferrite and cementite
For theamorphous volcanic glass, seeperlite.
icon
This articleneeds additional citations forverification. Please helpimprove this article byadding citations to reliable sources. Unsourced material may be challenged and removed.
Find sources: "Pearlite" – news ·newspapers ·books ·scholar ·JSTOR
(November 2010) (Learn how and when to remove this message)
Steels
Phases
Microstructures
Classes
Other iron-based materials
SEM micrograph of etched pearlite, 2000X.
Atom probe tomography of pearlite. The red dots indicate the positions of carbon atoms. Iron atoms are not shown. The nanotube is shown for size reference.
Pearlite occurs at theeutectoid of the iron-carbon phase diagram (near the lower left).

Pearlite is atwo-phased,lamellar (or layered) structure composed of alternating layers offerrite (87.5 wt%) andcementite (12.5 wt%) that occurs in somesteels andcast irons. During slow cooling of an iron-carbon alloy, pearlite forms by aeutectoid reaction asaustenite cools below 727 °C (1,341 °F) (the eutectoid temperature). Pearlite is a microstructure occurring in many common grades of steels.

Composition

[edit]

The eutectoid composition of austenite is approximately 0.8%carbon; steel with less carbon content (hypoeutectoid steel) will contain a corresponding proportion of relatively pure ferrite crystallites that do not participate in the eutectoid reaction and cannot transform into pearlite. Likewise steels with higher carbon content (hypereutectoid steels) will form cementite before reaching the eutectoid point. The proportion of ferrite and cementite forming above the eutectoid point can be calculated from the iron/iron—carbide equilibrium phase diagram using thelever rule.

Steels with pearlitic (eutectoid composition) or near-pearlitic microstructure (near-eutectoid composition) can be drawn into thin wires. Such wires, often bundled into ropes, are commercially used as piano wires, ropes for suspension bridges, and as steel cord for tire reinforcement. High degrees of wire drawing (logarithmic strain above 3) leads to pearlitic wires with yield strengths of several gigapascals. It makes pearlite one of the strongest structural bulk materials on earth.[1]Some hypereutectoid pearlitic steel wires, when cold wire drawn to true (logarithmic) strains above 5, can even show a maximal tensile strength above 6 GPa (870 ksi).[2] Although pearlite is used in many engineering applications, the origin of its extreme strength is not well understood. It has been recently shown that cold wire drawing not only strengthens pearlite by refining the lamellae structure, but also simultaneously causes partial chemical decomposition of cementite, associated with an increased carbon content of the ferrite phase, deformation induced lattice defects in ferrite lamellae,[3] and even a structural transition from crystalline to amorphous cementite. The deformation-induced decomposition and microstructural change of cementite is closely related to several other phenomena such as a strong redistribution of carbon and other alloy elements likesilicon andmanganese in both the cementite and the ferrite phase; a variation of the deformation accommodation at the phase interfaces due to a change in the carbon concentration gradient at the interfaces; and mechanical alloying.[4]

Pearlite was first identified byHenry Clifton Sorby and initially named sorbite, however the similarity of microstructure tonacre and especially the optical effect caused by the scale of the structure made the alternative name more popular.

Pearlite forms as a result of the cooperative growth of ferrite and cementite during the decomposition of austenite. The morphology of pearlite is significantly affected by the cooling rate and coiling temperature. At lower coiling temperatures, pearlite forms with finer lamellar spacing, resulting in enhanced mechanical properties due to the finer distribution of ferrite and cementite layers. Conversely, at higher coiling temperatures, pearlite forms with coarser lamellae, and a smaller amount of pearlite is observed as coarse cementite particles tend to dominate the structure. The carbon diffusion during the formation of pearlite, just ahead of the growth front, is critical in determining the thickness of the lamellae and, consequently, the strength of the steel.[5]

Bainite is a similar structure with lamellae much smaller than thewavelength ofvisible light and thus lacks this pearlescent appearance. It is prepared by more rapid cooling. Unlike pearlite, whose formation involves the diffusion of all atoms, bainite grows by a displacive transformation mechanism.

The transformation of pearlite to austenite takes place at lower critical temperature of 723 °C (1,333 °F). At this temperature pearlite changes to austenite because of nucleation process.

Eutectoid steel

[edit]

Eutectoid steel can in principle be transformed completely into pearlite; hypoeutectoid steels can also be completely pearlitic if transformed at a temperature below the normal eutectoid.[6][7] Pearlite can be hard and strong but is not particularlytough. It can be wear-resistant because of a strong lamellar network of ferrite and cementite. Examples of applications includecutting tools, high strengthwires,knives,chisels, andnails.

References

[edit]
  1. ^Raabe, D.; Choi, P. P.; Li, Y. J.; Kostka, A.; Sauvage, X.; Lecouturier, F.; Hono, K.; Kirchheim, R.; Pippan, R.; Embury, D. (2010),Metallic composites processed via extreme deformation - Toward the limits of strength in bulk materials, vol. 35, MRS Bulletin, p. 982.
  2. ^Li, Y.; Raabe, D.; Herbig, M. J.; Choi, P.P.; Goto, S.; Kostka, A.; Yarita, H.; Bochers, C.; Kirchheim, R. (2014), "Segregation stabilizes nanocrystalline bulk steel with near theoretical strength",Physical Review Letters,113 (10) 106104,Bibcode:2014PhRvL.113j6104L,doi:10.1103/PhysRevLett.113.106104,PMID 25238372.
  3. ^Chen, Y. Z.; Csiszár, G.; Cizek, J.; Westerkamp, S.; Borchers, C.; Ungár, T.; Goto, S.; Liu, F.; Kirchheim, R. (2013-04-10). "Defects in Carbon-Rich Ferrite of Cold-Drawn Pearlitic Steel Wires".Metallurgical and Materials Transactions A.44 (8):3882–3889.Bibcode:2013MMTA...44.3882C.doi:10.1007/s11661-013-1723-x.ISSN 1073-5623.S2CID 135839236.
  4. ^Li, Y.J.; Choi, P.P.; Borchers, C.; Westerkamp, S.; Goto, S.; Raabe, D.; Kirchheim, R. (2011), "Atomic-scale mechanisms of deformation-induced cementite decomposition in pearlite",Acta Materialia,59 (10): 3965,Bibcode:2011AcMat..59.3965L,doi:10.1016/j.actamat.2011.03.022.
  5. ^Alvarenga HD, Van Steenberge N, Sietsma J, Terryn H (Feb 2017). "The Kinetics of Formation and Decomposition of Austenite in Relation to Carbide Morphology".Metall Mater Trans A.48:828–840.doi:10.1007/s11661-016-3874-z.
  6. ^Alvarenga HD, Van de Putte T, Van Steenberge N, Sietsma J, Terryn H (Apr 2009). "Influence of Carbide Morphology and Microstructure on the Kinetics of Superficial Decarburization of C-Mn Steels".Metall Mater Trans A.46:123–133.doi:10.1007/s11661-014-2600-y.S2CID 136871961.
  7. ^"Eutectoid Steel - Engineering Dictionary - EngNet". Archived fromthe original on 2011-07-10. Retrieved2010-11-15.

Further reading

[edit]

External links

[edit]
  • Media related toPearlite at Wikimedia Commons
Retrieved from "https://en.wikipedia.org/w/index.php?title=Pearlite&oldid=1319428772"